KR20190111251A - Building material and method for manufacturing the same - Google Patents

Building material and method for manufacturing the same Download PDF

Info

Publication number
KR20190111251A
KR20190111251A KR1020180033152A KR20180033152A KR20190111251A KR 20190111251 A KR20190111251 A KR 20190111251A KR 1020180033152 A KR1020180033152 A KR 1020180033152A KR 20180033152 A KR20180033152 A KR 20180033152A KR 20190111251 A KR20190111251 A KR 20190111251A
Authority
KR
South Korea
Prior art keywords
layer
sheet
substrate
adhesive
building material
Prior art date
Application number
KR1020180033152A
Other languages
Korean (ko)
Inventor
심응문
심대용
Original Assignee
주식회사 멜텍
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 멜텍 filed Critical 주식회사 멜텍
Priority to KR1020180033152A priority Critical patent/KR20190111251A/en
Publication of KR20190111251A publication Critical patent/KR20190111251A/en

Abstract

The present invention relates to a building material to improve the service life. The building material comprises: a substrate; a basic material layer located on the substrate; an adhesive layer positioned between the substrate and the basic material layer and bonding the basic material layer on the substrate; and an olefin sheet positioned on the basic material layer.

Description

건축 자재 및 그 제조 방법{BUILDING MATERIAL AND METHOD FOR MANUFACTURING THE SAME}BUILDING MATERIAL AND METHOD FOR MANUFACTURING THE SAME

본 발명은 건축 자재 및 그 제조 방법에 관한 것으로서, 보다 상세하게는 마루 바닥재 및 그 제조 방법에 관한 것이다. BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to building materials and methods of manufacturing the same, and more particularly to flooring materials and methods of manufacturing the same.

종래에 건축 자재 중 하나로 널리 알려져 있는 바닥재, 특히 마루 바닥재는 베니어(veneer)를 이용하여 제조된 합판을 이용한 합판층을 기재층으로 하여 그 위에 접착제를 이용하여 무늬목을 적층하여 무늬목층을 형성한 후 표면 도장 처리를 하여 완성하였다.The flooring material, especially flooring flooring, which is widely known as one of the building materials in the related art, is made of a plywood layer using plywood manufactured using veneer as a base layer, and a veneer layer is formed by laminating veneer using adhesive thereon. It was completed by surface coating treatment.

하지만, 이러한 바닥재는 기판과 그 위에 위치한 무늬층이 서로 박리되는 현상이 발생하여 사용자의 만족도가 떨어지며 바닥재의 수명이 오래 가지 못하는 문제가 발생한다.However, such a flooring material has a phenomenon in which the substrate and the pattern layer disposed thereon are peeled off from each other, so that the user's satisfaction decreases and the life of the flooring material does not last long.

대한민국 등록특허 제10-0537541호(등록일자: 2005년12월12일, 발명의 명칭: 대칭구조를 이용한 무늬목과 합성수지층을 갖는 마루바닥재 및 그 제조방법)Republic of Korea Patent No. 10-0537541 (Registration date: December 12, 2005, the name of the invention: flooring material having a veneer and synthetic resin layer using a symmetrical structure and its manufacturing method) 대한민국 등록특허 제10-0696119호(등록일자: 2007년03월12일, 발명의 명칭: 합성수지를 이용한 표면층 및 목질계 보드를 포함하는 마루바닥재)Republic of Korea Patent No. 10-0696119 (Registration Date: March 12, 2007, the name of the invention: flooring material including a surface layer and wood-based board using a synthetic resin)

본 발명이 해결하려는 과제는 건축 자재의 사용 수명을 향상시키기 위한 것이다.The problem to be solved by the present invention is to improve the service life of building materials.

본 발명이 해결하려는 다른 과제는 건축 자재를 사용하는 사용자의 만족도를 향상시키기 위한 것이다.Another problem to be solved by the present invention is to improve the satisfaction of users using building materials.

상기 과제를 해결하기 위한 본 발명의 건축 자재는 기판, 상기 기판 위에 위치하는 기재층, 상기 기판과 상기 기재층 사이에 위치하여 상기 기판 위에 상기 기재층을 접착시키는 접착제층, 및 상기 기재층 위에 위치하는 올레핀 시트를 포함한다. The building material of the present invention for solving the above problems is a substrate, a substrate layer positioned on the substrate, an adhesive layer positioned between the substrate and the substrate layer to adhere the substrate layer on the substrate, and positioned on the substrate layer The olefin sheet to be included is included.

상기 올레핀 시트는 상기 기재층 위에 상기 올레핀 시트를 접착하기 위한 접착제층, 상기 접착제층 위에 위치하는 시트 기재층, 및 상기 시트 기재층 위에 위치하는 코팅층을 포함할 수 있다. The olefin sheet may include an adhesive layer for adhering the olefin sheet on the substrate layer, a sheet substrate layer positioned on the adhesive layer, and a coating layer positioned on the sheet substrate layer.

상기 올레핀 시트는 상기 시트 기재층과 상기 코팅층 사이에 위치하는 무늬층을 더 포함할 수 있다.The olefin sheet may further include a pattern layer positioned between the sheet base layer and the coating layer.

상기 코팅층은 자외선을 차단하는 UV 코팅층일 수 있다.The coating layer may be a UV coating layer to block ultraviolet rays.

상기 시트 기재층은 폴리에틸렌(polyethylene), 폴리프로필렌(polypropylene) 또는 폴리에틸렌테레프탈레이트(PET, polyethylene terephthalate)로 이루어질 수 있다.The sheet base layer may be made of polyethylene, polypropylene, or polyethylene terephthalate (PET).

상기 특징에 따른 건축 자재는 상기 기재층의 상부면에 부착되어 있는 무늬 시트를 더 포함할 수 있다.The building material according to the above feature may further include a patterned sheet attached to an upper surface of the base layer.

상기 기판은 목질계 보드, 무기질계 보드 또는 합성수지 보드로 이루어질 수 있다.The substrate may be made of a wood board, an inorganic board, or a synthetic board.

상기 기재층은 수지 함침 크라프트지일 수 있다.The base layer may be a resin impregnated kraft paper.

상기 기재층의 개수는 적어도 하나일 수 있다.The number of the base layer may be at least one.

상기 접착제층과 접하고 있는 상기 기재층의 하부면은 요철면일 수 있다.The lower surface of the base layer in contact with the adhesive layer may be an uneven surface.

본 발명의 다른 특징에 따른 건축 자재의 제조 방법은 기판의 상부면 위에 접착제를 도포하는 단계, 상기 접착제가 도포된 상기 기판의 상부면 위에 기재층을 위치시키는 단계, 상기 기재층의 상부면 위에 무늬 시트를 부착하는 단계, 및 상기 무늬 시트의 상부면 위에 올레핀 시트를 위치시키는 단계를 포함한다.According to another aspect of the present invention, a method of manufacturing a building material includes applying an adhesive on an upper surface of a substrate, placing a substrate layer on an upper surface of the substrate on which the adhesive is applied, and patterning the upper surface of the substrate layer. Attaching the sheet, and positioning the olefin sheet over the top surface of the patterned sheet.

상기 올레핀 시트는 상기 기재층 위에 상기 올레핀 시트를 접착하기 위한 접착제층, 상기 접착제층 위에 위치하는 시트 기재층, 및 상기 시트 기재층 위에 위치하는 코팅층을 포함할 수 있다.The olefin sheet may include an adhesive layer for adhering the olefin sheet on the substrate layer, a sheet substrate layer positioned on the adhesive layer, and a coating layer positioned on the sheet substrate layer.

본 발명의 또 다른 특징에 따른 건축 자재의 제조 방법은 기판의 상부면 위에 접착제를 도포하는 단계, 상기 접착제가 도포된 상기 기판의 상부면 위에 기재층을 위치시키는 단계, 및 상기 기재층의 상부면 위에 무늬층을 구비한 올레핀 시트를 위치시키는 단계를 포함한다.According to another aspect of the present invention, there is provided a method of manufacturing a building material, comprising: applying an adhesive on an upper surface of a substrate, placing a substrate layer on an upper surface of the substrate on which the adhesive is applied, and an upper surface of the substrate layer Positioning an olefin sheet having a patterned layer thereon.

상기 올레핀 시트는 상기 기재층 위에 상기 올레핀 시트를 접착하기 위한 접착제층, 상기 접착제층 위에 위치하는 시트 기재층, 및 상기 시트 기재층 위에 위치하는 코팅층을 더 포함할 수 있고, 상기 무늬층은 상기 접착제층과 상기 시트 기재층 사이 또는 상기 시트 기재층과 상기 코팅층 사이에 위치할 수 있다.The olefin sheet may further include an adhesive layer for adhering the olefin sheet on the substrate layer, a sheet substrate layer positioned on the adhesive layer, and a coating layer positioned on the sheet substrate layer, wherein the pattern layer is the adhesive. It may be located between the layer and the sheet base layer or between the sheet base layer and the coating layer.

이러한 특징에 따르면, 다이옥신 등과 같은 독성 물질의 배출이 이루어는 PVC(pernicious vile compound)로 이루어진 시트 대신에 친환경 물질인 올레핀으로 이루어진 올레핀 시트를 마감재로 사용하므로, 장시간 사용 시에도 유해 물질의 배출이 이루어지지 않는다.According to this feature, instead of the sheet made of PVC (pernicious vile compound) to release the toxic substances such as dioxin, olefin sheet made of olefin, which is an environmentally friendly material, is used as a finishing material. I do not lose.

또한, 수지 성분을 함유하고 있는 크라프트지로 이루어진 기재층을 매개로 하여 올레핀 시트가 기판 위에 부착되므로, 올레핀 시트의 접착력이 증가하여 기판에서 올레핀 시트가 박리되는 현상이 크게 감소하여 건축 자재의 수명이 연장된다.In addition, since the olefin sheet adheres to the substrate via a substrate layer made of kraft paper containing a resin component, the adhesive force of the olefin sheet is increased and the phenomenon in which the olefin sheet is peeled from the substrate is greatly reduced, thereby extending the life of the building material. do.

이처럼, 올레핀 시트와 기재층 간의 접착력이 증가함에 따라, 올레핀 시트와 기재층 사이에 위치한 무늬 시트와 올레핀 시트 사이의 접착력 역시 증가하여, 건축 자재의 무늬의 선명도가 향상된다.As such, as the adhesive force between the olefin sheet and the substrate layer increases, the adhesive force between the pattern sheet and the olefin sheet located between the olefin sheet and the substrate layer also increases, thereby improving the sharpness of the pattern of the building material.

도 1은 본 발명의 일 실시예에 따른 건축 자재의 단면도이다.
도 2는 본 발명의 일 실시예에 따른 건축 자재의 제조 공정을 도시한 순서도이다.
도 3은 본 발명의 다른 실시예에 따른 건축 자재의 단면도이다.
도 4는 본 발명의 다른 실시예에 따른 건축 자재의 제조 공정을 도시한 순서도이다.1 is a cross-sectional view of a building material according to an embodiment of the present invention.
2 is a flowchart illustrating a manufacturing process of a building material according to an embodiment of the present invention.
3 is a cross-sectional view of a building material according to another embodiment of the present invention.
4 is a flowchart illustrating a manufacturing process of a building material according to another embodiment of the present invention.

이하, 첨부된 도면을 참조하여 본 발명의 실시예들을 상세히 설명한다. 본 발명을 설명하는데 있어서, 해당 분야에 이미 공지된 기술 또는 구성에 대한 구체적인 설명을 부가하는 것이 본 발명의 요지를 불분명하게 할 수 있다고 판단되는 경우에는 상세한 설명에서 이를 일부 생략하도록 한다. 또한, 본 명세서에서 사용되는 용어들은 본 발명의 실시예들을 적절히 표현하기 위해 사용된 용어들로서, 이는 해당 분야의 관련된 사람 또는 관례 등에 따라 달라질 수 있다. 따라서, 본 용어들에 대한 정의는 본 명세서 전반에 걸친 내용을 토대로 내려져야 할 것이다.Hereinafter, with reference to the accompanying drawings will be described embodiments of the present invention; In describing the present invention, if it is determined that adding specific descriptions of techniques or configurations already known in the art may make the gist of the present invention unclear, some of them will be omitted from the detailed description. In addition, terms used in the present specification are terms used to properly express the embodiments of the present invention, which may vary according to related persons or customs in the art. Therefore, the definitions of the terms should be made based on the contents throughout the specification.

여기서 사용되는 전문용어는 단지 특정 실시예를 언급하기 위한 것이며, 본 발명을 한정하는 것을 의도하지 않는다. 여기서 사용되는 단수 형태들은 문구들이 이와 명백히 반대의 의미를 나타내지 않는 한 복수 형태들도 포함한다. 명세서에서 사용되는 '포함하는'의 의미는 특정 특성, 영역, 정수, 단계, 동작, 요소 및/또는 성분을 구체화하며, 다른 특정 특성, 영역, 정수, 단계, 동작, 요소, 성분 및/또는 군의 존재나 부가를 제외시키는 것은 아니다.The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. As used herein, the singular forms “a,” “an,” and “the” include plural forms as well, unless the phrases clearly indicate the opposite. As used herein, the meaning of “comprising” specifies a particular characteristic, region, integer, step, operation, element, and / or component, and other specific characteristics, region, integer, step, operation, element, component, and / or group. It does not exclude the presence or addition of.

이하, 첨부된 도면을 참조하여 본 발명의 일 실시예에 따른 건축 자재 및 그 제조 방법에 대해서 설명하도록 한다.Hereinafter, with reference to the accompanying drawings will be described for a building material and a manufacturing method according to an embodiment of the present invention.

먼저, 도 1을 참고로 하여 본 발명의 일 실시예에 따른 건축 자재에 대하여 설명한다.First, a building material according to an embodiment of the present invention will be described with reference to FIG. 1.

도 1을 참고로 하면, 기판(10), 접착제층(20)에 의해 기판(10)의 상부면에 부착되어 있는 기재층(30), 기재층(20) 위에 부착되어 있는 무늬 시트(40), 그리고 무늬 시트(40)의 상부면에 위치하는 올레핀(olefin) 시트(50)를 구비한다.Referring to FIG. 1, the substrate 10, the substrate layer 30 attached to the upper surface of the substrate 10 by the adhesive layer 20, and the pattern sheet 40 attached on the substrate layer 20. And an olefin sheet 50 positioned on the upper surface of the pattern sheet 40.

기판(10)은 합판이나 MDF(medium density fiberboard) 등의 목질계 보드, 석고 보드나 마그네슘 보드와 같은 무기질계 보드, 또는 합성수지로 이루어진 합성수지 보드 등으로 이루어져 있는 층으로서, 본 예의 건축 자재의 바닥면을 이룬다.The substrate 10 is a layer made of plywood or wood-based boards such as MDF (medium density fiberboard), inorganic boards such as gypsum board or magnesium board, or synthetic resin board made of synthetic resin. To achieve.

기재층(30)은 그 위에 위치하는 무늬 시트(40)와의 접착력을 증가시키기 위한 층으로서, 크라프트지(kraft paper)로 이루어져 있다.The base material layer 30 is a layer for increasing the adhesive force with the patterned sheet 40 located thereon, and is made of kraft paper.

이때, 크라프트지는 수지에 설정 시간 동안 함침된 수지 함침 크라프트지일 수 있다.In this case, the kraft paper may be a resin impregnated kraft paper impregnated with a resin for a predetermined time.

크라프트지가 함침되는 수지액에 사용되는 수지는 페놀 수지, 아크릴 수지, 에폭시 수지, PVAc(polyvinyl acetate) 수지, 멜라민(melamine) 수지, 요소 수지, 우레탄 수지 또는 PVA(poly vinyl alcohol) 수지 등일 수 있다.The resin used for the resin solution impregnated with kraft paper may be a phenol resin, an acrylic resin, an epoxy resin, a polyvinyl acetate (PVAc) resin, a melamine resin, a urea resin, a urethane resin, or a PVA (poly vinyl alcohol) resin.

이러한 기재층(30)은 이미 기술한 것처럼 접착제층(20)에 의해 기판(10)의 상부면에 접착되어 있다.This base material layer 30 is adhered to the upper surface of the substrate 10 by the adhesive layer 20 as described above.

이처럼, 기재층(30)을 기판(10) 위에 접착하기 위해 사용되는 접착제는 열경화성 접착제, 열가소성 접착제 또는 상온 경화 접착제가 사용될 수 있다.As such, the adhesive used to adhere the substrate layer 30 onto the substrate 10 may be a thermosetting adhesive, a thermoplastic adhesive, or a room temperature curing adhesive.

이때, 접착제가 도포되어 접착제층(20)이 형성되는 기재층(30)의 하부면은 요철면을 갖고 있으므로, 기판(10)과의 접착력이 향상되어 기재층(30)과 기판(10)의 박리 현상이 크게 감소한다. 따라서, 본 예의 건축 자재의 수명이 증가하여 사용자의 만족도가 향상된다.At this time, since the lower surface of the base material layer 30 on which the adhesive is applied to form the adhesive layer 20 has an uneven surface, the adhesive force with the substrate 10 is improved, so that the base material layer 30 and the substrate 10 Peeling phenomenon is greatly reduced. Therefore, the life of the building material of the present example is increased, and the user's satisfaction is improved.

이때, 기재층(30)의 요철면은 샌더(sander)를 사용한 샌딩 공법, 샌드블라스트법 또는 코로나 공정 등을 이용하여 형성될 수 있다. In this case, the uneven surface of the base layer 30 may be formed using a sanding method using a sander, a sandblasting method, a corona process, or the like.

이러한 기재층(30)의 무게는 150g/m2~300g/m2일 수 있다.The weight of the base layer 30 may be 150g / m 2 ~ 300g / m 2 .

하지만, 대안적인 예에서, 기재층(30)의 하부면은 요철면이 아닌 평탄면을 가질 수 있다.However, in an alternative example, the bottom surface of the substrate layer 30 may have a flat surface rather than an uneven surface.

무늬 시트(40)는 외부로 노출되는 건축 자재의 무늬를 결정하는 층으로서 나무 무늬 등과 같이 다양한 무늬가 인쇄되어 있는 시트이다.The pattern sheet 40 is a layer for determining the pattern of the building material exposed to the outside is a sheet is printed a variety of patterns, such as wood pattern.

이러한 무늬 시트(40)의 하부면에는 접착제가 함침 처리되어 있으므로, 기재층(30)의 상부면 위에 별도로 접착제를 도포할 필요없이 기재층(30)의 상부면에 바로 무늬 시트(40)를 부착하여 기재층(30) 위에 무늬 시트(40)를 위치시킨다.Since the adhesive is impregnated on the lower surface of the pattern sheet 40, the pattern sheet 40 is directly attached to the upper surface of the substrate layer 30 without the need to apply an adhesive on the upper surface of the substrate layer 30. The pattern sheet 40 is positioned on the base layer 30.

하지만, 대안적인 예에서, 무늬 시트(40)는 접착제가 함침 처리 되지 않을 수 있고, 이 경우, 기재층(30) 상부면에 별도의 접착제 도포 동작이 행해질 수 있다.However, in an alternative example, the pattern sheet 40 may not be impregnated with an adhesive, and in this case, a separate adhesive coating operation may be performed on the upper surface of the base layer 30.

올레핀 시트(50)는 투명한 시트로서, 그 하부에 위치한 무늬 시트(40)의 무늬가 외부로 드러나게 된다.The olefin sheet 50 is a transparent sheet, and the pattern of the pattern sheet 40 disposed below is exposed to the outside.

이러한 올레핀 시트(50)는 시트 기재층(53), 시트 기재(53)의 하부면에 위치한 접착제층(51), 시트 기재층(53)의 상부면에 위치한 코팅층(55)을 구비한다.The olefin sheet 50 includes a sheet base layer 53, an adhesive layer 51 located on the bottom surface of the sheet base 53, and a coating layer 55 located on the top surface of the sheet base layer 53.

시트 기재층(53)은 폴리에틸렌(polyethylene), 폴리프로필렌(polypropylene) 또는 폴리에틸렌테레프탈레이트(PET, polyethylene terephthalate) 등으로 이루어질 수 있다.The sheet base layer 53 may be made of polyethylene, polypropylene, or polyethylene terephthalate (PET).

접착제층(51)은 시트 기재층(53)을 무늬 시트(40)의 상부면에 부착하기 위한 층으로서, 접착제의 도포에 의해 형성된다. 이때, 사용되는 접착제 역시 열경화성 접착제나 열가소성 접착제가 이용될 수 있다.The adhesive layer 51 is a layer for attaching the sheet base layer 53 to the upper surface of the pattern sheet 40 and is formed by application of an adhesive. At this time, the adhesive used may also be a thermosetting adhesive or a thermoplastic adhesive.

이러한 접착제층(51)은 바닥재 프라이머(primer)의 기능을 수행할 수 있어 시트 기재층(53)의 하부면의 상태를 균일하게 해주고 시트 기재층(53)을 보호하여 하부의 무늬 시트(40)와의 접착 상태와 접착력을 향상시킬 수 있다.The adhesive layer 51 may perform a function of a flooring primer to uniformize the state of the lower surface of the sheet base layer 53 and protect the sheet base layer 53 so that the lower pattern sheet 40 Adhesion state and adhesive force with can be improved.

이러한 프라이버 기능을 위해 접착제층(51)은 폴리우레탄(PU, PolyUrethane)계 물질, 불포화폴리에스터(UPE, Unsaturated polyEster)계 물질 또는 핫 멜트(Hot melt)계 물질 등을 이용해 형성될 수 있다.코팅층(55)은 본 예의 건축 자재의 최상부층을 이루는 층으로서 외부의 충격이나 힘으로 인한 흠집 발생을 최소화하며 표면을 매끄럽게 해준다.For the privacy function, the adhesive layer 51 may be formed using a polyurethane (PU, PolyUrethane) material, an unsaturated polyester (UPE, Unsaturated polyEster) material, or a hot melt material. Coating layer 55 is a layer forming the top layer of the building material of the present example to minimize the occurrence of scratches due to external impact or force and smooth the surface.

본 예의 코팅층(55)은 자외선(UV)을 차단해주는 UV 코팅으로서, 자외선으로 인해 건축 자재가 탈색되거나 황변 또는 갈변 현상을 방지한다.The coating layer 55 of the present example is a UV coating that blocks ultraviolet rays (UV), and prevents discoloration or yellowing or browning of building materials due to ultraviolet rays.

이러한 코팅층(55)으로 인해, 하부에 위치한 무늬 시트(40)에 인쇄된 무늬가 외부로 좀 더 선명하고 자연스럽게 노출되어 건축 자재의 고급화가 이루어지며, 또한 건축 자재는 쉽게 변형되거나 휘지 않으며 습기에 강하여 내구성과 수명이 향상된다. Due to the coating layer 55, the pattern printed on the pattern sheet 40 located at the bottom is exposed to the outside more vividly and naturally to make the building material high-quality, and also the building material is not easily deformed or bent and is resistant to moisture. Durability and service life are improved.

이와 같이, 본 예의 건축 자재는 다이옥신 등과 같은 독성 물질의 배출이 이루어는 PVC(pernicious vile compound)로 이루어진 시트 대신에 친환경 물질인 올레핀으로 이루어진 올레핀 시트를 마감재로 사용하므로, 장시간 사용 시에도 유해 물질의 배출이 이루어지지 않는다.As described above, the building material of the present example uses an olefin sheet made of environmentally friendly olefins as a finishing material instead of a sheet made of PVC (pernicious vile compound) in which toxic substances such as dioxins are discharged. No discharge is made.

또한, 수지 성분을 함유하고 있는 크라프트지로 이루어진 기재층(30)을 매개로 하여 올레핀 시트(50)가 기판(10) 위에 부착되므로, 기판(10)에서 올레핀 시트(50)가 박리되는 현상이 크게 감소한다. In addition, since the olefin sheet 50 is attached onto the substrate 10 via the substrate layer 30 made of kraft paper containing the resin component, the phenomenon in which the olefin sheet 50 is peeled off from the substrate 10 is greatly increased. Decreases.

즉, 본 예의 기재층(30)은 수지 성분을 함유하고 있는 수지 함침 크라프트지로 이루어져 있으므로, 크리프트지에 함유된 수지 성분에 의해 올레핀 시트(50)와 기재층(30) 간의 접착력 및 기재층(30)과 기판(10) 간의 접착력이 더욱 향상되므로, 올레핀 시트(50)가 기판(10)으로부터 박리되는 현상이 크게 감소한다. 이로 인해, 본 예의 건축 자재의 수명이 증가한다.That is, since the base material layer 30 of this example consists of resin impregnated kraft paper containing a resin component, the adhesive force between the olefin sheet 50 and the base material layer 30 and the base material layer 30 by the resin component contained in a kraft paper ), The adhesion between the substrate 10 and the substrate 10 is further improved, so that the phenomenon in which the olefin sheet 50 is peeled from the substrate 10 is greatly reduced. For this reason, the lifetime of the building material of this example increases.

또한, 올레핀 시트(50)와 기재층(30) 간의 접착력이 증가함에 따라, 올레핀 시트(50)와 기재층(30) 사이에 위치한 무늬 시트(40)와 올레핀 시트(50) 사이의 접착력 역시 증가하게 된다.In addition, as the adhesion between the olefin sheet 50 and the substrate layer 30 increases, the adhesion between the olefin sheet 50 and the olefin sheet 50 positioned between the olefin sheet 50 and the substrate layer 30 also increases. Done.

이로 인해, 투명한 올레핀 시트(50)를 통해 외부로 비춰지는 무늬 시트(40)의 무늬의 선명도는 더욱더 증가한다.As a result, the sharpness of the pattern of the pattern sheet 40 projected to the outside through the transparent olefin sheet 50 is further increased.

도 1에 도시한 건축 자재에서, 하나의 기재층(30)이 위치하지만, 이와는 달리 두 개 이상의 기재층(30)이 연속해 위치할 수 있다.In the building material shown in FIG. 1, one substrate layer 30 is located, but alternatively two or more substrate layers 30 may be located in succession.

이때, 복수 개의 기재층(30)은 열처리 공정이나 별도의 접착제 등을 이용하여 서로 인접한 기재층(30)과 접착될 수 있다.In this case, the plurality of substrate layers 30 may be adhered to the substrate layers 30 adjacent to each other by using a heat treatment process or a separate adhesive.

적층되는 기재층(30)의 개수는 건축 자재의 사용 용도에 따른 건축 자재의 강도나 두께 등에 따라 정해질 수 있다.The number of the base material layers 30 to be laminated may be determined according to the strength or thickness of the building material according to the use of the building material.

이러한 본 예의 건축 자재에 대한 제조 공정에 대하여 도 2를 참고로 하여 설명한다.The manufacturing process for this building material of this example is demonstrated with reference to FIG.

도 2에 도시한 것처럼, 먼저, 기판(10)의 상부면 위에 접착제를 도포한 후(S11), 요철면을 구비한 기재층(20)을 접착제가 도포된 기판(10)의 상부면에 위치시킨다(S13). 이때, 기재층(20)의 요철면이 기판(10)의 상부면과 접하도록 위치시킨다.As shown in FIG. 2, first, an adhesive is applied on the upper surface of the substrate 10 (S11), and then the base layer 20 having the uneven surface is positioned on the upper surface of the substrate 10 on which the adhesive is applied. (S13). At this time, the uneven surface of the substrate layer 20 is positioned in contact with the upper surface of the substrate 10.

다음, 기재층(20)의 상부면 즉, 요철면의 반대편에 위치한 평탄면 위에 접착제가 함침 처리되어 있거나 함침 처리되지 않은 무늬 시트(40)를 부착하여, 기재층(20)의 상부면에 무늬 시트(40)를 위치시킨다(S15).Next, an adhesive-impregnated or unimpregnated pattern sheet 40 is attached to an upper surface of the substrate layer 20, that is, a flat surface opposite to the uneven surface, and the pattern is formed on the upper surface of the substrate layer 20. Position the sheet 40 (S15).

그런 다음, 무늬 시트(40) 위에 접착제가 도포된 올레핀 시트(50)를 위치시킨 후(S17) 열처리 동작을 실시하여 접착제를 경화시켜 접착제층(20, 51)을 형성한다. 이때, 접착제층(51)은 프라이머 기능을 구비할 수 있다.Then, after placing the olefin sheet 50 coated with the adhesive on the pattern sheet (40) (S17) is subjected to a heat treatment operation to cure the adhesive to form the adhesive layer (20, 51). At this time, the adhesive layer 51 may have a primer function.

이때, 접착제층(20 51)을 위한 열처리 공정은 각 접착제층(20, 51)을 개별적으로 형성하기 위해 복수 회 행해질 수 있다.In this case, the heat treatment process for the adhesive layer 20 51 may be performed a plurality of times to individually form the adhesive layers 20 and 51.

또한, 대안적인 예에서, 올레핀 시트(50)의 상부면에 위치한 코팅층(55)은 별도의 공정을 통해 형성될 수 있다. Also, in an alternative example, the coating layer 55 located on the top surface of the olefin sheet 50 may be formed through a separate process.

즉, 시트 기재층(53)의 하부면에 접착제를 도포하여 예비 올레핀 시트를 형성하여, 형성된 예비 올레핀 시트를 데코 시트(40) 위에 위치시킨 다음, 시트 기재층(53)의 상부면에 코팅제를 도포한 후 열처리 공정을 통해 접착제층(20, 51)과 코팅층(55)을 구비한 올레핀 시트(50)를 형성해, 건축 자재를 완성할 수 있다. 물론 이 경우에도, 열처리 동작은 필요할 때마다 별개의 공정으로 복수 번 행해질 수 있다.In other words, an adhesive is applied to the lower surface of the sheet base layer 53 to form a preliminary olefin sheet, and the preliminary olefin sheet formed is placed on the decor sheet 40, and then a coating agent is applied to the upper surface of the sheet base layer 53. After coating, the olefin sheet 50 including the adhesive layers 20 and 51 and the coating layer 55 may be formed through a heat treatment process to complete a building material. Of course, even in this case, the heat treatment operation may be performed a plurality of times in a separate process whenever necessary.

본 예에서, 접착제가 상온 경화형 접착제를 이용하는 경우, 해당 접착제층(20, 51)을 형성하기 위한 열처리 공정은 생략된다.In the present example, when the adhesive uses a room temperature curing type adhesive, the heat treatment step for forming the adhesive layers 20 and 51 is omitted.

다음, 도 3을 참고로 하여, 본 발명의 다른 실시예에 따른 건축 자재를 설명한다.Next, a building material according to another embodiment of the present invention will be described with reference to FIG. 3.

도 1과 비교하여, 동일한 구조를 갖고 같은 기능을 수행하는 구성요소에 대해서는 도 1의 도면 부호와 같은 도면 보호를 부여하였고 그에 대한 자세한 설명 역시 생략한다.Compared to FIG. 1, components having the same structure and performing the same function are given the same protection as those of FIG. 1, and detailed description thereof is also omitted.

도 3에 도시한 본 예의 건축 자재는 기판(10), 기판(10) 위에 위치하는 기재층(30), 기판(10)과 기재층(30) 사이에 위치한 접착제층(20), 그리고 기재층(30) 위에 위치하며 투명한 올레핀 시트(50a)를 구비한다.The building material of this example shown in FIG. 3 includes a substrate 10, a substrate layer 30 positioned on the substrate 10, an adhesive layer 20 located between the substrate 10 and the substrate layer 30, and a substrate layer. Located above 30 and having a transparent olefin sheet 50a.

이러한 본 예의 건축 자재는 별도의 무늬 시트는 구비하지 않는 대신 본 예의 올레핀 시트(50a)의 상부나 하부에 원하는 무늬를 인쇄한 무늬층을 구비하고 있다.The building material of this example is not provided with a separate pattern sheet, but is provided with the pattern layer which printed the desired pattern on the upper part or the lower part of the olefin sheet 50a of this example.

따라서, 도 3에 도시한 것처럼, 올레핀 시트(50a)는 도 1의 올레핀 시트(50)와 동일하게 시트 기재층(53), 시트 기재층(53)의 하부에 위치한 접착제층(51), 그리고 시트 기재층(53)의 상부에 위치한 코팅층(55)을 구비한다. Thus, as shown in FIG. 3, the olefin sheet 50a is the same as the olefin sheet 50 of FIG. 1, the sheet base layer 53, the adhesive layer 51 positioned below the sheet base layer 53, and The coating layer 55 is positioned on the sheet base layer 53.

이에 추가적으로 본 예의 올레핀 시트(50a)는 코팅층(55)과 시트 기재층(53) 사이 또는 올레핀 시트(53)의 하부면과 접착제층(51) 사이에 위치한 무늬층(57)을 구비한다.In addition, the olefin sheet 50a of the present example includes a pattern layer 57 positioned between the coating layer 55 and the sheet base layer 53 or between the lower surface of the olefin sheet 53 and the adhesive layer 51.

무늬층(57)은 잉크를 코팅해 원하는 무늬를 형성한 층으로서, 무늬층(57)의 무늬가 올레핀 시트(50a)의 외부로 비춰진다.The pattern layer 57 is a layer which coats ink and forms a desired pattern, and the pattern of the pattern layer 57 is reflected to the exterior of the olefin sheet 50a.

이와 같이, 별도의 무늬 시트가 생략되므로, 무늬 시트의 부착 시 발생하는 불량율이 감소하여, 본 예의 건축 자재에 대한 수율이 향상된다.In this way, since the separate pattern sheet is omitted, the defective rate generated when the pattern sheet is attached is reduced, and the yield for the building material of the present example is improved.

이러한 건축 자재는 도 4와 같은 하나의 예시적인 공정을 통해 제조될 수 있다.Such building materials may be manufactured through one exemplary process such as FIG. 4.

즉, 도 4에 도시한 것처럼, 기판(10)의 상부면 위에 접착제를 도포하고(S21), 접착제가 도포된 기판(10)의 상부면 위에 요철면을 구비한 기재층(30)을 위치시킨다(S23). 이미 기술한 것처럼, 접착제와 기재층(30) 간의 접착력을 증가시키기 위해 요철면이 접착제와 접착하도록 기재층(30)을 기판(10)의 상부면에 위치시킨다.That is, as shown in FIG. 4, the adhesive is applied on the upper surface of the substrate 10 (S21), and the base layer 30 having the uneven surface is placed on the upper surface of the substrate 10 to which the adhesive is applied. (S23). As already described, the substrate layer 30 is positioned on the upper surface of the substrate 10 so that the uneven surface adheres to the adhesive to increase the adhesive force between the adhesive and the substrate layer 30.

그런 다음, 무늬층(57) 및 코팅층(55)이 위치하고 하부면에 접착제가 도포된 올레핀 시트(50a)를 기재층(30) 위에 위치시킨 후(S25) 열처리하여, 접착제층(20, 51)을 이용해 기판(10)에 기재층(30)를 접착시키고 기재층(30) 위에 올레핀 시트(50a)를 접착시켜 건축 자재를 완성한다.Then, the pattern layer 57 and the coating layer 55 is positioned and the olefin sheet 50a coated with an adhesive on the lower surface is placed on the base layer 30 (S25) and then heat treated to form an adhesive layer (20, 51) The base material layer 30 is adhered to the substrate 10 using the substrate, and the olefin sheet 50a is adhered on the base material layer 30 to complete the building material.

대안적인 예에서, 무늬층(57)과 코팅층(55)은 형성되지 않고 시트 기재층(53)의 하부에 접착제만 도포된 예비 올레핀 시트를 먼저 기재층(30) 위에 위치시킨 후 열처리하여 접착제층(20)을 이용해 기판(10)과 기재층(30)을 접착하고 또한 접착제층(51)을 이용해 기재층(30) 위에 예비 올레핀 시트를 접착시킨 다음, 예비 올레핀 시트의 상부면에 원하는 색상의 잉크를 인쇄하여 인쇄층(55)을 형성하고 다시 코팅층(55)을 형성할 수 있다. In an alternative example, the pattern layer 57 and the coating layer 55 are not formed, and the pre-olefin sheet having only an adhesive applied to the bottom of the sheet base layer 53 is first placed on the base layer 30 and then heat treated to form an adhesive layer. (20) to bond the substrate 10 and the base layer 30, and also to the pre-olefin sheet on the base layer 30 using the adhesive layer 51, and then to the upper surface of the pre-olefin sheet of the desired color The ink may be printed to form the printing layer 55 and the coating layer 55 may be formed again.

이때, 각 층(57, 55)의 형성과 접착제(20, 51)를 이용한 접착 동작을 위한 열처리 공정에 한번에 행해지거나 필요에 따라 별개의 공정으로 행해질 수 있다.At this time, the heat treatment process for the formation of each layer (57, 55) and the adhesive operation using the adhesive (20, 51) may be performed at once or may be performed in a separate process as necessary.

도 1을 참고로 하여 이미 기술한 것처럼, 기재층(30)의 개수 역시 적어도 하나 이상일 수 있다.As already described with reference to FIG. 1, the number of base layers 30 may also be at least one.

본 실시예에 따른 건축 자재는 마루 바닥재와 같은 바닥재로 사용될 수 있다.The building material according to the present embodiment can be used as a flooring material such as a flooring flooring.

이상, 본 발명의 건축 자재 및 그 제조 방법의 실시예들에 대해 설명하였다. 본 발명은 상술한 실시예 및 첨부한 도면에 한정되는 것은 아니며, 본 발명이 속하는 분야에서 통상의 지식을 가진 자의 관점에서 다양한 수정 및 변형이 가능할 것이다. 따라서 본 발명의 범위는 본 명세서의 청구범위뿐만 아니라 이 청구범위와 균등한 것들에 의해 정해져야 한다.In the above, the Example of the building material of this invention and its manufacturing method was demonstrated. The present invention is not limited to the above-described embodiment and the accompanying drawings, and various modifications and variations will be possible in view of those skilled in the art to which the present invention pertains. Therefore, the scope of the present invention should be defined not only by the claims of the present specification but also by the equivalents of the claims.

10: 기판 20, 51: 접착제층
30: 기재층 40: 무늬 시트
50, 50a: 올레핀 시트 53: 시트 기재층
55: 코팅층 57: 무늬층10: substrate 20, 51: adhesive layer
30: base material layer 40: pattern sheet
50, 50a: olefin sheet 53: sheet base material layer
55: coating layer 57: pattern layer

Claims (14)

기판;
상기 기판 위에 위치하는 기재층;
상기 기판과 상기 기재층 사이에 위치하여 상기 기판 위에 상기 기재층을 접착시키는 접착제층; 및
상기 기재층 위에 위치하는 올레핀 시트
를 포함하는 건축 자재.Board;
A substrate layer on the substrate;
An adhesive layer disposed between the substrate and the substrate layer to bond the substrate layer on the substrate; And
Olefin sheet located on the base layer
Building materials, including. 제1항에서,
상기 올레핀 시트는,
상기 기재층 위에 상기 올레핀 시트를 접착하기 위한 접착제층;
상기 접착제층 위에 위치하는 시트 기재층; 및
상기 시트 기재층 위에 위치하는 코팅층
을 포함하는 건축 자재.In claim 1,
The olefin sheet,
An adhesive layer for adhering the olefin sheet on the substrate layer;
A sheet base layer positioned on the adhesive layer; And
Coating layer positioned on the sheet base layer
Building materials, including. 제2항에서,
상기 올레핀 시트는 상기 시트 기재층과 상기 코팅층 사이에 위치하는 무늬층을 더 포함하는 건축 자재.In claim 2,
The olefin sheet further comprises a patterned layer located between the sheet base layer and the coating layer. 제2항에서,
상기 코팅층은 자외선을 차단하는 UV 코팅층인 건축 자재.In claim 2,
The coating layer is a building material which is a UV coating layer to block ultraviolet rays. 제2항에서,
상기 시트 기재층은 폴리에틸렌(polyethylene), 폴리프로필렌(polypropylene) 또는 폴리에틸렌테레프탈레이트(PET, polyethylene terephthalate)로 이루어져 있는 건축 자재.In claim 2,
The sheet base layer is a building material consisting of polyethylene (polyethylene), polypropylene (polypropylene) or polyethylene terephthalate (PET, polyethylene terephthalate). 제1항에서,
상기 기재층의 상부면에 부착되어 있는 무늬 시트를 더 포함하는 건축 자재.In claim 1,
Building material further comprising a patterned sheet attached to the upper surface of the base layer. 제1항에서,
상기 기판은 목질계 보드, 무기질계 보드 또는 합성수지 보드로 이루어져 있는 건축 자재.In claim 1,
The substrate is a building material consisting of wood-based board, inorganic board or synthetic resin board. 제1항에서,
상기 기재층은 수지 함침 크라프트지인 건축 자재.In claim 1,
The base material layer is a building material of resin impregnated kraft paper. 제1항 또는 제8항에서,
상기 기재층의 개수는 적어도 하나인 건축 자재.In claim 1 or 8,
The number of the base material layers is at least one building material. 제1항에서,
상기 접착제층과 접하고 있는 상기 기재층의 하부면은 요철면인 건축 자재.In claim 1,
The lower surface of the said base material layer which contact | connects the said adhesive bond layer is a building material. 기판의 상부면 위에 접착제를 도포하는 단계;
상기 접착제가 도포된 상기 기판의 상부면 위에 기재층을 위치시키는 단계;
상기 기재층의 상부면 위에 무늬 시트를 부착하는 단계; 및
상기 무늬 시트의 상부면 위에 올레핀 시트를 위치시키는 단계
를 포함하는 건축 자재의 제조 방법.Applying an adhesive over the top surface of the substrate;
Positioning a substrate layer on an upper surface of the substrate to which the adhesive is applied;
Attaching a patterned sheet on an upper surface of the base layer; And
Positioning an olefin sheet on an upper surface of the patterned sheet
Method of manufacturing a building material comprising a. 제11항에서,
상기 올레핀 시트는,
상기 기재층 위에 상기 올레핀 시트를 접착하기 위한 접착제층;
상기 접착제층 위에 위치하는 시트 기재층; 및
상기 시트 기재층 위에 위치하는 코팅층
을 포함하는 건축 자재의 제조 방법.In claim 11,
The olefin sheet,
An adhesive layer for adhering the olefin sheet on the substrate layer;
A sheet base layer positioned on the adhesive layer; And
Coating layer positioned on the sheet base layer
Method of manufacturing a building material comprising a. 기판의 상부면 위에 접착제를 도포하는 단계;
상기 접착제가 도포된 상기 기판의 상부면 위에 기재층을 위치시키는 단계; 및
상기 기재층의 상부면 위에 무늬층을 구비한 올레핀 시트를 위치시키는 단계
를 포함하는 건축 자재의 제조 방법.Applying an adhesive over the top surface of the substrate;
Positioning a substrate layer on an upper surface of the substrate to which the adhesive is applied; And
Positioning an olefin sheet having a patterned layer on an upper surface of the substrate layer
Method of manufacturing a building material comprising a. 제13항에서,
상기 올레핀 시트는,
상기 기재층 위에 상기 올레핀 시트를 접착하기 위한 접착제층;
상기 접착제층 위에 위치하는 시트 기재층; 및
상기 시트 기재층 위에 위치하는 코팅층
을 더 포함하고,
상기 무늬층은 상기 접착제층과 상기 시트 기재층 사이 또는 상기 시트 기재층과 상기 코팅층 사이에 위치하는
건축 자재의 제조 방법.
In claim 13,
The olefin sheet,
An adhesive layer for adhering the olefin sheet on the substrate layer;
A sheet base layer positioned on the adhesive layer; And
Coating layer positioned on the sheet base layer
More,
The pattern layer is located between the adhesive layer and the sheet base layer or between the sheet base layer and the coating layer.
Method of manufacturing building materials.
KR1020180033152A 2018-03-22 2018-03-22 Building material and method for manufacturing the same KR20190111251A (en)