WO2005108639A1 - Sputter targets and methods of forming same by rotary axial forging - Google Patents
Sputter targets and methods of forming same by rotary axial forging Download PDFInfo
- Publication number
- WO2005108639A1 WO2005108639A1 PCT/US2005/015839 US2005015839W WO2005108639A1 WO 2005108639 A1 WO2005108639 A1 WO 2005108639A1 US 2005015839 W US2005015839 W US 2005015839W WO 2005108639 A1 WO2005108639 A1 WO 2005108639A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- metal plate
- target
- texture
- sputter target
- preform
- Prior art date
Abstract
Description
Claims