JPH10191806A - Collar made of bark for roadside tree - Google Patents
Collar made of bark for roadside treeInfo
- Publication number
- JPH10191806A JPH10191806A JP9011985A JP1198597A JPH10191806A JP H10191806 A JPH10191806 A JP H10191806A JP 9011985 A JP9011985 A JP 9011985A JP 1198597 A JP1198597 A JP 1198597A JP H10191806 A JPH10191806 A JP H10191806A
- Authority
- JP
- Japan
- Prior art keywords
- bark
- collar
- street
- tree
- street tree
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、道路沿いに植えら
れる街路樹の根本に配されて好適な街路樹用樹皮製カラ
ーに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a bark collar for a roadside tree suitable for being placed at the root of a roadside tree planted along a road.
【０００２】[0002]
【従来の技術】従来、街並を飾るために、道路沿いには
イチョウやケヤキ等の樹木を植えられるようになってい
る。すなわち、道路沿いの歩道は、コンクリートやアス
ファルトの舗装が行われるが、一定間間隔をおいてコン
クリート等の舗装が行われない土の部分を設け、この土
の部分に上記イチョウやケヤキ等の樹木を植えて都市生
活等に潤いを与えている。2. Description of the Related Art Conventionally, trees such as ginkgo and zelkova have been planted along roads to decorate the streets. That is, the sidewalk along the road is paved with concrete or asphalt, but is provided with a portion of soil that is not paved with concrete or the like at regular intervals. Planting to give moisture to city life.
【０００３】しかしながら、街路樹は、四季折々に、追
肥や枝落とし等の手入れが必要であり、特に、街路樹の
根本の周囲に雑草が生えてきた場合には、街路樹の美観
を損ねないようにするため、この雑草を刈り取る等の作
業が必要であった。[0003] However, the roadside trees require maintenance such as topdressing and pruning every season. Especially when weeds grow around the roots of the roadside trees, the appearance of the roadside trees is not impaired. In order to do so, it was necessary to cut the weeds.
【０００４】[0004]
【発明が解決しようとする課題】ところで、上記従来の
コンクリート等の舗装が行われない土の部分にイチョウ
等の樹木を単に植えるものにあっては、街路樹の手入れ
の際に関し、街路樹の樹皮を傷つけるという問題があっ
た。特に、街路樹周囲に生えてきた雑草を刈り取る際
に、回転刃を利用した草刈り機が使用されると、この際
に、誤って、前記回転刃により、街路樹自体を伐採して
しまったり、街路樹の樹皮を損傷したりすることがあっ
た。In the above-mentioned conventional plant in which trees such as ginkgo are simply planted in a portion of the soil that is not paved with concrete or the like, the maintenance of the street trees is not a problem. There was a problem of damaging the bark. In particular, when a weeder that uses a rotary blade is used to cut weeds that have grown around the street tree, at this time, the road blade itself is accidentally cut by the rotary blade, In some cases, the bark of the tree was damaged.
【０００５】そこで、本発明は、街路樹の根本の周囲に
雑草が生える事態を防止するとともに、街路樹の樹皮を
損傷したりすることがない街路樹用樹皮製カラーを提供
することを目的とする。Accordingly, an object of the present invention is to provide a color made of bark for a street tree which prevents weeds from growing around the root of the street tree and does not damage the bark of the street tree. I do.
【０００６】[0006]
【課題を解決するための手段】上記課題を解決するため
に、本願請求項１に係る発明の街路樹用樹皮製カラー
は、所定大の樹皮片に接着剤を添加した樹皮製材料が、
ドーナツ状に形成されたことを特徴とする。また、本願
請求項２に係る発明は、前記請求項１に係る街路樹用樹
皮製カラーにおいて、前記ドーナツ状に形成された樹皮
製材料が、層状に形成されたことを特徴とする。さら
に、本願請求項３に係る発明は、前記請求項１に係る街
路樹用樹皮製カラーにおいて、前記ドーナツ状に形成さ
れた樹皮製材料にクレオソートおよびアスファルトが混
合されていることを特徴とする。In order to solve the above-mentioned problems, a bark collar for a street tree according to the first aspect of the present invention is a bark material obtained by adding an adhesive to a bark piece having a predetermined size.
It is characterized by being formed in a donut shape. The invention according to claim 2 of the present application is characterized in that, in the bark collar for a street tree according to claim 1, the donut-shaped bark material is formed in a layer shape. Furthermore, the invention according to claim 3 of the present application is characterized in that, in the bark collar for a street tree according to claim 1, creosote and asphalt are mixed in the donut-shaped bark material. .
【０００７】[0007]
【発明の実施の形態】以下、本発明の一実施の形態を図
面を参照しながら説明する。 （第１の実施の形態）本発明に係る一実施の形態に係る
街路樹用樹皮製カラーは、図１、図２に示すように、い
わゆるドーナツ状の所定大に粉砕された樹皮片２に接着
剤３を添加して形成された樹皮製材料１Ａが層状に加圧
成形された街路樹用樹皮製カラー１である。そして、こ
のドーナツ状の街路樹用樹皮製カラー１の一箇所に切断
面１ａが形成されている。この切断面１ａは、街路樹の
根本に街路樹用樹皮製カラー１を施設する場合に使用さ
れる。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS An embodiment of the present invention will be described below with reference to the drawings. (First Embodiment) A bark collar for a street tree according to an embodiment of the present invention is a so-called donut-shaped bark piece 2 crushed to a predetermined size as shown in FIGS. The bark material 1A formed by adding the adhesive 3 is a bark collar 1 for a street tree, which is formed into a layer by pressure. A cut surface 1a is formed at one location of the donut-shaped street bark collar 1. The cut surface 1a is used when installing a bark collar 1 for a street tree at the root of the street tree.
【０００８】この街路樹用樹皮製カラー１の大きさは、
ここでは外径が直径３０ｃｍ、内径が直径１５ｃｍ、厚
さが３ｃｍの大きさのもので説明するが、本発明は、こ
の大きさに限定されるものではない。街路樹の大きさは
様々であるが、例えば、大きな街路樹の場合、街路樹用
樹皮製カラー１を半分ずつ成形した２つ割で、これら組
み合わせて使用するものでも良い。また、厚さは、これ
よりも厚くしたり薄くしたりしても良い。[0008] The size of the bark collar 1 for street trees is
Here, the outer diameter is 30 cm, the inner diameter is 15 cm, and the thickness is 3 cm. However, the present invention is not limited to this size. Although the size of the street tree varies, for example, in the case of a large street tree, the bark collar 1 for the street tree may be divided into two halves and used in combination. Further, the thickness may be made thicker or thinner.
【０００９】この樹皮製材料１Ａに使用される粉砕され
た樹皮片２の大きさは、約３ｍｍから７ｍｍに粉砕され
たものである。しかし、この大きさに限られるものでは
なく、これよりも若干荒く、約５ｍｍから１０ｍｍの樹
皮片２でも良いことはもちろんである。通常、荒い大き
さのものを用いた方が柔軟性に優れ、細かな大きさのも
のを用いた方が硬質なものとなる。この樹皮片２として
は、廃材の有効利用を図るため、北海道に多いカラマツ
材の樹皮の所定の大きさとした樹皮片２を使用したが、
自然の樹木の樹皮を所定大とした樹皮片２であれば広く
使用することができる。なお、硬質性をだすために、鋸
屑等の木製粉を混ぜ合わせることも可能である。The size of the crushed bark pieces 2 used for the bark material 1A is crushed to about 3 mm to 7 mm. However, the size of the bark 2 is not limited to this size, but may be slightly rougher than this, and may be about 5 mm to 10 mm. Generally, the use of a material having a rough size is excellent in flexibility, and the use of a material having a small size is harder. As bark pieces 2, bark pieces 2 having a predetermined size of larch bark, which are common in Hokkaido, were used in order to effectively use waste wood.
Any bark piece 2 having a natural tree bark of a predetermined size can be widely used. In addition, it is also possible to mix wood powder such as sawdust in order to obtain hardness.
【００１０】上記接着剤３は、ウレタン系接着剤３が使
用されている。このウレタン系接着剤３は、紫外線によ
り分解するものが良い。実際には、三井東圧化学株式会
社製のＨＩＰＲＥＮＥ ＢＡ−２０（商品名）を使用し
た。この接着剤３によれば、硬度のしっかりした成形物
が得られる。As the adhesive 3, a urethane adhesive 3 is used. The urethane adhesive 3 is preferably one that is decomposed by ultraviolet rays. Actually, HIPRENE BA-20 (trade name) manufactured by Mitsui Toatsu Chemicals, Inc. was used. According to the adhesive 3, a molded product having firm hardness can be obtained.
【００１１】このように使用される街路樹用樹皮製カラ
ー１は、樹皮片２に接着剤３も生分解性のものであるた
めに、いわゆる自然と人に優しく、環境保護に適するも
のである。なお、上記樹皮製材料は自然環境に適合した
生分解性を有するため、街路樹に有益な有機質を与える
ことともなる。[0011] The bark collar 1 for street trees used in this manner is so-called nature and human friendly and suitable for environmental protection, since the adhesive 3 is also biodegradable to the bark pieces 2. . In addition, since the bark material has biodegradability suitable for the natural environment, it also provides useful organic matter to street trees.
【００１２】次に、本実施の形態の街路樹用樹皮製カラ
ー１の製造方法を詳細に説明する。前提として、カラマ
ツ等の樹皮が貯滞されている貯滞場で、篩により、予め
樹皮の１次選抜と２次選抜と３次選抜を行い、所定の大
きさの樹皮片２を選抜する。Next, a method of manufacturing the bark collar 1 for a street tree according to the present embodiment will be described in detail. As a premise, primary selection, secondary selection and tertiary selection of bark are previously performed by a sieve in a storage place where bark such as larch is stored, and bark pieces 2 having a predetermined size are selected.
【００１３】１次選抜としては、篩の網目のサイズが２
０×２０ｍｍを使用し、２次選抜としては、篩の網目の
サイズ１０×１０ｍｍを使用する。この場合、これらの
篩にかけるために樹皮を粉砕する粉砕機を使用しても良
い。そして、これら篩にかけて残った樹皮片２につい
て、更に篩にかけ（３次選抜）、約３ｍｍから７ｍｍの
樹皮片２と、これ以外の例えば約５ｍｍから１０ｍｍの
樹皮片２に選別する。[0013] As the primary selection, the sieve mesh size is 2
0 × 20 mm is used, and as the secondary selection, a sieve mesh size of 10 × 10 mm is used. In this case, a crusher for crushing bark may be used for sieving. Then, the bark pieces 2 remaining after being sieved are further sieved (third selection), and are separated into bark pieces 2 of about 3 mm to 7 mm and other bark pieces 2 of, for example, about 5 mm to 10 mm.
【００１４】このように、慎重に篩にかけることによ
り、樹皮片２の粉（パウダー）の部分とを分ける。パウ
ダーの分が多く含まれていると、上記接着剤３の使用量
が多くなってしまうからである。そして、後日乾燥させ
ることにより、樹皮製材料１Ａの樹皮片２となる。In this way, by carefully sieving, the bark pieces 2 are separated from the powder (powder) portion. This is because the use amount of the adhesive 3 increases when the amount of the powder is large. Then, by drying at a later date, bark pieces 2 of bark material 1A are obtained.
【００１５】樹皮製材料１Ａの製造には、約３ｍｍから
７ｍｍのカラマツの樹樹皮片２を約２リットルから２．
５リットル用意した。また、ウレタン系接着剤３である
三井東圧化学株式会社製のＨＩＰＲＥＮＥ ＢＡ−２０
（商品名）を用意した。上記外径が直径３０ｃｍ、内径
が直径１５ｃｍ、厚さが３ｃｍの大きさの街路樹用樹皮
製カラー１の場合で、約５０〜１２５ｇ用意した。そし
て、図３に示すように、上記樹皮片２を容器７に入れ、
接着剤３を加えて、十分撹拌して樹皮製材料１Ａを作製
した。ここでは、ミキサー等の撹拌機を使用することが
効率的である。For the production of the bark material 1A, larch bark pieces 2 of about 3 mm to 7 mm are used.
Five liters were prepared. In addition, the urethane adhesive 3, HIPRENE BA-20 manufactured by Mitsui Toatsu Chemicals, Inc.
(Product name) was prepared. In the case of the color 1 made of bark for a street tree having an outer diameter of 30 cm, an inner diameter of 15 cm, and a thickness of 3 cm, about 50 to 125 g was prepared. Then, as shown in FIG. 3, the bark pieces 2 are put in a container 7,
The adhesive 3 was added, and the mixture was sufficiently stirred to produce a bark material 1A. Here, it is efficient to use a stirrer such as a mixer.
【００１６】そして、図４に示すように、上記樹皮片２
と木製粉とを容器７に入れ、タンク３ａに入れられた接
着剤３を加えて十分撹拌して、樹皮製材料１Ａを作製す
る。次に、木製の成形用型枠４を用意し、図５に示すよ
うに、この成形用型枠４に上記樹皮製材料１Ａを充填し
加圧成形する。すなわち、この成形用型枠４は、外径が
直径３０ｃｍ、内径が直径１５ｃｍ、厚さが３ｃｍの大
きさの街路樹用樹皮製カラー１を製造する大きさに対応
した大きさのもので、蓋を被せて使用される。そして、
加圧機５により加圧成形される。この場合の加圧力を調
節して、街路樹用樹皮製カラー１の柔軟性を調節する。Then, as shown in FIG.
And the wooden powder are placed in the container 7, the adhesive 3 placed in the tank 3a is added, and the mixture is sufficiently stirred to produce the bark material 1A. Next, a wooden molding form 4 is prepared, and as shown in FIG. 5, the bark material 1A is filled in the molding form 4 and pressure molded. That is, the molding form 4 has a size corresponding to a size for manufacturing a bark collar 1 for street trees having an outer diameter of 30 cm, an inner diameter of 15 cm, and a thickness of 3 cm. Used with a lid. And
It is press-formed by the press machine 5. The flexibility of the street bark collar 1 is adjusted by adjusting the pressing force in this case.
【００１７】次いで、図６に示すように、養生機６に入
れて、約８０°Ｃの高温で養生する。なお、温度は常温
での養生も可能である。すると、図１に示す街路樹用樹
皮製カラー１が製造される。このような製造方法によ
り、工場等で上記街路樹用樹皮製カラー１を大量に製造
することができる。したがって、後は、街路樹用樹皮製
カラー１をやや曲げて（図１参照）、上記切断面１ａか
ら街路樹の根本に施設して、使用に供される。Next, as shown in FIG. 6, it is placed in a curing machine 6 and cured at a high temperature of about 80.degree. Curing at normal temperature is also possible. Then, the bark collar 1 for street trees shown in FIG. 1 is manufactured. According to such a manufacturing method, the bark collar 1 for street trees can be manufactured in large quantities in factories and the like. Accordingly, after that, the bark collar 1 for the street tree is slightly bent (see FIG. 1), and the cut piece 1a is installed at the root of the street tree for use.
【００１８】（第２の実施の形態）本実施の形態の街路
樹用樹皮製カラーは、野ネズミや害虫による害から街路
樹を保護するもので、上述した樹皮製材料にクレオソー
トとアスファルトが混合されていることを特徴とする。
まず、本実施の形態の大きさは、外径が直径３０ｃｍ、
内径が直径１５ｃｍである点は、第１の実施の形態と同
じであるが、厚さが約７ｃｍである点が第１の実施の形
態と異なる。このように厚くする理由は、野ネズミによ
る害を有効に防止するためには、約７ｃｍ程度にする必
要があるとも言われていることを考慮したためである。
ただし、これよりも厚くしたり、薄くすることも実施に
応じ任意である。(Second Embodiment) A bark collar for a street tree according to the present embodiment protects a street tree from harm caused by rodents and pests. Creosote and asphalt are used in the bark material described above. It is characterized by being mixed.
First, the size of the present embodiment has an outer diameter of 30 cm,
The point that the inner diameter is 15 cm is the same as that of the first embodiment, but differs from the first embodiment in that the thickness is about 7 cm. The reason for this thickening is to take into account that it is said that the thickness needs to be about 7 cm in order to effectively prevent the harm caused by rodents.
However, it is optional to make it thicker or thinner depending on the implementation.
【００１９】次に、本実施の形態は、上記第１の実施の
形態の樹皮製材料料１Ａにクレオソートとアスファルト
が混合されている。すなわち、本実施の形態の樹皮製材
料１Ａを製造するには、図４に示すように、上記樹皮片
２を容器７に入れ、タンク３ａに入れられた接着剤３を
加えて十分撹拌した後、上記クレオソートとアスファル
トを加え更に撹拌して作製される。Next, in this embodiment, creosote and asphalt are mixed with the bark material 1A of the first embodiment. That is, in order to manufacture the bark material 1A of the present embodiment, as shown in FIG. 4, the bark pieces 2 are placed in a container 7, the adhesive 3 placed in the tank 3a is added, and the mixture is sufficiently stirred. And the above creosote and asphalt are added and further stirred.
【００２０】上記アスファルトは、道路の舗装等に使用
される、炭化水素を主成分とするものである。一方、ク
レオソート（creosote）は、おもにブナ属植物のほか、
ナシ、モミジ、マツなどから得た木タールを蒸留して水
より重い留分を精製したもので、グアヤコール、クレゾ
ールなど約１０種のフェノール類の混合物である。無色
又は微黄色の透明な液で特異なにおいがあり、舌を焼く
ような味がする。水に溶けにくく、エタノール（エチル
アルコール）、エーテル、グリセリンとよく混合する。
また、殺菌、防腐作用を有する。ここでは、野ネズミや
害虫からの害を防止するための防虫剤として使用する
が、このような防虫剤の他、防臭剤を混合することも実
施に応じ任意である。The above-mentioned asphalt is mainly used for pavement of roads, etc., mainly composed of hydrocarbons. Creosote, on the other hand, mainly consists of beech plants,
Wood tar obtained from pear, maple, pine and the like is distilled to purify a fraction heavier than water, and is a mixture of about 10 phenols such as guaiacol and cresol. It is a colorless or faint yellow transparent liquid with a unique smell and tastes like burning a tongue. Poorly soluble in water, mix well with ethanol (ethyl alcohol), ether and glycerin.
In addition, it has a bactericidal and antiseptic action. Here, it is used as an insect repellent for preventing harm from wild rats and pests. In addition to such an insect repellent, it is also possible to mix a deodorant according to the practice.
【００２１】ところで、従来野ネズミ等の害から街路樹
を保護するものとしては、一定の大きさの金網を街路樹
の根本に配設するものがある。そして、このような金網
は冬が来る前に配置され、春になると取り外される。こ
れは街路樹の成長を圧迫しないようにするためと、美観
上好ましくないことによる。しかし、本実施の形態の街
路樹用樹皮製カラー１は、前記樹皮製材料１Ａにクレオ
ソートが混合されていることにより、このクレオソート
のにおいにより野ネズミや害虫が寄りつかなくなり、野
ネズミ等の害から街路樹を守ることができる。また、前
記樹皮製材料にアスファルトが混合されているが、これ
は、このアスファルトがクレオソートをマスキングし
て、雨が降ってもクレオソートが流れ出さないようにす
るためである。したがって、本実施の形態によれば、ク
レオソート等の薬品を混入することにより、野ネズミ等
の被害も防止することができる。By the way, as a conventional method of protecting a street tree from harm of wild rats and the like, there is a method in which a wire net having a certain size is arranged at the root of the street tree. And such wire mesh is placed before winter comes and is removed in spring. This is due to the fact that the growth of the roadside tree is not oppressed and that it is not aesthetically pleasing. However, the bark collar 1 for a street tree according to the present embodiment has a structure in which creosote is mixed with the bark material 1A, so that the smell of the creosote prevents the rodents and pests from approaching. It can protect street trees from harm. The asphalt is mixed with the bark material so that the asphalt masks the creosote so that the creosote does not flow out even if it rains. Therefore, according to the present embodiment, damage to wild rats and the like can be prevented by mixing a chemical such as creosote.
【００２２】以上、本実施の形態では、ドーナツ状の街
路樹用樹皮製カラーについて説明したが、内側が街路樹
の形状に合わせた円形状のものであれば、外形が円形状
のものに限らず四角形状のものであっても良く、又、街
路樹が植えられる土の部分の状に合わせた形状のもので
あっても良いことは言うまでもない。また、本実施の形
態の街路樹用樹皮製カラーは、実際の使用においては、
上記説明のものよりも、薄くして、逆に、厚くしたりす
ることにより調節すると良い。In the present embodiment, the color of the dough-shaped bark for a street tree has been described. However, if the inside has a circular shape corresponding to the shape of the street tree, the outer shape is not limited to the circular shape. Needless to say, the shape may be a square shape, or may be a shape that matches the shape of the soil portion where the street tree is planted. In addition, the bark collar for the street tree of the present embodiment, in actual use,
It is preferable to adjust the thickness by making it thinner and conversely making it thicker than that described above.
【００２３】[0023]
【発明の効果】本発明の街路樹用樹皮製カラーは、この
街路樹用樹皮製カラーを街路樹の根本に施設されること
により、街路樹の根本に雑草が生えることを防止できる
とともに、街並木の美観を整えることもできる。したが
って、従来問題となっていた街路樹の根本に生えた雑草
を刈る際に、街路樹を回転刃を利用した草刈り機等で伐
採してしまったり、樹皮をキズつけてしまうような事態
を防止することができる。また、本発明の街路樹用樹皮
製カラーは、所定大の樹皮片に接着剤を添加して混合さ
れた樹皮製材料が使用されるものであるから、自然環境
に適合した生分解性を有し、長期間施設されても、従来
の金網のように街路樹の根本を圧迫するようなこともな
い。According to the bark collar for a street tree of the present invention, by installing the bark collar for a street tree at the root of the street tree, weeds can be prevented from growing at the root of the street tree, and You can also improve the beauty of the row of trees. Therefore, when cutting weeds that grew on the roots of street trees, which has been a problem in the past, it is possible to prevent situations such as cutting down the street trees with a mowing machine using a rotary blade or scratching the bark. be able to. Further, since the bark collar for street trees of the present invention uses a bark material obtained by adding an adhesive to a bark piece of a predetermined size, it has biodegradability suitable for a natural environment. Even if the facility is installed for a long period of time, it does not squeeze the roots of the street tree unlike conventional wire mesh.
【００２４】そして、本発明の街路樹用樹皮製カラー
は、前記樹皮製材料にクレオソートが混合されることに
より、そのにおいにより野ネズミや害虫の害から街路樹
を守ることができる。In the bark collar for street trees of the present invention, creosote is mixed with the bark material, whereby the street trees can be protected from the harm of wild rats and pests due to the smell.
【００２５】すなわち、本願請求項１の発明によれば、
この街路樹用樹皮製カラーを街路樹の根本に施設するこ
とにより、街路樹の根本の周囲から雑草が生えることを
有効に防止することができる。また、上記発明によれ
ば、所定大の樹皮片に接着剤を添加して混合された樹皮
製材料が使用されていることから、長期間施設されて
も、街路樹の根本を圧迫して、街路樹の成長を損なうこ
ともない。That is, according to the invention of claim 1 of the present application,
By installing the bark collar for the roadside tree at the root of the roadside tree, weeds can be effectively prevented from growing around the root of the roadside tree. Further, according to the above invention, since a bark material mixed by adding an adhesive to a bark piece of a predetermined size is used, even if the facility is installed for a long time, the root of the street tree is pressed, It does not impair the growth of street trees.
【００２６】また、本願請求項２の発明によれば、前記
樹皮製材料にクレオソートが混合されることにより、そ
のにおいにより野ネズミや害虫の害から街路樹を守るこ
とができる。また、前記樹皮製材料にアスファルトが混
合されていることにより、このアスファルトがクレオソ
ートをマスキングして、雨によりクレオソートが流れ出
すことを有効に防止することができる。According to the second aspect of the present invention, by mixing creosote with the bark material, it is possible to protect the street tree from the harm of wild rats and pests due to its odor. Further, since the asphalt is mixed with the bark material, the asphalt masks the creosote, and it is possible to effectively prevent the creosote from flowing out due to rain.
【図１】本発明の一実施の形態の街路樹用樹皮製カラー
の斜視図である。FIG. 1 is a perspective view of a bark collar for a street tree according to an embodiment of the present invention.
【図２】本発明の一実施の形態の街路樹用樹皮製カラー
の斜視図である。FIG. 2 is a perspective view of a bark collar for a street tree according to an embodiment of the present invention.
【図３】上記一実施の形態の製造工程を示すもので、樹
皮製材料を製造する工程を説明する斜視図である。FIG. 3 is a perspective view illustrating a manufacturing process of the embodiment, and illustrating a process of manufacturing a bark material.
【図４】上記一実施の形態の製造工程を示すもので、樹
皮製材料を製造する工程を説明する斜視図である。FIG. 4 is a perspective view illustrating a manufacturing process of the embodiment and illustrating a process of manufacturing a bark material.
【図５】上記一実施の形態の製造工程を示すもので、樹
皮製材料を加圧成形する状態を説明する斜視図である。FIG. 5 is a perspective view showing a manufacturing process of the embodiment and illustrating a state where a bark material is pressure-formed.
【図６】上記一実施の形態の製造工程を示すもので、成
形用型枠を養生機に入れ、養生させる状態を説明する斜
視図である。FIG. 6 is a perspective view illustrating a manufacturing process of the embodiment, illustrating a state in which a forming mold is put into a curing machine and cured.
１・・・街路樹用樹皮製カラー １Ａ・・・樹皮製材料 ２・・・樹皮片 ３・・・接着剤 DESCRIPTION OF SYMBOLS 1 ... Bark color for street tree 1A ... Bark material 2 ... Bark piece 3 ... Adhesive
Claims (3)
製材料が、ドーナツ状に形成されたことを特徴とする街
路樹用樹皮製カラー。1. A bark collar for street trees, wherein a bark material obtained by adding an adhesive to bark pieces of a predetermined size is formed in a donut shape.
状に形成された樹皮製材料が、層状に形成されたことを
特徴とする請求項１に記載の街路樹用樹皮製カラー。2. The bark collar for a street tree according to claim 1, wherein the bark collar for a street tree is formed by layering a bark material formed in a donut shape.
状に形成された樹皮製材料にクレオソートおよびアスフ
ァルトが混合されていることを特徴とする請求項１記載
の街路樹用樹皮製カラー。3. The bark collar for a street tree according to claim 1, wherein said bark collar for a street tree is obtained by mixing creosote and asphalt into a bark material formed in a donut shape.