WO2006026379A1 - Coating compositions having improved stability - Google Patents
Coating compositions having improved stability Download PDFInfo
- Publication number
- WO2006026379A1 WO2006026379A1 PCT/US2005/030303 US2005030303W WO2006026379A1 WO 2006026379 A1 WO2006026379 A1 WO 2006026379A1 US 2005030303 W US2005030303 W US 2005030303W WO 2006026379 A1 WO2006026379 A1 WO 2006026379A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- grams
- acid
- meth
- vinyl
- monomer
- Prior art date
Abstract
Description
Claims