WO2002066702A1 - Process for treating multi-metal articles - Google Patents
Process for treating multi-metal articles Download PDFInfo
- Publication number
- WO2002066702A1 WO2002066702A1 PCT/US2002/004529 US0204529W WO02066702A1 WO 2002066702 A1 WO2002066702 A1 WO 2002066702A1 US 0204529 W US0204529 W US 0204529W WO 02066702 A1 WO02066702 A1 WO 02066702A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- zinc
- ion
- phosphate
- composition
- ceramic composite
- Prior art date
Abstract
Description
Claims