JPH07155634A - Method and device for grinding waste glass product or the like and solid material using ground waste glass product - Google Patents
Method and device for grinding waste glass product or the like and solid material using ground waste glass productInfo
- Publication number
- JPH07155634A JPH07155634A JP33926393A JP33926393A JPH07155634A JP H07155634 A JPH07155634 A JP H07155634A JP 33926393 A JP33926393 A JP 33926393A JP 33926393 A JP33926393 A JP 33926393A JP H07155634 A JPH07155634 A JP H07155634A
- Authority
- JP
- Japan
- Prior art keywords
- waste
- waste glass
- water tank
- glass product
- high temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は廃ガラス製品、廃陶磁器
等を表面が滑らかでない形状に粉砕することができる廃
ガラス製品等の粉砕方法、粉砕装置および廃ガラス製品
等を粉砕したものを用いた固形物に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention uses a crushing method for crushing waste glass products, waste porcelain, etc. into a shape whose surface is not smooth, a crushing device, and a crushed waste glass product. The solids that were present.
【0002】[0002]
【従来の技術】従来、瓶は透明あるいは茶色のものにつ
いては粉砕して瓶を作る場合の再利用原料として使用す
ることができるが、その他の色に着色された瓶は再利用
できず、産業廃棄物として処理場に埋設処理されてい
る。2. Description of the Related Art Conventionally, bottles that are transparent or brown can be used as a recycled raw material when they are crushed to make bottles, but bottles colored in other colors cannot be reused, and they can be reused in the industry. It is buried as waste in the treatment plant.
【0003】[0003]
【本発明が解決しようとする課題】従来、茶色以外に着
色された瓶は処理場に埋設処理しているため、処理に手
数がかかるとともに、コスト高になるという欠点があ
る。また、埋設処理するため再利用できず、不経済であ
るという欠点があった。Conventionally, since bottles colored other than brown are buried in the treatment plant, there are drawbacks that the treatment is troublesome and the cost is high. In addition, since it is buried, it cannot be reused, which is uneconomical.
【0004】本発明は以上のような従来の欠点に鑑み、
廃ガラス製品、廃陶磁器等を楽に、かつ安全で、騒音や
粉塵を出すことなく表面が滑らかでない形状に粉砕する
ことができる廃ガラス製品等の粉砕方法および粉砕装置
を提供することを目的としている。In view of the above-mentioned conventional drawbacks, the present invention has been made.
An object of the present invention is to provide a crushing method and a crushing device for waste glass products, etc., which can crush waste glass products, waste porcelain, etc. easily and safely into a shape whose surface is not smooth without producing noise or dust. .
【0005】また、本発明は表面が滑らかでない形状に
粉砕されたガラス等の粉砕物と廃プラスチック、アスフ
ァルト廃材等の結合材とで固定したり、あるいはコンク
リート廃材等と凝固剤やコンクリートを用いて固定し、
ブロックや林道等に使用される路盤材等として使用でき
る廃ガラス製品等を粉砕したものを用いた固形物を提供
することを目的としている。Further, according to the present invention, a ground material such as glass whose surface is not smooth is fixed with a binding material such as waste plastic or asphalt waste material, or a concrete waste material is used together with a coagulant or concrete. Fixed,
It is an object of the present invention to provide a solid material using crushed waste glass products, etc. that can be used as a roadbed material used for blocks, forest roads, etc.
【0006】本発明の前記ならびにそのほかの目的と新
規な特徴は次の説明を添付図面と照らし合わせて読む
と、より完全に明らかになるであろう。ただし、図面は
もっぱら解説のためのものであって、本発明の範囲を限
定するものではない。The above and other objects and novel characteristics of the present invention will become more fully apparent when the following description is read in view of the accompanying drawings. However, the drawings are for explanation only and do not limit the scope of the present invention.
【0007】[0007]
【課題を解決するための手段】上記目的を達成するため
に、本発明は廃ガラス製品、廃陶磁器等を焼いて高温に
加熱する加熱工程と、この加熱工程で高温に加熱された
加熱物を高温の状態で水槽に投入して表面が滑らかでな
い形状に粉砕する急冷工程とで廃ガラス製品等の粉砕方
法を構成している。In order to achieve the above object, the present invention provides a heating step of burning waste glass products, waste ceramics, etc. to a high temperature, and a heating material heated to a high temperature in this heating step. A crushing method for waste glass products and the like is configured by a quenching process in which the glass is poured into a water tank at a high temperature and crushed into a shape whose surface is not smooth.
【0008】また、本発明は廃ガラス製品、廃陶磁器等
を焼いて高温に加熱することができる流動式炉と、この
流動式炉の排出口の下部に配置された該流動式炉の排出
口より排出される高温の加熱物を急冷して表面が滑らか
でない形状に粉砕する水槽と、この水槽内に溜まったガ
ラス等の粉砕物を該水槽外へ移送する移送装置とで廃ガ
ラス製品等の粉砕装置を構成している。The present invention also relates to a fluidized furnace capable of burning waste glass products, waste ceramics and the like to a high temperature, and an outlet of the fluidized furnace disposed below the outlet of the fluidized furnace. A waste water product such as waste glass products is cooled by a water tank that rapidly cools the high-temperature heated material discharged into a shape that does not have a smooth surface, and a transfer device that transfers the ground material such as glass accumulated in the water tank to the outside of the water tank. It constitutes a crusher.
【0009】さらに、本発明は廃ガラス製品、廃陶磁器
等を焼いて高温にした後、急冷して表面が滑らかでない
形状に粉砕したガラス等の粉砕物と、廃プラスチック、
アスファルト廃材等の結合材とを混合して該結合材を溶
解するように加熱した後、所定形状に加工して冷却して
固定させたことで廃ガラス製品等を粉砕したものを用い
た固形物を構成している。Further, according to the present invention, waste glass products, waste ceramics, etc. are burned to a high temperature and then rapidly cooled to obtain a crushed product such as glass crushed into a shape whose surface is not smooth;
A solid material obtained by crushing waste glass products, etc. by mixing with a binder such as asphalt waste material and heating to dissolve the binder, processing it into a prescribed shape, cooling and fixing Are configured.
【0010】[0010]
【作用】上記のように構成された廃ガラス製品等の粉砕
方法は、廃ガラス製品、廃陶磁器等を高温に加熱した
後、水槽に投入して急冷するため、自動的に表面が滑ら
かでない形状に粉砕される。In the method of crushing waste glass products, etc. configured as described above, after the waste glass products, waste ceramics, etc. are heated to a high temperature, they are put into a water tank and rapidly cooled, so that the surface is not smooth automatically. Is crushed into.
【0011】[0011]
【本発明の実施例】以下、図面に示す実施例により、本
発明を詳細に説明する。BEST MODE FOR CARRYING OUT THE INVENTION The present invention will be described in detail below with reference to the embodiments shown in the drawings.
【0012】図1ないし図3の本発明の第1の実施例に
おいて、1は廃ガラス製品、廃陶磁器等を焼いて高温に
加熱することができる流動式炉で、この流動式炉1は台
座2と、この台座2に複数個の耐熱キャスター3を介し
て回転可能に取付けられた後端部が大径に形成された耐
熱回転ドラム4と、この回転ドラム4の先端部を上下移
動させて該回転ドラム4の傾斜角度を任意に設定するこ
とができる上下移動装置5と、前記回転ドラム4の先端
部寄りの前記台座2に取付けられた該回転ドラム4内へ
廃ガラス製品、廃陶磁器等を投入するための投入シュー
ト6と、前記回転ドラム4内の後端部寄りの前記台座2
に取付けられた該回転ドラム4内へ火炎を噴射して投入
された廃ガラス製品、廃陶磁器を高温に加熱するブロア
ー7を用いた燃焼装置8と、前記回転ドラム4を回転さ
せるチェーン大歯車9、チェーン10、チェーン小歯車
11、減速機12およびモーター13を用いた回転装置
14とから構成されている。In the first embodiment of the present invention shown in FIGS. 1 to 3, reference numeral 1 denotes a fluidized furnace capable of burning waste glass products, waste ceramics, etc. and heating them to a high temperature. The fluidized furnace 1 is a pedestal. 2, a heat-resistant rotary drum 4 rotatably attached to the pedestal 2 through a plurality of heat-resistant casters 3 and having a large rear end, and a tip end of the rotary drum 4 is vertically moved. A vertical moving device 5 capable of arbitrarily setting the inclination angle of the rotary drum 4, and waste glass products, waste ceramics, etc. in the rotary drum 4 mounted on the pedestal 2 near the tip of the rotary drum 4. Charging chute 6 for charging the machine and the pedestal 2 near the rear end of the rotary drum 4.
A combustion device 8 using a blower 7 for heating a waste glass product and waste ceramics injected by injecting flames into the rotary drum 4 attached to the rotary drum 4, and a chain gear 9 for rotating the rotary drum 4. , A chain 10, a small chain gear 11, a speed reducer 12, and a rotating device 14 using a motor 13.
【0013】前記燃焼装置8は従来から一般に使用され
ている燃料を燃焼させるものや、廃プラスチックを燃焼
させるもの等が使用されるが、なるべく燃料費が安価な
ものが使用される。The combustion device 8 used is one that burns a fuel that has been generally used in the past, one that burns waste plastic, or the like, but a fuel cost is preferably as low as possible.
【0014】なお、前記流動式炉1で焼かれる廃ガラス
製品や廃陶磁器等は、水に投入され急冷されると粉砕さ
れる温度、例えば50℃〜900℃まで加熱される。The waste glass products, waste ceramics and the like baked in the fluidized furnace 1 are heated to a temperature at which they are ground when they are poured into water and rapidly cooled, for example, 50 ° C to 900 ° C.
【0015】15は前記流動式炉1の回転ドラム4の後
端部より排出される高温に焼かれた廃ガラス製品、廃陶
磁器が落下して投入される部位に配置された水槽で、こ
の水槽15の底面はV字状となるように形成されてい
る。Reference numeral 15 denotes a water tank disposed at a portion where the waste glass product burned at a high temperature discharged from the rear end portion of the rotary drum 4 of the fluidized-bed furnace 1 and the waste ceramics are dropped and introduced. The bottom surface of 15 is formed in a V shape.
【0016】16は前記水槽15内の底面に位置する熱
収縮により表面が滑らかでない形状に粉砕されたガラス
等の粉砕物17を該水槽15外へ排出するコンベアー1
8を用いた移送装置である。A conveyor 1 for discharging a crushed material 17 such as glass crushed into a shape whose surface is not smooth due to heat shrinkage located at the bottom of the water tank 15 to the outside of the water tank 15
8 is a transfer device.
【0017】上記構成の廃ガラス製品等の粉砕装置19
は燃焼装置8で燃料を燃焼させ、燃焼火炎を回転ドラム
4内へ吹き込むとともに、回転装置14を駆動させ、回
転ドラム4を回転させ、投入シュート6より廃ガラス製
品20や廃陶磁器21を投入することにより、投入され
た廃ガラス製品20や廃陶磁器21は順次加熱されなが
ら回転ドラム4の後端部へ移動する加熱工程を経て、回
転ドラム4の後端部より水22が収納された水槽15内
へ落下投入され、熱収縮によって表面が滑らかでない形
状に粉砕される急冷工程が行なわれる。この急冷工程で
粉砕されたガラス等の粉砕物17は水槽15の底面に溜
まり、移送装置16の駆動によって水槽15外へ排出さ
れる。Crushing device 19 for waste glass products and the like having the above construction
Burns fuel in the combustion device 8, blows combustion flame into the rotary drum 4, drives the rotary device 14, rotates the rotary drum 4, and inputs the waste glass product 20 and the waste ceramics 21 from the charging chute 6. As a result, the waste glass product 20 and the waste ceramics 21 that have been put into the water tank 15 in which water 22 is stored from the rear end of the rotary drum 4 are subjected to a heating process in which the waste glass product 20 and the waste ceramic 21 are sequentially heated and moved to the rear end of the rotary drum 4. A quenching process is carried out in which the material is dropped into the inside and crushed into a shape whose surface is not smooth due to heat shrinkage. The crushed material 17 such as glass crushed in this quenching step is accumulated on the bottom surface of the water tank 15 and is discharged to the outside of the water tank 15 by driving the transfer device 16.
【0018】上記のようにして形成されたガラス等の粉
砕物17は、図4に示すように廃プラスチックあるいは
アスファルト廃材等の結合材23を使用目的に応じて1
0〜80パーセント混合して加熱し、溶解したところ
で、図5に示すように型24に入れて凝固させて、プロ
ック状あるいは林道等に使用される路盤材等の形状の固
形物25に加工する。As shown in FIG. 4, the crushed material 17 made of glass or the like, which is formed as described above, uses a binder 23 such as waste plastic or asphalt waste material depending on the purpose of use.
When the mixture is mixed with 0 to 80% and heated and melted, it is put into a mold 24 as shown in FIG. 5 to be solidified and processed into a solid material 25 in the shape of a block or a roadbed material used for forest roads. .
【0019】このようにして形成された固形物25はガ
ラス等の粉砕物17の表面が滑らかな形状でないため、
結合材23と強固に結合して割れずらい固形物25とな
る。In the solid material 25 thus formed, the surface of the crushed material 17 such as glass is not smooth,
The solid material 25 is firmly bonded to the binding material 23 and is hard to crack.
【0020】また、図6に示すようにガラス等の粉砕物
17にフライアッシュ、ボトムアッシュ等の焼却灰26
や、コンクリート廃材27等とセメント28あるいは凝
固剤を混合し、水を入れて混練し、図7に示すように型
24に入れてブロック状あるいは路盤材等の形状の固形
物25Aにしてもよい。Further, as shown in FIG. 6, incinerated ash 26 such as fly ash and bottom ash is added to crushed material 17 such as glass.
Alternatively, the concrete waste material 27 and the like are mixed with the cement 28 or the coagulant, water is added and kneaded, and the solid material 25A in the shape of the block or the roadbed material is put into the mold 24 as shown in FIG. .
【0021】[0021]
【本発明の効果】以上の説明から明らかなように、本発
明にあっては次に列挙する効果が得られる。As is apparent from the above description, the following effects can be obtained in the present invention.
【0022】(1)廃ガラス製品、廃陶磁器等を焼いて
高温に加熱する加熱工程と、この加熱工程で高温に加熱
された加熱物を高温の状態で水槽に投入して表面が滑ら
かでない形状に粉砕する急冷工程とからなるので、廃ガ
ラス製品、廃陶磁器等を楽にかつ安全に、騒音や粉塵を
出すことなく、表面が滑らかでない形状に粉砕すること
ができる。したがって、従来のプレスによる粉砕のよう
に表面が滑らかで鋭角状の突起がないため、安全に取扱
いすることができる。(1) A heating process in which waste glass products, waste ceramics, etc. are baked and heated to a high temperature, and a heating object heated to a high temperature in this heating process is put in a water tank in a high temperature state and the surface is not smooth. Since it comprises a rapid cooling step of crushing into pieces, waste glass products, waste porcelain, etc. can be crushed into a shape with a smooth surface easily and safely without generating noise or dust. Therefore, unlike the conventional crushing with a crushed surface, the surface is smooth and there are no sharp-angled protrusions, so that it can be handled safely.
【0023】(2)前記(1)によって、ブロックや林
道等に埋設される路盤材に使用できるガラス等の粉砕物
にできる。(2) According to the above (1), it is possible to obtain a crushed material such as glass that can be used as a roadbed material buried in a block or a forest road.
【0024】(3)前記(1)によって、再利用のでき
るガラス等の粉砕物にできるため資源の有効利用を図る
ことができるとともに、公害問題の解消を図ることがで
きる。(3) According to the above (1), it is possible to make crushed materials such as reusable glass, so that resources can be effectively used and pollution problems can be solved.
【0025】(4)請求項2も前記(1)〜(3)と同
様な効果が得られるとともに、特別な装置を用いなくて
もよいので、比較的安価に設置することができる。(4) According to the second aspect, the same effects as the above (1) to (3) can be obtained, and since no special device is required, the device can be installed relatively inexpensively.
【0026】(5)請求項3、4は廃ガラス製品、廃陶
磁器を用いて林道等に埋設される路盤材等の固形物にな
るので、費用をかけて捨てていた廃ガラス製品、廃陶磁
器を有効利用することができる。(5) Claims 3 and 4 are waste glass products and waste ceramics, which are solid materials such as roadbeds buried in forest roads and the like, so waste glass products and waste ceramics that have been discarded at high cost. Can be effectively used.
【図1】本発明の第1の実施例を示す断面図。FIG. 1 is a sectional view showing a first embodiment of the present invention.
【図2】本発明の第1の実施例を示す平面図。FIG. 2 is a plan view showing a first embodiment of the present invention.
【図3】本発明の第1の実施例を示す側面図。FIG. 3 is a side view showing the first embodiment of the present invention.
【図4】固形物の製造方法の説明図。FIG. 4 is an explanatory view of a method for manufacturing a solid material.
【図5】固形物の形成方法の説明図。FIG. 5 is an explanatory view of a method for forming solid matter.
【図6】固形物の異なる製造方法の説明図。FIG. 6 is an explanatory view of different manufacturing methods of solid materials.
【図7】固形物の形成方法の説明図。FIG. 7 is an explanatory view of a method for forming solid matter.
1:流動式炉、 2:台座、3:耐熱
キャスター、 4:回転ドラム、5:上下移
動装置、 6:投入シュート、7:ブロワ
ー、 8:燃焼装置、9:チェーン大
歯車、 10:チェーン、11:チェーン小
歯車、 12:減速機、13:モーター、
14:回転装置、15:水槽、
16:移送装置、17:ガラス等の粉砕物、
18:コンベアー、19:廃ガラス製品等の粉
砕装置、20:廃ガラス製品、21:廃陶磁器、
22:水、23:結合材、
24:型、25、25A:固形物、 26:
焼却灰、27:コンクリート廃材、 28:セメ
ント。1: Fluidized furnace, 2: Pedestal, 3: Heat-resistant caster, 4: Rotating drum, 5: Vertical moving device, 6: Input chute, 7: Blower, 8: Combustion device, 9: Chain gear, 10: Chain, 11: Chain small gear, 12: Reducer, 13: Motor,
14: Rotating device, 15: Water tank,
16: transfer device, 17: crushed material such as glass,
18: conveyor, 19: crushing device for waste glass products, 20: waste glass products, 21: waste ceramics,
22: water, 23: binder,
24: Mold, 25, 25A: Solid, 26:
Incinerated ash, 27: waste concrete material, 28: cement.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 FI 技術表示箇所 B09B 3/00 ZAB C04B 18/16 B09B 3/00 301 S 303 B ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI Technical display location B09B 3/00 ZAB C04B 18/16 B09B 3/00 301 S 303 B
Claims (4)
に加熱する加熱工程と、この加熱工程で高温に加熱され
た加熱物を高温の状態で水槽に投入して表面が滑らかで
ない形状に粉砕する急冷工程とを含むことを特徴とする
廃ガラス製品等の粉砕方法。1. A heating step of burning waste glass products, waste ceramics, etc. to a high temperature, and heating the material heated to a high temperature in this heating step into a water tank at a high temperature to make the surface not smooth. A method for crushing waste glass products, which comprises a quenching step of crushing.
に加熱することができる流動式炉と、この流動式炉の排
出口の下部に配置された該流動式炉の排出口より排出さ
れる高温の加熱物を急冷して表面が滑らかでない形状に
粉砕する水槽と、この水槽内に溜まったガラス等の粉砕
物を該水槽外へ移送する移送装置とを備えることを特徴
とする廃ガラス製品等の粉砕装置。2. A fluidized furnace capable of burning waste glass products, waste porcelain, etc. to a high temperature and discharging from a discharge outlet of the fluidized furnace arranged below the discharge outlet of the fluidized furnace. Waste glass characterized by comprising a water tank for rapidly cooling a high-temperature heated material into a shape whose surface is not smooth, and a transfer device for transferring the ground material such as glass accumulated in the water tank to the outside of the water tank Equipment for crushing products, etc.
にした後、急冷して表面が滑らかでない形状に粉砕した
ガラス等の粉砕物と、廃プラスチック、アスファルト廃
材等の結合材とを混合して該結合材を溶解するように加
熱した後、所定形状に加工して冷却して固定させたこと
を特徴とする廃ガラス製品等を粉砕したものを用いた固
形物。3. A crushed product such as glass crushed into a shape whose surface is not smooth by burning waste glass products, waste porcelain, etc. to a high temperature, and a binder such as waste plastic or asphalt waste material. Then, after heating so that the binder is melted, it is processed into a predetermined shape, cooled and fixed, and a solid material using a crushed waste glass product or the like.
にした後、急冷して表面が滑らかでない形状に粉砕した
ガラス等の粉砕物と、焼却灰、コンクリート廃材等の混
合物とに凝固剤やコンクリートを用いて所定形状に加工
したことを特徴とする廃ガラス製品等を粉砕したものを
用いた固形物。4. A coagulant for a crushed product of glass or the like, which is obtained by burning waste glass products, waste porcelain, etc. to a high temperature and then rapidly cooling them to obtain a shape whose surface is not smooth, and a mixture of incinerated ash, concrete waste materials, etc. Solid material made by crushing waste glass products, etc., characterized by being processed into a predetermined shape using concrete or concrete.