WO1999015211A1 - Improved hydrogel for tissue engineering - Google Patents
Improved hydrogel for tissue engineering Download PDFInfo
- Publication number
- WO1999015211A1 WO1999015211A1 PCT/US1998/019417 US9819417W WO9915211A1 WO 1999015211 A1 WO1999015211 A1 WO 1999015211A1 US 9819417 W US9819417 W US 9819417W WO 9915211 A1 WO9915211 A1 WO 9915211A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- hydrogel
- composition
- alginate
- animal
- cells
- Prior art date
Abstract
Description
Claims