JPH11217535A - Antislip agent for carton - Google Patents
Antislip agent for cartonInfo
- Publication number
- JPH11217535A JPH11217535A JP3376898A JP3376898A JPH11217535A JP H11217535 A JPH11217535 A JP H11217535A JP 3376898 A JP3376898 A JP 3376898A JP 3376898 A JP3376898 A JP 3376898A JP H11217535 A JPH11217535 A JP H11217535A
- Authority
- JP
- Japan
- Prior art keywords
- slip agent
- agent according
- latex
- weight
- slip
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は段ボール箱やクラフ
ト紙袋等の紙器をパレットに積載して運送する際に、該
紙器が荷崩れするのを防止するために紙器の表面に塗布
して使用する紙器スリップ防止剤に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention is applied to a paper container such as a cardboard box or a kraft paper bag, which is applied to the surface of a paper container in order to prevent the paper container from collapsing when being transported by being loaded on a pallet. The present invention relates to a paper container anti-slip agent.
【０００２】[0002]
【従来の技術】従来、パレット上に積み重ねられた段ボ
ール箱等が搬送中に荷崩れするのを防止する方法とし
て、バインディング処理やシュリンク処理が行なわれて
いる。しかし、かかる処理は手間がかかり、コストも高
くつくという欠点がある。2. Description of the Related Art Conventionally, as a method for preventing a cardboard box or the like stacked on a pallet from being collapsed during transportation, a binding process or a shrink process is performed. However, such a process has the drawback that it is troublesome and costly.
【０００３】また、段ボール箱等の紙器の製造時に、そ
の表面又は底面に、コロイダルシリカを配合したアクリ
ル共重合体エマルジョンをスリップ防止剤として予め塗
布して摩擦係数を高め、積み上げ時にスリップするのを
防止したものも用いられている。しかし、この場合、段
ボールの製造時の印刷工程にスリップ防止剤を塗布する
設備を追加する必要があり、製造コストを高める原因と
なっていた。[0003] Further, when a paper container such as a corrugated cardboard box is manufactured, an acrylic copolymer emulsion containing colloidal silica is previously applied as an anti-slip agent to the surface or bottom surface of the paper container to increase the coefficient of friction and prevent slippage during stacking. Prevented ones are also used. However, in this case, it is necessary to add a facility for applying an anti-slip agent in a printing process at the time of manufacturing corrugated cardboard, which causes an increase in manufacturing cost.
【０００４】一方、段ボール箱等の紙器をパレットに積
み上げる際、現場にて、紙器の表面にホットメルト型接
着剤を点状又は線状に塗布することも行なわれている。
しかし、ホットメルト型接着剤を塗布するためには、こ
れを加熱するか、有機溶剤に溶かす必要がある。また、
品質検査や配送センターでの小分け作業の際に積み替え
が行なわれた場合、該接着剤の荷崩れ防止効果は無くな
り、再接着する為には再度接着剤を塗布する必要が生じ
る。また、荷降ろし時に接着剤塗布箇所で紙が破損する
こともあり、商品イメージを著しく落すという問題があ
った。On the other hand, when stacking paper containers such as a cardboard box on a pallet, a hot-melt adhesive is applied on the surface of the paper containers in a dot-like or linear manner.
However, in order to apply the hot melt adhesive, it is necessary to heat it or dissolve it in an organic solvent. Also,
If reloading is performed during quality inspection or subdivision work at the distribution center, the effect of preventing the adhesive from collapsing is lost, and it is necessary to apply the adhesive again to re-adhere. In addition, the paper may be damaged at the place where the adhesive is applied when unloading, and there is a problem that the product image is remarkably deteriorated.
【０００５】[0005]
【発明が解決しようとする課題】本発明は、パレット積
み上げ時、現場にて、加熱や有機溶剤の使用を必要とす
ることなく紙器の表面に簡単に塗布して定着させること
ができるとともに、積み替え作業も紙を剥離させること
なく楽に行える、スリップ防止性に優れた紙器スリップ
防止剤を提供することを目的とする。SUMMARY OF THE INVENTION According to the present invention, it is possible to easily apply and fix a pallet on the surface of a paper container without need of heating or use of an organic solvent at the time of stacking pallets, and to reload. An object of the present invention is to provide a paper container anti-slip agent excellent in anti-slip property, which can be easily performed without peeling paper.
【０００６】[0006]
【課題を解決するための手段】上記目的は、本発明によ
れば、平均粒子径９nm以下のコロイダルシリカと、有機
ポリマーラテックスと、水分散性又は水可溶性の高分子
化合物とを含有する水分散液からなる紙器スリップ防止
剤によって達成される。According to the present invention, there is provided an aqueous dispersion containing colloidal silica having an average particle diameter of 9 nm or less, an organic polymer latex, and a water-dispersible or water-soluble polymer compound. This is achieved by a paper container anti-slip agent comprising a liquid.
【０００７】すなわち、本発明は、平均粒子径９nm以下
の微細なコロイダルシリカと、有機ポリマーラテックス
とを組み合わせるとともに、これに水分散性又は水可溶
性の高分子化合物を配合することにより、塗布時には適
度な粘性を備えて紙器表面に接着し、乾燥時には防滑性
は高いがブロッキングしない塗膜となる水性組成物を調
製した点に特徴を有する。本発明のスリップ防止剤は水
性であるため、塗布に際して、そのまま紙器に塗るだけ
でよく、加熱や有機溶剤を使用する必要はない。また、
本発明の構成によれば、組成物全量の１０％以下、好ま
しくは６％以下の低い固形物含量で塗布性に優れ且つ耐
ブロッキング性及び防滑性の良好な組成物を提供できる
点で極めて有用である。That is, the present invention combines a fine colloidal silica having an average particle diameter of 9 nm or less with an organic polymer latex, and mixes it with a water-dispersible or water-soluble polymer compound, so that it can be suitably coated. It is characterized by the fact that an aqueous composition is prepared which has a high viscosity and adheres to the surface of a paper container, and has a high anti-slip property when dried, but forms a coating film which does not block. Since the antislip agent of the present invention is water-based, it can be simply applied to a paper container as it is, and there is no need to heat or use an organic solvent. Also,
ADVANTAGE OF THE INVENTION According to the structure of this invention, it is very useful at the point which can provide the composition which is excellent in applicability | coating at the low solid content of 10% or less, preferably 6% or less of the total amount of a composition, and is excellent in blocking resistance and slip resistance. It is.
【０００８】本発明で用いるコロイダルシリカは公知で
あるが、本発明においては、平均粒子径９nm以下のもの
を使用することが必要であり、好ましくは平均粒子径３
〜９nm、特に好ましくは４〜６nmの範囲内のものが使用
される。かかる微細な粒径のコロイダルシリカは、各種
製造業者から入手可能であり、例えば、スノーテックス
−ＸＳ（日産化学（株）製）などの商品名で水分散液と
して販売されているものを用いることができる。該コロ
イダルシリカは、スリップ防止剤の全重量を基準とし
て、好ましくは0.10〜10重量％、更に好ましくは0.10〜
0.49重量％配合するとよい。該コロイダルシリカの配合
量が１０重量％を越えると、重ね合わせた紙器を分離し
にくくなる。該コロイダルシリカの配合量が0.10重量％
よりも少ないと、十分なスリップ防止効果が得られな
い。The colloidal silica used in the present invention is known, but in the present invention, it is necessary to use a colloidal silica having an average particle diameter of 9 nm or less.
Those having a diameter of from 9 to 9 nm, particularly preferably from 4 to 6 nm, are used. The colloidal silica having such a fine particle size is available from various manufacturers. For example, it is possible to use those sold as an aqueous dispersion under a trade name such as Snowtex-XS (manufactured by Nissan Chemical Industries, Ltd.). Can be. The colloidal silica is preferably 0.1 to 10% by weight, more preferably 0.10 to 10% by weight, based on the total weight of the anti-slip agent.
It is advisable to add 0.49% by weight. If the amount of the colloidal silica exceeds 10% by weight, it becomes difficult to separate the stacked paper containers. 0.10% by weight of the colloidal silica
If it is less than this, a sufficient slip prevention effect cannot be obtained.
【０００９】本発明で用いる有機ポリマーラテックスと
しては、アクリル系、メタクリル系、スチレン系、スチ
レンコポリマー系の他、天然ゴム系又はＳＢＲラテック
ス、ＮＢＲラテックス等の合成ゴム系のラテックスも使
用することができる。ゴム系ラテックスは、ガラス転移
温度（Ｔｇ）が−５０〜−１５℃、好ましくは−４５〜
−３０℃であるものが好ましく、具体的には、ＮＢＲラ
テックスＬＸ５１１（日本ゼオン（株）製）等が挙げら
れる。該有機ポリマーラテックスは、スリップ防止剤の
全重量を基準として、好ましくは0.10〜10重量％、更に
好ましくは0.10〜0.49重量％配合するとよい。該有機ポ
リマーラテックスの配合量が１０重量％を越えると、重
ね合わせた紙器を分離しにくくなる。該有機ポリマーラ
テックスの配合量が0.10重量％よりも少ないと、十分な
スリップ防止効果が得られない。As the organic polymer latex used in the present invention, natural rubber-based or synthetic rubber-based latex such as SBR latex or NBR latex can be used in addition to acrylic-based, methacryl-based, styrene-based, and styrene copolymer-based latexes. . The rubber-based latex has a glass transition temperature (Tg) of -50 to -15C, preferably -45 to -15C.
The temperature is preferably −30 ° C., and specific examples include NBR latex LX511 (manufactured by Nippon Zeon Co., Ltd.). The organic polymer latex is preferably contained in an amount of 0.1 to 10% by weight, more preferably 0.10 to 0.49% by weight, based on the total weight of the anti-slip agent. When the compounding amount of the organic polymer latex exceeds 10% by weight, it becomes difficult to separate the stacked paper containers. If the amount of the organic polymer latex is less than 0.10% by weight, a sufficient anti-slip effect cannot be obtained.
【００１０】本発明で用いる水分散性又は水可溶性の高
分子化合物は、上記コロイダルシリカ及び有機ポリマー
ラテックスの分散安定剤及び紙器への接着助剤として機
能する。かかる高分子化合物としては、例えば、カルボ
キシメチルセルロース（ＣＭＣ）等のセルロース系化合
物、ポリビニルアルコール、アルギン酸ナトリウムなど
の遊離のカルボキシル基を有する化合物から選ばれた少
なくとも１種を用いることができる。該高分子化合物
は、スリップ防止剤の粘度を５０〜５００ｃｐ、好まし
くは１５０〜３００ｃｐ（２５℃、Ｂ型粘度計測定値）
とするに十分な量だけ配合することが好ましく、具体的
な添加量は個々の高分子化合物によって当業者が適宜選
択することができる。該高分子化合物の通常の添加量
は、スリップ防止剤の全重量を基準として0.1〜20重量
％、好ましくは3.5〜６重量％程度とすることが可能で
ある。該高分子化合物の添加量が20重量％よりも多い
と、重ね合わせた紙器を分離しにくくなる。該高分子化
合物の添加量が0.1重量％よりも少ないと、スリップ防
止剤が塗膜を形成し難くなる。The water-dispersible or water-soluble polymer compound used in the present invention functions as a dispersion stabilizer for the above-mentioned colloidal silica and organic polymer latex and as a bonding aid for paper containers. As such a polymer compound, for example, at least one selected from cellulosic compounds such as carboxymethylcellulose (CMC) and compounds having a free carboxyl group such as polyvinyl alcohol and sodium alginate can be used. The polymer compound has a viscosity of the anti-slip agent of 50 to 500 cp, preferably 150 to 300 cp (25 ° C., B-type viscometer measured value).
It is preferable to mix them in an amount sufficient to satisfy the following conditions, and a person skilled in the art can appropriately select the specific amount to be added depending on the individual polymer compound. The usual addition amount of the polymer compound can be about 0.1 to 20% by weight, preferably about 3.5 to 6% by weight, based on the total weight of the anti-slip agent. When the amount of the polymer compound is more than 20% by weight, it becomes difficult to separate the stacked paper containers. If the amount of the polymer compound is less than 0.1% by weight, it becomes difficult for the anti-slip agent to form a coating film.
【００１１】更に、本発明のスリップ防止剤には、必要
に応じて、防腐又は防黴剤、凍結防止剤、ｐＨ調節剤等
の各種添加剤を配合することができる。The anti-slip agent of the present invention may further contain various additives such as an antiseptic or antifungal agent, an antifreezing agent and a pH adjuster, if necessary.
【００１２】防腐又は防黴剤としては、ホルムアルデヒ
ド、安息香酸ナトリウム、フェノール系防腐剤等を用い
ることができる。フェノール系防腐剤としては、ペンタ
クロロフェノレート、ｐ−ヒドロキシ安息香酸エステル
等が挙げられる。As preservatives or fungicides, formaldehyde, sodium benzoate, phenol preservatives and the like can be used. Examples of the phenolic preservative include pentachlorophenolate, p-hydroxybenzoate and the like.
【００１３】凍結防止剤としては、グリセリン、エチレ
ングリコール、プロピレングリコール、及びこれらのエ
ステル等が挙げられる。スリップ防止剤の安定性の点か
ら、グリセリンが好ましく用いられる。該凍結防止剤
は、スリップ防止剤の全重量を基準として0.1〜10重
量、好ましくは2.0〜5.0重量％配合される。Examples of the antifreezing agent include glycerin, ethylene glycol, propylene glycol, and esters thereof. Glycerin is preferably used from the viewpoint of the stability of the anti-slip agent. The antifreezing agent is incorporated in an amount of 0.1 to 10% by weight, preferably 2.0 to 5.0% by weight based on the total weight of the antislip agent.
【００１４】ｐＨ調節剤は、コロイダルシリカや水分散
性又は水溶性高分子化合物を水中で安定な分散状態に保
つために用いられ、スリップ防止剤のｐＨを７よりも大
きく１１以下、好ましくは7.5〜10.5の範囲に調製する
に十分な量だけ添加することが好ましい。かかるｐＨ調
節剤としては、アンモニア水、水酸化ナトリウム、水酸
化カリウム、安息香酸ナトリウム又はモノエタノールア
ミンなどが挙げられる。The pH adjuster is used to keep the colloidal silica or the water-dispersible or water-soluble polymer compound in a stable dispersion state in water, and adjusts the pH of the anti-slip agent to more than 7 and 11 or less, preferably 7.5 or less. Preferably, it is added in an amount sufficient to make the amount in the range of 110.5. Examples of such a pH adjuster include aqueous ammonia, sodium hydroxide, potassium hydroxide, sodium benzoate and monoethanolamine.
【００１５】本発明のスリップ防止剤は、例えば、上記
コロイダルシリカの水分散液と、上記有機ポリマーラテ
ックスの水分散液と、上記水分散性又は水溶性高分子化
合物の水分散液とを撹拌混合し、必要に応じて水及び／
又は上記添加剤を混合することによって容易に製造する
ことができる。但し、これらの各水分散液には予め界面
活性剤が含まれている場合があるため、混合時に一方の
分散液が他方の分散液の安定性に影響を与えることがあ
るが、これらの相性は、使用する分散液の種類に応じて
当業者が適宜判断することができる。水としては、イオ
ン交換水を使用することが好ましいが、硬度として５０
ppm以上の不純物混入水を化学的に処理することによっ
て使用することも可能である。The anti-slip agent of the present invention is prepared by, for example, stirring and mixing the aqueous dispersion of colloidal silica, the aqueous dispersion of the organic polymer latex, and the aqueous dispersion of the water-dispersible or water-soluble polymer compound. Water and / or
Alternatively, it can be easily produced by mixing the above additives. However, since each of these aqueous dispersions may contain a surfactant in advance, one of the dispersions may affect the stability of the other dispersion during mixing. Can be appropriately determined by those skilled in the art according to the type of dispersion used. As the water, it is preferable to use ion-exchanged water.
It is also possible to use water by chemically treating contaminated water of ppm or more.
【００１６】本発明のスリップ防止剤は、紙器の封函
後、パレット積み上げ時に、現場で、ブラシ、ローラー
やスプレー等の塗布手段を用いて紙器に塗布することが
できる。塗膜の乾燥は室温で放置するだけで可能であ
る。かかる使用形態では、本発明のスリップ防止剤は、
コロイダルシリカと、有機ポリマーラテックスと、高分
子化合物とを固形分換算でスリップ防止剤の全重量を基
準として0.2〜６重量％含有するように調製することが
好ましい。The anti-slip agent of the present invention can be applied to a paper container on site by using an application means such as a brush, a roller or a spray at the time of stacking pallets after packing the paper container. Drying of the coating is possible only by leaving it at room temperature. In such a form of use, the anti-slip agent of the present invention comprises
It is preferable to prepare colloidal silica, an organic polymer latex, and a polymer compound so as to contain 0.2 to 6% by weight in terms of solid content based on the total weight of the anti-slip agent.
【００１７】本発明のスリップ防止剤は、ハンドスプレ
ー付の容器等に詰められた形態として提供することもで
きる。また、段ボール箱やクラフトバッグ等の紙器の製
造工程において、その紙表面に本発明のスリップ防止剤
を予め塗布しておくことを妨げるものではない。The anti-slip agent of the present invention can be provided in a form packed in a container or the like with a hand spray. Further, it does not prevent the anti-slip agent of the present invention from being applied in advance to the paper surface in the manufacturing process of paper containers such as cardboard boxes and craft bags.
【００１８】[0018]
【実施例】以下、本発明を実施例により詳しく説明する
が、本発明はこれらに限定されるものではない。The present invention will be described in more detail with reference to the following Examples, which should not be construed as limiting the invention thereto.
【００１９】実施例１ 表１に示す配合にて、各種成分を撹拌混合し、本発明の
スリップ防止剤を調製した。Example 1 The components shown in Table 1 were mixed with stirring to prepare the anti-slip agent of the present invention.
【００２０】[0020]
【表１】 [Table 1]
【００２１】３５０ml缶ビール包装用（24個詰め）段ボ
ール箱に該缶ビール２４個を充填し、該箱を閉じた後、
上述のように調製したスリップ防止剤を0.5〜１ｇづつ
該箱の天面の４隅の面積約６０mm×７０mmの領域に塗布
した。After filling 24 cans of beer into a 350 ml can beer packaging (packed with 24 cans) cardboard box and closing the box,
The anti-slip agent prepared as described above was applied in an amount of 0.5 to 1 g to the area of about 60 mm × 70 mm at the four corners of the top surface of the box.
【００２２】かくしてスリップ防止剤が塗布された段ボ
ール箱をJISP8147に従いテスト機のテーブル上に２段に
積み重ねて１分間放置した後、該テーブルを１分間に３
０度の速度で傾斜させて上の箱が下の箱に対して滑り始
める傾斜角度を測定したところ、該傾斜角度は４３度で
あった。また、段ボール箱を積み重ねて１５分間放置し
た以外上記と同様に試験したところ、試験機の上限値で
ある傾斜角度５５度に達しても荷崩れしないことが判っ
た。流通業界の基準では、この傾斜角度が４０度以上で
ある場合に合格とされていることから、本発明のスリッ
プ防止剤がこの基準を充分満足するものであることは明
らかである。The cardboard boxes coated with the anti-slip agent are stacked on a table of a test machine in two stages in accordance with JISP8147 and allowed to stand for 1 minute.
The tilt angle was measured at an angle of 0 °, and the tilt angle at which the upper box began to slide relative to the lower box was 43 °. In addition, a test was performed in the same manner as described above except that the cardboard boxes were stacked and left for 15 minutes, and it was found that the load did not collapse even when the inclination angle reached 55 degrees, which is the upper limit of the tester. According to the standards in the distribution industry, if the angle of inclination is 40 degrees or more, it is determined that the anti-slip agent of the present invention sufficiently satisfies this standard.
【００２３】スリップ防止剤のブロッキング性について
は、上記と同様の方法でスリップ防止剤を塗布した段ボ
ール箱を１０段積み重ね、環境温度２５℃、相対湿度６
５％に管理された調整室に２４時間保管した後、各段ボ
ール箱を分離してブロッキングの有無を目視で検査し
た。その結果、スリップ防止剤のブロッキングは発生し
ていないことが確かめられた。その際の分離性について
も、普通の消費者が違和感なく分離できる程度に良好で
あることも確かめられた。With respect to the blocking property of the anti-slip agent, cardboard boxes coated with the anti-slip agent in the same manner as described above are stacked in 10 layers, and the environmental temperature is 25 ° C. and the relative humidity is 6
After being stored in a control room controlled at 5% for 24 hours, each cardboard box was separated and visually inspected for blocking. As a result, it was confirmed that blocking of the antislip agent did not occur. It was also confirmed that the separability at that time was good enough for ordinary consumers to separate without any discomfort.
【００２４】[0024]
【発明の効果】本発明の紙器スリップ防止剤によれば、
コロイダルシリカと、有機ポリマーラテックスと、水分
散性又は水可溶性の高分子化合物とからなる水ベースの
組成物が得られる。かくして、有機溶剤等に溶解したり
加熱溶融させる必要なしに、パレットへ積み上げる前
に、該スリップ防止剤を現場にてスプレー等で紙器へ塗
布するだけでスリップ防止膜を形成できる。このスリッ
プ防止剤の塗膜は、パレットの傾斜角度４５°以上の高
度な滑り防止性を発揮し、また、ブロッキングを起すこ
ともないので荷降ろし時の操作も簡単に行え、紙器の表
面を損傷させることもない。According to the paper container anti-slip agent of the present invention,
A water-based composition comprising colloidal silica, an organic polymer latex, and a water-dispersible or water-soluble polymer compound is obtained. Thus, the anti-slip film can be formed simply by spraying the anti-slip agent on a paper container by spraying or the like before stacking on a pallet without dissolving in an organic solvent or the like and heating and melting. This anti-slip agent coating exhibits a high degree of anti-slip properties for pallets with a tilt angle of 45 ° or more. Also, since it does not cause blocking, it can be easily operated when unloading and damages the surface of paper containers. I won't let you.
Claims (26)
と、有機ポリマーラテックスと、水分散性又は水可溶性
の高分子化合物とを含有する水分散液からなる紙器スリ
ップ防止剤。1. A paper container anti-slip agent comprising an aqueous dispersion containing colloidal silica having an average particle diameter of 9 nm or less, an organic polymer latex, and a water-dispersible or water-soluble polymer compound.
〜９nmの範囲内である請求項１に記載のスリップ防止
剤。2. An average particle diameter of the colloidal silica is 3
The anti-slip agent according to claim 1, wherein the anti-slip agent is in a range of from 9 to 9 nm.
〜６nmの範囲内である請求項２に記載のスリップ防止
剤。3. An average particle diameter of the colloidal silica is 4
3. An anti-slip agent according to claim 2, which is in the range of ~ 6 nm.
止剤の全重量を基準として0.10〜10重量％含有してなる
請求項１に記載のスリップ防止剤。4. The anti-slip agent according to claim 1, comprising 0.1 to 10% by weight of the colloidal silica based on the total weight of the anti-slip agent.
止剤の全重量を基準として0.10〜0.49重量％含有してな
る請求項４に記載のスリップ防止剤。5. The anti-slip agent according to claim 4, wherein the colloidal silica is contained in an amount of 0.10 to 0.49% by weight based on the total weight of the anti-slip agent.
ップ防止剤の全重量を基準として0.10〜10重量％含有し
てなる請求項１に記載のスリップ防止剤。6. The anti-slip agent according to claim 1, comprising 0.1 to 10% by weight of the organic polymer latex based on the total weight of the anti-slip agent.
ップ防止剤の全重量を基準として0.10〜0.49重量％含有
してなる請求項６に記載のスリップ防止剤。7. The anti-slip agent according to claim 6, comprising 0.10 to 0.49% by weight of the organic polymer latex based on the total weight of the anti-slip agent.
ル系ラテックス、メタクリル系ラテックス、スチレン系
ラテックス、又はスチレンコポリマー系ラテックスであ
る請求項１に記載のスリップ防止剤。8. The anti-slip agent according to claim 1, wherein the organic polymer latex is an acrylic latex, a methacrylic latex, a styrene latex, or a styrene copolymer latex.
ラテックス、ＮＢＲラテックス及びその他の合成又は天
然ゴム系ラテックスである請求項１に記載のスリップ防
止剤。9. The organic polymer latex is SBR
The anti-slip agent according to claim 1, wherein the anti-slip agent is latex, NBR latex or other synthetic or natural rubber-based latex.
度（Ｔｇ）は−５０℃〜−１５℃である請求項９に記載
のスリップ防止剤。10. The anti-slip agent according to claim 9, wherein the rubber-based latex has a glass transition temperature (Tg) of −50 ° C. to −15 ° C.
止剤の粘度を５０〜５００ｃｐ（２５℃、Ｂ型粘度計測
定値）とするに十分な量だけ含有する請求項１に記載の
スリップ防止剤。11. The anti-slip agent according to claim 1, wherein the polymer compound is contained in an amount sufficient to make the viscosity of the anti-slip agent 50 to 500 cp (at 25 ° C., measured by a B-type viscometer).
剤の全重量を基準として0.1〜20重量％含有してなる請
求項１に記載のスリップ防止剤。12. The anti-slip agent according to claim 1, comprising 0.1 to 20% by weight of the polymer compound based on the total weight of the anti-slip agent.
剤の全重量を基準として3.5〜６重量％含有してなる請
求項１２に記載のスリップ防止剤。13. The anti-slip agent according to claim 12, comprising 3.5 to 6% by weight of the polymer compound based on the total weight of the anti-slip agent.
物、ポリビニルアルコール及びアルギン酸ナトリウムか
らなる群より選ばれた少なくとも１種の化合物である請
求項１２に記載のスリップ防止剤。14. The anti-slip agent according to claim 12, wherein the polymer compound is at least one compound selected from the group consisting of a cellulosic compound, polyvinyl alcohol and sodium alginate.
求項１に記載のスリップ防止剤。15. The anti-slip agent according to claim 1, further comprising an antiseptic or antifungal agent.
ヒド、安息香酸ナトリウム又はフェノール系防腐又は防
黴剤である請求項１５に記載のスリップ防止剤。16. The antislip agent according to claim 15, wherein the antiseptic or fungicide is formaldehyde, sodium benzoate or a phenolic antiseptic or fungicide.
ペンタクロロフェノレート又はｐ−ヒドロキシ安息香酸
エステルである請求項１６に記載のスリップ防止剤。17. The phenol-based preservative or antifungal agent,
The anti-slip agent according to claim 16, which is pentachlorophenolate or p-hydroxybenzoate.
項１に記載のスリップ防止剤。18. The anti-slip agent according to claim 1, further comprising an anti-freezing agent.
レングリコール、プロピレングリコール又はこれらのエ
ステルである請求項１８に記載のスリップ防止剤。19. The anti-slip agent according to claim 18, wherein the anti-freezing agent is glycerin, ethylene glycol, propylene glycol or an ester thereof.
の全重量を基準として0.1〜10重量％含有してなる請求
項１８に記載のスリップ防止剤。20. The anti-slip agent according to claim 18, comprising 0.1 to 10% by weight of the anti-freezing agent based on the total weight of the anti-slip agent.
の全重量を基準として2.0〜5.0重量％含有してなる請求
項２０に記載のスリップ防止剤。21. The anti-slip agent according to claim 20, comprising 2.0 to 5.0% by weight of the anti-freezing agent based on the total weight of the anti-slip agent.
項１に記載のスリップ防止剤。22. The anti-slip agent according to claim 1, further comprising a pH adjuster.
化ナトリウム、水酸化カリウム、安息香酸ナトリウム又
はモノエタノールアミンである請求項２２に記載のスリ
ップ防止剤。23. The anti-slip agent according to claim 22, wherein the pH adjuster is aqueous ammonia, sodium hydroxide, potassium hydroxide, sodium benzoate or monoethanolamine.
ムラテックスと、前記高分子化合物とを固形分換算で前
記スリップ防止剤の全重量を基準として0.2〜６重量％
含有する請求項１に記載のスリップ防止剤。24. The colloidal silica, the synthetic rubber latex, and the polymer compound are 0.2 to 6% by weight in terms of solid content based on the total weight of the anti-slip agent.
The anti-slip agent according to claim 1 which contains.
されてなる段ボール箱。25. A cardboard box coated with the paper container anti-slip agent according to claim 1.
１の紙器スリップ防止剤を塗布することを特徴とする紙
器スリップ防止方法。26. A method for preventing slippage of a paper box according to claim 1, wherein the paperboard slip preventing agent according to claim 1 is applied to the surface of the paper box after the box is sealed.