WO2004029155A2 - Curable thermoplastic elastomeric blend, method of manufacture, and use thereof - Google Patents
Curable thermoplastic elastomeric blend, method of manufacture, and use thereof Download PDFInfo
- Publication number
- WO2004029155A2 WO2004029155A2 PCT/US2003/031230 US0331230W WO2004029155A2 WO 2004029155 A2 WO2004029155 A2 WO 2004029155A2 US 0331230 W US0331230 W US 0331230W WO 2004029155 A2 WO2004029155 A2 WO 2004029155A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- acrylate
- rubber
- copolymer
- meth
- cross
- Prior art date
Abstract
Description
Claims