US20180057922A1 - Material for thermal spraying and production method thereof, method for thermal spraying, and product of thermal spraying - Google Patents
Material for thermal spraying and production method thereof, method for thermal spraying, and product of thermal spraying Download PDFInfo
- Publication number
- US20180057922A1 US20180057922A1 US15/553,119 US201615553119A US2018057922A1 US 20180057922 A1 US20180057922 A1 US 20180057922A1 US 201615553119 A US201615553119 A US 201615553119A US 2018057922 A1 US2018057922 A1 US 2018057922A1
- Authority
- US
- United States
- Prior art keywords
- thermal spraying
- fine particles
- particles
- pulverized
- over
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- 238000007751 thermal spraying Methods 0.000 title claims abstract description 266
- 239000000463 material Substances 0.000 title claims abstract description 255
- 238000004519 manufacturing process Methods 0.000 title claims abstract description 85
- 238000000034 method Methods 0.000 title claims description 32
- 239000011347 resin Substances 0.000 claims abstract description 129
- 229920005989 resin Polymers 0.000 claims abstract description 129
- 239000010419 fine particle Substances 0.000 claims abstract description 122
- 239000002245 particle Substances 0.000 claims abstract description 109
- 239000011802 pulverized particle Substances 0.000 claims abstract description 105
- 239000007788 liquid Substances 0.000 claims abstract description 66
- 238000010298 pulverizing process Methods 0.000 claims abstract description 21
- 239000000919 ceramic Substances 0.000 claims abstract description 12
- 239000000203 mixture Substances 0.000 claims abstract description 12
- 229910052751 metal Inorganic materials 0.000 claims abstract description 9
- 239000002184 metal Substances 0.000 claims abstract description 9
- 238000003756 stirring Methods 0.000 claims description 91
- 239000000126 substance Substances 0.000 claims description 87
- 238000000576 coating method Methods 0.000 claims description 30
- 239000000758 substrate Substances 0.000 claims description 28
- 239000011248 coating agent Substances 0.000 claims description 27
- 238000001816 cooling Methods 0.000 claims description 21
- 239000002994 raw material Substances 0.000 claims description 6
- 238000000790 scattering method Methods 0.000 claims description 5
- 238000002296 dynamic light scattering Methods 0.000 claims description 4
- 238000004064 recycling Methods 0.000 abstract description 6
- 239000002105 nanoparticle Substances 0.000 description 16
- 239000002002 slurry Substances 0.000 description 15
- 239000007789 gas Substances 0.000 description 14
- MCMNRKCIXSYSNV-UHFFFAOYSA-N Zirconium dioxide Chemical compound O=[Zr]=O MCMNRKCIXSYSNV-UHFFFAOYSA-N 0.000 description 11
- 239000003795 chemical substances by application Substances 0.000 description 11
- 230000007423 decrease Effects 0.000 description 7
- 239000006185 dispersion Substances 0.000 description 7
- 239000000843 powder Substances 0.000 description 7
- 239000002904 solvent Substances 0.000 description 7
- XKRFYHLGVUSROY-UHFFFAOYSA-N Argon Chemical compound [Ar] XKRFYHLGVUSROY-UHFFFAOYSA-N 0.000 description 6
- 239000000047 product Substances 0.000 description 6
- 238000002156 mixing Methods 0.000 description 5
- 238000005507 spraying Methods 0.000 description 5
- 230000008859 change Effects 0.000 description 4
- 239000002826 coolant Substances 0.000 description 4
- 238000009826 distribution Methods 0.000 description 4
- 238000005516 engineering process Methods 0.000 description 4
- 238000005194 fractionation Methods 0.000 description 4
- 230000008569 process Effects 0.000 description 4
- 238000010079 rubber tapping Methods 0.000 description 4
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 4
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 description 3
- 229910052786 argon Inorganic materials 0.000 description 3
- 239000012298 atmosphere Substances 0.000 description 3
- 230000008901 benefit Effects 0.000 description 3
- 238000011049 filling Methods 0.000 description 3
- 238000002844 melting Methods 0.000 description 3
- 230000008018 melting Effects 0.000 description 3
- 238000007873 sieving Methods 0.000 description 3
- 229920001187 thermosetting polymer Polymers 0.000 description 3
- 239000004925 Acrylic resin Substances 0.000 description 2
- 229920000178 Acrylic resin Polymers 0.000 description 2
- UQSXHKLRYXJYBZ-UHFFFAOYSA-N Iron oxide Chemical compound [Fe]=O UQSXHKLRYXJYBZ-UHFFFAOYSA-N 0.000 description 2
- XLOMVQKBTHCTTD-UHFFFAOYSA-N Zinc monoxide Chemical compound [Zn]=O XLOMVQKBTHCTTD-UHFFFAOYSA-N 0.000 description 2
- 238000004378 air conditioning Methods 0.000 description 2
- QVQLCTNNEUAWMS-UHFFFAOYSA-N barium oxide Chemical compound [Ba]=O QVQLCTNNEUAWMS-UHFFFAOYSA-N 0.000 description 2
- 229910002113 barium titanate Inorganic materials 0.000 description 2
- 230000015572 biosynthetic process Effects 0.000 description 2
- 239000003054 catalyst Substances 0.000 description 2
- 238000005229 chemical vapour deposition Methods 0.000 description 2
- 239000011247 coating layer Substances 0.000 description 2
- 229910052681 coesite Inorganic materials 0.000 description 2
- 229910052906 cristobalite Inorganic materials 0.000 description 2
- 230000003247 decreasing effect Effects 0.000 description 2
- 238000010438 heat treatment Methods 0.000 description 2
- AMWRITDGCCNYAT-UHFFFAOYSA-L hydroxy(oxo)manganese;manganese Chemical compound [Mn].O[Mn]=O.O[Mn]=O AMWRITDGCCNYAT-UHFFFAOYSA-L 0.000 description 2
- 239000012770 industrial material Substances 0.000 description 2
- 238000009413 insulation Methods 0.000 description 2
- 238000005259 measurement Methods 0.000 description 2
- 239000002923 metal particle Substances 0.000 description 2
- 150000002739 metals Chemical class 0.000 description 2
- 230000004048 modification Effects 0.000 description 2
- 238000012986 modification Methods 0.000 description 2
- 239000002114 nanocomposite Substances 0.000 description 2
- 239000007783 nanoporous material Substances 0.000 description 2
- -1 silicon carbide Chemical class 0.000 description 2
- 239000000377 silicon dioxide Substances 0.000 description 2
- NDVLTYZPCACLMA-UHFFFAOYSA-N silver oxide Chemical compound [O-2].[Ag+].[Ag+] NDVLTYZPCACLMA-UHFFFAOYSA-N 0.000 description 2
- 229910052682 stishovite Inorganic materials 0.000 description 2
- 229910052905 tridymite Inorganic materials 0.000 description 2
- 229910017083 AlN Inorganic materials 0.000 description 1
- PIGFYZPCRLYGLF-UHFFFAOYSA-N Aluminum nitride Chemical compound [Al]#N PIGFYZPCRLYGLF-UHFFFAOYSA-N 0.000 description 1
- RYGMFSIKBFXOCR-UHFFFAOYSA-N Copper Chemical compound [Cu] RYGMFSIKBFXOCR-UHFFFAOYSA-N 0.000 description 1
- QPLDLSVMHZLSFG-UHFFFAOYSA-N Copper oxide Chemical compound [Cu]=O QPLDLSVMHZLSFG-UHFFFAOYSA-N 0.000 description 1
- 239000005751 Copper oxide Substances 0.000 description 1
- LFQSCWFLJHTTHZ-UHFFFAOYSA-N Ethanol Chemical compound CCO LFQSCWFLJHTTHZ-UHFFFAOYSA-N 0.000 description 1
- 240000007594 Oryza sativa Species 0.000 description 1
- 235000007164 Oryza sativa Nutrition 0.000 description 1
- 229910020279 Pb(Zr, Ti)O3 Inorganic materials 0.000 description 1
- 229910052581 Si3N4 Inorganic materials 0.000 description 1
- GWEVSGVZZGPLCZ-UHFFFAOYSA-N Titan oxide Chemical compound O=[Ti]=O GWEVSGVZZGPLCZ-UHFFFAOYSA-N 0.000 description 1
- WGLPBDUCMAPZCE-UHFFFAOYSA-N Trioxochromium Chemical compound O=[Cr](=O)=O WGLPBDUCMAPZCE-UHFFFAOYSA-N 0.000 description 1
- XHCLAFWTIXFWPH-UHFFFAOYSA-N [O-2].[O-2].[O-2].[O-2].[O-2].[V+5].[V+5] Chemical compound [O-2].[O-2].[O-2].[O-2].[O-2].[V+5].[V+5] XHCLAFWTIXFWPH-UHFFFAOYSA-N 0.000 description 1
- 239000000654 additive Substances 0.000 description 1
- 230000000996 additive effect Effects 0.000 description 1
- 239000000443 aerosol Substances 0.000 description 1
- 239000000956 alloy Substances 0.000 description 1
- 229910045601 alloy Inorganic materials 0.000 description 1
- 229910052782 aluminium Inorganic materials 0.000 description 1
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 description 1
- JRPBQTZRNDNNOP-UHFFFAOYSA-N barium titanate Chemical compound [Ba+2].[Ba+2].[O-][Ti]([O-])([O-])[O-] JRPBQTZRNDNNOP-UHFFFAOYSA-N 0.000 description 1
- 238000007664 blowing Methods 0.000 description 1
- BRPQOXSCLDDYGP-UHFFFAOYSA-N calcium oxide Chemical compound [O-2].[Ca+2] BRPQOXSCLDDYGP-UHFFFAOYSA-N 0.000 description 1
- 239000000292 calcium oxide Substances 0.000 description 1
- ODINCKMPIJJUCX-UHFFFAOYSA-N calcium oxide Inorganic materials [Ca]=O ODINCKMPIJJUCX-UHFFFAOYSA-N 0.000 description 1
- 239000000969 carrier Substances 0.000 description 1
- 229910010293 ceramic material Inorganic materials 0.000 description 1
- VNNRSPGTAMTISX-UHFFFAOYSA-N chromium nickel Chemical compound [Cr].[Ni] VNNRSPGTAMTISX-UHFFFAOYSA-N 0.000 description 1
- 229910000428 cobalt oxide Inorganic materials 0.000 description 1
- IVMYJDGYRUAWML-UHFFFAOYSA-N cobalt(ii) oxide Chemical compound [Co]=O IVMYJDGYRUAWML-UHFFFAOYSA-N 0.000 description 1
- 150000001875 compounds Chemical class 0.000 description 1
- 238000011109 contamination Methods 0.000 description 1
- 238000010924 continuous production Methods 0.000 description 1
- 229910052802 copper Inorganic materials 0.000 description 1
- 239000010949 copper Substances 0.000 description 1
- 229910000431 copper oxide Inorganic materials 0.000 description 1
- 230000001419 dependent effect Effects 0.000 description 1
- 238000000151 deposition Methods 0.000 description 1
- AJNVQOSZGJRYEI-UHFFFAOYSA-N digallium;oxygen(2-) Chemical compound [O-2].[O-2].[O-2].[Ga+3].[Ga+3] AJNVQOSZGJRYEI-UHFFFAOYSA-N 0.000 description 1
- KZHJGOXRZJKJNY-UHFFFAOYSA-N dioxosilane;oxo(oxoalumanyloxy)alumane Chemical compound O=[Si]=O.O=[Si]=O.O=[Al]O[Al]=O.O=[Al]O[Al]=O.O=[Al]O[Al]=O KZHJGOXRZJKJNY-UHFFFAOYSA-N 0.000 description 1
- 239000003822 epoxy resin Substances 0.000 description 1
- 229910052839 forsterite Inorganic materials 0.000 description 1
- 229910001195 gallium oxide Inorganic materials 0.000 description 1
- YBMRDBCBODYGJE-UHFFFAOYSA-N germanium oxide Inorganic materials O=[Ge]=O YBMRDBCBODYGJE-UHFFFAOYSA-N 0.000 description 1
- 230000005484 gravity Effects 0.000 description 1
- 239000001307 helium Substances 0.000 description 1
- 229910052734 helium Inorganic materials 0.000 description 1
- SWQJXJOGLNCZEY-UHFFFAOYSA-N helium atom Chemical compound [He] SWQJXJOGLNCZEY-UHFFFAOYSA-N 0.000 description 1
- 230000006872 improvement Effects 0.000 description 1
- 238000009776 industrial production Methods 0.000 description 1
- 239000000976 ink Substances 0.000 description 1
- 239000003350 kerosene Substances 0.000 description 1
- 239000010410 layer Substances 0.000 description 1
- HFGPZNIAWCZYJU-UHFFFAOYSA-N lead zirconate titanate Chemical compound [O-2].[O-2].[O-2].[O-2].[O-2].[Ti+4].[Zr+4].[Pb+2] HFGPZNIAWCZYJU-UHFFFAOYSA-N 0.000 description 1
- 238000003754 machining Methods 0.000 description 1
- HCWCAKKEBCNQJP-UHFFFAOYSA-N magnesium orthosilicate Chemical compound [Mg+2].[Mg+2].[O-][Si]([O-])([O-])[O-] HCWCAKKEBCNQJP-UHFFFAOYSA-N 0.000 description 1
- 239000000395 magnesium oxide Substances 0.000 description 1
- CPLXHLVBOLITMK-UHFFFAOYSA-N magnesium oxide Inorganic materials [Mg]=O CPLXHLVBOLITMK-UHFFFAOYSA-N 0.000 description 1
- AXZKOIWUVFPNLO-UHFFFAOYSA-N magnesium;oxygen(2-) Chemical compound [O-2].[Mg+2] AXZKOIWUVFPNLO-UHFFFAOYSA-N 0.000 description 1
- 150000001247 metal acetylides Chemical class 0.000 description 1
- 229910052863 mullite Inorganic materials 0.000 description 1
- 229910001120 nichrome Inorganic materials 0.000 description 1
- 229910000480 nickel oxide Inorganic materials 0.000 description 1
- 150000004767 nitrides Chemical class 0.000 description 1
- 238000005457 optimization Methods 0.000 description 1
- 239000011368 organic material Substances 0.000 description 1
- TWNQGVIAIRXVLR-UHFFFAOYSA-N oxo(oxoalumanyloxy)alumane Chemical compound O=[Al]O[Al]=O TWNQGVIAIRXVLR-UHFFFAOYSA-N 0.000 description 1
- SIWVEOZUMHYXCS-UHFFFAOYSA-N oxo(oxoyttriooxy)yttrium Chemical compound O=[Y]O[Y]=O SIWVEOZUMHYXCS-UHFFFAOYSA-N 0.000 description 1
- PVADDRMAFCOOPC-UHFFFAOYSA-N oxogermanium Chemical compound [Ge]=O PVADDRMAFCOOPC-UHFFFAOYSA-N 0.000 description 1
- GNRSAWUEBMWBQH-UHFFFAOYSA-N oxonickel Chemical compound [Ni]=O GNRSAWUEBMWBQH-UHFFFAOYSA-N 0.000 description 1
- RVTZCBVAJQQJTK-UHFFFAOYSA-N oxygen(2-);zirconium(4+) Chemical compound [O-2].[O-2].[Zr+4] RVTZCBVAJQQJTK-UHFFFAOYSA-N 0.000 description 1
- 239000012188 paraffin wax Substances 0.000 description 1
- 239000004033 plastic Substances 0.000 description 1
- 229920000647 polyepoxide Polymers 0.000 description 1
- 229920000728 polyester Polymers 0.000 description 1
- 239000011148 porous material Substances 0.000 description 1
- 239000002244 precipitate Substances 0.000 description 1
- 235000009566 rice Nutrition 0.000 description 1
- 239000004065 semiconductor Substances 0.000 description 1
- 238000010008 shearing Methods 0.000 description 1
- HBMJWWWQQXIZIP-UHFFFAOYSA-N silicon carbide Chemical compound [Si+]#[C-] HBMJWWWQQXIZIP-UHFFFAOYSA-N 0.000 description 1
- 229910010271 silicon carbide Inorganic materials 0.000 description 1
- HQVNEWCFYHHQES-UHFFFAOYSA-N silicon nitride Chemical compound N12[Si]34N5[Si]62N3[Si]51N64 HQVNEWCFYHHQES-UHFFFAOYSA-N 0.000 description 1
- 229910052814 silicon oxide Inorganic materials 0.000 description 1
- 229910001923 silver oxide Inorganic materials 0.000 description 1
- 238000005245 sintering Methods 0.000 description 1
- 239000012720 thermal barrier coating Substances 0.000 description 1
- 230000009974 thixotropic effect Effects 0.000 description 1
- OGIDPMRJRNCKJF-UHFFFAOYSA-N titanium oxide Inorganic materials [Ti]=O OGIDPMRJRNCKJF-UHFFFAOYSA-N 0.000 description 1
- ZNOKGRXACCSDPY-UHFFFAOYSA-N tungsten trioxide Chemical compound O=[W](=O)=O ZNOKGRXACCSDPY-UHFFFAOYSA-N 0.000 description 1
- 229910001935 vanadium oxide Inorganic materials 0.000 description 1
- 238000003466 welding Methods 0.000 description 1
- 239000008256 whipped cream Substances 0.000 description 1
- 239000011787 zinc oxide Substances 0.000 description 1
- 229910052845 zircon Inorganic materials 0.000 description 1
- GFQYVLUOOAAOGM-UHFFFAOYSA-N zirconium(iv) silicate Chemical compound [Zr+4].[O-][Si]([O-])([O-])[O-] GFQYVLUOOAAOGM-UHFFFAOYSA-N 0.000 description 1
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
- C23C4/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
- C23C4/12—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge characterised by the method of spraying
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
- C23C4/04—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge characterised by the coating material
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
- C23C4/04—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge characterised by the coating material
- C23C4/06—Metallic material
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
- C23C4/04—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge characterised by the coating material
- C23C4/10—Oxides, borides, carbides, nitrides or silicides; Mixtures thereof
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
- C23C4/12—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge characterised by the method of spraying
- C23C4/129—Flame spraying
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
- C23C4/12—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge characterised by the method of spraying
- C23C4/134—Plasma spraying
Definitions
- the present invention relates to the technology for forming a coating on a substrate by plasma thermal spraying, flame thermal spraying, or laser thermal spraying.
- thermal spraying In plasma thermal spraying, flame thermal spraying, and laser thermal spraying, a powder material, such as a metal and a ceramic, is introduced into a hot plasma flow, a hot flame flow, and a concentrated laser beam, and then a melted particle material is sprayed and deposited on a surface of a substrate to thereby form a coating.
- thermal spraying methods have been established as industrial production technologies. These thermal spraying methods have no need to locate a subject in a closed space and are applicable to a large area and to a long object.
- the layered structural bodies using fine particles which are called nanoparticles have been applied in various field and products, such as a coating, an element, etc.
- those may form a dense composition or a structure by methods, such as aerosol deposition method (AD method) and chemical vapor deposition (CVD method).
- AD method aerosol deposition method
- CVD method chemical vapor deposition
- these methods may not be used under an atmosphere environment and are not suitable for a continuous production, an application to a large or long object, or their mass productions.
- a coating such as a dense coating layer
- the thermal spraying technology using nanoparticles enables the production of a coating having performance and functions which were not achieved by the conventional thermal spraying, such as formation of a layer in which two or more kinds of particle materials are uniformly mixed at a nanosized level or a heat insulation function having nanosized pores.
- the lower limit of the particle diameter of a powder material which is introduced into a hot section which serves as a heat source of thermal spraying, such as plasma and flame is about 1-5 micrometers.
- a conveying tube for introducing the powder material into a hot section may be blocked.
- nanoparticles are aggregated and exist as particles each having a size of several ten micrometers under an atmosphere at a room-temperature. If such aggregated particles are introduced into a plasma flow, the particles become an aggregated droplet when the particles are melted in a hot plasma part and thus do not reach a substrate as nanoparticles. As a result, the properties of the nanoparticles may not be effectively utilized.
- Japanese Patent Application Publication No. 2011-256465 discloses a flame thermal spraying.
- slurry is obtained by preliminarily dispersing ceramic particles each having a particle diameter of 0.1-5 micrometers in a solvent which is an alcohol or kerosene. And then thermal spraying is carried out by spraying the slurry in aflame.
- it is not easy to disperse the ceramic particles uniformly in a solvent when the particle diameter of the ceramic particles is too small.
- a feeding apparatus for feeding the line material is needed. Also, the optimizations of the cross-sectional area and feeding speed, etc., of the line material are needed. Further, it is not easy to use two or more materials by changing a material to another one during one step of thermal spraying.
- the present invention is directed to a method for producing a material for thermal spraying used for plasma thermal spraying, flame thermal spraying, or laser thermal spraying.
- the purpose of the present invention is to readily carry out thermal spraying using fine particles which ware difficult to be handled in the conventional art.
- the present invention is also directed to a material for thermal spraying which is produced by the method, a method for thermal spraying using the material for thermal spraying, and a product obtained by thermal spraying comprising a substrate and a coating which is formed on the substrate by the method for thermal spraying.
- a method for producing a material for thermal spraying comprises the steps of: a) dispersing fine particles of a ceramic or a metal in a liquid resin; b) pulverizing a cured material from a mixture obtained in the step a) to obtain a material for thermal spraying having a particle diameter which is larger than that of the fine particles and is within a predetermined target particle diameter range; and c) repeating the step a) and step b), wherein over-pulverized particles having a particle diameter below the target particle diameter range obtained when the cured material is pulverized in a completed step b) are also added to the liquid resin and are dispersed in a second or later time step a).
- thermal spraying may be readily carried out using particles which were difficult to be handled in the conventional art.
- the over-pulverized particles are added to the liquid resin in a second or later time step a) after the fine particles are dispersed in the liquid resin.
- time for pulverizing the cured material in the step b) is determined in advance based on percentages of the material for thermal spraying and the over-pulverized particles obtained in a step b).
- the material for thermal spraying is obtained using a sieve from the cured material after the cured material is pulverized in the step b), and the over-pulverized particles added to the liquid resin in a second or later time step a) are separated from the material for thermal spraying by a sieve in a completed step b) and are aggregated.
- the over-pulverized particles added to the liquid resin in the second or later time step a) are all of the over-pulverized particles obtained in a previous step b).
- the fine particles have an average particle diameter of not less than 25 nm and not more than 1000 nm when the average particle diameter is measured by a laser diffraction scattering method or a dynamic-light-scattering method.
- the liquid resin has room-temperature curing properties and wherein the step a) comprises the steps of: a1) stirring an intermediate substance obtained by adding the fine particles to the liquid resin for a predetermined unit stirring time; a2) cooling the intermediate substance after the step a1); and a3) repeating the step a1) and the step a2) until a total stirring time of the intermediate substance amounts to not less than a required stirring time.
- FIG. 1 shows a configuration of a thermal spraying apparatus.
- FIG. 2 shows the flow of the production of a material for thermal spraying.
- FIG. 3 shows a part of the flow of the production of a material for thermal spraying.
- FIG. 4 shows a cross-section of a cured material.
- FIG. 5 shows a part of the flow of the production of a material for thermal spraying.
- FIG. 6 shows the flow of a thermal spraying operation.
- FIG. 7 shows a part of the flow of the production of a material for thermal spraying.
- FIG. 8 shows a cross-section of a cured material.
- FIG. 9 shows a cross-section of a cured material.
- FIG. 10 shows a cross-section of a cured material.
- FIG. 11 shows a cross-section of a cured material.
- FIG. 12 shows another example of a thermal spraying apparatus.
- FIG. 13 shows the flow of a thermal spraying operation.
- FIG. 1 shows a configuration of a thermal spraying apparatus 1 .
- the thermal spraying apparatus 1 is an apparatus which carries out plasma thermal spraying on a substrate 9 and comprises a thermal spraying gun 11 , a gas supplying part 12 , a material storing part 13 , an air supplying part 14 , and a material conveying part 15 .
- the thermal spraying gun 11 generates plasma flare 8 .
- the gas supplying part 12 supplies argon gas to the thermal spraying gun 11 .
- the gas supplied by the gas supplying part 12 is not limited to argon gas, but may be helium gas or other gas.
- the material storing part 13 stores a material for thermal spraying used for thermal spraying.
- the air supplying part 14 supplies air to the material conveying part 15 .
- the material conveying part 15 supplies a material for thermal spraying into the plasma flare 8 by using the air from the air supplying part 14 .
- the gas used for the conveyance (hereinafter referred to as “career gas”)
- the thermal spraying gun 11 is a spraying nozzle which carries out thermal spraying.
- the thermal spraying gun 11 internally comprises a flow path 21 of argon gas.
- a cathode 22 is located in the center of the flow path 21 .
- An anode 23 is located at a downstream position relative to the cathode 22 such that the flow path is surrounded by the anode 23 .
- the plasma flare 8 blows out from a spraying hole 24 by an electrical discharge between the cathode 22 and the anode 23 .
- the material conveying part 15 comprises a constant-amount supplying part 31 and a conveying pipe 32 .
- the constant-amount supplying part 31 brings out a material for thermal spraying at a constant amount per unit time from the material storing part 13 and merges the material and the career gas.
- the end of the conveying pipe 32 serves as a spraying hole 33 .
- the material for thermal spraying blows out together with career gas from the spraying hole 33 .
- the material for thermal spraying is vertically introduced from the side of the advancing direction of the plasma flare 8 toward the center of the plasma flare 8 .
- the material for thermal spraying is a powder.
- Each of the powder particles has a size which does not block the conveying pipe 32 .
- each of the powder particles is a resin containing finer particles.
- the fine particles contained in the material for thermal spraying are ceramic particles or metal particles.
- the resin of the material for thermal spraying is burned down by the plasma flare 8 , and the fine particles in a molten state or in a semimolten state flow together with the plasma flare 8 toward the substrate 9 . As a result, the fine particles are deposited on the substrate 9 , and thereby a coating is formed.
- FIG. 2 shows the flow of the production of a material for thermal spraying.
- ceramic particles or metal particles are prepared as the fine particles.
- a resin having room-temperature curing properties is prepared as the liquid resin.
- the resin having room-temperature curing properties is a resin whose curing naturally proceeds at a room temperature (for example, an environment at a temperature of 15 to 35° C.).
- the fine particles used in the production example are zirconia particles having an average particle diameter of 200 nm (a product of KCM Corporation, brand name “KZ-8YF”).
- the average particle diameter here is a median size (d50) calculated from a particle size distribution calculated by a laser diffraction scattering method.
- the zirconia fine particles will be referred to merely as “particles.”
- the raw material of the fine particles is not limited to above-described zirconia (ZrO 2 ), but may be variously changed.
- ZrO 2 zirconia
- Various metals such as aluminum and copper, may be used as a material for the fine particles when the particles comprise a metal.
- the raw material of the fine particles may comprise two or more kinds of mixed metals. Further, a ceramic and a metal may be mixed as a raw material of the fine particles.
- the average particle diameter of the fine particles may also be changed variously.
- the average particle diameter of the fine particles is so small that the particles are difficult to be handled directly by air conveyance in the thermal spraying apparatus 1 . That is, the average particle diameter of the fine particles is a size of so-called nanoparticles.
- the average particle diameter of the fine particles according to a laser diffraction scattering method or a dynamic-light-scattering method is not less than 25 nm and not more than 1,000 nm (not less than 25 ⁇ 10 ⁇ 9 m and not more than 1,000 ⁇ 10 ⁇ 9 m).
- the average particle diameter of the fine particles is less than 25 nm, it will be difficult to supply the fine particles to the central part of the plasma flare because the amount of the fine particles which may keep a monodispersion state in the resin decreases, and thus the specific gravity of the material for thermal spraying will be too small. If the average particle diameter of the fine particles exceeds 1,000 nm, the fine particles will precipitate easily when the fine particles are mixed with a resin, and thus it will be difficult to keep a monodispersion state of the fine particles.
- the average particle diameter is not less than 50 nm and not more than 500 nm, which is easily available.
- the measurement may be carried out by a dynamic-light-scattering method when the measurement by a laser diffraction scattering method is difficult to carry out.
- a particle diameter indicated by the manufacturer of the fine particles may also be used as the average particle diameter.
- a multicomponent-type resin (so-called a two-component resin) whose curing proceeds at a room temperature when a base resin and a curing agent (so-called a catalyst) are mixed is used as a liquid resin having room-temperature-curing-properties.
- the curing of the two-component resin is accelerated by raising the temperature within a range from a room temperature to a temperature higher to some extent than the room temperature (for example, a temperature range from a room temperature to a temperature higher by about 10 degrees than the room temperature).
- the specific resin used in the production example is a polyester two-component resin (a product of Marumoto Struers, Inc., brand name “REIKAN UMEKOMI JUSHI No.
- Various resins may be used as the resin having room-temperature curing properties as long as the resin mainly contains an organic material.
- An acrylic resin and an epoxy resin may be used.
- a moisture-curable resin and a solvent-volatilizing type resin may also be used as the resin having room-temperature curing properties.
- a liquid resin having room-temperature curing properties is generated by mixing and stirring a curing agent and a base resin which has room-temperature curing properties in a container (Step S 11 ).
- the temperature of the liquid resin is about 32 degrees (° C.), for example.
- the base resin and the curing agent are mixed approximately uniformly, and thereby the curing of the resin is initiated.
- the stirring of the mixture of the base resin and the curing agent is manually carried out using a stirring rod in a plastic container having a diameter of a 50 mm and a depth of 80 mm, for example.
- Step S 12 comprises Steps S 121 -S 123 shown in FIG. 3 .
- Step S 12 first, the fine particles are added to the liquid resin having room-temperature curing properties in the container. Thereby an intermediate substance is obtained. The percentage of the fine particles contained in the intermediate substance is about 40 volume %, for example. Then the intermediate substance in the container is stirred for a predetermined unit stirring time (Step S 121 ).
- the stirring of the intermediate substance in Step S 121 is carried out, for example, by a stirring and defoaming apparatus which may rotate and revolve.
- the rotation is at 350 rpm and the revolution is at 1060 rpm in the condition of stirring and defoaming in the stirring and defoaming apparatus.
- the unit stirring time is 30 seconds, for example.
- the temperature of the intermediate substance increases due to the friction between the fine particles, the heat resulting from the stirring and defoaming apparatus, etc.
- the temperature of the intermediate substance after Step S 121 is completed is, for example, about 45 to 50 degrees. Even while Step S 121 is carried out, the curing of the resin having room-temperature curing properties in the intermediate substance proceeds and is accelerated by increasing the temperature.
- Step S 122 the container which stores the intermediate substance is ejected from the stirring and defoaming apparatus, and then the intermediate substance is cooled (Step S 122 ).
- Step S 122 the intermediate substance is cooled, for example, by a coolant which is colder rather than a room temperature.
- quick cooling of the intermediate substance is carried out by contacting the container which stores the intermediate substance with running water or ice which is colder than a room temperature.
- the intermediate substance indirectly contacts the running water or ice which is colder than a room temperature via the container. Thereby, the curing of the resin having room-temperature curing properties in the intermediate substance is prevented.
- the cooling of the intermediate substance in Step S 122 is carried out, for example, until the temperature of the intermediate substance is lowered to a predetermined temperature for resuming stirring.
- the temperature for resuming stirring is, for example, not more than a temperature which is about 10 degrees higher than a room temperature. In detail, the temperature for resuming stirring is about 40 to 45 degrees.
- the cooling of the intermediate substance in Step S 122 may be carried out, for example, for a predetermined cooling time. The cooling time is about 60 seconds, for example.
- Step S 122 a total of the stirring time of the intermediate substance after the fine particles are added to the liquid resin (hereinafter referred to as a “total stirring time”) is compared with a predetermined required stirring time (Step S 123 ).
- the required stirring time is longer than the unit stirring time.
- the required stirring time is 600 seconds, for example. If the total stirring time is less than the required stirring time, the process returns to Step S 121 , and the stirring of the intermediate substance for the unit stirring time and the cooling of the intermediate substance after the stirring are carried out (Steps S 121 and S 122 ).
- Step S 12 Steps S 121 and S 122 are repeated until the total stirring time of the intermediate substance amounts to not less than the required stirring time. Thereby, nano-slurry comprising fine particles which are so-called nanoparticles and are uniformly monodispersed is obtained.
- the required stirring time is about 600 seconds, for example.
- the required stirring time is determined based on an experimentally calculated time-course change of the viscosity property of the intermediate substance, for example.
- the relation between the stirring speed and the shearing stress while changing the total stirring time is experimentally calculated, and a total stirring time until when the state of the hysteresis which appears in a viscosity curve shows almost no change or a time obtained by adding a predetermined margin time to the total stirring time may be adopted as the required stirring time.
- a total stirring time until when the time-course change of the thixotropic property of the intermediate substance does not appear or a time obtained by adding a predetermined margin time to the other total stirring time may be adopted as the required stirring time.
- the volume percentage of the fine particles in the nano-slurry may be variously changed. However, if the volume percentage is too low, the film forming speed by thermal spraying will be slow, and thus the film forming efficiency will decrease.
- the upper limit of the volume percentage is dependent on the particle diameter and the size of the solvent molecule which enters between the particles. That is, for example, the maximum filling rate is about 51%, in a case where the particles each have an ideal spherical body having a particle diameter of 150 nm, and the solvent molecule has a thickness of 15 nm, and each of the particles is located on the lattice point of a hexagonal close-packed lattice.
- the maximum value of the filling rate changes depending on the conditions of the fine particles and the solvent.
- the actual filling rate differs from the theoretical value because the fine particles actually have a particle size distribution which is not with in an ideal distribution in a significant range.
- a nano-slurry which is a mixture obtained in Step S 12 is ejected from the container.
- the curing of the resin having room-temperature curing properties has already proceeded to some extent, and the nano-slurry has a shape of soft rice cake.
- the nano-slurry in the container may be integrally handled. If a thermosetting resin was used instead of the resin having room-temperature curing properties, it would not be easy to integrally handle a mixture obtained in Step S 12 because the mixture would be like whipped cream.
- a resin having room-temperature curing properties is used as the liquid resin, a nano-slurry may be integrally handled, and the nano-slurry may be easily ejected from the container. Further, the yield rate of a material for thermal spraying may also be improved because a part of the nano-slurry may be prevented (or inhibited) from adhering to and remaining in the container when the nano-slurry is ejected.
- the nano-slurry ejected from the container is thinly stretched, for example, on a piece of paraffin paper and is shaped. Then the nano-slurry becomes a cured material while keeping a monodispersion state of the fine particles due to the curing of the resin having room-temperature curing properties with the lapse of time (Step S 13 ).
- FIG. 4 shows a cross-section of the cured material observed by a scanning electron microscope. It is confirmed from FIG. 4 that the fine particles do not contact each other and are independently dispersed in a monodispersed state in the cured material.
- the cured material (namely, the cured material obtained by curing the mixture obtained in Step S 12 ) is pulverized using, for example, a hand-worked fracturing apparatus or an oscillating mill.
- the cured material after it is pulverized (hereinafter referred to as a “pulverized material”) is fractionated using a sieve. Thereby, a material for thermal spraying comprising particles having a particle diameter larger than the above-described fine particles is obtained (Step S 14 ).
- the pulverized material is fractionated into a range of a particle diameter of not less than 45 micrometers and not more than 106 micrometers (not less than 45 ⁇ 10 ⁇ 6 m and not more than 106 ⁇ 10 ⁇ 6 m) which is a predetermined target particle diameter range, and into other fractions.
- the particle diameter range may be variously changed as long as the particles may be used in the thermal spraying apparatus 1 .
- the particle diameter range may be defined by the opening of the sieve used for the fractionation.
- the particle diameter of the particles obtained by pulverizing a cured material may be variously determined as long as the particle diameter is larger than that of the fine particles contained in the particles.
- the particle diameter range of the pulverized particles may be suitably determined between 1 micrometer and 120 micrometers (not less than 1 ⁇ 10 ⁇ 6 m and not more than 120 ⁇ 10 ⁇ 6 m). More preferably, the particle diameter of the pulverized particles is more than 5 times of the particle diameter of the fine particles, and is not less than 5 micrometers and not more than 120 micrometers from a viewpoint that the thermal spraying apparatus readily carries out air conveying.
- FIG. 5 shows an example of the detailed flow of Step S 14 .
- Step S 14 comprises Steps S 141 -S 145 shown in FIG. 5 .
- the cured material obtained in Step S 13 is roughly pulverized by a hand-worked fracturing apparatus and thereby becomes a pulverized material having a particle diameter below 400 micrometers (Step S 141 ).
- the pulverized material obtained in Step S 141 is supplied on a sieve having an opening of 106 micrometers and then is fractionated in a vibration sieving process using a sieve shaker (Step S 142 ).
- a tapping component such as a tapping ball and a tapping block
- a tapping component is added on the sieve.
- the sieve is prevented from being blocked, and thus the fractionation of the pulverized material may be efficiently carried out.
- the particles which each have a particle diameter of not less than 106 micrometers and remained on the sieve namely, a residue
- Step S 143 and S 144 are pulverized again using a mill
- Step S 142 are fractionated again using the sieve.
- the pulverization by a mill and the fractionation by a sieve are repeated until the particle diameters of all the pulverized materials become less than 106 micrometers (Steps S 142 -S 144 ).
- the pulverized material obtained in Steps S 142 -S 144 is supplied on a sieve having an opening of 45 micrometers and is fractionated in a vibration sieving process using a sieve shaker.
- a tapping component is preferably added on the sieve along with the pulverized material.
- the particles which each have a particle diameter of not less than 45 micrometers (and less than 106 micrometers) and remain on the sieve are obtained as a material for thermal spraying having a particle diameter within the target particle diameter range (Step S 145 ).
- the over-pulverized particles which pass the sieve and have a particle diameter of less than 45 micrometers are collected and used in the after-mentioned second or later time production of a material for thermal spraying.
- the particle diameter of the over-pulverized particles is not less than the particle diameter of the fine particles and is usually larger than the particle diameter of the fine particles.
- the fine particles are dispersed uniformly in the over-pulverized particles.
- the over-pulverized particles separated from the material for thermal spraying by the sieve in Step S 145 are collected in an aggregational state.
- Step S 14 in order to confirm that the particle diameter of the pulverized material obtained in the above-mentioned step S 141 is less than 400 micrometers, the pulverized material may be supplied on a sieve having an opening of 400 micrometers and then be fractionated in a vibration sieving process using a sieve shaker between Step S 141 and Step S 142 . If the pulverized material remains on the sieve, the remaining pulverized material is pulverized by a mill, etc., until the particle diameter of it becomes less than 400 micrometers.
- the pulverization by a mill in Step S 144 is carried out, for example, for a predetermined pulverization time.
- the pulverization time of a cured material is determined in advance based on the percentages of the material for thermal spraying and the over-pulverized particle obtained in Step S 144 (namely, their percentages to the cured material supplied to a mill in Step S 144 ).
- the pulverization of a cured material is repeatedly carried out while changing the pulverization time, and thus the particle size distributions of the pulverized material which each correspond to two or more pulverization times may be calculated. Thereby, the rates of the material for thermal spraying and the over-pulverized particles which each correspond to the two or more pulverization time may be calculated.
- the improvement in efficiency of the producing operation needs to be achieved by increasing the amount of the material for thermal spraying obtained in one time of step S 144 and thereby decreasing the number of times to repeat Step S 144 . Further, the percentage of a material for thermal spraying obtained at Step S 14 to an entire cured material (namely, the yield rate of the material for thermal spraying) needs to be increased by suppressing the amount of the over-pulverized particles generated at one time of step S 144 .
- the appropriate pulverization time which satisfies these requirements is determined as the pulverization time in Step S 144 .
- the pulverization time in Step S 144 is 40 seconds, for example.
- FIG. 6 shows the flow of the thermal spraying by the thermal spraying apparatus 1 .
- the material for thermal spraying is produced by the production method according to the above-mentioned steps S 11 -S 14 (Step S 21 ).
- the material storing part 13 is filled with the material for thermal spraying (Step S 22 ).
- plasma thermal spraying is carried out using the material for thermal spraying.
- the heated fine particles are fused together on the substrate 9 , and a coating is formed on the substrate 9 (Step S 23 ).
- the fine particles are melted and fused together to thereby form a dense coating.
- the conditions may be determined such that the fine particles reach the substrate 9 while the fine particles are in a semimolten state. In this case, a porous coating is formed.
- thermal spraying may be readily carried out even when a thermal spraying apparatus having a structure similar to conventional one is used and even when fine particles each having a size of so-called a nanoparticle which were difficult to be handled in the conventional art are used.
- the cost required for thermal spraying may be prevented from increasing.
- the efficiency of the thermal spraying operation is prevented from decreasing. That is, a high production speed may be achieved by the thermal spraying technology even when a subject is long and large.
- the use of a material having dramatically improved physicochemical properties, such as nano composite material and a nano porous material which take advantage of nanoparticles, as an industrial material may also be achieved.
- Step S 12 the dispersion of fine particles in a resin
- the intermediate substance obtained by adding the fine particles to the liquid resin having room-temperature curing properties is stirred for the predetermined unit stirring time, and then the intermediate substance is cooled (Steps S 121 and S 122 ). Then Steps S 121 and S 122 are repeated until the total stirring time of the intermediate substance amounts to not less than the required stirring time (Step S 123 ).
- the resin would be cured in a state where the fine particles are insufficiently dispersed because the temperature of the intermediate substance would increase excessively during the stirring. If particles obtained by pulverizing a cured material comprising the fine particles which are insufficiently dispersed are used as a material for thermal spraying, it would be difficult to form a uniform coating on the substrate.
- Step S 12 by carrying out Steps S 121 -S 123 in Step S 12 in the above-mentioned production of a material for thermal spraying, the liquid resin having room-temperature curing properties may be prevented from curing before the fine particles are dispersed, and a material for thermal spraying comprising the fine particles which are dispersed in a monodispersion state in the resin having room-temperature curing properties may be readily produced. Further, a material for thermal spraying may be produced more readily because it is not necessary to heat the intermediate substance or to irradiate the intermediate substance due to the use of the resin having room-temperature curing properties as the liquid resin, when the intermediate substance comprising the fine particles which are dispersed in a monodispersion state is cured.
- the quick cooling of the intermediate substance may be readily achieved by cooling the intermediate substance using a coolant (for example, running water or ice) colder than a room temperature.
- a coolant for example, running water or ice
- the intermediate substance may be cooled more quickly by indirectly contacting the intermediate substance to the coolant, and thereby the curing of the intermediate substance after it is stirred may be further suppressed.
- the cooling of the intermediate substance is carried out until the temperature of the intermediate substance decreases to a temperature for resuming stirring. Therefore, excessive increase of the temperature of the intermediate substance and excessive progress of the curing may be suppressed when the intermediate substance is again stirred after it is cooled.
- a liquid resin having room-temperature curing properties is generated by mixing and stirring a base resin having room-temperature curing properties and a curing agent (Step S 11 ). Accordingly, by stirring the base resin and the curing agent to generate a liquid resin prior to the addition of the fine particles, the fine particles may be dispersed approximately uniformly in a resin having room-temperature curing properties whose components are approximately uniform.
- FIG. 7 shows a part of the flow of the second or later time production of a material for thermal spraying.
- the over-pulverized particles obtained when a cured material is pulverized in a completed Step S 14 for producing a material for thermal spraying are also added to and dispersed in the liquid resin in Step S 12 .
- the other flow of the production is approximately the same as that of Steps S 11 -S 14 shown in FIGS. 2, 3, and 5 .
- a liquid resin having room-temperature curing properties is generated by mixing and stirring a base resin having room-temperature curing properties and a curing agent in a container (Step S 11 ). Then, fine particles and over-pulverized particles are dispersed in the liquid resin generated in Step S 11 (Step S 12 ).
- Step S 12 as shown in FIG. 3 , first, the above-mentioned fine particles are added to a liquid resin having room-temperature curing properties to obtain an intermediate substance, and then the intermediate substance is stirred for a unit stirring time (Step S 121 ).
- the percentage of the fine particles contained in the intermediate substance is the about 40 volume % as in the first time production of a material for thermal spraying.
- Step S 121 is completed, the intermediate substance is cooled (Step S 122 ). Then Steps S 121 and S 122 are repeated until the total stirring time of the intermediate substance amounts to not less than the required stirring time while comparing them (Step S 123 ).
- the over-pulverized particles obtained in a completed production of a material for thermal spraying is added to the intermediate substance (namely, to a mixture of a liquid resin and fine particles).
- the added over-pulverized particle is in an aggregational state as described above.
- the over-pulverized particles added to the intermediate substance are preferably all of the over-pulverized particles obtained in Step S 14 in a previous production of a material for thermal spraying (for example, in Step S 14 in the first time production of a material for thermal spraying when the second time production of a material for thermal spraying is carried out).
- the percentage of the over-pulverized particles to the intermediate substance after the over-pulverized particle is added is, for example, about 30 weight % or less, and is about 20 weight % in this embodiment.
- Step S 124 the intermediate substance obtained by adding the fine particles and the over-pulverized particles to the liquid resin is stirred for a predetermined unit stirring time.
- the unit stirring time in Step S 124 may be the same as or different from the above-mentioned unit stirring time in the step S 121 .
- the stirring of the intermediate substance in Step S 124 is carried out, for example, by the same stirring and defoaming apparatus as that used in Step S 121 .
- Step S 125 the intermediate substance is cooled (Step S 125 ).
- the cooling of the intermediate substance in Step S 125 is carried out, for example, by a coolant (running water or ice) which is colder than a room temperature until the temperature of the intermediate substance decreases to a predetermined temperature for resuming stirring.
- the cooling of the intermediate substance in Step S 125 may be carried out, for example, for a predetermined cooling time.
- the temperature for resuming stirring and the cooling time in Step S 125 may be the same as the temperature for resuming stirring and the cooling time in Step S 122 , respectively, or may be different from them.
- Step S 124 and S 125 are repeated until the total stirring time of the intermediate substance in Step S 124 amounts to not less than the required stirring time while comparing them (Step S 126 ).
- the total stirring time in Step S 124 and the required stirring time in Step S 126 may be the same as the total stirring time in Step S 121 and the required stirring time in Step S 123 , respectively, or may be different from them.
- the nano-slurry which is a mixture generated in Step S 12 becomes a cured material due to the curing of the resin having room-temperature curing properties with the lapse of time (Step S 13 ).
- the fine particles and the over-pulverized particles are in a monodispersion state.
- FIG. 8 shows a cross-section of the cured material observed by a scanning electron microscope.
- FIG. 9 shows a cross-section of the cured material which is generated in the first time production of a material for thermal spraying (namely, a cured material which does not contain over-pulverized particles) observed similarly as in FIG. 8 .
- the parts having a deeper color than the other parts in FIG. 8 comprise the over-pulverized particles. It has been confirmed from FIG. 8 that the over-pulverized particles do not contact each other and are dispersed separately and independently in a mono dispersion state in the cured material generated in the second or later time production of a material for thermal spraying.
- FIGS. 10 and 11 show enlarged views of a part of FIGS. 8 and 9 , respectively.
- FIG. 10 shows an area including a part of one over-pulverized particle.
- the solid line 71 in FIG. 10 shows a boundary between the over-pulverized particle and the surrounding part. The lower left part relative to the solid line 71 corresponds to the over-pulverized particle.
- FIG. 10 shows that both the fine particles contained in the over-pulverized particle and the fine particles located in the other part surrounding the over-pulverized particle are dispersed approximately uniformly in a similar manner. Further, FIGS. 10 and 11 show that, even when the over-pulverized particles are added to a liquid resin, the fine particles are dispersing uniformly and approximately similarly as in the case where the over-pulverized particles are not added.
- the cured material obtained in Step S 13 is pulverized, for example, by a hand-worked fracturing apparatus or an oscillating-type mill.
- the cured material after it is pulverized is fractionated using a sieve. Thereby, a material for thermal spraying having a particle diameter within the target particle diameter range (for example, not less than 45 micrometers and not more than 106 micrometers) is obtained (Step S 14 ).
- the weight percentages of the material for thermal spraying and the over-pulverized particles obtained in Step S 14 to the cured material obtained in Step S 13 are the almost same as the weight percentages of the material for thermal spraying and the over-pulverized particles which are obtained in Step S 14 from a cured material which does not contain over-pulverized particles, respectively.
- the weight percentages of the material for thermal spraying and the over-pulverized particles when the cured material does not contain over-pulverized particles are about 64% and about 29%, respectively.
- the weight percentages of the material for thermal spraying and the over-pulverized particles when the cured material contains over-pulverized particles are about 67% and about 27%, respectively. Accordingly, it has been confirmed that there hardly occurs a phenomenon that the over-pulverized particles are not appropriately pulverized by exfoliating from the cured material containing over-pulverized particles when the cured material is pulverized in Step S 14 .
- the material for thermal spraying obtained by the second or later time production is also used for the thermal spraying in the thermal spraying apparatus 1 . That is, a material for thermal spraying produced by the production method of the steps of S 11 -S 14 is prepared (Step S 21 ). Then the material for thermal spraying is filled into the material storing part 13 (Step S 22 ). Then plasma thermal spraying is carried out using the material for thermal spraying. Thereby, the heated fine particles are fused together on the substrate 9 , and thus a coating is formed on the substrate 9 (Step S 23 ).
- thermal spraying may be readily carried out while using nano-level fine particles which were difficult to be handled in the conventional art and while using a thermal spraying apparatus which has the same structure as that of a conventional apparatus.
- the increase of the cost required for thermal spraying may be suppressed, and the decrease in the efficiency of the thermal spraying operation may also be prevented.
- the use of a material having dramatically improved physicochemical properties, such as nano composite material and a nano porous material which take advantage of nanoparticles, as an industrial material may also be achieved.
- Step S 12 in addition to dispersing the fine particles in a liquid resin, the over-pulverized particles obtained when a cured material is pulverized in a completed step S 14 are also added and dispersed in the liquid resin.
- the yield rate of the material for thermal spraying produced from the fine particles and the resin may be improved by recycling the over-pulverized particles which are too small to be used as a material for thermal spraying in the next or later time production of a material for thermal spraying in the thermal spraying apparatus 1 .
- over-pulverized particles in the production of a material for thermal spraying
- the fine particles contained in over-pulverized particles are collected and recycled as the fine particles which are mixed with a liquid resin in Step S 121 .
- a step for heating over-pulverized particles or melting over-pulverized particles in a solvent is required. Therefore, much work is required to collect the particles. Further, it is difficult to prevent foreign substances from adhering to and contaminating in the particles in the collecting step.
- over-pulverized particles are collected and pelletized into particles each having a particle diameter within the target particle diameter range.
- the over-pulverized particles are required to be melted to be pelletized, and re-curing of a resin after it is melted is technically difficult.
- the recycle of over-pulverized particles may be readily carried out because the fine particles and the over-pulverized particles are dispersed in a liquid resin in Step S 12 , and therefore a step for heating or melting over-pulverized particles, etc., is made unnecessary. Further, in the step for recycling over-pulverized particles, the adhesion and contamination of foreign substances to the fine particles in the over-pulverized particle may also be prevented. Further, the ratio of the fine particles to the resin in the over-pulverized particles is substantially the same as the ratio of the fine particles to the liquid resin in Step S 121 .
- the percentages of the fine particles in the cured material and in the material for thermal spraying which are obtained by the second or later time production which recycles over-pulverized particles are substantially equal to the percentages of the fine particles in the cured material and the material for thermal spraying which are obtained by the first time production in which over-pulverized particles are not recycled, respectively. For this reason, whenever a material for thermal spraying is produced and used, a uniform coating may be formed on the substrate 9 by the thermal spraying using the thermal spraying apparatus 1 .
- Step S 12 the addition of over-pulverized particles to the liquid resin (Step S 124 ) is carried out after the fine particles are dispersed in the liquid resin (Step S 121 ).
- the over-pulverized particles are prevented from affecting the dispersion of the fine particles in the resin.
- the fine particles may be prevented from affecting the dispersion of the over-pulverized particles in the resin because the fine particles are dispersed in a monodispersion state in the resin when the over-pulverized particles are added.
- both the fine particles and the over-pulverized particles may be readily dispersed uniformly in the liquid resin.
- the pulverization time of a cured material in Step S 144 is determined in advance based on the percentages of the material for thermal spraying and over-pulverized particles which are obtained in Step S 14 .
- the production efficiency may be improved by increasing the amount of a material for thermal spraying obtained at one time of step S 144 .
- the yield rate of the material for thermal spraying obtained in Step S 14 may also be efficiently improved by reducing the amount of over-pulverized particles generated at one time of step S 144 .
- the over-pulverized particles to be added to the liquid resin in Step S 12 are separated from a material for thermal spraying by a sieve in a completed step S 14 and are in an aggregational state.
- the handling of the over-pulverized particles during the collection of the over-pulverized particles or the addition of the over-pulverized particles to a liquid resin may be made easier.
- the scattering and loss of the over-pulverized particles obtained in Step S 14 due to air-conditioning, etc. are suppressed. As a result, the yield rate of a material for thermal spraying may be further improved.
- the over-pulverized particles added to a liquid resin in Step S 12 are all of the over-pulverized particles obtained in a previous step S 14 .
- the production of a material for thermal spraying may be simplified.
- a material for thermal spraying may also be efficiently produced.
- Step S 12 an intermediate substance obtained by adding the fine particles to a liquid resin having room-temperature curing properties is stirred for the unit stirring time, and then the intermediate substance is cooled (Steps S 121 and S 122 ). Then Steps S 121 and S 122 are repeated until the total stirring time of the intermediate substance amounts to not less than the required stirring time (Step S 123 ).
- the liquid resin having room-temperature curing properties may be prevented from curing before the fine particles are dispersed, and thus a material for thermal spraying comprising the fine particles dispersed in a resin having room-temperature curing properties in a monodispersion state may be readily produced.
- a material for thermal spraying may be produced more readily because it is unnecessary to heat the intermediate substance or to irradiate the intermediate substance when the intermediate substance comprising the fine particles dispersed in a monodispersion state is cured.
- Step S 12 an intermediate substance obtained by adding the fine particles and the over-pulverized particles to a liquid resin having room-temperature curing properties is stirred for the unit stirring time, and then the intermediate substance is cooled (Steps S 124 and S 125 ). Then Steps S 124 and S 125 are repeated until the total stirring time of the intermediate substance amounts to not less than the required stirring time (Step S 126 ).
- the liquid resin having room-temperature curing properties may be prevented from curing before the over-pulverized particles are dispersed, and thus a material for thermal spraying comprising over-pulverized particles dispersed in a resin having room-temperature curing properties in a monodispersion state may be readily produced.
- FIG. 12 shows another example of a thermal spraying apparatus 1 a .
- the thermal spraying apparatus 1 a has two material storing parts 13 and two constant-amount supplying parts 31 .
- the conveying pipes 32 extending from the two respective constant-amount supplying parts 31 join together on the way.
- the materials for thermal spraying which are stored in the two material storing parts 13 are different from each other. That is, in the two kinds of materials for thermal spraying, the raw materials of the fine particles contained in resin particles are different from each other.
- the two kinds of materials for thermal spraying are produced by the above-described production method of a material for thermal spraying.
- Steps S 124 -S 126 the recycle of over-pulverized particles (Steps S 124 -S 126 ) is preferably carried out.
- Which of the material storing parts 13 supplies a material for thermal spraying to a thermal spraying gun 11 is determined by controlling two valves 34 which are installed on the conveying pipes 32 and an air supplying part 14 .
- Other configurations of the thermal spraying apparatus 1 a are the same as those of the thermal spraying apparatus 1 in FIG. 1 . The same numbers are given to the same components.
- FIG. 13 shows the flow of the operation when thermal spraying is carried out by the thermal spraying apparatus 1 a of FIG. 12 .
- Two kinds of materials for thermal spraying are prepared by the above-described production method (Step S 31 ). Then they are filled into the two material storing parts 13 (Step S 32 ). Then a coating is formed by carrying out thermal spraying using one of the materials for thermal spraying to fuse the fine particles on a substrate 9 (Step S 33 ). Next, another coating is formed by carrying out thermal spraying using the other of the materials for thermal spraying to fuse the different kind of fine particles on the existing coating formed in Step S 33 (Step S 34 ).
- the change of a material for thermal spraying may be readily achieved only by changing its supply route.
- three or more material storing parts 13 may be installed, and three or more coating layers may be stacked using three or more kinds of materials for thermal spraying. Further, two or more kinds of coatings may be stacked repeatedly. That is, in the thermal spraying apparatus 1 a , two or more kinds of coatings may be readily stacked on the substrate 9 .
- the above-described production of a material for thermal spraying and the thermal spraying apparatus 1 , 1 a may be variously changed.
- the stirring of the intermediate substance in Steps S 121 and S 124 may be carried out by any of various apparatuses or may be manually carried out by an operator using a stirring rod, etc.
- the unit stirring time may be suitably changed as long as the curing of the resin having room-temperature curing properties in the intermediate substance does not excessively proceed.
- the cooling of the intermediate substance in Steps S 122 and S 125 may be carried out by any of various methods.
- the intermediate substance may be cooled by blowing gas at a room temperature or a temperature lower than the room temperature toward the intermediate substance.
- the cooling of the intermediate substance may be carried out by leaving the intermediate substance in the atmosphere at a room temperature.
- the temperature for resuming stirring and the cooling time may be changed suitably as long as the curing of the resin having room-temperature curing properties in the intermediate substance does not excessively proceed.
- the over-pulverized particles added to a liquid resin in Step S 124 may not necessarily be all of the over-pulverized particles obtained in a previous production of a material for thermal spraying and may be a part of the over-pulverized particles. Further, the over-pulverized particles added to a liquid resin may be over-pulverized particles obtained in a second last or former time production of a material for thermal spraying. Further, in Step S 124 , the over-pulverized particles which are in an aggregational state may be disintegrated and then added to a liquid resin.
- Step S 124 -S 126 (dispersion of over-pulverized particles) may be carried out in Step S 12 in parallel with Steps S 121 -S 123 (dispersion of fine particles).
- the fine particles and the over-pulverized particles are mixed in a liquid resin approximately at the same time, and an intermediate substance which is a liquid resin containing the fine particles and the over-pulverized particles is stirred for the unit stirring time.
- the intermediate substance is cooled for the predetermined cooling time or until the temperature of the intermediate substance decreases to the temperature for resuming stirring.
- the stirring and cooling of the intermediate substance are repeated until the total stirring time of the intermediate substance amounts to not less than the required stirring time.
- Steps S 124 -S 126 may be carried out prior to Steps S 121 -S 123 .
- the yield rate of a material for thermal spraying may be improved by recycling over-pulverized particles to produce a material for thermal spraying.
- the fine particles are added to a liquid resin after the liquid resin is generated by mixing a curing agent and a base resin which has room-temperature curing properties.
- the addition of the fine particles may be carried out in parallel with the mix of a base resin and a curing agent.
- the addition of fine particles and over-pulverized particles may be carried out in parallel with mixing a base resin and a curing agent.
- the liquid resin used in the above-mentioned production method of a material for thermal spraying may not necessarily be a room-temperature-curing resin which naturally cures at a room temperature.
- the liquid resin may be, for example, a thermosetting resin which starts to cure by heat or a photocurable resin which starts to cure by the irradiation with light.
- Steps S 122 , S 123 , S 125 , and S 126 may be skipped in the above-mentioned step S 12 .
- the thermal spraying in the above-mentioned embodiment is applicable to the production of various products of thermal spraying which comprise a substrate and a coating formed on the substrate. Further, only a coating portion may also be used as a product.
- the thermal spraying is applicable to the production of carriers for a catalyst, various battery electrodes, additive agents, filters, functional inks, semiconductor devices, thermal barrier coatings, insulation covers, etc.
- the thermal spraying is applicable to the production of, for example, anticorrosion coatings, machining parts (such as a cutter), and heat-resistant parts (a crucible, a boiler tube, etc.).
- the thermal spraying apparatus 1 , 1 a may also be an apparatus for carrying out flame thermal spraying or laser thermal spraying.
- the thermal spraying gun 11 may be a thermal spraying gun of another type.
- the material for thermal spraying produced by the above-mentioned production method may also be used for flame thermal spraying or laser thermal spraying.
- flame thermal spraying or laser thermal spraying using the material for thermal spraying are carried out, the heated fine particles are fused to form a coating on a substrate.
- nanoparticles may be readily used for thermal spraying.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Physics & Mathematics (AREA)
- Plasma & Fusion (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Coating By Spraying Or Casting (AREA)
- Nozzles (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2015037754A JP6548406B2 (ja) | 2015-02-27 | 2015-02-27 | 溶射材料およびその製造方法、溶射方法並びに溶射製品 |
JP2015-037754 | 2015-02-27 | ||
PCT/JP2016/051077 WO2016136319A1 (ja) | 2015-02-27 | 2016-01-15 | 溶射材料およびその製造方法、溶射方法並びに溶射製品 |
Publications (1)
Publication Number | Publication Date |
---|---|
US20180057922A1 true US20180057922A1 (en) | 2018-03-01 |
Family
ID=56789402
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US15/553,119 Abandoned US20180057922A1 (en) | 2015-02-27 | 2016-01-15 | Material for thermal spraying and production method thereof, method for thermal spraying, and product of thermal spraying |
Country Status (5)
Country | Link |
---|---|
US (1) | US20180057922A1 (zh) |
EP (1) | EP3263734B1 (zh) |
JP (1) | JP6548406B2 (zh) |
CN (1) | CN107250420B (zh) |
WO (1) | WO2016136319A1 (zh) |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN111575634A (zh) * | 2020-05-27 | 2020-08-25 | 苏州联咏成精密机械有限公司 | 一种适用于复杂精密模具的表面硬化处理工艺 |
Family Cites Families (13)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4076883A (en) * | 1975-07-30 | 1978-02-28 | Metco, Inc. | Flame-sprayable flexible wires |
JPH086166B2 (ja) * | 1991-07-31 | 1996-01-24 | トーカロ株式会社 | 耐溶融亜鉛性に優れる溶射用粉末材料および溶融亜鉛浴部材用溶射皮膜 |
EP0866885A4 (en) * | 1995-11-13 | 2000-09-20 | Univ Connecticut | NANOSTRUCTURE PRODUCTS FOR HOT SPRAYING |
US6723387B1 (en) * | 1999-08-16 | 2004-04-20 | Rutgers University | Multimodal structured hardcoatings made from micro-nanocomposite materials |
EP1134302A1 (en) * | 2000-03-17 | 2001-09-19 | Consorzio Interuniversitario per lo Sviluppo dei Sistemi a Grande Interfase, C.S.G.I | New process for the production of nanostructured solid powders and nano-particles films by compartimentalised solution thermal spraying (CSTS) |
JP2002332558A (ja) * | 2001-03-08 | 2002-11-22 | Shin Etsu Chem Co Ltd | 溶射用球状粒子およびその製造方法並びに溶射部材 |
US6916534B2 (en) * | 2001-03-08 | 2005-07-12 | Shin-Etsu Chemical Co., Ltd. | Thermal spray spherical particles, and sprayed components |
US20030219544A1 (en) * | 2002-05-22 | 2003-11-27 | Smith William C. | Thermal spray coating process with nano-sized materials |
JP2010133021A (ja) * | 2008-10-31 | 2010-06-17 | Topy Ind Ltd | 溶射用粒子 |
JP5195312B2 (ja) * | 2008-11-06 | 2013-05-08 | 新日鐵住金株式会社 | 溶射材料とその製造方法、及び溶射施工体 |
WO2011003439A1 (de) * | 2009-07-07 | 2011-01-13 | Sulzer Metco Ag | Spritzwerkstoff auf eisenbasis und verfahren zur herstellung eines spritzwerkstoffs, sowie thermische spritzschicht und spritzverfahren |
JP5584161B2 (ja) * | 2011-03-30 | 2014-09-03 | 関西電力株式会社 | 溶射材料 |
JP6571308B2 (ja) * | 2013-08-29 | 2019-09-04 | 日立造船株式会社 | 溶射材料およびその製造方法、並びに、溶射方法 |
-
2015
- 2015-02-27 JP JP2015037754A patent/JP6548406B2/ja active Active
-
2016
- 2016-01-15 WO PCT/JP2016/051077 patent/WO2016136319A1/ja active Application Filing
- 2016-01-15 EP EP16755069.8A patent/EP3263734B1/en active Active
- 2016-01-15 CN CN201680011418.XA patent/CN107250420B/zh active Active
- 2016-01-15 US US15/553,119 patent/US20180057922A1/en not_active Abandoned
Also Published As
Publication number | Publication date |
---|---|
CN107250420A (zh) | 2017-10-13 |
EP3263734B1 (en) | 2020-04-08 |
WO2016136319A1 (ja) | 2016-09-01 |
EP3263734A1 (en) | 2018-01-03 |
JP6548406B2 (ja) | 2019-07-24 |
JP2016160447A (ja) | 2016-09-05 |
CN107250420B (zh) | 2019-03-29 |
EP3263734A4 (en) | 2018-09-12 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
TWI775955B (zh) | 經加成製造之組件、積層製造方法及粉末用於積層製造方法之用途 | |
JP6463746B2 (ja) | 高エネルギービームと共に目標方法/材料の組合せに適した粉体を用いる、粉体粒子の融解又は焼結による部品の付加的な製造方法 | |
TWI474882B (zh) | 合金超微粒子及其製造方法 | |
JP4602401B2 (ja) | 放電表面処理用電極の製造方法および放電表面処理用電極 | |
CN105731462A (zh) | 球状粉末及其制备方法 | |
WO2009119668A1 (ja) | 透明蛍光体及びその製造方法 | |
JP6571308B2 (ja) | 溶射材料およびその製造方法、並びに、溶射方法 | |
CN106660060B (zh) | 热喷涂组件及其使用方法 | |
CN110039061A (zh) | 丝材低压等离子雾化装置和3d打印高强铝合金粉末的制备方法 | |
CN106270490A (zh) | 一种表层为金属陶瓷层的硬质合金及其制备方法 | |
CN106270513A (zh) | 一种硬质合金及其制备方法 | |
JP2008038163A5 (zh) | ||
JP2008038163A (ja) | コンポジット構造を有するナノ球状粒子、粉末、及び、その製造方法 | |
EP3263734B1 (en) | Thermal spray material, method for manufacturing same and thermal spraying method | |
CN106282718B (zh) | 一种梯度分布硬质合金及其制备方法 | |
US20210061716A1 (en) | Powder for a thermal barrier | |
JP5890843B2 (ja) | 溶射用Mo粉末およびそれを用いたMo溶射膜並びにMo溶射膜部品 | |
JP6630047B2 (ja) | 溶射材料の製造方法、および、溶射方法 | |
WO2022118958A1 (ja) | 溶射材料、それを用いた溶射方法、溶射皮膜 | |
TWI471266B (zh) | 碳化物微粒子之製造方法 | |
KR102673179B1 (ko) | 복합 입자 및 복합 입자의 제조 방법 | |
JP2012112012A (ja) | Hvaf溶射用粉末及び溶射皮膜の形成方法 | |
US20120156384A1 (en) | Pressure controlled droplet spraying (pcds) method for forming particles of compound materials from melts | |
JP2019104991A (ja) | 溶射被膜および溶射製品 | |
JP5139386B2 (ja) | コンポジット構造を有するナノ球状粒子、粉末、及び、その製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: HITACHI ZOSEN CORPORATION, JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:UEHARA, SATOSHI;KATSUKI, MAKOTO;ITOH, HANAKO;AND OTHERS;REEL/FRAME:043375/0586 Effective date: 20170721 |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: NON FINAL ACTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: FINAL REJECTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: NON FINAL ACTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: RESPONSE AFTER FINAL ACTION FORWARDED TO EXAMINER |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: ADVISORY ACTION MAILED |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |