WO2005065634A1 - Dental abrasive system - Google Patents
Dental abrasive system Download PDFInfo
- Publication number
- WO2005065634A1 WO2005065634A1 PCT/GB2005/000011 GB2005000011W WO2005065634A1 WO 2005065634 A1 WO2005065634 A1 WO 2005065634A1 GB 2005000011 W GB2005000011 W GB 2005000011W WO 2005065634 A1 WO2005065634 A1 WO 2005065634A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- silica
- abrasive
- aluminosilicate
- abrasive system
- range
- Prior art date
Abstract
Description
Claims