WO1999034252A1 - Polyamic acid composition, liquid crystal aligning film, and liquid crystal display element - Google Patents
Polyamic acid composition, liquid crystal aligning film, and liquid crystal display element Download PDFInfo
- Publication number
- WO1999034252A1 WO1999034252A1 PCT/JP1998/005547 JP9805547W WO9934252A1 WO 1999034252 A1 WO1999034252 A1 WO 1999034252A1 JP 9805547 W JP9805547 W JP 9805547W WO 9934252 A1 WO9934252 A1 WO 9934252A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyamic acid
- liquid crystal
- independently
- bis
- tetracarboxylic dianhydride
- Prior art date
Abstract
Description
Claims