WO2008007737A1 - Tuyau coudé et son procédé de fabrication - Google Patents
Tuyau coudé et son procédé de fabrication Download PDFInfo
- Publication number
- WO2008007737A1 WO2008007737A1 PCT/JP2007/063904 JP2007063904W WO2008007737A1 WO 2008007737 A1 WO2008007737 A1 WO 2008007737A1 JP 2007063904 W JP2007063904 W JP 2007063904W WO 2008007737 A1 WO2008007737 A1 WO 2008007737A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- less
- bend pipe
- strength
- toughness
- weld
- Prior art date
Description
Claims