WO2004062704A1 - Biomedical foams - Google Patents
Biomedical foams Download PDFInfo
- Publication number
- WO2004062704A1 WO2004062704A1 PCT/NL2004/000010 NL2004000010W WO2004062704A1 WO 2004062704 A1 WO2004062704 A1 WO 2004062704A1 NL 2004000010 W NL2004000010 W NL 2004000010W WO 2004062704 A1 WO2004062704 A1 WO 2004062704A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- formula
- polymer
- foam
- segment
- phase
- Prior art date
Abstract
Description
Claims