WO2004069404A1 - Particulate water absorbent containing water absorbent resin as a main component - Google Patents
Particulate water absorbent containing water absorbent resin as a main component Download PDFInfo
- Publication number
- WO2004069404A1 WO2004069404A1 PCT/JP2004/001358 JP2004001358W WO2004069404A1 WO 2004069404 A1 WO2004069404 A1 WO 2004069404A1 JP 2004001358 W JP2004001358 W JP 2004001358W WO 2004069404 A1 WO2004069404 A1 WO 2004069404A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- water absorbent
- particulate water
- salt concentration
- aqueous solution
- absorbent resin
- Prior art date
Abstract
Description
Claims