KR100686213B1 - Manufacture method of static eletricity proof tile and static eletricity proof tile - Google Patents

Manufacture method of static eletricity proof tile and static eletricity proof tile Download PDF

Info

Publication number
KR100686213B1
KR100686213B1 KR1020050012952A KR20050012952A KR100686213B1 KR 100686213 B1 KR100686213 B1 KR 100686213B1 KR 1020050012952 A KR1020050012952 A KR 1020050012952A KR 20050012952 A KR20050012952 A KR 20050012952A KR 100686213 B1 KR100686213 B1 KR 100686213B1
Authority
KR
South Korea
Prior art keywords
tile
layer
base layer
antistatic
conductive medium
Prior art date
Application number
KR1020050012952A
Other languages
Korean (ko)
Other versions
KR20060088457A (en
Inventor
이문수
Original Assignee
(주)우경인더스트리
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)우경인더스트리 filed Critical (주)우경인더스트리
Publication of KR20060088457A publication Critical patent/KR20060088457A/en
Application granted granted Critical
Publication of KR100686213B1 publication Critical patent/KR100686213B1/en

Abstract

본 발명은 정전기 방지 타일의 제조방법 및 이로부터 제조되는 정전기방지 타일에 관한 것으로, 특히 종래에 다겹으로 이루어진 정전기방지타일의 박리현상을 극복할 수 있고, 표면의 전기저항이 일정한 정전기 방지타일을 제공하는 것을 목적으로 한다.The present invention relates to a method for manufacturing an antistatic tile and an antistatic tile manufactured therefrom, and in particular, to overcome the phenomenon of peeling an antistatic tile made of a conventional multi-layer, and to provide an antistatic tile with a constant electric resistance of the surface. It aims to do it.

본 발명에 따른 정전기 방지 타일의 제조방법은 The method for producing an antistatic tile according to the present invention

기재층 준비단계; Substrate layer preparation step;

상기 기재층 상면에 기재층과 동일한 재질에 전도성매체를 포함시킨 시트를 적층하는 단계;Stacking a sheet including a conductive medium on the same material as the base layer on an upper surface of the base layer;

상기 전도성매체를 포함시킨 시트 상면에 기재층과 동일한 재질에 칼라잉크를 포함시킨 잉크코팅층을 적층하는 단계를 거쳐 타일을 제조하고,A tile is manufactured by laminating an ink coating layer including a color ink on the same material as the base layer on an upper surface of the sheet including the conductive medium.

상기 타일에 발포제를 넣고 발포시키는 단계를 포함하여 이루어지는 것을 특징으로 한다.It characterized in that it comprises the step of foaming the foam into the tile.

본 발명에 의하면, 본 발명은 종래에 다수개의 시트를 합지하는 공정 중 열합지 공정을 생략하여 제조비용 및 제조시간을 절약할 수 있고, 다겹으로 이루어진 타일의 박리현상을 방지할 수 있음과 더불어 정전기 및 전자파를 차폐할 수 있는 효과가 있다.According to the present invention, the present invention can save the manufacturing cost and manufacturing time by omitting the thermal lamination process of the conventional process of laminating a plurality of sheets, and can prevent the peeling phenomenon of the multi-layered tiles and electrostatic And it is effective to shield the electromagnetic waves.

타일, 발포제, 잉크코팅층, 카본코팅층 Tile, foaming agent, ink coating layer, carbon coating layer

Description

정전기 방지 타일의 제조방법 및 이로부터 제조되는 정전기방지 타일{MANUFACTURE METHOD OF STATIC ELETRICITY PROOF TILE AND STATIC ELETRICITY PROOF TILE}Method of manufacturing antistatic tile and antistatic tile manufactured therefrom {MANUFACTURE METHOD OF STATIC ELETRICITY PROOF TILE AND STATIC ELETRICITY PROOF TILE}

도 1은 종래에 열합지로 제조되는 타일을 도시한 도이고,1 is a view showing a tile conventionally made of thermal paper,

도 2는 본 발명에 의한 타일의 제조공정을 도시한 도이고,2 is a diagram illustrating a manufacturing process of a tile according to the present invention;

도 3은 도 2에 의하여 제조된 타일의 제조공정으로 제조된 타일의 단면도.3 is a cross-sectional view of the tile produced by the manufacturing process of the tile manufactured by FIG.

*도면의 주요부호에 대한 설명** Description of the major symbols in the drawings *

120: 카본필름 130: 타일본체 140: 칼라인쇄필름 120: carbon film 130: tile body 140: color printing film

150: 투명필름 10: 기재층 20: 카본코팅층150: transparent film 10: base layer 20: carbon coating layer

30: 잉크코팅층 40: 투명필름층 50: 나노은층30: ink coating layer 40: transparent film layer 50: nano silver layer

본 발명은 본 발명은 정전기 방지 타일의 제조방법 및 이로부터 제조되는 정전기방지 타일에 관한 것으로, 특히 본 발명은 정전기방지 타일의 제조공정을 단 순화하고 제조원가를 절감하고, 제조시간을 절감할 수 있음과 더불어 타일의 박리현상을 방지할 수 있는 정전기 방지 타일의 제조방법 및 이로부터 제조되는 정전기 방지 타일에 관한 것이다.The present invention relates to a method for producing an antistatic tile and to an antistatic tile manufactured therefrom. In particular, the present invention can simplify the manufacturing process of the antistatic tile, reduce manufacturing costs, and reduce manufacturing time. In addition, the present invention relates to a method for manufacturing an antistatic tile capable of preventing peeling of a tile and an antistatic tile manufactured therefrom.

본 발명의 명세서에서는 타일에 한정하여 설명하였지만, 반드시 본 발명에서의 타일은 타일 자체로 한정되는 것이 아니라 매트 및 롤 형태의 타일 등을 포함하는 의미로 사용된다.In the specification of the present invention has been described as limited to the tile, the tile in the present invention is not necessarily limited to the tile itself, but is used in the meaning including a tile in the form of a mat and a roll.

종래의 정전기 타일은 본 출원인이 출원하여 등록 받은 등록 제10-0367885가 있고, 이 발명은 합성수지재 타일 본체(130), 상기 타일 본체 상부에 구비되어 합지되는 칼라 인쇄 필름(140), 상기 칼라 인쇄 필름(140) 상부에 구비되어 합지되는 투명 필름(150)으로 구성되는 합성수지 타일에 있어서,Conventional electrostatic tile has a registration No. 10-0367885 filed by the applicant, the present invention is a synthetic resin tile body 130, the color printing film 140 is provided on the tile body and laminated, the color printing In the synthetic resin tile composed of a transparent film 150 is provided on the film 140 and laminated,

상기 타일 본체(130) 하부에는 두께가 타일 본체(130)보다 얇은 카본 필름(120)을 구비하여 이루어진다.A lower portion of the tile body 130 includes a carbon film 120 having a thickness thinner than that of the tile body 130.

이 발명의 경우에는 합성수지 본체에 카본 필름을 코팅함으로서 표면 저항이

Figure 112005008240935-pat00001
Ω/㎤까지 떨어져 정전기 방지에는 효과가 있으나 다음과 같은 문제점이 있다.In the present invention, the surface resistance is improved by coating the carbon film on the synthetic resin body.
Figure 112005008240935-pat00001
It is effective to prevent static electricity by dropping to Ω / cm 3, but has the following problems.

이 발명의 경우에는 In the case of this invention

첫째, 합성수지 타일 본체, 칼라인쇄필름 및 투명필름을 열압착 합지하는 방식을 취하였으나, 이 경우 열압착과정중에 투명 필름이 손상이 되어 칼라인쇄필름에 정확한 무늬 구현이 어려웠고, 그 제조공정에 상당한 비용 및 시간이 소요되는 문제점이 있었다.First, the synthetic resin tile body, color printing film and transparent film were thermally compressed and laminated, but in this case, the transparent film was damaged during the thermocompression process, so that it was difficult to realize accurate patterns on the color printing film, and a considerable cost was applied to the manufacturing process. And time consuming problems.

둘째, 이 발명의 경우에는 타일본체에 열 압착된 칼라인쇄필름, 투명필름이 박리되는 문제점이 있어 외관상에 문제점이 있었고, 카본 필름이 타일본체에서 박리되거나 사이가 벌어지게 되어 정전기가 발생되는 원인이 되고 있다.Secondly, in the case of the present invention, there is a problem in that the color printing film and the transparent film that are thermally compressed on the tile body have a problem of peeling, and the carbon film is peeled off from the tile body or the gap is caused to cause static electricity. It is becoming.

본 발명은 상기의 문제점을 달성하기 위한 것으로, 본 발명의 제1목적은 다겹으로 이루어진 타일의 박리현상을 방지하는 타일의 제조공법을 제공하는 것이다.The present invention is to achieve the above problems, the first object of the present invention is to provide a tile manufacturing method for preventing the peeling phenomenon of a multi-layered tile.

본 발명의 제2목적은 제조 시간 및 제조 비용을 절감할 수 있는 타일의 제조공법을 제공하는 것이다.It is a second object of the present invention to provide a manufacturing method of a tile which can reduce manufacturing time and manufacturing cost.

본 발명의 제3목적은 표면의 전기저항이 일정한 정전기 방지타일을 제공하는 것이다.It is a third object of the present invention to provide an antistatic tile having a constant electric resistance on its surface.

본 발명은 상기의 목적을 달성하기 위한 것으로, 본 발명에 따른 정전기 방지용 타일의 제조방법은 The present invention is to achieve the above object, the method for producing an antistatic tile according to the present invention

기재층 준비단계; Substrate layer preparation step;

상기 기재층 상면에 기재층과 동일한 재질에 전도성매체를 포함시킨 시트를 적층하는 단계;Stacking a sheet including a conductive medium on the same material as the base layer on an upper surface of the base layer;

상기 전도성매체를 포함시킨 시트 상면에 기재층과 동일한 재질에 칼라잉크를 포함시킨 잉크코팅층을 적층하는 단계를 거쳐 타일을 제조하고,A tile is manufactured by laminating an ink coating layer including a color ink on the same material as the base layer on an upper surface of the sheet including the conductive medium.

상기 타일에 발포제를 넣고 발포시키는 단계를 포함하여 이루어진다.And foaming the foaming agent into the tile.

또한, 상기 기재층 하면에 기재층과 동일한 재질에 전도성매체를 포함시킨 시트를 적층하는 단계;In addition, laminating a sheet including a conductive medium on the same material as the base layer on the lower surface of the base layer;

상기 전도성매체를 포함시킨 시트 하면에 기재층과 동일한 재질에 칼라잉크를 포함시켜 잉크코팅층을 적층하는 단계를 더 포함하여 이루어지는 것을 특징으로 한다.It characterized in that it further comprises the step of laminating the ink coating layer by including a color ink on the same material as the base layer on the lower surface of the sheet containing the conductive medium.

또한, 상기 기재층은 EVA, NBR, PE, PVC폼, PU 중 어느 하나를 사용하는 것을 특징으로 한다.In addition, the base layer is characterized by using any one of EVA, NBR, PE, PVC foam, PU.

또한, 상기 전도성 매체를 포함하는 시트에 혼합되는 전도성 매체의 비율을 10 내지 50 중량%인 것을 특징으로 하는 한다.In addition, the ratio of the conductive medium mixed in the sheet containing the conductive medium is characterized in that 10 to 50% by weight.

또한, 상기 잉크코팅층의 표면에는 투명필름층을 더 코팅하는 것을 특징으로 한다.In addition, the surface of the ink coating layer is characterized by further coating a transparent film layer.

또한, 상기 투명필름층의 표면에는 나노은을 코팅한 것을 특징으로 한다.In addition, the surface of the transparent film layer is characterized in that the coating of nano silver.

또한, 상기 전도성매체는 카본, 알루미늄, 구리, 철, 은, 니켈, 칼륨, 마그네슘, 카드늄 중 어느 하나인 것을 특징으로 하는 정전기 방지 타일의 제조방법.The conductive medium may be any one of carbon, aluminum, copper, iron, silver, nickel, potassium, magnesium, and cadmium.

이하, 본 발명의 바람직한 실시예를 첨부된 도면에 의거하여 상세히 설명하면 다음과 같다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

이하의 실시예에서는 전도성매체를 카본에 한정하여 설명하였지만, 전도성매체는 카본에 한정되는 것이 아니라 알루미늄, 구리, 철, 은, 니켈, 칼륨, 마그네슘, 카드늄 중 어느 하나 이들을 일정비율 혼합하여 사용하는 것이 가능하다고 할 것이다.In the following examples, the conductive medium is limited to carbon, but the conductive medium is not limited to carbon, but any one of aluminum, copper, iron, silver, nickel, potassium, magnesium, and cadmium may be mixed in a predetermined ratio. It would be possible.

도 2는 본 발명의 제조공정을 나타내는 도로서, 본 발명은 기재층 준비단계;(S1)2 is a view showing a manufacturing process of the present invention, the present invention is a substrate layer preparing step; (S1)

상기 기재층 상하면에 기재층과 동일 재질에 카본을 포함시켜 완성시킨 카본코팅층을 코팅하는 단계;(S2)Coating a carbon coating layer on the upper and lower surfaces of the base layer to include carbon in the same material as the base layer; (S2)

상기 코팅층 표면에 기재층과 동일한 재질에 칼라잉크를 포함시켜 완성시킨 잉크코팅층을 코팅하는 단계;(S3)Coating the finished ink coating layer by including a color ink on the same material as the base layer on the surface of the coating layer; (S3)

상기 잉크코팅층 표면에 투명필름층을 코팅하는 단계;를 거쳐 타일을 제조하고,(S4)Coating the transparent film layer on the surface of the ink coating layer; to prepare a tile, and (S4)

상기 타일에 발포제를 넣고 발포시키는 단계;(S5)Adding a foaming agent to the tile and foaming; (S5)

상기 발포된 타일에 나노은을 코팅하는 단계(S6)를 포함하여 이루어진다.
물론, 상기 발포단계(S5)와 관련하여 이는 경우에 따라서 투명필름층의 코팅단계 후 행하는 것이 아니라 앞서 언급한 바 있는 방법인 잉크코팅층을 코팅한 단계 후에도 가능하다. It comprises a step (S6) of coating the nano-silver on the foamed tile.
Of course, in relation to the foaming step (S5), this may not be performed after the coating step of the transparent film layer in some cases, but also after the step of coating the ink coating layer, which is the aforementioned method.

상기 기재층(10)은 EVA, NBR, PE, PVC폼, PU 중 어느 하나를 사용하나를 사용하는 것이 바람직하고, 상기 기재층(10)을 EVA를 사용하는 것이 가장 바람직하다.The base layer 10 is preferably any one of EVA, NBR, PE, PVC foam, PU, and most preferably using the EVA as the base layer 10.

상기 기재층(10) 상하면에는 액상상태의 카본코팅층(20)을 적층하는 것으로, 상기 카본코팅층(20)은 상기 기재층(10)과 동일한 재질을 액상상태로 만든 후, 카본의 중량비가 10 내지 50중량% 정도가 되도록 카본을 첨가하여 완성하게 된다.The upper and lower surfaces of the base layer 10 are laminated with a carbon coating layer 20 in a liquid state. The carbon coating layer 20 is made of the same material as that of the base layer 10 in a liquid state, and a weight ratio of carbon is 10 to 10. It is completed by adding carbon to about 50% by weight.

상기 카본코팅층의 중량비를 카본을 기준으로 10 내지 50 중량%로 한 이유는 카본의 중량이 50중량%를 넘는 경우에 기재층 상면에 카본코팅층이 잘 코팅되지 않는 문제점이 있기 때문이고, 10중량% 미만으로 할 경우에는 표면의 전기저항이

Figure 112005008240935-pat00002
Ω/㎠ 이상이 되어 절연체의 표면저항이 되어 전기전도성이 없게 된다.The weight ratio of the carbon coating layer is 10 to 50% by weight based on carbon because the carbon coating layer is not well coated on the upper surface of the base layer when the weight of the carbon exceeds 50% by weight, 10% by weight If less, the surface electrical resistance
Figure 112005008240935-pat00002
It becomes ohm / cm <2> or more and becomes the surface resistance of an insulator, and becomes electrical conductivity.

또한, 상기 카본코팅층(20)의 표면에는 기재층과 동일한 재질을 액상상태로 만들고, 액상재질의 기재층에 사용자가 원하는 칼라를 지니는 잉크를 혼합한 다음에 카본코팅층 상면에 잉크코팅층(30)을 코팅한다.In addition, the surface of the carbon coating layer 20 is made of the same material as the base layer in a liquid state, the ink having a color desired by the user is mixed with the base material of the liquid material and then the ink coating layer 30 on the upper surface of the carbon coating layer Coating.

상기 발포제는 고분자반응 중 기포를 형성하여 주는 물질로, 플라스틱이나 고무 등에 첨가하거나 또는 분해하여 기포를 만들어 내는 물질·화공약품 등을 총칭하는 개념으로서, 발포제를 사용해 플라스틱이나 고무를 발포시키고자 할 때는 수지 또는 고무의 종류와 특성·용도·가공방법·조건 등에 따라 적합한 발포제를 선택하는 것이 바람직하다. The foaming agent is a substance that forms bubbles during polymer reaction, and is a generic term for materials and chemicals that are added to plastics or rubber or decomposed to form bubbles. When a foaming agent is used to foam the plastic or rubber, It is preferable to select a suitable blowing agent according to the type and properties, uses, processing methods, and conditions of the resin or rubber.

상기 발포제로는 1987년 몰트리올의정서가 채택되어 프레온의 생산량과 소비량을 규제한 이후 대체 발포제로서 수소를 함유한 수소화염화불화탄소(HCFC)가 사용되기 시작하였고, 발포제로서는 이 수소화염화불화탄소를 사용하는 것이 바람직하다.
좀 더 구체적으로 상기 발포과정과 관련하여 이는 타일의 외면만을 발포제에 반응되게 할 수 있고, 기재층 등에 발포제를 첨가하여 발포시키는 경우 모두 가능하다 할 것이다. 특히, 후자의 경우에 있어서는 발포단계 전의 공정에서 각 층에 발포제를 미리 첨가해두어야 하는 것이며, 각 층의 적층 후에 발포공정을 통하여 발포를 진행하게 되는 것이다.Since the Molytriol Protocol was adopted in 1987 to regulate the production and consumption of freon, hydrogen-containing hydrochlorofluorocarbons (HCFCs) were used as alternative blowing agents. It is preferable to use.
More specifically, in relation to the foaming process, only the outer surface of the tile may be made to react with the foaming agent, and the foaming may be possible by adding the foaming agent to the base layer and the like. In particular, in the latter case, the foaming agent should be added to each layer in the process before the foaming step, and foaming is performed through the foaming process after lamination of each layer.

또한, 상기 잉크코팅층(30)의 표면에는 투명필름층(40)을 더 코팅하는 것이 바람직한데, 상기와 같이 잉코코팅층(30) 표면에 투명필름층(40)을 코팅하여 잉크코팅층(30)을 보호하는 역할을 한다.In addition, it is preferable to further coat the transparent film layer 40 on the surface of the ink coating layer 30, as described above by coating the transparent film layer 40 on the surface of the incoating layer 30 to the ink coating layer 30 It protects you.

또한, 상기 투명필름층(40) 표면에는 나노은층(50)을 코팅함으로서 타일 자체에서 발생되는 냄새를 제거할 수 있음과 더불어 곰팜이 등 미생물의 서식을 방지할 수 있는 효과가 있다.In addition, by coating the nano-silver layer 50 on the surface of the transparent film layer 40 can remove the odor generated from the tile itself, and also has the effect of preventing the growth of microorganisms such as gom palm.

본 발명의 제조방법으로 제조된 타일은 도 3에 도시된 바와 같이 기재층(10), 상기 기재층(10) 상하면에 코팅된 카본코팅층(20), 상기 카본코팅층(20) 표면에 코팅되는 잉크코팅층(30), 상기 잉크코팅층(30) 표면에 코팅되는 투명필름층(40), 상기 투명필름층 표면에 코팅되는 나노은층(50)으로 이루어진다.As the tile manufactured by the manufacturing method of the present invention, as shown in Figure 3, the base layer 10, the carbon coating layer 20 coated on the upper and lower surfaces of the base layer 10, the ink coated on the surface of the carbon coating layer 20 The coating layer 30, the transparent film layer 40 coated on the surface of the ink coating layer 30, and the nano-silver layer 50 coated on the surface of the transparent film layer.

본 발명에 의한 제조공법으로 제조된 정전기 방지 타일은 부도체(또는 비전도성)인 기재층 상하면에 표면저항이

Figure 112005008240935-pat00003
Ω/㎠ 이하의 카본 필름을 합지할 경우, 터널링 효과(tunneling effect)에 의하여 타일 표면의 전기저항이
Figure 112005008240935-pat00004
Ω/㎠ 이하로 떨어지는 것으로 확인 되었다. 실무적으로 표면 전기 저항이
Figure 112005008240935-pat00005
Ω/㎠이하이면, 충분한 정전기 방지 효과를 나타내는 것으로 알려져 있다. 참고로, 미국 밀스펙(military spec)상 정전기 그레이드(Anti-static grade)는
Figure 112005008240935-pat00006
Ω/㎠이상
Figure 112005008240935-pat00007
Ω/㎠ 미만이다.The antistatic tile produced by the manufacturing method according to the present invention has a surface resistance on the upper and lower surfaces of the nonconductive (or nonconductive) substrate layer.
Figure 112005008240935-pat00003
When laminating carbon films of Ω / cm 2 or less, the electrical resistance of the tile surface is reduced by the tunneling effect.
Figure 112005008240935-pat00004
It was confirmed to fall below Ω / cm 2. Practically no surface electrical resistance
Figure 112005008240935-pat00005
If it is ohm / cm <2> or less, it is known to show sufficient antistatic effect. For reference, the anti-static grade in the US mill spec is
Figure 112005008240935-pat00006
Ω / ㎠ or more
Figure 112005008240935-pat00007
Less than Ω / cm 2.

이상에서 본 발명을 설명함에 있어 특허청구범위에 청구된 청구항을 위주로 설명하였으나 본 발명은 당업자에 의하여 다양한 변형 및 변경이 가능하고, 이러한 변형 및 변경은 본 발명의 보호범위에 속하는 것으로 해석되어야 한다.In the above description of the present invention, the claims claimed in the claims are described mainly, but the present invention may be variously modified and changed by those skilled in the art, and such modifications and changes should be construed as belonging to the protection scope of the present invention.

본 발명에 의하면, According to the invention,

첫째, 종전의 다층 타일 대신에 타일을 일체로 형성하고 이 타일에 발포제로 넣고 발포시킴으로서 종전 타일에서 발생하는 박리현상을 방지할 수 있고, 특히 기재층 하면에 코팅된 카본코팅층의 박리현상을 방지함으로서 정전기를 효율적으로 방지할 수 있다.First, it is possible to prevent the peeling phenomenon occurring in the conventional tile by forming the tiles integrally instead of the conventional multi-layer tile and foaming the tile into the foam, in particular by preventing the peeling phenomenon of the carbon coating layer coated on the lower surface of the base layer Static electricity can be effectively prevented.

둘째, 다층 타일을 종전에는 열압착 합지하는 방식을 취하였으나 본 발명의 경우에는 다층 타일을 일체로 형성하고 이를 발포제를 넣고 발포시켜 정전기 방지 타일을 일체로 형성시키므로 제조원가 및 제조시간을 단축시킬 수 있다.Second, the multi-layer tile was conventionally a method of thermocompression lamination, but in the case of the present invention, since the multi-layer tile is integrally formed and foamed with the foaming agent, the anti-static tile is integrally formed, thereby reducing manufacturing cost and manufacturing time. .

Claims (8)

기재층 준비단계;Substrate layer preparation step; 상기 기재층 상면에 기재층과 동일한 재질에 전도성매체를 포함시킨 시트를 적층하는 단계;Stacking a sheet including a conductive medium on the same material as the base layer on an upper surface of the base layer; 상기 전도성매체를 포함시킨 시트 상면에 기재층과 동일한 재질에 칼라잉크를 포함시킨 잉크코팅층을 적층하는 단계를 거쳐 타일을 제조하고,A tile is manufactured by laminating an ink coating layer including a color ink on the same material as the base layer on an upper surface of the sheet including the conductive medium. 상기 타일에 발포제를 넣고 발포시키는 단계를 포함하여 이루어지는 정전기 방지 타일의 제조방법.Method of producing an antistatic tile comprising the step of foaming the foam into the tile. 제1항에 있어서,The method of claim 1, 상기 기재층 하면에 기재층과 동일한 재질에 전도성매체를 포함시킨 시트를 적층하는 단계;Stacking a sheet including a conductive medium on the same material as the base layer under the base layer; 상기 전도성매체를 포함시킨 시트 하면에 기재층과 동일한 재질에 칼라잉크를 포함시켜 잉크코팅층을 적층하는 단계를 더 포함하여 이루어지는 것을 특징으로 하는 정전기 방지용 타일의 제조방법.The method of manufacturing an anti-static tile, characterized in that further comprising the step of laminating the ink coating layer by including a color ink on the same material as the base layer on the lower surface of the sheet containing the conductive medium. 제1항에 있어서,The method of claim 1, 상기 기재층은 EVA, NBR, PE, PVC폼, PU 중 어느 하나를 사용하는 것을 특징으로 하는 정전기 방지용 타일의 제조방법. The base layer is a method of producing an antistatic tile, characterized in that using any one of EVA, NBR, PE, PVC foam, PU. 제1항 또는 제2항에 있어서,The method according to claim 1 or 2, 상기 전도성 매체를 포함하는 시트에 혼합되는 전도성 매체의 비율을 10 내지 50 중량%인 것을 특징으로 하는 정전기 방지용 타일의 제조방법.Method for producing an anti-static tile, characterized in that the ratio of the conductive medium mixed in the sheet containing the conductive medium 10 to 50% by weight. 제1항 또는 제2항에 있어서,The method according to claim 1 or 2, 상기 잉크코팅층의 표면에는 투명필름층을 더 코팅하는 것을 특징으로 하는 정전기 방지용 타일의 제조방법.Method for producing an antistatic tile, characterized in that the surface of the ink coating layer further coating a transparent film layer. 제5항에 있어서,The method of claim 5, 상기 투명필름층의 표면에는 나노은을 코팅한 것을 특징으로 하는 정전기 방지용 타일의 제조방법.Method for producing an anti-static tile, characterized in that the coating of nano-silver on the surface of the transparent film layer. 제1항 또는 제2항에 있어서,The method according to claim 1 or 2, 상기 전도성매체는 카본, 알루미늄, 구리, 철, 은, 니켈, 칼륨, 마그네슘, 카드늄 중 어느 하나인 것을 특징으로 하는 정전기 방지 타일의 제조방법.The conductive medium is carbon, aluminum, copper, iron, silver, nickel, potassium, magnesium, cadmium manufacturing method of the antistatic tile, characterized in that any one. 제1항 내지 제3항 중 어느 하나의 항에 의한 제조방법으로 제조되는 정전기 방지용 타일.Antistatic tile produced by the manufacturing method according to any one of claims 1 to 3.
KR1020050012952A 2005-02-01 2005-02-17 Manufacture method of static eletricity proof tile and static eletricity proof tile KR100686213B1 (en)