JP7428918B2 - サワー環境での使用に適した継目無鋼管 - Google Patents
サワー環境での使用に適した継目無鋼管 Download PDFInfo
- Publication number
- JP7428918B2 JP7428918B2 JP2021509086A JP2021509086A JP7428918B2 JP 7428918 B2 JP7428918 B2 JP 7428918B2 JP 2021509086 A JP2021509086 A JP 2021509086A JP 2021509086 A JP2021509086 A JP 2021509086A JP 7428918 B2 JP7428918 B2 JP 7428918B2
- Authority
- JP
- Japan
- Prior art keywords
- seamless steel
- steel pipe
- test
- content
- quenching
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本実施形態による継目無鋼管は、母材と、母材の表面上に形成されている脱炭層とを備える。
本実施形態による継目無鋼管を構成する母材の化学組成は、次の元素を含有する。
炭素(C)は鋼材の焼入れ性を高め、鋼材の降伏強度を高める。Cはさらに、製造工程中の焼戻し時において、炭化物の球状化を促進し、鋼材の耐SSC性を高める。炭化物が分散されればさらに、鋼材の降伏強度が高まる。C含有量が低すぎれば、これらの効果が得られない。一方、C含有量が高すぎれば、鋼材の靭性が低下し、焼割れが発生しやすくなる。したがって、C含有量は0.20~0.50%である。C含有量の好ましい下限は0.22%であり、より好ましくは0.24%であり、さらに好ましくは0.25%である。C含有量の好ましい上限は0.48%であり、より好ましくは0.45%であり、さらに好ましくは0.40%である。
シリコン(Si)は鋼を脱酸する。Si含有量が低すぎれば、この効果が得られない。一方、Si含有量が高すぎれば、鋼材の耐SSC性が低下する。Si含有量が高すぎればさらに、脱炭層が深く形成され、鋼材の超音波探傷精度が低下する場合がある。したがって、Si含有量は0.05~0.50%である。Si含有量の好ましい下限は0.08%であり、より好ましくは0.10%である。Si含有量の好ましい上限は0.48%であり、より好ましくは0.46%であり、さらに好ましくは0.44%である。
マンガン(Mn)は鋼を脱酸する。Mnはさらに、鋼材の焼入れ性を高め、鋼材の降伏強度を高める。Mn含有量が低すぎれば、これらの効果が得られない。一方、Mn含有量が高すぎれば、P及びS等の不純物とともに、Mnが粒界に偏析する。この場合、鋼材の耐SSC性が低下する。したがって、Mn含有量は0.01~1.00%である。Mn含有量の好ましい下限は0.02%であり、より好ましくは0.03%であり、さらに好ましくは0.10%である。Mn含有量の好ましい上限は0.98%であり、より好ましくは0.95%である。
燐(P)は不純物である。すなわち、P含有量は0%超である。Pは粒界に偏析して、鋼材の耐SSC性を低下させる。したがって、P含有量は0.0300%以下である。P含有量の好ましい上限は0.0250%であり、より好ましくは0.0200%である。P含有量はなるべく低い方が好ましい。ただし、P含有量の極端な低減は、製造コストを大幅に高める。したがって、工業生産を考慮した場合、P含有量の好ましい下限は0.0001%であり、より好ましくは0.0003%である。
硫黄(S)は不純物である。すなわち、S含有量は0%超である。Sは粒界に偏析して、鋼材の耐SSC性を低下させる。したがって、S含有量は0.0100%以下である。S含有量の好ましい上限は0.0095%であり、より好ましくは0.0090%であり、さらに好ましくは0.0085%である。S含有量はなるべく低い方が好ましい。ただし、S含有量の極端な低減は、製造コストを大幅に高める。したがって、工業生産を考慮した場合、S含有量の好ましい下限は0.0001%であり、より好ましくは0.0003%である。
アルミニウム(Al)は鋼を脱酸する。Al含有量が低すぎれば、この効果が得られない。一方、Al含有量が高すぎれば、粗大な酸化物系介在物が生成して、鋼材の耐SSC性が低下する。したがって、Al含有量は0.005~0.100%である。Al含有量の好ましい下限は0.015%であり、より好ましくは0.020%である。Al含有量の好ましい上限は0.095%であり、より好ましくは0.090%であり、さらに好ましくは0.085%である。本明細書にいう「Al」含有量は「酸可溶Al」、つまり、「sol.Al」の含有量を意味する。
クロム(Cr)は焼戻し軟化抵抗を高めて高温焼戻しを可能とし、鋼材の耐SSC性を高める。Cr含有量が低すぎれば、この効果が得られない。Cr含有量が低すぎればさらに、脱炭層が深く形成され、鋼材の超音波探傷精度が低下する場合がある。一方、Cr含有量が高すぎれば、鋼材中に粗大な炭化物が生成し、鋼材の耐SSC性が低下する。したがって、Cr含有量は0.30~1.20%である。Cr含有量の好ましい下限は0.32%であり、より好ましくは0.35%であり、さらに好ましくは0.40%である。Cr含有量の好ましい上限は1.15%であり、より好ましくは1.10%であり、さらに好ましくは1.05%である。
モリブデン(Mo)は焼戻し軟化抵抗を高めて高温焼戻しを可能とし、鋼材の耐SSC性を高める。Mo含有量が低すぎれば、この効果が得られない。一方、Mo含有量が高すぎれば、鋼材中に粗大な炭化物が生成し、鋼材の耐SSC性が低下する。したがって、Mo含有量は0.30~1.50%である。Mo含有量の好ましい下限は0.35%であり、より好ましくは0.40%である。Mo含有量の好ましい上限は1.45%であり、より好ましくは1.40%である。
チタン(Ti)は窒化物を形成し、ピンニング効果により、結晶粒を微細化する。その結果、鋼材の降伏強度が高まる。Ti含有量が低すぎれば、この効果が得られない。一方、Ti含有量が高すぎれば、Ti窒化物が多量に形成し、鋼材の耐SSC性が低下する。したがって、Ti含有量は0.002~0.050%である。Ti含有量の好ましい下限は0.003%であり、より好ましくは0.004%である。Ti含有量の好ましい上限は0.040%であり、より好ましくは0.030%であり、さらに好ましくは0.020%である。
バナジウム(V)は焼戻し軟化抵抗を高めて高温焼戻しを可能とし、鋼材の耐SSC性を高める。Vはさらに、C及び/又はNと結合して、炭化物、窒化物又は炭窒化物(以下、「炭窒化物等」という)を形成する。炭窒化物等は、ピンニング効果により鋼材のサブ組織を微細化し、鋼材の耐SSC性を高める。Vはさらに、Cと結合して微細な炭化物を形成する。その結果、鋼材の降伏強度が高まる。V含有量が低すぎれば、これらの効果が得られない。一方、V含有量が高すぎれば、鋼材の靭性が低下する。したがって、V含有量は0.01~0.30%である。V含有量の好ましい下限は0.03%であり、より好ましくは0.05%であり、さらに好ましくは0.07%である。V含有量の好ましい上限は0.25%であり、より好ましくは0.20%であり、さらに好ましくは0.15%である。
ニオブ(Nb)はC及び/又はNと結合して、炭窒化物等を形成する。炭窒化物等は、ピンニング効果により鋼材のサブ組織を微細化し、鋼材の耐SSC性を高める。Nbはさらに、Cと結合して微細な炭化物を形成する。その結果、鋼材の降伏強度が高まる。Nb含有量が低すぎれば、これらの効果が得られない。一方、Nb含有量が高すぎれば、炭窒化物等が過剰に生成して、鋼材の耐SSC性が低下する。したがって、Nb含有量は0.002~0.100%である。Nb含有量の好ましい下限は0.003%であり、より好ましくは0.005%であり、さらに好ましくは0.010%である。Nb含有量の好ましい上限は0.095%であり、より好ましくは0.090%であり、さらに好ましくは0.080%である。
ホウ素(B)は鋼材中に固溶して鋼材の焼入れ性を高め、鋼材の降伏強度を高める。B含有量が低すぎれば、この効果が得られない。一方、B含有量が高すぎれば、鋼材中に粗大な窒化物が生成して、鋼材の耐SSC性が低下する。したがって、B含有量は0.0001~0.0050%である。B含有量の好ましい下限は0.0003%であり、より好ましくは0.0005%であり、さらに好ましくは0.0012%である。B含有量の好ましい上限は0.0045%であり、より好ましくは0.0040%であり、さらに好ましくは0.0035%である。
窒素(N)は不可避に含有される。すなわち、N含有量は0%超である。NはTiと結合して窒化物を形成し、ピンニング効果により結晶粒を微細化する。その結果、鋼材の降伏強度が高まる。一方、N含有量が高すぎれば、粗大な窒化物が形成され、鋼材の耐SSC性が低下する。したがって、N含有量は0.0100%以下である。N含有量の好ましい上限は0.0090%であり、より好ましくは0.0080%である。上記効果を有効に得るためのN含有量の好ましい下限は0.0005%であり、より好ましくは0.0010%であり、さらに好ましくは0.0015%であり、さらに好ましくは0.0020%である。
酸素(O)は不純物である。すなわち、O含有量は0%超である。Oは粗大な酸化物を形成し、鋼材の耐SSC性を低下させる。したがって、O含有量は0.0050%以下である。O含有量の好ましい上限は0.0048%であり、より好ましくは0.0045%である。O含有量はなるべく低い方が好ましい。ただし、O含有量の極端な低減は、製造コストを大幅に高める。したがって、工業生産を考慮した場合、O含有量の好ましい下限は0.0001%であり、より好ましくは0.0003%である。
上述の鋼材の化学組成はさらに、Feの一部に代えて、Ca、Mg、Zr、及び、希土類元素(REM)からなる群から選択される1種以上を含有してもよい。これらの元素はいずれも任意元素であり、鋼材中のSを硫化物として無害化して、鋼材の耐SSC性を高める。
カルシウム(Ca)は任意元素であり、含有されなくてもよい。すなわち、Ca含有量は0%であってもよい。含有される場合、Caは鋼材中のSを硫化物として無害化して、鋼材の耐SSC性を高める。Caが少しでも含有されれば、この効果がある程度得られる。しかしながら、Ca含有量が高すぎれば、鋼材中の酸化物が粗大化して、鋼材の耐SSC性が低下する。したがって、Ca含有量は0~0.0100%である。Ca含有量の好ましい下限は0%超であり、より好ましくは0.0001%であり、さらに好ましくは0.0003%であり、さらに好ましくは0.0006%である。Ca含有量の好ましい上限は0.0060%であり、より好ましくは0.0050%であり、さらに好ましくは0.0030%である。
マグネシウム(Mg)は任意元素であり、含有されなくてもよい。すなわち、Mg含有量は0%であってもよい。含有される場合、Mgは鋼材中のSを硫化物として無害化して、鋼材の耐SSC性を高める。Mgが少しでも含有されれば、この効果がある程度得られる。しかしながら、Mg含有量が高すぎれば、鋼材中の酸化物が粗大化して、鋼材の耐SSC性が低下する。したがって、Mg含有量は0~0.0100%である。Mg含有量の好ましい下限は0%超であり、より好ましくは0.0001%であり、さらに好ましくは0.0003%であり、さらに好ましくは0.0006%である。Mg含有量の好ましい上限は0.0060%であり、より好ましくは0.0050%であり、さらに好ましくは0.0030%である。
ジルコニウム(Zr)は任意元素であり、含有されなくてもよい。すなわち、Zr含有量は0%であってもよい。含有される場合、Zrは鋼材中のSを硫化物として無害化して、鋼材の耐SSC性を高める。Zrが少しでも含有されれば、この効果がある程度得られる。しかしながら、Zr含有量が高すぎれば、鋼材中の酸化物が粗大化して、鋼材の耐SSC性が低下する。したがって、Zr含有量は0~0.0100%である。Zr含有量の好ましい下限は0%超であり、より好ましくは0.0001%であり、さらに好ましくは0.0003%であり、さらに好ましくは0.0006%である。Zr含有量の好ましい上限は0.0060%であり、より好ましくは0.0050%であり、さらに好ましくは0.0030%である。
希土類元素(REM)は任意元素であり、含有されなくてもよい。すなわち、REM含有量は0%であってもよい。含有される場合、REMは鋼材中のSを硫化物として無害化して、鋼材の耐SSC性を高める。REMはさらに、鋼材中のPと結合して、結晶粒界におけるPの偏析を抑制する。そのため、Pの偏析に起因した、鋼材の低温靭性及び耐SSC性の低下が抑制される。REMが少しでも含有されれば、これらの効果がある程度得られる。しかしながら、REM含有量が高すぎれば、酸化物が粗大化して、鋼材の低温靭性及び耐SSC性が低下する。したがって、REM含有量は0~0.0100%である。REM含有量の好ましい下限は0%超であり、より好ましくは0.0001%であり、さらに好ましくは0.0003%であり、さらに好ましくは0.0006%である。REM含有量の好ましい上限は0.0060%であり、より好ましくは0.0050%であり、さらに好ましくは0.0030%である。
コバルト(Co)は任意元素であり、含有されなくてもよい。すなわち、Co含有量は0%であってもよい。含有される場合、Coはサワー環境において保護性の腐食被膜を形成し、水素侵入を抑制する。その結果、鋼材の耐SSC性が高まる。Coが少しでも含有されれば、この効果がある程度得られる。しかしながら、Co含有量が高すぎれば、鋼材の焼入れ性が低下して、鋼材の降伏強度が低下する。したがって、Co含有量は0~0.50%である。Co含有量の好ましい下限は0%超であり、より好ましくは0.02%であり、さらに好ましくは0.03%であり、さらに好ましくは0.05%である。Co含有量の好ましい上限は0.45%であり、より好ましくは0.40%である。
タングステン(W)は任意元素であり、含有されなくてもよい。すなわち、W含有量は0%であってもよい。含有される場合、Wはサワー環境において保護性の腐食被膜を形成し、水素侵入を抑制する。その結果、鋼材の耐SSC性が高まる。Wが少しでも含有されれば、この効果がある程度得られる。しかしながら、W含有量が高すぎれば、鋼材中に粗大な炭化物が生成して、鋼材の耐SSC性が低下する。したがって、W含有量は0~0.50%である。W含有量の好ましい下限は0%超であり、より好ましくは0.02%であり、さらに好ましくは0.03%であり、さらに好ましくは0.05%である。W含有量の好ましい上限は0.45%であり、より好ましくは0.40%である。
銅(Cu)は任意元素であり、含有されなくてもよい。すなわち、Cu含有量は0%であってもよい。含有される場合、Cuは鋼材の焼入れ性を高め、鋼材の降伏強度を高める。Cuが少しでも含有されれば、この効果がある程度得られる。一方、Cu含有量が高すぎれば、鋼材の焼入れ性が高くなりすぎ、鋼材の耐SSC性が低下する。したがって、Cu含有量は0~0.50%である。Cu含有量の好ましい下限は0%超であり、より好ましくは0.02%であり、さらに好ましくは0.03%であり、さらに好ましくは0.05%である。Cu含有量の好ましい上限は0.40%であり、より好ましくは0.30%であり、さらに好ましくは0.20%であり、さらに好ましくは0.15%である。
ニッケル(Ni)は任意元素であり、含有されなくてもよい。すなわち、Ni含有量は0%であってもよい。含有される場合、Niは鋼材の焼入れ性を高め、鋼材の降伏強度を高める。Niが少しでも含有されれば、この効果がある程度得られる。一方、Ni含有量が高すぎれば、局部的な腐食を促進させ、鋼材の耐SSC性が低下する。したがって、Ni含有量は0~0.50%である。Ni含有量の好ましい下限は0%超であり、より好ましくは0.02%であり、さらに好ましくは0.05%であり、さらに好ましくは0.10%である。Ni含有量の好ましい上限は0.40%であり、より好ましくは0.30%であり、さらに好ましくは0.20%であり、さらに好ましくは0.15%である。
本実施形態による継目無鋼管を構成する母材の降伏強度は655MPa以上であり、母材の降伏比は85.0%以上である。要するに、本実施形態による継目無鋼管は、95ksi以上である。本実施形態による継目無鋼管を構成する母材が、上述の化学組成を有し、降伏強度が655MPa以上であり、かつ、降伏比が85.0%以上である結果、本実施形態による継目無鋼管は、655MPa以上の降伏強度と、優れた耐SSC性とを有する。
本実施形態による継目無鋼管を構成する母材のミクロ組織は、焼戻しマルテンサイト及び焼戻しベイナイトの体積率の合計が90%以上である。ミクロ組織の残部はたとえば、フェライト、又は、パーライトである。本実施形態においては、上述の化学組成を満たす母材の降伏強度が655MPa以上(95ksi以上)であり、かつ、降伏比が85.0%以上であれば、母材のミクロ組織は、焼戻しマルテンサイト及び焼戻しベイナイトの体積率の合計が90%以上であるものとする。好ましくは、母材のミクロ組織は焼戻しマルテンサイト及び/又は焼戻しベイナイトのみからなる。
本実施形態による継目無鋼管はさらに、上述の母材の表面上に形成されている脱炭層を備える。本実施形態による継目無鋼管を構成する脱炭層は、深さが150μm以下である。上述のとおり、本実施形態による継目無鋼管を構成する脱炭層は、継目無鋼管の表面部分が酸化されることによって形成される、C含有量が低減された層である。
本実施形態による継目無鋼管では、降伏強度ごとに、優れた耐SSC性を定義する。なお、本実施形態による継目無鋼管の耐SSC性は、いずれの降伏強度においても、NACE TM0177-2005 Method Aに準拠した方法によって評価できる。
降伏強度が655~758MPa未満(95~110ksi未満、95ksi級)である場合、継目無鋼管の耐SSC性は次の方法で評価できる。5.0質量%塩化ナトリウムと0.5質量%酢酸とを含む混合水溶液(NACE solution A)を、試験溶液とする。本実施形態による継目無鋼管の肉厚中央部から、丸棒試験片を採取する。丸棒試験片の大きさは、たとえば、径6.35mm、平行部の長さ25.4mmである。なお、丸棒試験片の軸方向は、継目無鋼管の管軸方向と平行である。
降伏強度が758~862MPa未満(110~125ksi未満、110ksi級)である場合、継目無鋼管の耐SSC性は次の方法で評価できる。5.0質量%塩化ナトリウムと0.5質量%酢酸とを含む混合水溶液(NACE solution A)を、試験溶液とする。本実施形態による継目無鋼管の肉厚中央部から、丸棒試験片を採取する。丸棒試験片の大きさは、たとえば、径6.35mm、平行部の長さ25.4mmである。なお、丸棒試験片の軸方向は、継目無鋼管の管軸方向と平行である。
降伏強度が862MPa以上(125ksi以上)である場合、継目無鋼管の耐SSC性は次の方法で評価できる。5.0質量%塩化ナトリウムと0.41質量%酢酸ナトリウムと2.5質量%酢酸とを含む混合水溶液(NACE solution B)を、試験溶液とする。本実施形態による継目無鋼管の肉厚中央部から、丸棒試験片を採取する。丸棒試験片の大きさは、たとえば、径6.35mm、平行部の長さ25.4mmである。なお、丸棒試験片の軸方向は、継目無鋼管の管軸方向と平行である。
以下、本実施形態による継目無鋼管の製造方法を説明する。本実施形態による継目無鋼管の製造方法の一例は、素管を準備する工程(準備工程)と、素管に対して焼入れ及び焼戻しを実施して、継目無鋼管とする工程(焼入れ工程及び焼戻し工程)とを備える。準備工程は、素材を準備する工程(素材準備工程)と、素材に熱間加工を実施して、素管を製造する工程(熱間加工工程)とを含んでもよい。以下、各工程について詳述する。
準備工程では、上述の化学組成を有する素管を準備する。素管が上述の化学組成を有していれば、素管を準備する方法は特に限定されない。準備工程は、素材を準備する工程(素材準備工程)と、素材を熱間加工して素管を製造する工程(熱間加工工程)とを含んでもよい。以下、素材準備工程と、熱間加工工程を含む場合について、詳述する。
素材準備工程では、上述の化学組成を有する溶鋼を用いて、素材を準備する。具体的には、上述の化学組成を有する溶鋼を用いて、連続鋳造法により鋳片(スラブ、ブルーム、又は、ビレット)を製造する。上述の化学組成を有する溶鋼を用いて、造塊法によりインゴットを製造してもよい。必要に応じて、スラブ、ブルーム、又は、インゴットに分塊圧延を実施して、鋼片(ビレット)を製造してもよい。以上の工程により素材(スラブ、ブルーム、ビレット、又は、インゴット)を準備する。
熱間加工工程では、準備された素材に熱間加工を実施して、素管を製造する。具体的には、まず、ビレットを加熱炉で加熱する。加熱温度は特に限定されないが、たとえば、1100~1300℃である。加熱炉から抽出されたビレットに対して熱間加工を実施して、素管(継目無鋼管)を製造する。なお、熱間加工工程における加熱炉は、特に限定されない。熱間加工工程における加熱炉では、加熱温度が高いことから、脱炭層の形成よりもスケールの形成が起こりやすいためである。
焼入れ工程では、準備された素管に対して、焼入れを実施する。本明細書において、「焼入れ」とは、A3点以上の素管を急冷することを意味する。本明細書において、熱間加工後に直接、又は、補熱を実施したA3点以上の素管を急冷することを「直接焼入れ」ともいう。本明細書において、熱処理炉で再加熱したA3点以上の素管を急冷することを「オフライン焼入れ」ともいう。以下、オフライン焼入れと後述するオフライン焼戻しとを総称して、「オフライン熱処理」ともいう。好ましい焼入れ温度は800~1000℃である。焼入れ温度とは、熱間加工後に直接焼入れを実施する場合、最終の熱間加工を実施する装置の出側に設置した温度計で測定された素管の表面温度に相当する。焼入れ温度とはさらに、熱間加工後に補熱炉又は熱処理炉を用いて焼入れを実施する場合、補熱炉又は熱処理炉(以下、焼入れ前の加熱に用いる補熱炉又は熱処理炉を、単に「焼入れ炉」ともいう)の温度に相当する。
焼戻し工程では、上記焼入れ工程後の素管に対して、焼戻しを実施する。本明細書において、「焼戻し」とは、焼入れ後の素管をAc1点以下で再加熱して、保持することを意味する。なお、本明細書において、オフライン焼入れに続いて実施される焼戻しを「オフライン焼戻し」ともいう。焼戻し温度は、鋼材の化学組成、及び、得ようとする降伏強度に応じて適宜調整する。つまり、本実施形態の化学組成を有する素管に対して、焼戻し温度を調整して、継目無鋼管の降伏強度を調整する。つまり、本実施形態の化学組成を有する素管に対して、焼戻し温度を調整して、継目無鋼管の降伏強度を655MPa以上(95ksi以上)に調整する。
上述の焼戻し処理後の各試験番号の継目無鋼管に対して、以下に説明する脱炭層深さ測定試験、引張試験、耐SSC性評価試験、及び、超音波探傷試験を実施した。
各試験番号の継目無鋼管を用いて、上述の方法で脱炭層の深さを測定した。具体的には、各試験番号の継目無鋼管の内表面を含み、管軸方向10mm、管径方向10mmの観察面を有する試験片を採取した。観察面を鏡面に研磨した後、2%ナイタール腐食液に10秒程度浸漬して、エッチングを行った。エッチングした観察面を、光学顕微鏡を用いて、明視野像にて10視野観察した。各視野の面積は、0.1mm2(倍率200倍)であった。
各試験番号の継目無鋼管を用いて、上述の方法で引張試験を実施して、降伏強度と引張強度と降伏比とを測定した。具体的に、引張試験はASTM E8/E8M(2013)に準拠して行った。各試験番号の継目無鋼管の肉厚中央部から、平行部直径4mm、平行部長さ35mmの丸棒試験片を作製した。丸棒試験片の軸方向は、継目無鋼管の管軸方向と平行であった。各試験番号の丸棒試験片を用いて、常温(25℃)、大気中にて引張試験を実施して、各試験番号の継目無鋼管の降伏強度(MPa)を得た。
各試験番号の継目無鋼管を用いて、NACE TM0177-2005 Method Aに準拠した方法によって、耐SSC性を評価した。具体的に、降伏強度が655~758MPa未満(95ksi級)である試験番号1-1~1-30の継目無鋼管と、降伏強度が758~862MPa未満(110ksi級)である試験番号2-1~2-37の継目無鋼管と、降伏強度が862~965MPa(125ksi級)である試験番号3-1~3-37の継目無鋼管とについて、耐SSC性の評価試験をそれぞれ説明する。
試験番号1-1~1-30の継目無鋼管の肉厚中央部から、径6.35mm、平行部の長さ25.4mmの丸棒試験片を採取した。丸棒試験片の軸方向は、継目無鋼管の管軸方向に平行であった。試験番号1-1~1-30の試験片の軸方向に引張応力を負荷した。このとき、NACE TM0177-2005 Method Aに準拠して、試験片に与えられる応力が、試験番号1-1~1-30の継目無鋼管の実降伏応力の90%になるように、調整した。
試験番号2-1~2-37の継目無鋼管の肉厚中央部から、径6.35mm、平行部の長さ25.4mmの丸棒試験片を採取した。丸棒試験片の軸方向は、継目無鋼管の管軸方向に平行であった。試験番号2-1~2-37の試験片の軸方向に引張応力を負荷した。このとき、NACE TM0177-2005 Method Aに準拠して、試験片に与えられる応力が、試験番号2-1~2-37の継目無鋼管の実降伏応力の90%になるように、調整した。
試験番号3-1~3-37の継目無鋼管の肉厚中央部から、径6.35mm、平行部の長さ25.4mmの丸棒試験片を採取した。丸棒試験片の軸方向は、継目無鋼管の管軸方向に平行であった。試験番号3-1~3-37の試験片の軸方向に引張応力を負荷した。このとき、NACE TM0177-2005 Method Aに準拠して、試験片に与えられる応力が、試験番号3-1~3-37の継目無鋼管の実降伏応力の90%になるように、調整した。
各試験番号の継目無鋼管を用いて、次の方法により超音波探傷試験を実施した。具体的には、局部水浸型超音波探傷装置を用いて、L方向斜角探傷により超音波探傷試験を実施して、SN比を求めた。超音波探傷装置の感度設定は、各試験番号の継目無鋼管の内表面から管径方向に肉厚の3%深さ位置に設けた人工欠陥を用いて行った。人工欠陥は放電加工により形成されたノッチであり、深さ0.275mm、幅1mm、長さ50.8mmとした。人工欠陥の長さ方向は、管周方向に平行とした。
表1、表2、及び、表3を参照して、試験番号1-1~1-3、1-5~1-8、及び、1-10~1-28の継目無鋼管は、母材の化学組成が適切であり、母材の降伏強度が665~758MPa未満(95ksi級)であり、母材の降伏比が85.0%以上であり、脱炭層深さが150μm以下であった。その結果、耐SSC性試験において、優れた耐SSC性を示した。その結果さらに、超音波探傷試験において、優れた超音波探傷精度を示した。
Claims (5)
- 継目無鋼管であって、
母材と、前記母材の表面上に形成されている脱炭層とを備え、
前記母材の化学組成は、質量%で、
C:0.20~0.50%、
Si:0.05~0.50%、
Mn:0.01~1.00%、
P:0.0300%以下、
S:0.0100%以下、
Al:0.005~0.100%、
Cr:0.30~1.20%、
Mo:0.30~1.50%、
Ti:0.002~0.050%、
V:0.03~0.30%、
Nb:0.002~0.100%、
B:0.0001~0.0050%、
N:0.0100%以下、
O:0.0050%以下、
Ca:0~0.0100%、
Mg:0~0.0100%、
Zr:0~0.0100%、
希土類元素:0~0.0100%、
Co:0~0.50%、
W:0~0.50%、
Cu:0~0.50%、
Ni:0~0.50%、及び、
残部がFe及び不純物からなり、
前記母材の降伏強度は、655MPa以上であり、
前記母材の降伏比は、85.0%以上であり、
前記脱炭層は、深さが150μm以下であり、
前記継目無鋼管は油井用鋼管である、
継目無鋼管。 - 請求項1に記載の継目無鋼管であって、
前記母材の化学組成は、
Ca:0.0001~0.0100%、
Mg:0.0001~0.0100%、
Zr:0.0001~0.0100%、及び、
希土類元素:0.0001~0.0100%からなる群から選択される1種以上を含有
する、
継目無鋼管。 - 請求項1又は請求項2に記載の継目無鋼管であって、
前記母材の化学組成は、
Co:0.02~0.50%、及び、
W:0.02~0.50%からなる群から選択される1種以上を含有する、
継目無鋼管。 - 請求項1~請求項3のいずれか1項に記載の継目無鋼管であって、
前記母材の化学組成は、
Cu:0.02~0.50%、及び、
Ni:0.02~0.50%からなる群から選択される1種以上を含有する、
継目無鋼管。 - 請求項1~請求項4のいずれか1項に記載の継目無鋼管であって、
前記脱炭層は、深さが130μm以下である、
継目無鋼管。