WO1992007674A1 - Casting of metal objects - Google Patents
Casting of metal objects Download PDFInfo
- Publication number
- WO1992007674A1 WO1992007674A1 PCT/AU1991/000510 AU9100510W WO9207674A1 WO 1992007674 A1 WO1992007674 A1 WO 1992007674A1 AU 9100510 W AU9100510 W AU 9100510W WO 9207674 A1 WO9207674 A1 WO 9207674A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mould
- casting
- metal
- cavity
- accordance
- Prior art date
Abstract
Description
Claims