JP5745831B2 - 固形天然ゴムおよびその製造方法 - Google Patents
固形天然ゴムおよびその製造方法 Download PDFInfo
- Publication number
- JP5745831B2 JP5745831B2 JP2010271681A JP2010271681A JP5745831B2 JP 5745831 B2 JP5745831 B2 JP 5745831B2 JP 2010271681 A JP2010271681 A JP 2010271681A JP 2010271681 A JP2010271681 A JP 2010271681A JP 5745831 B2 JP5745831 B2 JP 5745831B2
- Authority
- JP
- Japan
- Prior art keywords
- natural rubber
- solid natural
- rubber
- viscosity
- solid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明の固形天然ゴムは、分子鎖の切断により低分子量化されており、該分子鎖中にアルデヒド基を含まない。低分子量化については、RSS等の従来の未素練りの固形天然ゴムと比較して、分子量が小さければよい。低分子量化により、固形天然ゴムの粘度は低下する。例えば、ゲル浸透クロマトグラフィー(GPC)による重量平均分子量が、1×106以下であるとよい。また、加工性等の観点から、固形天然ゴムのムーニー粘度[ML(1+3)121℃]は、80以下であるとよい。ムーニー粘度[ML(1+3)121℃]が30以上70以下であると、より好適である。本明細書中、ムーニー粘度は、JIS K6300−1(2001)に準じて測定された値を採用する。また、アルデヒド基の有無は、上述したように、バリアン社製のNMR装置「INOVA−400」を用いた1H−NMR測定により、判断すればよい。
本発明の固形天然ゴムの製造方法は、ラジカル発生剤添加工程と固形化工程と、を有する。以下、各工程について説明する。
本工程は、天然ゴムラテックスにラジカル発生剤を添加して、ゴムの分子鎖を切断する酸化反応を進行させる工程である。天然ゴムラテックスとしては、タッピングにより採液されたフィールドラテックスや、それにアンモニアを加えて処理されたラテックス(ハイアンモニアラテックス)を用いればよい。天然ゴムラテックスのゴム分(乾燥ゴム質量、以下同じ)濃度は、特に限定されない。ゴム分濃度が低すぎると、得られる固形天然ゴムが少なくなり経済的ではない。反対に、ゴム分濃度が高すぎると、ラテックス中のゴム成分が不安定になり、酸化反応中にゴム粒子同士の凝集が起きて、酸化反応を均一に進行させにくくなる。例えば、ゴム分濃度を、10質量%以上60質量%以下とすることが望ましい。
本工程は、酸化反応後の天然ゴムラテックスを乾燥して固形化することにより、分子鎖中にアルデヒド基を含まない天然ゴムを得る工程である。天然ゴムラテックスの乾燥方法は、特に限定されない。スプレードライ、ドラムドライヤー、コンベア式乾燥機等により行えばよい。乾燥させる温度は、熱によるゴムの劣化を考慮して、効率良く水分を除去するという観点から、50〜200℃程度とすることが望ましい。また、乾燥処理は、数分以内に終えることが望ましい。なお、得られる固形天然ゴムの好適なムーニー粘度、およびアルデヒド基の有無の判断手法については、上述した通りである。
[実施例1]
天然ゴムラテックスとして、ゴールデンホープ社(マレーシア国)製のハイアンモニアラテックス(ゴム分濃度60.2質量%、アンモニア分濃度0.7質量%)を使用した。まず、ハイアンモニアラテックスを、ゴム分濃度が30質量%となるように希釈した。次に、希釈したラテックスのゴム分100gに対して、ラジカル発生剤の過硫酸カリウム(KPS)を所定量添加して、室温下で10分間攪拌した。そして、反応後のラテックスを、50℃のオーブンで乾燥して、固形化した。このようにして実施例1の固形天然ゴムを得た。
ラジカル発生剤を過硫酸アンモニウム(APS)に変更した以外は、実施例1と同様にして、実施例2の固形天然ゴムを得た。
ラジカル発生剤を過酸化ベンゾイル(BPO)に変更した以外は、実施例1と同様にして、実施例3の固形天然ゴムを得た。
得られた固形天然ゴムについて、ムーニー粘度を測定した。ムーニー粘度の測定は、(株)東洋精機製作所製のロータ式ムーニービスコメータを使用した。そして、L形ロータの回転速度を2rpm、測定温度を121℃として、予熱を1分間行った後、3分後のムーニー粘度を測定した。図1に、ラジカル発生剤の添加量に対する固形天然ゴムのムーニー粘度の値を示す。
Claims (5)
- 過硫酸カリウム、過硫酸アンモニウム、過酸化ベンゾイルから選ばれる一種以上のラジカル発生剤のみが添加された天然ゴムラテックスを固形化して得られ、分子鎖の切断により低分子量化されており、該分子鎖中にアルデヒド基を含まないことを特徴とする固形天然ゴム。
- ムーニー粘度[ML(1+3)121℃]が80以下である請求項1に記載の固形天然ゴム。
- 天然ゴムラテックスに過硫酸カリウム、過硫酸アンモニウム、過酸化ベンゾイルから選ばれる一種以上のラジカル発生剤のみを添加して室温下で撹拌することにより、ゴムの分子鎖を切断する酸化反応を進行させるラジカル発生剤添加工程と、
該酸化反応後の天然ゴムラテックスを乾燥して固形化することにより、該分子鎖中にアルデヒド基を含まない天然ゴムを得る固形化工程と、
を有することを特徴とする固形天然ゴムの製造方法。 - 前記ラジカル発生剤の添加量は、前記天然ゴムラテックス中のゴム分100質量部に対して0.1質量部以上5質量部以下である請求項3に記載の固形天然ゴムの製造方法。
- 前記固形化工程において得られる前記天然ゴムのムーニー粘度[ML(1+3)121℃]は80以下である請求項3または請求項4に記載の固形天然ゴムの製造方法。