WO1997007274A1 - Continuous filament nonwoven fabric - Google Patents
Continuous filament nonwoven fabric Download PDFInfo
- Publication number
- WO1997007274A1 WO1997007274A1 PCT/US1996/012732 US9612732W WO9707274A1 WO 1997007274 A1 WO1997007274 A1 WO 1997007274A1 US 9612732 W US9612732 W US 9612732W WO 9707274 A1 WO9707274 A1 WO 9707274A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- blend
- filaments
- weight
- percent
- flow rate
- Prior art date
Abstract
Description
Claims