WO2002094922A1 - Polyolefin coated steel pipes - Google Patents
Polyolefin coated steel pipes Download PDFInfo
- Publication number
- WO2002094922A1 WO2002094922A1 PCT/EP2002/005547 EP0205547W WO02094922A1 WO 2002094922 A1 WO2002094922 A1 WO 2002094922A1 EP 0205547 W EP0205547 W EP 0205547W WO 02094922 A1 WO02094922 A1 WO 02094922A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyolefin
- steel pipes
- coating
- propylene
- coated steel
- Prior art date
Abstract
Description
Claims