WO2000064831A1 - Liquid curable resin composition and cured products - Google Patents
Liquid curable resin composition and cured products Download PDFInfo
- Publication number
- WO2000064831A1 WO2000064831A1 PCT/NL2000/000260 NL0000260W WO0064831A1 WO 2000064831 A1 WO2000064831 A1 WO 2000064831A1 NL 0000260 W NL0000260 W NL 0000260W WO 0064831 A1 WO0064831 A1 WO 0064831A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- meth
- optical fiber
- composition
- acrylate
- oligomer
- Prior art date
Abstract
Description
Claims