JPH0386643A - Soft decoration plate and manufacture thereof - Google Patents
Soft decoration plate and manufacture thereofInfo
- Publication number
- JPH0386643A JPH0386643A JP22243789A JP22243789A JPH0386643A JP H0386643 A JPH0386643 A JP H0386643A JP 22243789 A JP22243789 A JP 22243789A JP 22243789 A JP22243789 A JP 22243789A JP H0386643 A JPH0386643 A JP H0386643A
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- flexible decorative
- resin
- decoration
- soft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
(産業上の利用分野)
本発明は、磁石機能をもった軟質の装飾板に関するもの
で、例えば車両のボディ外板、家具、扉、壁板、カンパ
ン板、エレベータ内壁等の磁石が吸着可能なものに適用
される。Detailed Description of the Invention (Industrial Application Field) The present invention relates to a soft decorative plate with a magnetic function, such as a vehicle body outer panel, furniture, doors, wall panels, campan boards, and elevator inner walls. Applicable to objects that can be attracted by magnets such as
(従来の技術)
余暇の増大、レジャーの多様化、ライフスタイルの個性
化、高級化等の趣向に加え、流行の変化の激しい時代を
迎えている。このような趣向の多様化に対応して車両の
ボディ外装は、メーカーの段階で、多様化、個性化、高
級化し、モデルチェンジも頻繁に行われるようになって
いる。(Prior Art) In addition to trends such as increased leisure time, diversification of leisure activities, individualization of lifestyles, and increasing luxury, we are entering an era of rapid changes in fashion. In response to these diversifying tastes, vehicle body exteriors are becoming more diverse, individualized, and luxurious at the manufacturer stage, and model changes are becoming more frequent.
しかし、車両を購入した個人の側では、ボディ外装の形
態が流行遅れになったとか飽きたとかで短期間のうちに
ボディ外装を変換することは経済的に困難であるので、
しばらくそのボディ外装で我慢することが多い、また、
社名や宣伝事項がボディに表記された車両は、社用車と
しては使えるが私用車としては使い難い。However, for the individual who purchased the vehicle, it is economically difficult to change the body exterior in a short period of time because the style of the body exterior has gone out of fashion or has become boring.
I often settle for that body exterior for a while, and
A vehicle with the company name or promotional information written on its body can be used as a company car, but it is difficult to use it as a private car.
このように車両の外装を手軽に変更したいという希望は
、ボディの塗装を塗り替えるか、ボディにプリントシー
ルな貼り付ける等によりかなえられる。The desire to easily change the exterior of a vehicle can be achieved by repainting the body or pasting printed stickers on the body.
(発明が解決しようとする課題)
しかしながら、車両等の外装を変更する従来の手段とし
ては、例えば塗装であれば、作業が煩雑で費用がかかり
、プリントシールであれば、剥離しやすいとか接着後に
これを剥離するのが困難である等の問題がある。(Problems to be Solved by the Invention) However, as conventional means for changing the exterior of vehicles etc., for example, painting is a complicated and expensive process, while printed stickers are easy to peel off and are difficult to apply after adhesion. There are problems such as difficulty in peeling this off.
本発明は、このような問題点を解決するため(こなされ
たもので、物品の装飾を簡単な作業で変更ができ、かつ
、取付は取外しにより簡単にもとの装飾に復帰できるよ
うにした柔軟性装飾板を提供することを目的とする。The present invention was developed in order to solve these problems, and it is possible to change the decoration of an article with a simple operation, and to easily restore the original decoration by attaching and removing it. The purpose is to provide a flexible decorative board.
(課題を解決するための手段)
そのために、本発明の第1の発明の柔軟性装飾板は、硬
質磁石材′料粉末と樹脂と可塑剤とを主成分とする磁性
シートと、この磁性シートの表面に付される装飾部とか
らなることを特徴とする。(Means for Solving the Problems) For this purpose, the flexible decorative board of the first aspect of the present invention comprises a magnetic sheet whose main components are hard magnet material powder, a resin, and a plasticizer, and a decorative portion attached to the surface.
本発明の第2の発明の柔軟性装飾板の製造法は、硬質磁
石材料粉末と樹脂と可塑剤とを添加してシート状に成形
する工程と、このシートに装飾手段を施す工程と、前記
シートを多極磁化する工程とからなることを特徴とする
。The method for manufacturing a flexible decorative board according to the second aspect of the present invention includes a step of adding hard magnetic material powder, a resin, and a plasticizer and forming it into a sheet, a step of applying a decorative means to the sheet, and The method is characterized by comprising a step of magnetizing the sheet with multipolar magnetization.
本発明の第3の発明の柔軟性装飾板の製造法は、前記シ
ート状に成形する工程を磁場中で行い磁石材料粉末を一
定の方向に揃えて行うことを特徴とする。The method for manufacturing a flexible decorative board according to the third aspect of the present invention is characterized in that the step of forming the sheet into a sheet is performed in a magnetic field so that the magnet material powder is aligned in a certain direction.
(作用)
本発明の製造法により得られる柔軟性装飾板によると、
材質が磁力をもった軟質樹脂になるため、平坦な鉄製品
等の外板はもちろん曲面をもった鉄板等に対しても簡単
に脱着ができ、必要に応じた装飾の付加、変更等が可能
である。また、この柔軟性装飾板を吸着することにより
、その物品の表面を損傷などから保護することができる
。(Function) According to the flexible decorative board obtained by the manufacturing method of the present invention,
Since the material is a soft resin with magnetic force, it can be easily attached and detached not only to the outer panels of flat iron products, but also to iron plates with curved surfaces, and decorations can be added or changed as necessary. It is. Moreover, by adsorbing this flexible decorative plate, the surface of the article can be protected from damage.
(実施例) 以下、本発明の実施例を図面にもとづいて説明する。(Example) Embodiments of the present invention will be described below based on the drawings.
第1図は社用車を私用車として使用するために柔軟性装
飾板を取付けた実施例を示す。FIG. 1 shows an embodiment in which a flexible decorative plate is attached to a company car for use as a private car.
社用車としての車両1は、第2図に示すように、そのボ
ディ2の前ドア3の下部に、例えば、「○○株式会社」
の如く社名表示4が記載されている。As shown in FIG. 2, the vehicle 1 as a company car has, for example, "XX Co., Ltd." written on the bottom of the front door 3 of its body 2.
Company name display 4 is written as shown below.
この第2図に示す社用車に対し、第1図に示す車両1で
は、第2図に示す社名表示4が覆い隠されるように社名
表示4の部分に第1の柔軟性装飾板5が磁力により接着
されている。さらに第1の柔軟性装飾板5の後方側の後
ドア6およびリアボディ8には、第2の柔軟性装飾板7
および第3の柔軟性装飾板9が同様にlin力により接
着されている。In contrast to the company car shown in FIG. 2, the vehicle 1 shown in FIG. 1 has a first flexible decorative plate 5 on the company name display 4 so that the company name display 4 shown in FIG. 2 is covered. Attached by magnetic force. Furthermore, a second flexible decorative plate 7 is provided on the rear door 6 and the rear body 8 on the rear side of the first flexible decorative plate 5.
And a third flexible decorative plate 9 is similarly bonded by lin force.
次にこの柔軟性装飾板5.7.9の製造法の一例につい
て説明する。Next, an example of a method of manufacturing this flexible decorative board 5.7.9 will be explained.
ストロンチウムフェライト(Sr0・6 F e xO
,)の粉末を仮焼結後、粒径l〜2μmに粉砕し、得ら
れたマグネットプライム構造をもつストロンチウムフェ
ライト微粉末に塩化ビニル樹脂を添加し、これに可塑剤
としてのフタル酸ジオクチル(DOP)を添加し、混合
し、均一に混練した。Strontium ferrite (Sr0.6 Fe xO
, ) was pre-sintered and then ground to a particle size of 1 to 2 μm. Vinyl chloride resin was added to the resulting fine strontium ferrite powder with a magnetic prime structure, and dioctyl phthalate (DOP) was added as a plasticizer. ) was added, mixed, and kneaded uniformly.
この場合のストロンチウムフェライト微粉末と塩化ビニ
ル樹脂とフタル酸ジオクチルの混合比は、重量比で78
: 20 : 2である。In this case, the mixing ratio of strontium ferrite fine powder, vinyl chloride resin, and dioctyl phthalate is 78 by weight.
:20:2.
その後、この混線物を200℃の温度でロール成形して
、厚さ:0.8mm、幅:1000mm、長さ:50m
のシートを製造した。このシートを厚さ0.8mm、幅
:500mm、長さ:1000mmに切断し、フェライ
ト6n石材料からなる磁性シートを得た。Thereafter, this mixed wire material was roll-formed at a temperature of 200°C to obtain a thickness of 0.8 mm, a width of 1000 mm, and a length of 50 m.
sheets were manufactured. This sheet was cut into pieces having a thickness of 0.8 mm, a width of 500 mm, and a length of 1000 mm to obtain a magnetic sheet made of ferrite 6n stone material.
一方、装飾手段としての楠の木材を80amの厚さにス
ライスし、得られた薄片シートをアルカリ処理により柔
軟化し、変色防止し、中和、乾燥し、含水率40%の装
飾用の薄片シートにした。On the other hand, the camphor wood used as a decorative means is sliced to a thickness of 80 am, and the obtained thin sheets are softened by alkali treatment, prevented from discoloring, neutralized, dried, and used as decorative thin sheets with a moisture content of 40%. I made it.
アルカリ処理したのは、薄片シートの適度の柔軟性を確
保するためである。The reason for the alkali treatment was to ensure appropriate flexibility of the thin sheet.
この木材の薄片シートを前記磁性シートの片面全体にビ
ニルウレタン樹脂を接着剤として塗布し、磁性シートと
木材の薄片シートを熱間圧縮プレスにより接着した。こ
の場合の接着剤は、ビニルウレタン樹脂を用いたが、そ
のほか、ポリエステル、シリコン系樹脂、エポキシ系樹
脂、スチレンブタジェンラバー(SBR)等を用いるこ
とができる。Vinyl urethane resin was applied as an adhesive to the entire one side of the magnetic sheet, and the magnetic sheet and the wood thin sheet were bonded together using a hot compression press. Although vinyl urethane resin was used as the adhesive in this case, other materials such as polyester, silicone resin, epoxy resin, styrene butadiene rubber (SBR), etc. can also be used.
そして接着剤は、耐候性、耐水性、耐紫外線特性の良好
なもので、柔軟性装飾板の柔軟性を損なわないものを用
いるのが望ましい。It is desirable to use an adhesive that has good weather resistance, water resistance, and ultraviolet ray resistance, and does not impair the flexibility of the flexible decorative board.
その後、前記木材の薄片シートの表面の艶出しと表面保
護を目的として、薄片シートの表面に透明ポリウレタン
樹脂をコーティングして皮膜を形成し、柔軟性装飾板を
得た。Thereafter, for the purpose of polishing and protecting the surface of the wood thin sheet, a transparent polyurethane resin was coated on the surface of the thin wood sheet to form a film, thereby obtaining a flexible decorative board.
この柔軟性装飾板を車両のボディの接着箇所のサイズに
切断した後、この柔軟性装飾板を多極着磁して磁力を付
与した。この磁力をもった柔軟性装飾板の磁性シート面
のEn束密度は380±10ガウスで満足すべき吸着力
が得られた。After cutting this flexible decorative plate to the size of the bonding area on the vehicle body, this flexible decorative plate was multipolar magnetized to impart magnetic force. The En flux density of the magnetic sheet surface of this flexible decorative board having magnetic force was 380±10 Gauss, and a satisfactory adsorption force was obtained.
この実施例の柔軟性装飾板によると、第2図に示す車両
の社名表示4の部分に吸着させ社名を覆い隠すことで、
ボディを傷めないで社用車から私用車に変更使用するこ
とができる。また逆に、私用車から社用車への変更使用
も可能である。さらに、この実施例では、第1、第2お
よび第3の柔軟性装飾板5.7.9を連結してストライ
ブ状に装着することにより、美感を高めたり、イメージ
チェンジしたりすることができる。また、柔軟性装飾板
は柔軟なものであるから、ボディに石が当たって凹む等
の損傷の防止の保護機能をも有する。According to the flexible decorative plate of this embodiment, by adhering it to the company name display 4 of the vehicle shown in FIG. 2 and covering the company name,
You can change from a company car to a private car without damaging the body. Conversely, it is also possible to change from a private car to a company car. Furthermore, in this embodiment, by connecting the first, second and third flexible decorative plates 5.7.9 and attaching them in a stripe shape, it is possible to enhance the beauty or change the image. can. Furthermore, since the flexible decorative board is flexible, it also has a protective function to prevent damage such as denting caused by stones hitting the body.
この柔軟性装飾板を車両に装着し、走行テストを行った
結果を以下に示す。The results of a driving test with this flexible decorative plate attached to a vehicle are shown below.
テスト条件:
■市街地走行 :26日
走行距離 ;101040
k晴れ13日、曇り8日、雨5日)
■高速道路走行 = 4日
走行距離 : 1200km
(晴れ2日、曇り1日、雨1日)
■の市街地走行後、■の高速道路走行を行い、合計30
日間の走行テストを行った。柔軟性装飾板の脱着は、毎
日必ず1回行った。Test conditions: ■City driving: 26 days mileage; 101,040k (13 sunny days, 8 cloudy days, 5 rainy days) ■Highway driving = 4 days Mileage: 1200km (2 sunny days, 1 cloudy day, 1 rainy day) After ■ city driving, ■ expressway driving, total 30
I did a day-long driving test. The flexible decorative board was attached and detached once every day.
テストの結果、脱落、位置ずれ等のトラブルは無く、脱
着時の柔軟性装飾板の欠けや折れ等の損傷、変色も無か
った。As a result of the test, there were no problems such as falling off or misalignment, and there was no damage such as chipping, bending, or discoloration of the flexible decorative board during attachment and detachment.
また、前述した第1、第2および第3の可撓性装飾板5
.7.9は、フレキシビリティ(可撓性)があるので、
ボディ外板に隙間なく馴染み、外板に傷を付けず、脱着
、保管の際、欠けたり折れたりしない。また前述の61
)性シートは所定の硬質磁石粉末と適量の樹脂と可塑剤
を添加しているので、適度の柔軟性および靭性があり、
また太陽光線や雨風、酸性の排ガス、ワックス等、油性
物質等にさらされても、その影響で変色したり、強度、
靭性の低下はほとんどない。In addition, the first, second and third flexible decorative plates 5 described above
.. 7.9 has flexibility, so
It fits perfectly into the body's outer panels, does not damage the outer panels, and does not chip or break when attached, removed, or stored. Also, the aforementioned 61
) sheet contains a specified hard magnetic powder and appropriate amounts of resin and plasticizer, so it has appropriate flexibility and toughness.
In addition, even if exposed to sunlight, rain and wind, acidic exhaust gas, wax, or other oily substances, the color may change or the strength may change.
There is almost no decrease in toughness.
なお、磁性シートの作製時、磁石材料微粉末と樹脂等の
混練物をロール成形するとき、シート板厚方向に磁力線
を当て磁場成形により異方性を高めたりすることもでき
る。装飾用の薄片シートは、本実施例では、楠の木目模
様のものを用いたが、楠、他の木材に限られず、そのほ
か、ポリエステルフィルム、塩化ビニル、紙等の材料を
用いることができ、必要に応じて、模様、文字、絵画を
描いた薄片シートを用いることができる。本発明の装飾
手段は、薄片シートに描かれている場合に限らず、磁性
シートに装飾を直接描いても良い。In addition, when producing a magnetic sheet, when roll-molding a kneaded material of a fine powder of magnet material and a resin, etc., it is also possible to increase the anisotropy by applying magnetic force lines in the thickness direction of the sheet and performing magnetic field forming. In this example, the decorative thin sheet was made of camphor tree with a wood grain pattern, but it is not limited to camphor tree or other woods, and other materials such as polyester film, vinyl chloride, and paper can also be used. If necessary, thin sheets with patterns, letters, or pictures may be used. The decoration means of the present invention is not limited to the case where the decoration is drawn on the thin sheet, but may be applied directly to the magnetic sheet.
なお、本発明に適用することのできる硬質磁石材料粉末
は、ストロンチウムフェライト、希土類磁石、バリウム
フエラト等を用いることができる。Note that, as the hard magnetic material powder that can be applied to the present invention, strontium ferrite, rare earth magnet, barium ferrite, etc. can be used.
樹脂としては、塩化ビニル樹脂のほか、ポリウレタン、
ポリエチレン、ポリエステル、ポリブタジェン、熱可塑
性エラストマー類等を用いることができる。また可塑剤
としてはフタル酸ジオクチルのばかフタル酸ジアリル、
クエン酸エステル、アジピン酸ポリエステル、リン酸エ
ステル等を用いることができる。In addition to vinyl chloride resin, polyurethane,
Polyethylene, polyester, polybutadiene, thermoplastic elastomers, etc. can be used. In addition, as a plasticizer, dioctyl phthalate, diallyl phthalate,
Citric acid ester, adipic acid polyester, phosphoric acid ester, etc. can be used.
(発明の効果)
以上説明したように、本発明の柔軟性装飾板によれば、
物品の表面に軟質の可撓性装飾板を着脱自在に取付可能
なので、脱着作業が容易で装飾を短時間で変更すること
ができ、また傷や汚れ等の付き易い部分や美感を損なう
部分を簡単な作業で手軽に隠すことができ、さらに物品
の“表面を損傷から確実に保護することができるという
効果がある。(Effects of the Invention) As explained above, according to the flexible decorative board of the present invention,
Since soft flexible decorative plates can be attached and detached to the surface of items, it is easy to attach and detach, allowing you to change the decoration in a short time. It can be easily hidden with a simple operation, and it also has the effect of reliably protecting the surface of the item from damage.
第1図は本発明の実施例を表わす斜視図、第2図は本発
明の実施例を適用した社用車を表わす斜視図である。
・・・車体、
・・・社名表示、
・・・第1の柔軟性装飾板、
・・・第2の柔軟性装飾板、
・・・第3の柔軟性装飾板。FIG. 1 is a perspective view showing an embodiment of the present invention, and FIG. 2 is a perspective view showing a company car to which the embodiment of the present invention is applied. ...Vehicle body, ...Company name display, ...First flexible decorative board, ...Second flexible decorative board, ...Third flexible decorative board.
Claims (3)
る磁性シートと、この磁性シートの表面に付される装飾
部とからなることを特徴とする柔軟性装飾板。(1) A flexible decorative board comprising a magnetic sheet whose main components are a hard magnetic material powder, a resin, and a plasticizer, and a decorative part attached to the surface of the magnetic sheet.
ート状に成形する工程と、このシートに装飾手段を施す
工程と、前記シートを多極磁化する工程とからなること
を特徴とする柔軟性装飾板の製造法。(2) It is characterized by comprising the steps of adding hard magnetic material powder, resin, and plasticizer and forming it into a sheet shape, applying decorative means to this sheet, and making the sheet multipolar magnetized. A manufacturing method for flexible decorative boards.
を特徴とする請求項2に記載の柔軟性装飾板の製造法。(3) The method for manufacturing a flexible decorative board according to claim 2, wherein the step of forming the sheet into a sheet is performed in a magnetic field.