WO2000059634A1 - Katalytisches element - Google Patents
Katalytisches element Download PDFInfo
- Publication number
- WO2000059634A1 WO2000059634A1 PCT/DE2000/000797 DE0000797W WO0059634A1 WO 2000059634 A1 WO2000059634 A1 WO 2000059634A1 DE 0000797 W DE0000797 W DE 0000797W WO 0059634 A1 WO0059634 A1 WO 0059634A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- catalytic element
- catalytic
- throttle
- throttle layer
- Prior art date
Abstract
Description
Claims