WO2009064594A2 - Hybrid three-dimensional woven/laminated struts for composite structural applications - Google Patents
Hybrid three-dimensional woven/laminated struts for composite structural applications Download PDFInfo
- Publication number
- WO2009064594A2 WO2009064594A2 PCT/US2008/080941 US2008080941W WO2009064594A2 WO 2009064594 A2 WO2009064594 A2 WO 2009064594A2 US 2008080941 W US2008080941 W US 2008080941W WO 2009064594 A2 WO2009064594 A2 WO 2009064594A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- woven
- layers
- preform
- central portion
- independent
- Prior art date
Abstract
Description
Claims