WO2009085679A1 - Composite nonwoven fibrous webs and methods of making and using the same - Google Patents
Composite nonwoven fibrous webs and methods of making and using the same Download PDFInfo
- Publication number
- WO2009085679A1 WO2009085679A1 PCT/US2008/086759 US2008086759W WO2009085679A1 WO 2009085679 A1 WO2009085679 A1 WO 2009085679A1 US 2008086759 W US2008086759 W US 2008086759W WO 2009085679 A1 WO2009085679 A1 WO 2009085679A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- fibers
- sub
- web
- population
- micrometer
- Prior art date
Abstract
Description
Claims