WO2006134860A1 - 合わせガラス - Google Patents
合わせガラス Download PDFInfo
- Publication number
- WO2006134860A1 WO2006134860A1 PCT/JP2006/311733 JP2006311733W WO2006134860A1 WO 2006134860 A1 WO2006134860 A1 WO 2006134860A1 JP 2006311733 W JP2006311733 W JP 2006311733W WO 2006134860 A1 WO2006134860 A1 WO 2006134860A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- glass
- laminated glass
- glass plate
- laminated
- film
- Prior art date
Abstract
Description
Claims