KR102641658B1 - Preparation Method for Eco-friendly Ice Pack Wrapping Paper - Google Patents
Preparation Method for Eco-friendly Ice Pack Wrapping Paper Download PDFInfo
- Publication number
- KR102641658B1 KR102641658B1 KR1020210091984A KR20210091984A KR102641658B1 KR 102641658 B1 KR102641658 B1 KR 102641658B1 KR 1020210091984 A KR1020210091984 A KR 1020210091984A KR 20210091984 A KR20210091984 A KR 20210091984A KR 102641658 B1 KR102641658 B1 KR 102641658B1
- Authority
- KR
- South Korea
- Prior art keywords
- film
- ice pack
- eco
- manufacturing
- solvent
- Prior art date
Abstract
본원에서는 친환경 아이스팩 포장재의 제조방법이 개시된다. 일실시예에 따른 친환경 아이스팩 포장지의 제조방법은, 저밀도 폴리에틸렌(LDPE)를 포함하는 제1 필름을 제조하는 단계; 고밀도 폴리에틸렌(HDPE)를 포함하는 제2 필름을 제조하는 단계; 및 제1 필름과 제2 필름을 무용제 접착제를 이용하여 상기 제1 필름과 상기 제2필름을 접착시키는 단계를 포함한다.Herein, a method for manufacturing an eco-friendly ice pack packaging material is disclosed. A method of manufacturing eco-friendly ice pack packaging according to one embodiment includes manufacturing a first film containing low-density polyethylene (LDPE); producing a second film comprising high density polyethylene (HDPE); and bonding the first film and the second film to the first film and the second film using a solvent-free adhesive.
Description
아래 실시예들은 친환경 아이스팩 포장지의 제조방법 또는 이에 의해 제조된 친환경 아이스팩 포장지 기술에 관한 것이다. The examples below relate to a method of manufacturing eco-friendly ice pack packaging or the technology of eco-friendly ice pack packaging produced thereby.
최근 운송업이 발달하면서 빠른 배송이 필요한 음식물에 대한 운송도 증가하고 있다.With the recent development of the transportation industry, the transportation of food that requires rapid delivery is also increasing.
음식물은 상온에 노출되면 빠르게 부패되기 때문에 저온에 보관하여 신선도를 유지시켜줘야 한다. 따라서, 음식물 운송 시에는 운송 수단에 냉동 및 냉장 보관이 가능한 수단이 별도로 필요하고, 소량의 음식물을 개별적으로 운송할 때에는 음식물이 담긴 상자 안에 드라이아이스나 아이스팩을 넣어 음식물의 부패를 방지한다.Food spoils quickly when exposed to room temperature, so it must be stored at low temperatures to maintain freshness. Therefore, when transporting food, a separate means of freezing and refrigeration is required, and when transporting a small amount of food individually, dry ice or ice packs are placed in the box containing the food to prevent spoilage of the food.
기존 아이스팩 포장지는 PET(Polyethylene terephthalate) 와 LDPE의 또는 NY(Nylon)와 LDPE의 두 가지 필름 합지로서, 두가지 필름의 합지는 LDPE를 필름 형태로 압출하여 유독한 휘발성 유기 화합물이 혼합된 접착제로 전처리된 필름에 붙여서 두 가지 필름을 합지하는 T-DIE(Extrusion Laminating) 공정으로 만들어지고 있다. 외층에는 제품의 내용물을 표시하는 인쇄층 및 외층의 손상(긁힘, 빛에 의한 변색 등)을 방지하기 위한 코팅층이 설치될 수 있다.Existing ice pack packaging is a composite of two films: PET (Polyethylene terephthalate) and LDPE, or NY (Nylon) and LDPE. The composite of the two films is pre-treated with an adhesive mixed with toxic volatile organic compounds by extruding LDPE into a film form. It is made using the T-DIE (Extrusion Laminating) process, which laminates two films by attaching them to a film. The outer layer may be provided with a printing layer that displays the contents of the product and a coating layer to prevent damage to the outer layer (scratches, discoloration by light, etc.).
이러한 다층포장재는 기존의 식품 포장인 캔이나 병보다 가볍고, 납작한 봉지 모양이라서 공간을 적게 차지하고, 개봉하기 쉽고 포장이 가볍고 유연해서 다칠 위험이 적고, 공기와 세균을 완전히 제거한 상태에서 밀봉되므로 보존료 등의 첨가물을 넣지 않아도 장기간 보존할 수 있고, 포장비가 저렴하고 제조과정에서 소모되는 에너지가 캔이나 병보다 1/4 정도 밖에 들지 않다는 장점이 있다.These multi-layer packaging materials are lighter than existing food packaging such as cans or bottles, take up less space because they are flat bag-shaped, are easy to open, and the packaging is light and flexible, so there is less risk of injury. It is sealed with air and bacteria completely removed, so no preservatives, etc. It has the advantage of being able to be stored for a long time without adding additives, packaging costs are low, and the energy consumed during the manufacturing process is only about 1/4 that of cans or bottles.
따라서, 포장지가 대부분 불투명해 변질된 제품 식별이 곤란하고, 뾰족하거나 날카로운 물체에 포장이 쉽게 파손되어 내용물이 흘러나올 수 있다는 단점에도 불구하고, 아이스팩 포장에는 이와 같은 장점을 가진 다층 포장재가 주로 사용되고 있다.Therefore, despite the disadvantages of the fact that most of the packaging is opaque, making it difficult to identify spoiled products, and that the packaging can be easily damaged by pointed or sharp objects and the contents may spill, multi-layer packaging materials with these advantages are mainly used for ice pack packaging. .
그러나, 최근 들어, 환경 문제에 대한 이슈가 많이 제기되면서 아이스팩 뿐만 아니라 아이스팩을 포장하는 포장재에 대해서도 친환경성에 대한 요구가 증가하고 있다. 기존의 아이스팩용 다층 포장재는 석유 유래의 플라스틱 제품을 사용한 것으로, 사용된 다층 포장재는 분리수거가 잘 이루어지지 않을 뿐만 아니라, 분리수거된 경우에도 재활용이 어려우며, 이를 소각, 매립하는 경우 유독가스가 발생하여 대기오염을 유발하고, 매립공간의 부족 및 환경오염을 유발시키는 원인이 된다. 이러한 기존의 아이스팩 포장재는 비닐류 “Other”로 분류되는 것으로 분리수거 되지 않기 문에 재활용성이 떨어지는 문제가 있다.However, in recent years, as many environmental issues have been raised, the demand for eco-friendliness is increasing not only for ice packs but also for the packaging materials used to package ice packs. Existing multi-layer packaging materials for ice packs use petroleum-derived plastic products. The multi-layer packaging materials used are not only difficult to separate and collect, but are also difficult to recycle even when separated, and toxic gases are generated when incinerated or landfilled. This causes air pollution, lack of landfill space, and environmental pollution. These existing ice pack packaging materials are classified as vinyl “Other” and are not separately collected, so there is a problem of low recyclability.
이러한 상황에서 본 발명자는 아이스팩 포장재로서 산소투과도 및 수분 투과도가 기준치 이하이며, 생분해성이 우수하여 재활용이 가능한 친환경 아이스팩 포장재를 개발하고자 노력하였으며, 그 결과 분리수거 분류상 비닐류 LDPE로 분류될 수 있도록, 나일론이나 PET가 첨가되지 않는 PE 층이 무용제 접착방식으로 합지된 친환경 아이스팩 포장재를 개발하였다. In this situation, the present inventor tried to develop an eco-friendly ice pack packaging material that has oxygen permeability and moisture permeability below the standard values and is excellent in biodegradability and can be recycled. As a result, it can be classified as vinyl LDPE in separate recycling classification. We developed an eco-friendly ice pack packaging material in which PE layers without nylon or PET are laminated using a solvent-free adhesive method.
실시예들은 아이스팩 포장재로서 산소투과도 및 수분 투과도가 기준치 이하이며, 생분해성이 우수하여 재활용이 가능한 친환경 아이스팩 포장재의 제조방법을 제공하는 것에 목적이 있다. 나아가, 냉온 효과가 양호하며 항균 효과를 가질 수 있는 방식의 아이스팩 포장재의 제조방법을 제공하는 것에 그 목적이 있다.The purpose of the examples is to provide a method of manufacturing an eco-friendly ice pack packaging material that has oxygen permeability and moisture permeability below standard values and is highly biodegradable and recyclable. Furthermore, the purpose is to provide a method of manufacturing an ice pack packaging material that has a good cooling effect and an antibacterial effect.
본 개시는 상기 과제를 해결하기 위하여, 친환경 아이스팩 포장지의 제조방법으로서, 저밀도 폴리에틸렌(LDPE)를 포함하는 제1 필름을 제조하는 단계; 고밀도 폴리에틸렌(HDPE)를 포함하는 제2 필름을 제조하는 단계; 및 상기 제1 필름과 상기 제2 필름을 무용제 접착제를 이용하여 제1 필름과 제2필름을 접착시키는 단계를 포함하는, 친환경 아이스팩 포장지의 제조방법을 제공한다.In order to solve the above problems, the present disclosure provides a method for manufacturing eco-friendly ice pack packaging, comprising the steps of manufacturing a first film containing low-density polyethylene (LDPE); producing a second film comprising high-density polyethylene (HDPE); and bonding the first film and the second film to the first film and the second film using a solvent-free adhesive.
일 구현예에 따르면, 상기 무용제 접착제는 폴리우레탄 프리폴리머(Polyurethane prepolymer)나 이온성 관능기를 갖는 inomer형 폴리우레탄 100중량부에 대하여 4,4'-메틸렌디페닐 디이소시아네이트[4,4'-methylenediphenyl diisocyanate] 1 내지 15 중량부, 폴리이소시아네이트(Polyisocyanate) 15 내지 30 중량부, 및 o-(p-이소시아나토벤질)페닐 이소시아네이트[o-(p-Isocyanatobenzyl)phenyl isocyanate] 0.1~2중량부가 혼합된 조성인 것일 수 있다.According to one embodiment, the solvent-free adhesive is 4,4'-methylenediphenyl diisocyanate [4,4'-methylenediphenyl diisocyanate] based on 100 parts by weight of polyurethane prepolymer or inomer-type polyurethane having an ionic functional group. ] 1 to 15 parts by weight, 15 to 30 parts by weight of polyisocyanate, and 0.1 to 2 parts by weight of o-(p-isocyanatobenzyl)phenyl isocyanate [o-(p-Isocyanatobenzyl)phenyl isocyanate] mixed composition It may be.
일 구현예에 따르면, 상기 제1 필름은 50 내지 90㎛의 두께를 가지고, 상기 제2 필름은 20 내지 40 ㎛의 두께를 가지며, 상기 저밀도 폴리에틸렌의 밀도는 0.915 내지 0.925 g/cm2이며, 상기 고밀도 폴리에틸렌의 밀도는 0.945 내지 0.955 g/cm2인 것일 수 있다.According to one embodiment, the first film has a thickness of 50 to 90 ㎛, the second film has a thickness of 20 to 40 ㎛, the density of the low density polyethylene is 0.915 to 0.925 g/cm 2 , and The density of high-density polyethylene may be 0.945 to 0.955 g/cm 2 .
일 구현예에 따르면, 상기 무용제 접착제는 폴리우레탄 프리폴리머(Polyurethane prepolymer)나 이온성 관능기를 갖는 inomer형 폴리우레탄 100중량부에 대하여 4,4'-메틸렌디페닐 디이소시아네이트[4,4'-methylenediphenyl diisocyanate] 1 내지 15 중량부, 폴리이소시아네이트(Polyisocyanate) 15 내지 30 중량부, 및 o-(p-이소시아나토벤질)페닐 이소시아네이트[o-(p-Isocyanatobenzyl)phenyl isocyanate] 0.1~2중량부가 혼합된 조성이며,According to one embodiment, the solvent-free adhesive is 4,4'-methylenediphenyl diisocyanate [4,4'-methylenediphenyl diisocyanate] based on 100 parts by weight of polyurethane prepolymer or inomer-type polyurethane having an ionic functional group. ] 1 to 15 parts by weight, 15 to 30 parts by weight of polyisocyanate, and 0.1 to 2 parts by weight of o-(p-isocyanatobenzyl)phenyl isocyanate [o-(p-Isocyanatobenzyl)phenyl isocyanate] mixed composition and
일 구현예에 따르면, 상기 제1 필름은 50 내지 90㎛의 두께를 가지고, 상기 제2 필름은 20 내지 40 ㎛의 두께를 가지며, 상기 저밀도 폴리에틸렌의 밀도는 0.915 내지 0.925 g/cm2이며, 상기 고밀도 폴리에틸렌의 밀도는 0.945 내지 0.955 g/cm2인 것일 수 있다. 상기 무용제 접착제는 폴리우레탄 프리폴리머(Polyurethane prepolymer)나 이온성 관능기를 갖는 inomer형 폴리우레탄 100중량부에 대하여 4,4'-메틸렌디페닐 디이소시아네이트[4,4'-methylenediphenyl diisocyanate] 5 내지 10 중량부, 폴리이소시아네이트(Polyisocyanate) 12 내지 20 중량부, 및 o-(p-이소시아나토벤질)페닐 이소시아네이트[o-(p-Isocyanatobenzyl)phenyl isocyanate] 0.1~1중량부가 혼합된 조성이며,According to one embodiment, the first film has a thickness of 50 to 90 ㎛, the second film has a thickness of 20 to 40 ㎛, the density of the low density polyethylene is 0.915 to 0.925 g/cm 2 , and The density of high-density polyethylene may be 0.945 to 0.955 g/cm 2 . The solvent-free adhesive contains 5 to 10 parts by weight of 4,4'-methylenediphenyl diisocyanate based on 100 parts by weight of polyurethane prepolymer or inomer-type polyurethane having an ionic functional group. , 12 to 20 parts by weight of polyisocyanate, and 0.1 to 1 part by weight of o-(p-isocyanatobenzyl)phenyl isocyanate [o-(p-Isocyanatobenzyl)phenyl isocyanate],
제1 필름은 60 내지 80㎛의 두께를 가지고, 제2 필름은 25 내지 35 ㎛의 두께를 가지며, 상기 저밀도 폴리에틸렌의 밀도는 0.915 내지 0.925 g/cm2이며, 상기 고밀도 폴리에틸렌의 밀도는 0.945 내지 0.955 g/cm2인 것일 수 있다.The first film has a thickness of 60 to 80 ㎛, the second film has a thickness of 25 to 35 ㎛, the density of the low density polyethylene is 0.915 to 0.925 g/cm 2 , and the density of the high density polyethylene is 0.945 to 0.955. It may be g/cm 2 .
일실시예에 따른 장치는 하드웨어와 결합되어 상술한 방법들 중 어느 하나의 항의 방법을 실행시키기 위하여 매체에 저장된 컴퓨터 프로그램에 의해 제어될 수 있다.The device according to one embodiment may be combined with hardware and controlled by a computer program stored in a medium to execute any one of the above-described methods.
실시예의 친환경 아이스팩 포장지의 제조방법에 의해 제조된 친환경 아이스팩은 나일론이나 PET를 포함하지 않으며, 두 폴리에틸렌 층이 무용제 라미네이팅(solventless laminating)으로 합지된 친환경 포장재이다. 구체적으로, 재활용이 가능한 비닐류(PE)로 분류될 수 있어, 제조사에 환경 분리배출 등급 정도에 따른 환경 부담금을 줄일수 있다. 나아가 저밀도 폴리에틸렌(LDPE) 뿐만 아니라 고밀도 폴리에틸렌(HDPE)의 층을 외부에 가짐에 따라 아이스팩 동결시 평평한 모양을 만들기가 유리해 다량 적재 용이하다. The eco-friendly ice pack manufactured by the eco-friendly ice pack packaging manufacturing method of the example does not contain nylon or PET, and is an eco-friendly packaging material in which two polyethylene layers are laminated by solventless laminating. Specifically, it can be classified as recyclable vinyl (PE), which can reduce the environmental burden on manufacturers depending on the level of environmental separation. Furthermore, as it has an external layer of high-density polyethylene (HDPE) as well as low-density polyethylene (LDPE), it is advantageous to create a flat shape when freezing the ice pack, making it easy to load large quantities.
한편, 실시예의 친환경 아이스팩 포장지의 제조방법에 의해 제조된 친환경 아이스팩은 낮은 산소투과도 및 수분 투과도를 나타낼 뿐만 아니라 항균 효과도 가짐이 확인되었다.Meanwhile, it was confirmed that the eco-friendly ice pack manufactured by the eco-friendly ice pack packaging manufacturing method of the example not only exhibited low oxygen permeability and moisture permeability but also had an antibacterial effect.
도 1은 일실시예에 따른 친환경 아이스팩 포장지의 제조방법의 단계를 나타내는 모식도이다.
도 2의 좌측은 본 발명에 따른 친환경 아이스팩 포장지이며, 도 2의 우측은 기존의 나일론과 PE로 구성된 아이스팩 포장지이다.Figure 1 is a schematic diagram showing the steps of a method of manufacturing eco-friendly ice pack packaging paper according to an embodiment.
The left side of Figure 2 is an eco-friendly ice pack packaging paper according to the present invention, and the right side of Figure 2 is an ice pack packaging material made of existing nylon and PE.
이하에서, 첨부된 도면을 참조하여 실시예들을 상세하게 설명한다. 그러나, 실시예들에는 다양한 변경이 가해질 수 있어서 특허출원의 권리 범위가 이러한 실시예들에 의해 제한되거나 한정되는 것은 아니다. 실시예들에 대한 모든 변경, 균등물 내지 대체물이 권리 범위에 포함되는 것으로 이해되어야 한다.Hereinafter, embodiments will be described in detail with reference to the attached drawings. However, various changes can be made to the embodiments, so the scope of the patent application is not limited or limited by these embodiments. It should be understood that all changes, equivalents, or substitutes for the embodiments are included in the scope of rights.
실시예들에 대한 특정한 구조적 또는 기능적 설명들은 단지 예시를 위한 목적으로 개시된 것으로서, 다양한 형태로 변경되어 실시될 수 있다. 따라서, 실시예들은 특정한 개시형태로 한정되는 것이 아니며, 본 명세서의 범위는 기술적 사상에 포함되는 변경, 균등물, 또는 대체물을 포함한다.Specific structural or functional descriptions of the embodiments are disclosed for illustrative purposes only and may be modified and implemented in various forms. Accordingly, the embodiments are not limited to the specific disclosed form, and the scope of the present specification includes changes, equivalents, or substitutes included in the technical spirit.
제1 또는 제2 등의 용어를 다양한 구성요소들을 설명하는데 사용될 수 있지만, 이런 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 해석되어야 한다. 예를 들어, 제1 구성요소는 제2 구성요소로 명명될 수 있고, 유사하게 제2 구성요소는 제1 구성요소로도 명명될 수 있다.Terms such as first or second may be used to describe various components, but these terms should be interpreted only for the purpose of distinguishing one component from another component. For example, a first component may be named a second component, and similarly, the second component may also be named a first component.
어떤 구성요소가 다른 구성요소에 "연결되어" 있다고 언급된 때에는, 그 다른 구성요소에 직접적으로 연결되어 있거나 또는 접속되어 있을 수도 있지만, 중간에 다른 구성요소가 존재할 수도 있다고 이해되어야 할 것이다.When a component is referred to as being “connected” to another component, it should be understood that it may be directly connected or connected to the other component, but that other components may exist in between.
실시예에서 사용한 용어는 단지 설명을 목적으로 사용된 것으로, 한정하려는 의도로 해석되어서는 안된다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 명세서에서, "포함하다" 또는 "가지다" 등의 용어는 명세서 상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.The terms used in the examples are for descriptive purposes only and should not be construed as limiting. Singular expressions include plural expressions unless the context clearly dictates otherwise. In this specification, terms such as “comprise” or “have” are intended to designate the presence of features, numbers, steps, operations, components, parts, or combinations thereof described in the specification, but are not intended to indicate the presence of one or more other features. It should be understood that this does not exclude in advance the possibility of the existence or addition of elements, numbers, steps, operations, components, parts, or combinations thereof.
다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 실시예가 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥 상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.Unless otherwise defined, all terms used herein, including technical or scientific terms, have the same meaning as generally understood by a person of ordinary skill in the technical field to which the embodiments belong. Terms defined in commonly used dictionaries should be interpreted as having a meaning consistent with the meaning in the context of the related technology, and unless explicitly defined in the present application, should not be interpreted in an ideal or excessively formal sense. No.
본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다. 그러나 본 발명은 이하에서 개시되는 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다.The advantages and features of the present invention and methods for achieving them will become clear by referring to the embodiments described in detail below along with the accompanying drawings. However, the present invention is not limited to the embodiments disclosed below and will be implemented in various different forms. The present embodiments only serve to ensure that the disclosure of the present invention is complete and that common knowledge in the technical field to which the present invention pertains is not limited. It is provided to fully inform those who have the scope of the invention, and the present invention is only defined by the scope of the claims.
본 발명의 실시예들에서, 별도로 다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥 상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 발명의 실시예에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.In the embodiments of the present invention, unless otherwise defined, all terms used herein, including technical or scientific terms, are the same as those commonly understood by a person of ordinary skill in the technical field to which the present invention pertains. It has meaning. Terms defined in commonly used dictionaries should be interpreted as having a meaning consistent with the meaning in the context of the related technology, and unless clearly defined in the embodiments of the present invention, have an ideal or excessively formal meaning. It is not interpreted as
본 발명의 실시예를 설명하기 위한 도면에 개시된 형상, 크기, 비율, 각도, 개수 등은 예시적인 것이므로 본 발명이 도시된 사항에 한정되는 것은 아니다. 또한, 본 발명을 설명함에 있어서, 관련된 공지 기술에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우 그 상세한 설명은 생략한다. 본 명세서 상에서 언급된 '포함한다', '갖는다', '이루어진다' 등이 사용되는 경우 '~만'이 사용되지 않는 이상 다른 부분이 추가될 수 있다. 구성 요소를 단수로 표현한 경우에 특별히 명시적인 기재 사항이 없는 한 복수를 포함하는 경우를 포함한다.The shapes, sizes, proportions, angles, numbers, etc. disclosed in the drawings for explaining embodiments of the present invention are illustrative, and the present invention is not limited to the matters shown. Additionally, in describing the present invention, if it is determined that a detailed description of related known technologies may unnecessarily obscure the gist of the present invention, the detailed description will be omitted. When 'includes', 'has', 'consists of', etc. mentioned in this specification are used, other parts may be added unless 'only' is used. When a component is expressed in the singular, the plural is included unless specifically stated otherwise.
구성 요소를 해석함에 있어서, 별도의 명시적 기재가 없더라도 오차 범위를 포함하는 것으로 해석한다.When interpreting a component, it is interpreted to include the margin of error even if there is no separate explicit description.
도면에서 나타난 각 구성의 크기 및 두께는 설명의 편의를 위해 도시된 것이며, 본 발명이 도시된 구성의 크기 및 두께에 반드시 한정되는 것은 아니다.The size and thickness of each component shown in the drawings are shown for convenience of explanation, and the present invention is not necessarily limited to the size and thickness of the components shown.
본 발명의 여러 실시예들의 각각 특징들이 부분적으로 또는 전체적으로 서로 결합 또는 조합 가능하며, 당업자가 충분히 이해할 수 있듯이 기술적으로 다양한 연동 및 구동이 가능하며, 각 실시예들이 서로에 대하여 독립적으로 실시 가능할 수도 있고 연관 관계로 함께 실시 가능할 수도 있다.Each feature of the various embodiments of the present invention can be partially or fully combined or combined with each other, and as can be fully understood by those skilled in the art, various technical interconnections and operations are possible, and each embodiment may be implemented independently of each other. It may be possible to conduct them together due to a related relationship.
본원의 일 실시예로서 친환경 아이스팩 포장지의 제조방법을 설명한다.As an example of the present application, a method of manufacturing eco-friendly ice pack packaging paper will be described.
친환경 아이스팩 포장지의 제조방법은, 저밀도 폴리에틸렌(LDPE)를 포함하는 제1 필름을 제조하는 단계 (S10);A method of manufacturing eco-friendly ice pack packaging includes manufacturing a first film containing low-density polyethylene (LDPE) (S10);
고밀도 폴리에틸렌(HDPE)를 포함하는 제2 필름을 제조하는 단계 (S20); 및Manufacturing a second film containing high-density polyethylene (HDPE) (S20); and
제1 필름과 제2 필름을 무용제 접착제를 이용하여 상기 제1 필름과 상기 제2필름을 접착시키는 단계 (S30)를 포함한다.It includes the step of adhering the first film and the second film to the first film and the second film using a solvent-free adhesive (S30).
저밀도 폴리에틸렌(LDPE)는 에틸렌을 중합하여 제조하는 합성수지로서 상온에서 투명한 고체(밀도가 0.91~0.94 g/cm2)로 결정화가 낮아 가공성과 유연성, 투명성이 우수해 농업용·포장용 투명필름, 전선피복, 각 종 랩 등의 원료로 사용될 수 있다. 본원의 친환경 아이스팩 포장지에서는 제1 필름으로서 아이스팩 포장지의 내층을 형성할 수 있다. Low-density polyethylene (LDPE) is a synthetic resin manufactured by polymerizing ethylene. It is a transparent solid at room temperature (density: 0.91~0.94 g/cm 2 ). It has low crystallization and is excellent in processability, flexibility, and transparency, so it is used as transparent film for agricultural and packaging purposes, wire covering, etc. It can be used as a raw material for various types of wraps, etc. In our eco-friendly ice pack packaging paper, the inner layer of the ice pack packaging paper can be formed as the first film.
본원의 일 구현예에 따르면, 상기 제1 필름은 50 내지 90㎛의 두께를 가질 수 있으며, 구체적으로, 상기 제1 필름은 60 내지 80㎛의 두께를 가질 수 있다. 상기 저밀도 폴리에틸렌의 밀도는 0.915 내지 0.925 g/cm2일 수 있다. According to one embodiment of the present application, the first film may have a thickness of 50 to 90 ㎛, and specifically, the first film may have a thickness of 60 to 80 ㎛. The density of the low density polyethylene may be 0.915 to 0.925 g/cm 2 .
고밀도 폴리에틸렌(HDPE)는 밀도가 높은 에틸렌 중합체 (밀도가 0.94 내지 0.96 g/cm2)로서, 환경호르몬이 검출되지 않은 무독성 친환경 플라스틱이다. 강도가 우수하며 주로 일회용 쇼핑백, 각종 용기, 완구 등을 만들 때 사용될 수 있다. 본 실시예의 친환경 아이스팩 포장지에서는 제2 필름으로서 아이스팩 포장지의 외층을 형성할 수 있다. 이 때 아이스팩 동결시 평평한 모양을 만들기 유리하도록 한다.High-density polyethylene (HDPE) is a high-density ethylene polymer (density of 0.94 to 0.96 g/cm 2 ) and is a non-toxic, eco-friendly plastic in which no environmental hormones are detected. It has excellent strength and can be mainly used to make disposable shopping bags, various containers, and toys. In the eco-friendly ice pack packaging paper of this embodiment, the outer layer of the ice pack packaging paper can be formed as a second film. At this time, it is advantageous to create a flat shape when freezing the ice pack.
본원의 일 구현예에 따르면, 상기 제2 필름은 20 내지 40 ㎛의 두께를 가질 수 있으며, 구체적으로, 25 내지 35 ㎛의 두께를 가질 수 있다. 상기 고밀도 폴리에틸렌의 밀도는 0.945 내지 0.955 g/cm2일 수 있다.According to one embodiment of the present application, the second film may have a thickness of 20 to 40 ㎛, specifically, 25 to 35 ㎛. The density of the high-density polyethylene may be 0.945 to 0.955 g/cm 2 .
무용제 접착제는 두 필름을 용매 사용 없이 접착하기 위해 사용되는 것이다. 예를 들면, 무용제형 에폭시계 접착제, 무용제형 우레탄계 접착제, 무용제형 아크릴계 접착제 등을 언급할 수 있다. 무용제형 접착제로서 이소시아네이트 화합물을 사용하는 LOCTITE LIOFOL LA 7735(Liofol UR 7735, 제조사:헨켈, 독일) 및 LOCTITE LIOFOL LA 7780(제조사: 헨켈, 독일) 등을 언급할 수 있다.Solvent-free adhesive is used to bond two films together without using a solvent. For example, solvent-free epoxy-based adhesives, solvent-free urethane-based adhesives, and solvent-free acrylic adhesives may be mentioned. As solvent-free adhesives, mention may be made of LOCTITE LIOFOL LA 7735 (Liofol UR 7735, manufacturer: Henkel, Germany) and LOCTITE LIOFOL LA 7780 (manufacturer: Henkel, Germany), which use isocyanate compounds.
본원의 일 구현예에 따르면, 상기 무용제 접착제는 폴리우레탄 프리폴리머(Polyurethane prepolymer)나 이온성 관능기를 갖는 inomer형 폴리우레탄 100중량부에 대하여 4,4'-메틸렌디페닐 디이소시아네이트[4,4'-methylenediphenyl diisocyanate] 1 내지 15 중량부, 폴리이소시아네이트(Polyisocyanate) 15 내지30 중량부, 및 o-(p-이소시아나토벤질)페닐 이소시아네이트[o-(p-Isocyanatobenzyl)phenyl isocyanate] 0.1~2중량부가 혼합된 조성을 갖는 무용제 라미네이트 접착제를 사용할 수 있다. 보다 구체적으로, 상기 무용제 접착제는 폴리우레탄 프리폴리머(Polyurethane prepolymer)나 이온성 관능기를 갖는 inomer형 폴리우레탄 100중량부에 대하여 4,4'-메틸렌디페닐 디이소시아네이트[4,4'-methylenediphenyl diisocyanate] 5 내지 10 중량부, 폴리이소시아네이트(Polyisocyanate) 12 내지 20 중량부, 및 o-(p-이소시아나토벤질)페닐 이소시아네이트[o-(p-Isocyanatobenzyl)phenyl isocyanate] 0.1~1중량부가 혼합된 조성일 수 있다.According to one embodiment of the present application, the solvent-free adhesive is 4,4'-methylenediphenyl diisocyanate [4,4'- 1 to 15 parts by weight of methylenediphenyl diisocyanate], 15 to 30 parts by weight of polyisocyanate, and 0.1 to 2 parts by weight of o-(p-isocyanatobenzyl)phenyl isocyanate [o-(p-Isocyanatobenzyl)phenyl isocyanate] are mixed. A solvent-free laminate adhesive having the desired composition can be used. More specifically, the solvent-free adhesive contains 4,4'-methylenediphenyl diisocyanate [4,4'-methylenediphenyl diisocyanate] 5 per 100 parts by weight of polyurethane prepolymer or inomer-type polyurethane having an ionic functional group. to 10 parts by weight, 12 to 20 parts by weight of polyisocyanate, and 0.1 to 1 part by weight of o-(p-isocyanatobenzyl)phenyl isocyanate [o-(p-Isocyanatobenzyl)phenyl isocyanate]. .
본원의 일 구현예에 따르면, 상기 아이스팩 포장지는 전체 두께가 90 내지 110㎛일 수 있다. 상기 아이스팩 포장지의 색상은 반투명일 수 있다. 이에 따라, 얼음과 반투명한 정도가 비슷하여 아이스팩 내부의 투명하지 않은 얼음이 감추어질 수 있다. 한편, 빳빳하기 때문에 동결시 평평하게 잘 얼 수 있다.According to one embodiment of the present application, the ice pack packaging may have a total thickness of 90 to 110 μm. The color of the ice pack packaging paper may be translucent. Accordingly, the degree of translucency is similar to that of ice, so the non-transparent ice inside the ice pack can be hidden. On the other hand, because it is stiff, it can freeze flat well when frozen.
실시예에 따르면, 상기 무용제 접착제의 조성과 LDPE 및 HDPE 층의 밀도 및 두께를 조절하여 아이스팩 포장지로서 우수한 효과를 가질 수 있다. According to an embodiment, the composition of the solvent-free adhesive and the density and thickness of the LDPE and HDPE layers can be adjusted to have excellent effects as an ice pack packaging paper.
이하, 구체적인 실시예와 비교예를 통하여 본 발명의 구성 및 그에 따른 효과를 보다 상세히 설명하고자 한다. 그러나, 본 실시예는 본 발명을 보다 구체적으로 설명하기 위한 것이며, 본 발명의 범위가 이들 실시예에 한정되는 것은 아니다.Hereinafter, the configuration of the present invention and its effects will be described in more detail through specific examples and comparative examples. However, these examples are for illustrating the present invention in more detail, and the scope of the present invention is not limited to these examples.
실시예 1Example 1
밀도가 0.92g/cm2의 저밀도 폴리에틸렌을 필름 성형기를 이용하여 두께가 70㎛인 제1 LDPE 필름을 제조하였다.A first LDPE film with a thickness of 70 ㎛ was manufactured using low-density polyethylene with a density of 0.92 g/cm 2 using a film molding machine.
밀도가 0.95g/cm2의 고밀도 폴리에틸렌(HDPE)을 그라비아 인쇄방식을 이용하여 두께가 30㎛인 제2 HDPE 필름을 제조하였다.A second HDPE film with a thickness of 30㎛ was manufactured using high-density polyethylene (HDPE) with a density of 0.95 g/cm 2 using a gravure printing method.
폴리우레탄 프리폴리머(Polyurethane prepolymer) 100중량부에 대하여 4,4'-메틸렌디페닐 디이소시아네이트[4,4'-methylenediphenyl diisocyanate: MDD] 10중량부, 폴리이소시아네이트(Polyisocyanate: PI) 20중량부, o-(p-이소시아나토벤질)페닐 이소시아네이트[o-(p-Isocyanatobenzyl)phenyl isocyanate: oPI] 0.5중량부가 혼합된 조성을 갖는 무용제 접착제를 제조하였다.Based on 100 parts by weight of polyurethane prepolymer, 10 parts by weight of 4,4'-methylenediphenyl diisocyanate (MDD), 20 parts by weight of polyisocyanate (PI), o- A solvent-free adhesive having a composition of 0.5 parts by weight of (p-isocyanatobenzyl)phenyl isocyanate [o-(p-Isocyanatobenzyl)phenyl isocyanate: oPI] was prepared.
제1 필름과 제2 필름은 상기 무용제 접착제를 이용하여 무용제 타입 합지기를 이용하여 합지한 후 압착하여 포장지를 제조하였으며, 상기 제조된 포장지에 냉매인 물을 채우고 밀봉하고 급냉하여 친환경 종이 아이스팩을 제조하였다.The first film and the second film were laminated using the solvent-free adhesive described above using a solvent-free type laminating machine and then pressed to produce packaging. The produced packaging was filled with water as a refrigerant, sealed, and quenched to produce an eco-friendly paper ice pack. .
실시예 2 내지 4Examples 2 to 4
실시예 1의 친환경 PE 기반 아이스팩을 제조하되, 표 1에 기재한 바와 같이 조성을 달리하여 제조하였다.The eco-friendly PE-based ice pack of Example 1 was manufactured with different compositions as shown in Table 1.
비교예 1Comparative Example 1
시중에 유통되고 있는 아이스팩으로서, 나일론과 폴리에틸렌의 재질로 형성된 ㈜그린아이스팩의 아이스팩을 준비하였다. 이는 폴리에틸렌 필름에 나일론 필름을 합지시켜 압출 라미네이팅에 의해 제조되는 것으로 알려져 있다.As an ice pack distributed on the market, an ice pack from Green Ice Pack Co., Ltd. made of nylon and polyethylene was prepared. It is known to be manufactured by laminating a nylon film to a polyethylene film and extrusion laminating.
비교예 2 내지 4Comparative Examples 2 to 4
실시예 1의 아이스팩을 제조하되, 표 1에 기재한 바와 같이 조성 또는 제조방법을 달리하여 제조하였다.The ice pack of Example 1 was manufactured with different compositions and manufacturing methods as shown in Table 1.
시험예 1 - 산화생분해성 시험Test Example 1 - Oxidative biodegradability test
실시예 1 내지 4 및 비교예 1 내지 4에서 제조된 아이스팩의 포장지를 아래와 같은 방법으로 테스트 하였다.The packaging paper of the ice packs manufactured in Examples 1 to 4 and Comparative Examples 1 to 4 were tested in the following manner.
ASTM D5510를 사용하여 시험물질의 열산화로 인한 분자량 손실 정도를 평가하였다.The degree of molecular weight loss due to thermal oxidation of the test material was evaluated using ASTM D5510.
ASTM D5338에 따라 위 열산화 시험에서 시편의 호기성 생분해 정도와 속도를 판단하였다. 이 시험법에서 시험물질은 퇴비 접종물과 함께 배양되었다.The degree and speed of aerobic biodegradation of the specimen were determined in the above thermal oxidation test according to ASTM D5338. In this test method, the test material was incubated with compost inoculum.
ASTM D6954는 제품이 식물과 동물의 삶에 미치는 영향을 결정하기 위한 여러가지 육상 및 수생 독성 시험으로서, 산화생분해 테스트 후 최종 처리 매체에서 테스트 물질의 생태학적 영향을 평가하였다.ASTM D6954 is a multi-terrestrial and aquatic toxicity test to determine the effects of products on plant and animal life. It evaluates the ecological impact of test substances in the final treatment medium after oxidative biodegradation testing.
상기 평가 기준에 모두 합격할 경우 ‘적합’, 어느 하나라도 불합격할 경우 ‘부적합’으로 판정하였다. 판정결과를 하기 표 2에 나타내었다.If all of the above evaluation criteria were passed, it was judged as ‘conforming’, and if any one of them failed, it was judged as ‘non-conforming’. The determination results are shown in Table 2 below.
시험예 2 - 수분 투과도/산소 투과도 측정Test Example 2 - Measurement of moisture permeability/oxygen permeability
실시예 1 내지 4 및 비교예 1 내지 4에서 제조된 아이스팩의 포장지를 아래와 같은 방법으로 테스트 하였다. 아이스팩의 포장지를 120 x 20mm로 재단하고 ASTM D3985에 따라 산소투과도, ASTM F1249에 따라 수분투과도를 측정하였다.The packaging paper of the ice packs manufactured in Examples 1 to 4 and Comparative Examples 1 to 4 were tested in the following manner. The ice pack packaging was cut to 120 x 20 mm, and oxygen permeability was measured according to ASTM D3985 and moisture permeability was measured according to ASTM F1249.
상기 물성 측정 결과를 하기 표 2에 나타내었다.The physical property measurement results are shown in Table 2 below.
시험예 3 - 냉온 효과Test Example 3 - Cold and hot effect
실시예 1 내지 4및 비교예 1 내지 4에서 제조된 아이스팩을 박스 내에 보관한 후 1시간 경과 후와 10시간 경과 후의 온도를 측정하였다. 1시간 경과 후와 10시간 경과 후의 온도와 비교하여 온도가 유지되는 경우 "양호"와 온도가 상승한 경우 "부적합"으로 하기 표 2에 나타내었다.The ice packs prepared in Examples 1 to 4 and Comparative Examples 1 to 4 were stored in a box and the temperature was measured 1 hour and 10 hours later. Compared to the temperature after 1 hour and after 10 hours, if the temperature is maintained, it is indicated as "good", and if the temperature rises, it is indicated as "unsuitable" in Table 2 below.
시험예 4 - 항균 효과Test Example 4 - Antibacterial effect
KS 0693 - 1990 시험법에 의거 사람의 피부와 비강표면에 일반적으로 존재하는 황색포도상구균(Staphylococcus aureus)을 균주로 하여 106 마리를 실시예 1 내지 6 및 비교예 1 내지 6에서 제조된 아이스팩에 대해 접종하고 항균도를 측정하였다.According to the KS 0693 - 1990 test method, 10 6 animals were placed on the ice packs prepared in Examples 1 to 6 and Comparative Examples 1 to 6 using Staphylococcus aureus, which is commonly present on human skin and nasal surfaces, as a strain. were inoculated and the antibacterial level was measured.
◎ : 미생물의 양 103이하◎: Quantity of microorganisms 10 3 or less
○ : 미생물의 양 104이하○: Quantity of microorganisms 10 4 or less
△ : 미생물의 양 105이하△: Quantity of microorganisms 10 5 or less
항균 효과는 표 2와 같이 나타내었다.The antibacterial effect is shown in Table 2.
cc/m2·day(23℃,0%RH)Oxygen Transmission Rate (OTR)
cc/m 2 ·day(23℃, 0%RH)
g/m2·day(38℃,90%RH)Moisture Transmission Rate (MVTR)
g/m 2 ·day (38℃, 90%RH)
상기 표 2를 참고하면, 실시예에 따른 친환경 아이스팩의 포장지는 산화 생분해성이 적합한 것으로 나타났으며, 우수한 산소투과도 (0.7 cc/m2·day 이하) 및 수분투과도 (1.3 g/m2·day 이하)를 보였다. 또한, 실시예에 따른 친환경 아이스팩의 포장지는 10시간 경과 후에도 온도 유지에 있어서 양호함을 나타냈으며, 항균효과 뛰어났다. 한편, 실시예들은 고밀도 폴리에틸렌(HDPE)의 층을 외부에 가짐에 따라 아이스팩 동결시 평평한 모양을 만들기가 유리하였다.Referring to Table 2 above, the packaging paper of the eco-friendly ice pack according to the example was found to be suitable for oxidative biodegradability, and had excellent oxygen permeability (0.7 cc/m 2 ·day or less) and moisture permeability (1.3 g/m 2 ·day) below) was shown. In addition, the packaging paper of the eco-friendly ice pack according to the example showed good temperature maintenance even after 10 hours and had excellent antibacterial effect. Meanwhile, the examples had a layer of high-density polyethylene (HDPE) on the outside, making it advantageous to create a flat shape when freezing the ice pack.
Claims (3)
저밀도 폴리에틸렌(LDPE)만으로 구성되며 아이스팩 포장지의 내층을 형성하는 제1 필름을 제조하는 단계;
고밀도 폴리에틸렌(HDPE)만으로 구성되며 아이스팩 포장지의 외층을 형성하는 제2 필름을 제조하는 단계; 및
제1 필름과 제2 필름을 무용제 접착제를 이용하여 상기 제1 필름과 상기 제2필름을 접착시키는 단계를 포함하는, 친환경 아이스팩 포장지의 제조방법으로서,
상기 무용제 접착제는 폴리우레탄 프리폴리머(Polyurethane prepolymer) 100중량부에 대하여 4,4'-메틸렌디페닐 디이소시아네이트[4,4'-methylenediphenyl diisocyanate] 10 중량부, 폴리이소시아네이트(Polyisocyanate) 20 중량부, 및 o-(p-이소시아나토벤질)페닐 이소시아네이트[o-(p-Isocyanatobenzyl)phenyl isocyanate] 0.5중량부가 혼합된 조성이며,
상기 제1 필름은 70 내지 80μm의 두께를 가지고, 상기 제2 필름은 35 내지 40 μm의 두께를 가지며, 상기 저밀도 폴리에틸렌의 밀도는 0.92 g/cm2이며, 상기 고밀도 폴리에틸렌의 밀도는 0.95 g/cm2인 것인,
친환경 아이스팩 포장지의 제조방법.
As a method of manufacturing eco-friendly ice pack packaging,
manufacturing a first film composed solely of low-density polyethylene (LDPE) and forming the inner layer of the ice pack packaging;
manufacturing a second film composed solely of high-density polyethylene (HDPE) and forming the outer layer of the ice pack packaging; and
A method of manufacturing eco-friendly ice pack packaging comprising the step of adhering the first film and the second film to the first film and the second film using a solvent-free adhesive,
The solvent-free adhesive contains 10 parts by weight of 4,4'-methylenediphenyl diisocyanate, 20 parts by weight of polyisocyanate, and o -(p-Isocyanatobenzyl)phenyl isocyanate [o-(p-Isocyanatobenzyl)phenyl isocyanate] is a mixture of 0.5 parts by weight,
The first film has a thickness of 70 to 80 μm, the second film has a thickness of 35 to 40 μm, the density of the low density polyethylene is 0.92 g/cm 2 , and the density of the high density polyethylene is 0.95 g/cm. 2 people,
Manufacturing method of eco-friendly ice pack packaging paper.