WO2002003445A1 - Method and apparatus for forming a silicon wafer with a denuded zone - Google Patents
Method and apparatus for forming a silicon wafer with a denuded zone Download PDFInfo
- Publication number
- WO2002003445A1 WO2002003445A1 PCT/US2001/015502 US0115502W WO0203445A1 WO 2002003445 A1 WO2002003445 A1 WO 2002003445A1 US 0115502 W US0115502 W US 0115502W WO 0203445 A1 WO0203445 A1 WO 0203445A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- wafer
- temperature
- set forth
- cooling rate
- sec
- Prior art date
Abstract
Description
Claims