WO2005104223A1

WO2005104223A1 - Process for the singulation of integrated devices in thin semiconductor chips

Info

Publication number: WO2005104223A1
Application number: PCT/EP2005/051694
Authority: WO
Inventors: Anna Ponza; Riccardo Depetro; Pietro Montanini
Original assignee: Stmicroelectronics S.R.L.
Priority date: 2004-04-20
Filing date: 2005-04-18
Publication date: 2005-11-03
Also published as: WO2005104223A8; CN100474563C; US20070141809A1; ITTO20040244A1; EP1745505A1; US7605015B2; CN1985369A; EP1745505B1; EP2261969A1

Abstract

A process for the fabrication of an integrated device in a semiconductor chip envisages: forming a semiconductor layer (5') partially suspended above a semiconductor substrate (2) and constrained to the substrate (2) by temporary anchorages (10, 15'); dividing the layer (5') into a plurality of portions (13) laterally separated from one another; and removing the temporary anchorages (10, 15'; 38), in order to free the portions (13).

Description

PROCESS FOR THE SINGULATION OF INTEGRATED DEVICES IN THIN SEMICONDUCTOR CHIPS

TECHNICAL FIELD The present invention relates to a process for the fabrication of integrated devices in small-thickness semiconductor chips.

BACKGROUND ART As is known, customary techniques of fabrication of semiconductor integrated devices (typically micro- electromechanical circuits or devices) envisage providing a plurality of units identical to one another on the same semiconductor wafer. At the end of the process, the so-called "singling" is carried out, i.e., the wafer is divided into a plurality of portions (dice) , each of which contains a respective device. Hereinafter, the portions obtained by cutting of a semiconductor wafer will be indicated for reasons of simplicity by the term "chips". Normally, a saw is used to cut the wafer.

Prior to singling, the wafer is normally thinned out, so as to reduce as much as possible the thickness of the chips containing the finished devices. This operation enables various advantages to be achieved. In the first place, thin chips have a lower thermal capacitance and a higher thermal conductivity and hence enable a better heat dispersion, which is particularly important when the integrated devices in the chips dissipate high power levels. Furthermore, minimizing the dimensions of the chips in general enables a considerable reduction in the overall dimensions of the devices after packaging in the external protective structures, especially in the case of devices with a number of stacked chips. In some devices, moreover, the current can flow also between the front and rear faces of the chip (vertical-current-flow devices) . In this case, the reduction of the thickness also involves a reduction in the electrical resistance and lower energy consumption.

Currently, semiconductor wafers are usually thinned out mechanically by grinding. In this way, however, the thickness cannot be reduced beyond a certain limit, because the wafer must in any case maintain a sufficient mechanical resistance both during thinning-out and in the final machining steps . In particular, the mechanical stresses in the grinding step and in the cutting step can bring about microcracks in the wafer, and the likelihood of damage is all the greater the smaller the thickness achieved. In practice, the final thickness of the wafer can hardly fall below 100 μ without a reduction in the yield of the process.

DISCLOSURE OF INVENTION The purpose of the present invention is to provide a process for the fabrication of integrated devices which will be free from the drawbacks described above. According to the present invention a process is provided for the fabrication of integrated devices in small-thickness semiconductor chips, as defined in Claim 1.

BRIEF DESCRIPTION OF THE DRAWINGS

For a better understanding of the invention, there are now described some embodiments, purely by way of non-limiting example and with reference to the attached drawings, in which:

- Figures 1-3 are cross-sectional views through a semiconductor wafer of the successive steps of fabrication according to a first embodiment of the present invention;

- Figure 4 is a top plan view of the semiconductor wafer illustrated in Figure 3, in a subsequent machining step;

- Figure 5 is a cross-sectional view of the wafer of Figure 4, taken according to the line V-V of Figure 4;

- Figure 6 is a cross-sectional view of the wafer of Figure 4, taken according to the line VI-VI of Figure 4;

- Figure 7 is the same view as that of Figure 5, in a subsequent step of the process; - Figure 8 is the same view as that of Figure 6, in a subsequent step of the process;

- Figures 9 and 10 show the same view as that of Figure 7 in subsequent machining steps;

- Figure 11 is a cross-sectional view of the wafer of Figure 10, taken according to the line XI-XI of Figure 10;

- Figure 12 shows the same view as that of Figure 10, in a subsequent machining step;

- Figure 13 is a side view of a chip obtained starting from the wafer of Figure 12;

- Figures 14 and 15 are top plan views of a second semiconductor wafer and a third semiconductor wafer, in intermediate steps of fabrication of processes according to a second embodiment and a third embodiment, respectively, of the present invention; and

- Figure 16-18 are cross-sectional views through a semiconductor wafer in successive machining steps according to a fourth embodiment of the process according to the present invention.

BEST MODE FOR CARRYING OUT THE INVENTION

As illustrated in Figures 1-3, a semiconductor wafer 1 comprising a substrate 2, for example made of monocrystalline silicon, is subjected to initial steps of fabrication as described also in the European patent application No. EP-A- 1 324 382, filed in the name of the present applicant.

In particular, (see Figure 1) after a first mask 3 has been formed, the wafer 1 is etched anisotropically, and rectilinear deep trenches 4 are dug. The deep trenches 4 are adjacent and parallel to one another and extend in a direction perpendicular to the plane of the drawing. The first mask 3 is then removed, and an epitaxial layer 5 is grown, which closes the deep trenches 4 forming buried cavities 4', completely surrounded by silicon (Figure 2) . During the epitaxial growth, the silicon is deposited in part also inside the deep trenches 4, before they are closed, and hence the buried cavities 4' have a substantially elliptical cross section, with the major axis perpendicular to the surface 5a free from the epitaxial layer 5.

A thermal step of annealing is then carried out, in which the cross section of the buried cavities 4' is modified (Figure 3) . In practice, when the wafer 1 is heated in deoxidizing atmosphere, the surface silicon atoms that surround the buried cavities 4' migrate and tend to assume a minimum-energy configuration, as explained in the article "A New Substrate Engineering for the Formation of Empty Space in Silicon (ESS) Induced by Silicon Surface Migration" by T. Sato, N. Aoki, I. Mizushima, and Y. Tsunashima, IEDM 1999, pp. 517-520. For example, if the wafer 1 is heated at 1150° for 5 hours, the buried cavities 4^f assume the shape of parallel buried channels 8, having a substantially circular cross section and separated from one another by silicon diaphragms 10. The width of the diaphragms 10 is determined both by the initial distance between immediately adjacent deep trenches 3, and by the duration of the annealing step. At the end of the annealing step, the channels 8 are overlaid by a structural silicon layer 5' having a thickness S that is determined by the duration of the step of epitaxial growth and by the duration of the annealing step. The thickness S is preferably comprised between 1 μm and 50 μm and, still more preferably, between 10 μ and 20 μm. Furthermore, the structural layer 5' is partially suspended above the substrate 2 and is constrained to the substrate 2 itself by means of the diaphragms 10, which function as temporary anchorages.

As illustrated in Figures 4-6, first and second service trenches 11, 12 are then dug, which have a depth equal at least to the thickness S of the structural layer 5' so as to reach the buried channels 8, and are preferably slightly deeper. In practice, then, the channels 8 are accessible from the outside through at least some of the service trenches 11, 12, when the latter are free. The first service trenches 11 are parallel to the channels 8, whereas the second service trenches 12 are substantially perpendicular thereto. Furthermore, the first and second service trenches 11, 12 intersect one another forming a grid and laterally delimit portions 13 of the structural layer 5' , which are then to be separated by the substrate 2 to form respective semiconductor chips. In this step of the process, the portions 13 are laterally isolated from one another and are connected to the substrate 2 by means of the diaphragms 10. Furthermore, the portions 13 are partially suspended above the substrate 2.

Next, the wafer 1 is thermally oxidized for a first controlled time interval, as illustrated in Figures 7 and 8. In this step, the service trenches 11, 12 are filled, and the walls of the channels 8 are coated with an oxide layer 15. Since the oxide layer 15 grows both towards the inside of the channels 8 and within the silicon, the duration of the step of thermal oxidation, i.e., the first time interval, is controlled in such a way that the diaphragms 10 are completely oxidized, without however occluding the channels 8.

After removing the oxide from the surface of the wafer 1 (Figure 9) , standard manufacturing steps are performed to provide a respective device 16 in each of the portions 13 of the structural layer 5' . In Figure 9, the devices 16 have been schematically illustrated using electrical symbols of active and passive components. In practice, the devices 16 can be of any type that may be integrated in a semiconductor chip, such as for example micro-electromechanical circuits or structures. The corresponding fabrication steps can be standard steps of fabrication of any type of semiconductor devices and may comprise, for example, masking, implantation, diffusion, etching, deposition and growth of layers, metallizations, etc. After the devices 16 have been completed, the wafer 1 is protected with a second photoresist mask 17, which leaves exposed only the first and second service trenches 11, 12, which are still filled with oxide.

The wafer 1 is then etched in a bath or in vapours of hydrofluoric acid HF for a second controlled time interval . During this step, initially the first and second trenches 11, 12 are freed from the oxide, which is selectively removed, laterally isolating once again the portions 13 of the structural layer 5' . Then, also the buried channels 8 are made accessible from the outside through at least the second service trenches 12. Consequently, the hydrofluoric acid HF can reach and etch the oxide layer (designated by 15' in Figures 10 and 11 is a residual oxide layer, which remains after etching) . The service trenches 11, 12 hence perform the dual function of delimiting laterally the portions 13 of the structural layer 5' and of providing an access from the outside to the buried channels 8 for etching of the oxide layer 15' .

The step of etching with hydrofluoric acid HF is interrupted before the residual oxide layer 15' is completely removed and, in particular, before the portions 13 of the structural layer 5' are separated from the substrate 2. In practice, in this step, the residual oxide layer 15' functions as a temporary anchorage for the portions 13 of the structural layer 5' , but it is weakened with respect to the silicon diaphragms 10.

After steps of testing of the devices 16, the portions 13 of the structural layer 5' are separated from the substrate 2 by a mechanical action (Figure 12) . More precisely, in succession on each portion 13 of the structural layer 5' a force F is applied, which is directed perpendicularly to the surface of the wafer 1 and is has a sufficient intensity to overcome the mechanical resistance of the residual oxide layer 15' . The residual oxide layer 15' fails where it is weaker, i.e., substantially along a median plane of the buried channels 8 parallel to the surface of the wafer 1. Preferably, together with the force F, a torque T is applied, which facilitates failure of the residual oxide layer 15' . The mechanical action necessary for separating the portions 13 from the substrate 2 can be obtained conveniently using vacuum pipettes 18, of the type commonly used for picking up the chips singled out after the operations of traditional cutting (pick-and-place operation) .

Chips 20 are thus obtained, each of which contains a respective device 16, as illustrated in Figure 13. The chips 20 have substantially the thickness S determined by the steps of epitaxial growth and of annealing of the silicon. The chips 20 are finally packaged in purposely provided protective structures equipped with contact pins, according to conventional process steps (not illustrated herein) .

Advantageously, then, it is possible to obtain chips of extremely contained thickness, even less than 10 μm, without increasing appreciably the risks of microcracks in the wafer during its fabrication. Instead, the yield can be increased.

In traditional processes, in fact, the portions of the initial wafer which are then to form the chips must be arranged at a distance apart from one another by an amount sufficient to enable passage of the cutting saw without any damage to the integrated devices, in practice at least 60-100 μ . According to the invention, instead, the service trenches are sufficient to guarantee lateral separation between the portions which are then to form the chips and can have a width even of just 1 μm.

The density is hence much greater, and it is possible to increase the number of chips per wafer. The present invention overcomes another limitation of traditional processes, which are tied to rectilinear cutting paths and consequently exclusively enable square or, at the most, rectangular chips to be obtained. According to the process described, instead, the shape of the chips is defined by the service trenches, which can extend in any pattern. Consequently, also the chips can have any appropriate shape. For example, Figures 14 and 15 illustrate two alternative embodiments of the process. In the embodiment of Figure 14, in a wafer 25 service trenches 26 are dug, which delimit hexagonal chips 27. Figure 15 shows, instead, a wafer 30, in which service trenches 31 have been dug, which delimit C- shaped chips 32.

According to a further embodiment of the invention, illustrated in Figures 16-18, in which parts that are the same as the ones already illustrated are designated by the same reference numbers, in a wafer 35 some adjacent channels 8 are separated by diaphragms 36 having a width greater than that of the diaphragms 10. During the step of thermal oxidation (Figure 17) , in which oxide layers 37 are formed, the diaphragms 36 are thinned out, but not completely oxidized, so as to form thin temporary silicon anchorages 38. In the subsequent etching step with hydrofluoric acid HF, which is performed after the devices 16 have been made, the oxide layer 37 is removed completely, and the portions 13 of the structural layer 5' remain constrained to the substrate 2 through the temporary anchorages 38 (Figure 18) „ In the final step of singling of the chips, the temporary anchorages 38 are broken by applying the force F and, possibly, the torque T, as explained previously.

In this way, a smaller precision in the control of the duration of the etching with hydrofluoric acid HF is required.

It should be noted that the temporary-anchorage silicon structures may have any suitable shape so as to present a controlled mechanical resistance (for example, they could be pillars) .

Finally, it is clear that modifications and variations can be made to the process described, without departing from the scope of the present invention as defined in the annexed claims .

Claims

1. A process for the fabrication of integrated devices in a semiconductor chip, comprising the steps of: - forming a semiconductor layer (5') partially suspended above a semiconductor substrate (2) and constrained to said substrate (2) by temporary anchorages (10, 15'; 38); - dividing said layer (5') into a plurality of portions (13; 27; 32) laterally separated from one another; and - removing said temporary anchorages (10, 15'; 38) in order to free said portions (13; 27; 32) .

2. The process according to Claim 1, comprising the step of weakening said temporary anchorages (10, 15'; 38).

3. The process according to Claim 2, wherein the step of weakening comprises oxidizing at least partially said temporary anchorages (10, 15'; 38).

4. The process according to Claim 3, wherein the step of weakening comprises chemical etching oxidized portions (15) of said temporary anchorages (10, 15'; 38).

5. The process according to Claim 4, wherein said step of etching comprises using hydrofluoric acid (HF) and has a controlled duration.

6. The process according to any one of the foregoing claims, wherein said step of removing comprises breaking said temporary anchorages (10, 15' ; 38) by means of a mechanical action (F, T) .

7. The process according to any one of the foregoing claims, wherein said step of dividing comprises digging service trenches (11, 12; 26; 31) delimiting said portions (13; 27; 32) and having a depth at least equal to a thickness (S) of said layer (5' ) .

8. The process according to any one of the foregoing claims, wherein said step of forming said layer (5' ) comprises making a plurality of buried cavities (4', 8).

9. The process according to Claim 8 as appended to Claim 7, wherein said buried cavities (4', 8) are accessible from outside through at least some of said service trenches (11, 12; 26; 31) .

10. The process according to Claim 8 as appended to Claim 3, wherein said step of oxidizing is interrupted before said buried cavities (4', 8) are obstructed.

11. The process according to any one of Claims 8-10, wherein said step of making buried cavities (4', 8) comprises:

- opening a plurality of adjacent deep trenches (4) within said substrate (2) ;

- growing an epitaxial layer (5) so as to close said deep trenches (4) ; and

- carrying out an annealing step.