JPS58158291A - Recording medium for color heat transfer - Google Patents

Recording medium for color heat transfer

Info

Publication number
JPS58158291A
JPS58158291A JP57039861A JP3986182A JPS58158291A JP S58158291 A JPS58158291 A JP S58158291A JP 57039861 A JP57039861 A JP 57039861A JP 3986182 A JP3986182 A JP 3986182A JP S58158291 A JPS58158291 A JP S58158291A
Authority
JP
Japan
Prior art keywords
color
ink layer
recording medium
yellow
heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP57039861A
Other languages
Japanese (ja)
Other versions
JPH038959B2 (en
Inventor
Yukio Tokunaga
徳永 幸生
Tadao Seto
瀬戸 忠雄
Ryoichi Shimazaki
島崎 良一
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujicopian Co Ltd
Nippon Telegraph and Telephone Corp
Original Assignee
Fuji Kagakushi Kogyo Co Ltd
Nippon Telegraph and Telephone Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fuji Kagakushi Kogyo Co Ltd, Nippon Telegraph and Telephone Corp filed Critical Fuji Kagakushi Kogyo Co Ltd
Priority to JP57039861A priority Critical patent/JPS58158291A/en
Publication of JPS58158291A publication Critical patent/JPS58158291A/en
Publication of JPH038959B2 publication Critical patent/JPH038959B2/ja
Granted legal-status Critical Current

Abstract

PURPOSE:To prevent the failure of color lapping in a multi-color printing by a method in which the melting temperatures of each heat-sensitive transferrable ink layer are stepwise differentiated according to the order of printing. CONSTITUTION:In a recording medium 10, heat-sensitive transferrable ink layers 2Y, 2M, and 2C of yellow, Magenta, and cyanine are arranged in a color repeating unit along the lengthwise direction of a base material 1 on the surface of the base material 1. The heat-sensitive transferrable ink layers of yellow, Magenta, and cyanine are constituted such that their melting temperatures are stepwise lowered or raised according to the order of printing. When these ink layers of three colors are stepwise lowered in melting temperature, the ink layer previously printed is already solidified and therefore, the peeling of the ink layer from recording paper does not occur and also the bleeding of colors does not occur. Also, when the melting temperatures of them are stepwisely raised, the ink layers are mixed with each other in completely melted state to give clear-cut pictures.

Description

【発明の詳細な説明】 本発明は新気なカラー熱転写用記―媒体に関する。さら
に胛しくは、感熱方式の多色プリンシにおけゐもの重ね
会わせ不良を紳除したカラー熱転写用記録媒体に関する
◇ 近時、感熱プリンターは取扱いが容易でかつ低コスシで
あるためにコンピュータの端末用として、あるいはファ
クシミリとして広く採用されている。かかる感熱プリン
ターでは、通常記#Is体として基材上に単色(黒色、
青色など)の感熱転写性インキ層を設けたものが用いら
れ、該インキ層が記録紙と対向するごと(記録紙と重ね
合わされ、基材裏面からの加熱ヘッドの印字により、イ
ンキ層を印字像の廖態で記−祇に溶融転写させるもので
ある。
DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a novel color thermal transfer recording medium. More particularly, it relates to a recording medium for color thermal transfer that eliminates overlapping defects in thermal multicolor printers.In recent years, thermal printers are easy to handle and inexpensive, so they are often used as computer terminals. It is widely used for business and facsimile purposes. In such thermal printers, a single color (black, black,
A thermally transferable ink layer of blue, etc.) is used, and each time the ink layer faces the recording paper (overlaid with the recording paper, the ink layer is transferred to the printed image by printing with a heating head from the back side of the base material). It is melt-transferred onto the paper in this state.

ところで感熱プリンターを用いるカラープリント方法は
、従来のインパタシプリント方式やインクを噴射させる
インクジェット方式によるカラープリント方法に比して
装置が小iig ”c’s、m性が高く、シかも安価で
あるばかりでな(、取扱いが容易であり、ざらに誦書の
発生がないなどの多くの利点を有しているために、その
実用化が強く望まれている。
By the way, the color printing method using a thermal printer requires a smaller device, has high performance, and is less expensive than the conventional color printing method using an impact printing method or an inkjet method that ejects ink. Not only that, but it has many advantages such as easy handling and no need for rough recitation, so its practical application is strongly desired.

感熱プリンターを用いるカラープリント方法としては、
イエロー、マゼンタおよびシアンの各色の感熱転写性イ
ンキ層を用いて記録紙上に順次それヤれの色の所電の一
億rt′fII融転写させ色の重ね合わせにより所望の
カラー画像をうる方法が一例としてあげられる。この方
決は取扱いが簡単でかつ解像度の高い鮮明なカラー画像
を作成するのにとくに好ましいものである。
Color printing methods using thermal printers include:
There is a method in which a desired color image is obtained by superimposing the colors by sequentially fusion-transferring each color onto a recording paper using heat-sensitive transferable ink layers of yellow, magenta, and cyan. This is an example. This solution is particularly preferred for ease of handling and for producing high resolution, sharp color images.

しかしながら、かかる色の重ね合わせによるカラープリ
ント方法においては、しばしば色の重ね合わせ不良がI
A生するという欠点がある。
However, in color printing methods that involve superimposing colors, poor color superposition often occurs.
There is a disadvantage of being an A student.

すなわち最初にイエρ−の感熱転写性インキを記録紙上
に溶融転写さ曽てイエV−の画像を形成し、ついでマゼ
ンタおよびシアンの感熱転写性インキを同様にして順次
同じ記録紙上に溶融転写させて!(ンタおよびシアンの
画像を前記イエローの両像に重ね合わせるばあい、たと
えばイエp−とマゼンタとの重ね合わせにより、赤色の
両像がえられるが、マゼンタのインキ層の溶融転写時に
該マゼンタのインキ層に加えられる熱によって該マゼン
タのインキ層と接触している記録紙上のイエローのイン
キ層が溶融し、マゼンタのインキ層に貼着して記録紙か
ら引き剥がされてしまうという欠点が生ずる。同様のこ
とはイエ四−とシアン、マゼンタとシアン、   ゛さ
らにイエ田−1!ゼンタおよびシアンの重ね合わせにお
いても生じ、満足すべきカラー画像をうゐことができな
い。
That is, first, a yellow ρ- heat-sensitive transfer ink is melt-transferred onto a recording paper to form a yellow-V- image, and then magenta and cyan heat-sensitive transfer inks are melt-transferred sequentially onto the same recording paper in the same manner. hand! (If an image of yellow and cyan is superimposed on both the yellow images, for example, by superimposing yellow and magenta, both red images are obtained, but when the magenta ink layer is melt-transferred, the magenta The heat applied to the ink layer causes the yellow ink layer on the recording paper that is in contact with the magenta ink layer to melt, stick to the magenta ink layer, and be peeled off from the recording paper. A similar problem occurs in the overlapping of yellow and cyan, magenta and cyan, and even yellow and cyan, making it impossible to produce a satisfactory color image.

本発明者らは叙上の欠点を排除すべく鋭意研究を重ねた
結果、少なくともイエ冑−、マゼンタおよびシアンの各
感熱転写性インキ層を基材上に設けるにあたり、これら
のインキ層を加熱ヘッドによる印字順位に従って段階的
に溶融温度を異ならしめるときは、叙上の欠点を排除し
うるというまったく新たな事実を見出し、本発明を完成
するにいたった。
The inventors of the present invention have conducted extensive research to eliminate the above-mentioned drawbacks, and have found that, when providing at least the yellow, magenta, and cyan heat-sensitive transferable ink layers on a substrate, these ink layers are transferred to a heating head. The present invention was completed based on the completely new discovery that the above-mentioned drawbacks can be eliminated if the melting temperature is varied stepwise according to the printing order according to the method.

以下、図面な用いて本発明の記録媒体を説明する。Hereinafter, the recording medium of the present invention will be explained with reference to the drawings.

第1図は本発明の記録媒体の一実施例を示す一部切欠概
略斜視図、第2wAは本発明の記録媒体の他の実施例を
示す概略平ETiWJ1第3図は第2図の(3)−(7
)S概略断面図、第4図は本発明の記録媒体のさらに他
の実施例を示す一部切欠概略平面図である。
FIG. 1 is a partially cutaway schematic perspective view showing one embodiment of the recording medium of the present invention, and FIG. 2wA is a schematic plan ETiWJ1 showing another embodiment of the recording medium of the present invention. )−(7
)S schematic sectional view, and FIG. 4 is a partially cutaway schematic plan view showing still another embodiment of the recording medium of the present invention.

第1図に示される記録媒体(至)はプラスチックフィル
ムまたは紙である基材(1)上にイエロー、マゼンタお
よびシアンの感熱転写性インキ層(2Y)、(2M)、
(20)が基材(1)の長さ方向に沿ってそれらの色の
繰返し単位で配列されたものであって、各インキ層の大
きさは記録紙(3)にか−一一中一啼と実質的に等しい
大き8(たとえば、ム4す(X”%)51イズなど)を
有する。
The recording medium (to) shown in FIG. 1 has yellow, magenta and cyan heat-sensitive transferable ink layers (2Y), (2M) on a base material (1) which is a plastic film or paper.
(20) are arranged in repeating units of those colors along the length direction of the base material (1), and the size of each ink layer is 1-1-1 in 1 on the recording paper (3). It has a magnitude 8 substantially equal to the sound (e.g., 4 % (X"%) 51 iz, etc.).

かかる記録媒体(至)は加熱ヘッド(4)としてライン
ヘッドを装備したカラー感熱プリンターやカラー感熱フ
ァクシミリに装着され、加熱ヘッド(4)にヨリ同一記
録紙(s)上にイエロー、マゼンタおよびシアンの各画
像(wJ示されていない)を順次形成せしめ、それらの
画像の重ね合わせにより所望のカラー画像をうるちので
ある。
This recording medium (to) is attached to a color thermal printer or color thermal facsimile equipped with a line head as a heating head (4), and the heating head (4) prints yellow, magenta and cyan on the same recording paper (s). Each image (wJ not shown) is formed in sequence, and a desired color image is created by overlapping these images.

また第2〜5wJに示される記録媒体−は細い帯状にS
*され、かつ各インキ層(27Y) 、(21M)、(
210)の長さが記録紙(1)の巾と実質的に等しい長
さで形成されるほかは第1FXJと同じものである。こ
のものはカラープリント用シリアルプリンターに装着さ
れ、記録紙(1)の一端から他端にかけて記録媒体−の
巾に相当する区分ごとにイエロー、マゼンタおよびシア
ンの4&画像が加熱ヘッド(財)により順次形成される
ものである。
Moreover, the recording medium shown in 2nd to 5th wJ is S in the form of a thin strip.
*, and each ink layer (27Y), (21M), (
It is the same as the first FXJ except that the length of the recording paper (210) is substantially equal to the width of the recording paper (1). This product is installed in a serial printer for color printing, and yellow, magenta, and cyan images are sequentially printed in sections corresponding to the width of the recording medium from one end of the recording paper (1) to the other using a heating head. It is something that is formed.

さらに第4図に示される記録謀体−は長い帯状の基材(
2)上にその長さ方向に沿って並列にイエa −、マゼ
ンタおよびシアンの各インキ層(32Y)、(52M)
、<520)を設けてなるものである。
Furthermore, the recording material shown in Figure 4 is a long strip-shaped base material (
2) Ie a-, magenta and cyan ink layers (32Y), (52M) in parallel along its length on top;
, <520).

これら第1〜4図に示される記録媒体−、−1−はいず
れもイエロー、マゼンタおよびシアンの各画像を記録紙
上に形成し、それらの重ね合わせにより所望のカラー−
像をうるという点で共通している。
Each of the recording media -, -1- shown in FIGS. 1 to 4 forms yellow, magenta, and cyan images on the recording paper, and by superimposing them, a desired color image is obtained.
What they have in common is that they capture images.

しかして本発明においては、イエ四−1!ゼンタおよび
シアンの各感熱転写性インキ層がそれらの印字順位に従
って段階的に溶融温度が低くまたは高くなるようにam
される。
However, in the present invention, Ie 4-1! The heat-sensitive transferable ink layers of zenta and cyan are each am
be done.

前記3色のインキ層の溶融温度が段階的に低(なるとき
は、さきに印字(転写)されたインキ層はすでに固化し
ており、該インキ層の上に他の色のインキ層が重ね合わ
されるばあいも完全には溶融しないために、記録紙から
引き剥がされることがなく、シかもさきに印字された色
のインキ層は溶融しないために色のにじみも生じさせる
ことがない。
When the melting temperature of the three color ink layers gradually decreases, the first printed (transferred) ink layer has already solidified, and the other color ink layers are superimposed on top of the previously printed (transferred) ink layer. Even if the ink layer is not completely melted, it will not be peeled off from the recording paper, and the ink layer of the color printed on the front side will not melt, so color bleeding will not occur.

また前記5色のインキ層の溶融温度が段階的に高くなる
ときは、さきに印字された低い溶融温度のインキ層上に
つぎのそれよりも高い溶融温度のインキ層が重ね合わさ
れることにより、これらのインキ層は完全に溶融した状
態で互いに混ざりあい、同時に記録紙内に浸透するため
に鮮明な色の画像をうろことができ、かつ印字の固着強
度をあげることができ、しかも転写がわるくなったり、
逆に印字が引き剥がされることもない。
Also, when the melting temperatures of the five color ink layers increase stepwise, the next ink layer with a higher melting temperature is superimposed on the previously printed ink layer with a lower melting temperature, so that These ink layers mix with each other in a completely molten state, and at the same time penetrate into the recording paper, making it possible to create a clear colored image, increasing the adhesion strength of the print, and reducing transfer. Become,
On the other hand, the printing will not be peeled off.

これに対して、各インキ層が同じ溶融温度を有するとき
は、重ね合わされる2つのインキ層が互いに半溶融状態
で接触されるために、さきに印字されたインキ層が剥離
し、えられるカラー両像にムラを生じさせる。
On the other hand, when each ink layer has the same melting temperature, the two superimposed ink layers are brought into contact with each other in a semi-molten state, so the ink layer that was printed earlier peels off, resulting in the resulting color. This causes unevenness in both images.

各感熱転写性インキ層はそれぞれの色の着色剤をバイン
ダー剤、微軟剤に混合せしめてなる単一層であって、前
述のごとく溶融温度が員なるインキ層を作成するには、
用いるバインダー剤や微軟剤の配合成分あるいは配合量
を適宜蛮えればよい。その際、各インキ層の溶融温度差
は印字順位に従って段階的に15〜20°Oの範囲とな
るようにするのが好重しい。溶融温度差が前記範囲より
大なるときは、最も融点の高いインキ層(たとえばイエ
ロー)を印字するばあいの印字エネルギーが異常に大音
くなり、印字速度の低下や加熱ヘッドの蓄熱が起こり、
會たつぎの色のインキ層を転写するばあいに加熱ヘッド
の温度を下げるのに多くの時間を必要とし、同様に印字
速度が遅くなり実際的ではない。また溶融温度差が前記
範囲より小なると會は色の重ね合わせ不良が生じるおそ
れがあり、溶融温度を壷える意味がなくなる。
Each heat-sensitive transferable ink layer is a single layer made by mixing a coloring agent of each color with a binder agent and a slight softener, and as mentioned above, in order to create an ink layer with a certain melting temperature,
The ingredients and amounts of the binder agent and softener used may be adjusted as appropriate. At this time, it is preferable that the melting temperature difference between each ink layer is set in a stepwise range of 15 to 20 degrees according to the printing order. When the melting temperature difference is larger than the above range, the printing energy when printing the ink layer with the highest melting point (for example, yellow) becomes abnormally loud, causing a decrease in printing speed and heat accumulation in the heating head.
When transferring an ink layer of a subsequent color, it takes a long time to lower the temperature of the heating head, which similarly slows down the printing speed, making it impractical. Furthermore, if the melting temperature difference is smaller than the above range, there is a risk of poor color overlay, and there is no point in controlling the melting temperature.

前記着色剤としては、色の重ね合わせにより所望の色を
発現しうる透明ないし半透明の着色剤(以下、透明着色
剤という)を用いるのが好ましい。
As the colorant, it is preferable to use a transparent or translucent colorant (hereinafter referred to as a transparent colorant) that can express a desired color by superimposing colors.

イエローを形成する透明着色剤としては、たとえばり四
ム黄(黄鉛)、ジンクエ四−ジンククpメート(m鉛1
ll)、レモンイエシー(クロム酸バリウム)、カドミ
ウム黄、ナフトールエa−8、へンザx vx −3(
)、 rs ンザx 田−3Ck、 ハンf 工Gl 
−G 、へンザヱローGll、ハンサエp−A1ハンサ
エローRM、ハンザエローR1ベンジジンエロー、ベン
ジジンエロー01ベンジジンエローGR,パーマ卓ンF
エローMOG 、キノリンエローレーキなどの顔料やオ
ーラミンなどの染料の1種または2種以上が用いられる
Transparent coloring agents that form yellow include, for example, 4-zinc p-mate (yellow),
ll), lemon yeshi (barium chromate), cadmium yellow, naphthol air a-8, henzah x vx-3 (
), rs nza x den-3Ck, han f engineering gl
-G, Henza Yellow Gll, Hansa Yellow p-A1 Hansa Yellow RM, Hanza Yellow R1 Benzidine Yellow, Benzidine Yellow 01 Benzidine Yellow GR, Permanent Table F
One or more pigments such as yellow MOG and quinoline yellow lake and dyes such as auramine are used.

またマゼンタf:形成する透明着色剤としては、たとえ
ばパーマネントレッド4R1ブリリアントフアストスカ
ーレツト、ブリリアントカーミンB8、パーマネントカ
ーミンIFB、リソールレッド、パーマネントレツドシ
5nsブリリアントカー鷹ン6msビグメントスカーレ
ツf5B、*−ダtンレーキ1、四−ダミンレーキY、
アリザリンレーキなどの顔料や田−ダミンなどの塗料の
11i!まfli2種以上が用いられる。
Magenta f: Transparent colorants to be formed include, for example, Permanent Red 4R1 Brilliant Fast Scarlet, Brilliant Carmine B8, Permanent Carmine IFB, Resole Red, Permanent Red 5ns Brilliant Car Hawk 6ms Pigment Scarlet f5B, *- Daton Lake 1, 4-Damin Lake Y,
11i of pigments such as alizarin lake and paints such as damin! Two or more types of mafli are used.

さらにシアンを形成する透明着色剤としては、たとえば
ビタシリアプルーレー中、無金属7#ロシア易ンプルー
、7タ田シア晶ンプA/N7アス)スカイブルーなどの
顔料やビク)リアブルーなどの染料の1種または2種以
上が用いられる。
Further, transparent coloring agents that form cyan include pigments such as Vitacilia Pluray, metal-free 7# Russian Emplure, 7Tada Cyan Crystal A/N 7A) Sky Blue, and dyes such as Vik) Rear Blue. One or more of these are used.

ここで、前記イエロー、マゼンタおよびシアンを形成す
る顔料とは、いずれもビヒクル(バインダー剤、柔軟剤
など)中に分散させたとき、透明ないし半透明に着色す
る顔料をいう。
Here, the pigments forming yellow, magenta, and cyan refer to pigments that become transparent or translucent when dispersed in a vehicle (binder, softener, etc.).

各透明着色剤は感熱転写インキ層の総量に対して1〜2
0部(重量部、以下同様)、より好ましくは5〜15部
の範囲で使用されうる。透明着色剤の食有鳳が前記範囲
より大なるときは透明性が低下し、色再現が困難となり
、まt−前記範囲より小なるときは着色力が低下し、い
ずれも好ましくない。
The amount of each transparent colorant is 1 to 2 based on the total amount of the thermal transfer ink layer.
It can be used in an amount of 0 parts (parts by weight, hereinafter the same), more preferably 5 to 15 parts. When the susceptibility of the transparent colorant is greater than the above range, the transparency decreases and color reproduction becomes difficult, and when it is less than the above range, the tinting power decreases, both of which are undesirable.

感熱転写性インキ層を形成する他の成分であるバインダ
ー剤としては、針入度が0.1〜30(25’fl)の
ワックス類を用いるのが、えられゐインキ層の感熱性を
向上せしめるうえで好ましい。
As the binder agent, which is another component forming the heat-sensitive transferable ink layer, it is recommended to use waxes with a penetration of 0.1 to 30 (25'fl) to improve the heat sensitivity of the ink layer. It is preferable in order to encourage people.

バインダー剤としては、たとえばカルナバワックス、マ
イク簡クリスタリンワックス、木ろう、ミツロウ、セレ
シンワックス、パラフィンワックス、鯨ロウなどのワッ
クス類から適宜選択され、これらのバインダー剤はイン
キ層総量100部に対して20〜80部の範囲で使用さ
れる。
The binder agent is appropriately selected from waxes such as carnauba wax, microcrystalline wax, Japanese wax, beeswax, ceresin wax, paraffin wax, spermaceti wax, etc., and these binders are used in an amount of 20 parts per 100 parts of the total amount of the ink layer. ~80 parts.

また柔軟剤としては、たとえば石油樹脂、ポリ酢醗ビニ
ル、ポリスチレン、スチレン−ブタジェン共重合体、セ
ルロースエーテル類、セルロースエステル類、アクリル
系樹脂類のごとき容易に熱溶融しうる物質または瀉滑油
から適宜選択される。これらの柔軟剤はインキ層総量1
00部に対して5〜25部の範囲で用いられる。
The softening agent may be made of easily heat-meltable substances such as petroleum resins, polyvinyl acetate, polystyrene, styrene-butadiene copolymers, cellulose ethers, cellulose esters, acrylic resins, or lube oil. Selected appropriately. These softeners have a total ink layer of 1
It is used in a range of 5 to 25 parts per 00 parts.

さらに本発明においては、感熱転写性インキ層に良好な
熱伝導性および溶融転写性を付与させるために粉体状熱
伝導性物質および(または)体質顔料を配合することが
できる。
Furthermore, in the present invention, a powdery thermally conductive substance and/or extender pigment may be blended in order to impart good thermal conductivity and melt transferability to the thermally transferable ink layer.

粉体状熱伝導性物質としては、たとえばアルミニウム、
銅、錫、亜鉛などの熱伝導率が6.0X10 〜25.
0X10  oal/s@a−cow−’Oの金属粉な
どがあげられる。また体質顔料としては、たとえば炭酸
マグネシウム、炭酸カルシウム、クレー、カオリン、ケ
イ酸カルシウム、アエロジル、ホワイFカーボンなどの
比較的透明性の高いものが好適に使用される。これらの
熱伝導性葉質や体質顔料はインキ層総量100sに対し
てそれぞれ0〜50部および0〜10部の割合で配合さ
れる。
Examples of powdered thermally conductive substances include aluminum,
Thermal conductivity of copper, tin, zinc, etc. is 6.0X10 to 25.
Examples include metal powder of 0x10 oal/s@a-cow-'O. Further, as extender pigments, relatively highly transparent ones such as magnesium carbonate, calcium carbonate, clay, kaolin, calcium silicate, Aerosil, and Why F carbon are preferably used. These thermally conductive leaf substances and extender pigments are blended in proportions of 0 to 50 parts and 0 to 10 parts, respectively, per 100 seconds of the total amount of the ink layer.

しかしてえられる各感熱転写性インキ層はその溶融転写
性を高めるうえで溶融温度が50〜15QC′oの範囲
内でその溶融温度を蛮えればよい。
However, in order to improve the melt transferability of each heat-sensitive transferable ink layer obtained, it is sufficient that the melting temperature is within the range of 50 to 15 QC'o.

またこれらのインキ層は粘度が20〜ID0OOoP(
溶融温度より3000高い温度での測定値)であるのが
好ましい。さらにインキ層は柔らかいと汚れやすくなる
ために硬い目のものが好ましく、具体的には針入度(J
xs x 2530 )が0.1〜50i7)範囲内で
あるのが好ましい。
In addition, these ink layers have a viscosity of 20 to ID0OOoP (
(measured at a temperature 3000° above the melting temperature). Furthermore, if the ink layer is soft, it is easily smudged, so it is preferable to use a hard ink layer.
xs x 2530) is preferably within the range of 0.1 to 50i7).

本発明における前記基材としては1適度な耐熱強度を有
し、かつ熱伝導性にすぐれたものであるのが好ましく、
たとえば厚さ3〜25μで密度0,9〜1−4p10−
のプラスチックフィルム(セルロースフィルふ、ミリイ
ミド、ポリエステル、プリエチレン、ポリスチレン、ポ
リプレピレンなど)または紙(:Iンデンサー紙、合成
紙、ラミネーF紙など)が好適に使用される。
The base material in the present invention preferably has a suitable heat resistance strength and excellent thermal conductivity,
For example, thickness 3-25μ and density 0,9-1-4p10-
Plastic films (cellulose film, myriimide, polyester, preethylene, polystyrene, polypropylene, etc.) or papers (indenser paper, synthetic paper, laminated F paper, etc.) are preferably used.

なお以上の説明においては、感熱転写性インキ層として
はイエロー、マゼンタおよびシアンの3色のものについ
て説明したが、これらの色の重ね合わ曽によって鮮用な
黒色を再現させるのが困難なばあいにはさらにブラック
の感熱転写性インキ層を基材上に設けるようにしてもよ
い。かかるブラックのインキ層はカーボンブラック、ニ
ゲ胃シンベースなどの着色剤を含有スるものである。
In the above explanation, three colors of yellow, magenta and cyan were explained as the heat-sensitive transfer ink layer, but if it is difficult to reproduce a vivid black color due to the overlapping of these colors, Furthermore, a black heat-sensitive transferable ink layer may be provided on the base material. Such a black ink layer contains a coloring agent such as carbon black or black paint base.

つぎに実施例をあげて本発明の記録媒体を説明する。Next, the recording medium of the present invention will be described with reference to Examples.

実施例1 厚さ12μ、密度1−25p/a m3のコンデン賃−
紙を基材として用い、該基材を中297311111の
帯状に切断した。ついで111表に示す組成からなるイ
エロー、マゼンタおよびシアンの各感熱転写性インキ層
をホットメルトコーティングにより基材上にその長さ方
向に沿って巾210臘鳳で順次塗布し、ム4版の大きさ
の感熱転写性インキ層を有する第1図に示されるごとき
記録媒体をえた。
Example 1 Condensation layer with a thickness of 12μ and a density of 1-25p/am3.
Paper was used as a base material, and the base material was cut into strips of medium size. Next, heat-sensitive transfer ink layers of yellow, magenta and cyan having the compositions shown in Table 111 were sequentially applied onto the substrate along its length by hot-melt coating in a width of 210 mm, and the size of the 4th plate was coated. A recording medium as shown in FIG. 1 was obtained having a heat-sensitive transferable ink layer.

第   1    表 太られた各感熱転写性インキ層の厚さ、溶融温度、粘度
および針入度は第2表のとおりである。
Table 1 The thickness, melting temperature, viscosity and penetration of each heat-sensitive transfer ink layer are shown in Table 2.

第   2   表 (注1) 溶融温度より50℃高い湿度での測定値 (注2)  J工8に2flに規定される試験法による
測定値 かくして見られた記録媒体を用いてカラー画像を作成す
るために、実験用として単色用ラインヘッドを装備した
感熱ファクシミリ(三菱電機■製のメルファス)を用い
てム4版の普通紙にイエロ−、マゼンタおよびシアンの
順で各画像を溶融転写させた。その結果、イエローとマ
ゼンタ、マゼンタとシアン、イエローとシアン、さらに
イエp−とマゼンタとシアンとが重ね合わされた部位の
カラー両像は色の重ね合わせ不良がまったく認められず
、カテー閾像は鮮明で高い解像度を有していた。
Table 2 (Note 1) Values measured at a humidity 50°C higher than the melting temperature (Note 2) Values measured by the test method specified in J Engineering 8 2fl Create a color image using the recording medium thus obtained For experimental purposes, each image was melt-transferred in the order of yellow, magenta, and cyan onto 4-size plain paper using a thermal facsimile (Melfas, manufactured by Mitsubishi Electric Corporation) equipped with a monochrome line head. As a result, no defective color superposition was observed in the color images of areas where yellow and magenta, magenta and cyan, yellow and cyan, and even yellow and magenta and cyan were superimposed, and the cath threshold image was clear. It had high resolution.

実施例2 イエロー、マゼンタおよびシアンの各感熱転写性インキ
層として第3表に示す組成のものをそれぞれ用いたほか
は実施例1と同様にして記録媒体をえた。
Example 2 A recording medium was obtained in the same manner as in Example 1, except that the compositions shown in Table 3 were used as the yellow, magenta, and cyan heat-sensitive transfer ink layers.

第    6    表 (単位二部) えられた各感熱転写性インキ層の厚さ、溶融温度、粘度
および針入度は84表のとおりであるO 第4表 かくしてえられた記録媒体を用いて実m例1と同様にし
てカラー画像を作成した。その結果、色の重ね合わせ部
位における重ね合わせ不良はまったく認められず、また
きわめて鮮明でかつ固着強度および怒牢性にすぐれた高
い解像度のカラー画像かえられた。
Table 6 (unit: 2 copies) The thickness, melting temperature, viscosity and penetration of each heat-sensitive transfer ink layer obtained are as shown in Table 84. A color image was created in the same manner as in Example 1. As a result, no overlay defects were observed at the color overlapping portions, and a high-resolution color image was obtained which was extremely clear and had excellent adhesion strength and durability.

【図面の簡単な説明】[Brief explanation of the drawing]

第1図は本発明の記録媒体の一実施例を示す一部切欠概
略平面図、第2図は本発明の記録媒体の他の実施例を示
す概略平面図、第35Aは第2図の(1)−(1)線概
略断面図、第4図は本発明の記録媒体のさらに他の実施
例を示す一部切欠概略平面図である。 (図面の主要符り (1)、・υ:基 材 (2Y)、(2M)、(20) (21Yχ(21M)、 (210)
FIG. 1 is a partially cutaway schematic plan view showing one embodiment of the recording medium of the present invention, FIG. 2 is a schematic plan view showing another embodiment of the recording medium of the present invention, and FIG. 1)--(1), and FIG. 4 is a partially cutaway schematic plan view showing still another embodiment of the recording medium of the present invention. (Main symbols in the drawing (1), ・υ: Base material (2Y), (2M), (20) (21Yχ(21M), (210)

Claims (1)

【特許請求の範囲】 1 基材上に少なくともイエ田−1!ゼンタおよびシア
ンの感熱転写性インキ層を設け、加熱ヘッドにより各色
のインキ層を記録紙上に溶融転写させて色の重ね会わ甘
により多色プリン)を行なうためのカラー熱転写用記録
媒体において、前記イエーー、マ(ン夕およびシアンの
各感熱転写性インキ層が加熱ヘッドによる印字順位に従
って段階的に溶融温度差が生じゐように構成されてなる
カラー熱転写用記録媒体・0 2 溶融温度差が印字順位に従って段階的に低くなるよ
うに構成されてなる特許請求の範囲第1項記載の記−一
体。 3 溶融温度差が印字順位に従ってRWII的に高(な
るように構成されてなる特許請求の範囲$11111記
載の記−媒体0 44)色の感熱板21性インキ層が溶融濃度50〜j5
0”Elf)@腸内で千の印字順位に従って段階的にS
〜20”CJI)@融温度差を有してなゐ特許請求の範
囲第1項記載の記働媒体。 5 番感熱転写性インキ層がそれぞれの色の透明ないし
半透明の着色剤な1有してなる特許請求の範囲第11[
記載の記―媒体。
[Claims] 1. At least Ieda-1 on the base material! In a color thermal transfer recording medium for forming a thermally transferable ink layer of zenta and cyan, and melting and transferring each color ink layer onto a recording paper using a heating head to create a multicolor pudding by overlapping colors, A recording medium for color thermal transfer in which each of the color, yellow, and cyan heat-sensitive transferable ink layers is configured such that a difference in melting temperature occurs stepwise according to the printing order by the heating head. 3. The scope of claim 1 is structured so that the melting temperature difference becomes lower stepwise according to the printing order. Recording medium 0 described in 11111 44) The colored heat-sensitive plate 21 ink layer has a melting density of 50 to j5
0”Elf) @S in stages according to the 1000 print order
The recording medium according to claim 1, which does not have a difference in melting temperature of ~20''CJI). Claim 11 [
Record of description - medium.
JP57039861A 1982-03-13 1982-03-13 Recording medium for color heat transfer Granted JPS58158291A (en)