WO2008066914A1 - Polyisobutylenes and process for making same - Google Patents
Polyisobutylenes and process for making same Download PDFInfo
- Publication number
- WO2008066914A1 WO2008066914A1 PCT/US2007/024674 US2007024674W WO2008066914A1 WO 2008066914 A1 WO2008066914 A1 WO 2008066914A1 US 2007024674 W US2007024674 W US 2007024674W WO 2008066914 A1 WO2008066914 A1 WO 2008066914A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- primary
- terminated polyisobutylene
- compound
- terminated
- integer
- Prior art date
Abstract
Description
Claims