JP2021536415A - モレキュラーシーブの製造方法 - Google Patents
モレキュラーシーブの製造方法 Download PDFInfo
- Publication number
- JP2021536415A JP2021536415A JP2021510415A JP2021510415A JP2021536415A JP 2021536415 A JP2021536415 A JP 2021536415A JP 2021510415 A JP2021510415 A JP 2021510415A JP 2021510415 A JP2021510415 A JP 2021510415A JP 2021536415 A JP2021536415 A JP 2021536415A
- Authority
- JP
- Japan
- Prior art keywords
- mixture
- optionally
- molecular sieve
- sio
- morphology modifier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
少なくとも四価元素Xの供給源、モルフォロジー変性剤L及び水を組み合わせて、合成混合物を形成するステップと;
約1時間〜100日間の時間、結晶化条件下で、前記合成混合物を加熱し、モレキュラーシーブの結晶を形成するステップと;
合成混合物からモレキュラーシーブの前記結晶を回収するステップと
を含み、モルフォロジー変性剤Lは、少なくとも1個のC12以上のヒドロカルビル基を含む単一第四級アンモニウム基を有するカチオン界面活性剤、ノニオン界面活性剤、アニオン界面活性剤、糖及びその組合せからなる群から選択され、且つ結晶の核形成又は結晶化が開始する前に合成混合物中に存在し;
モレキュラーシーブが構造指向剤Qを必要とするものである場合、モルフォロジー変性剤Lは構造指向剤Qとは異なり、且つ構造指向剤Qに加えて存在し;合成混合物中のモル比L:Xは0.0001〜0.03の範囲であり;且つ合成混合物は、液体又は固体及び液体の混合物であり、液体は実質的に単相である、調製プロセスを提供する。
上記の通り、合成混合物は、従来の方法に従って調製可能である。モルフォロジー変性剤Lは、結晶の核形成又は結晶化が開始する前に、いつでも合成混合物に含まれてよい。任意選択的に、モルフォロジー変性剤Lは、四価元素Xの供給源が添加される前に、合成混合物の他の成分と組み合わせられる。例えば、混合物を形成するために、水、水酸化物イオンの供給源(存在する場合)、構造指向剤(存在する場合)、三価元素Yの供給源(存在する場合)、種(存在する場合)及びいずれかの他の成分も、いずれかの順番で組み合わせることができ、次いで、四価元素の供給源をその混合物と組み合わせる。
モルフォロジー変性剤Lは、少なくとも1個のヒドロカルビル、好ましくはアルキル、少なくとも12個の炭素原子を有する基を含む単一第四級アンモニウム基を有するカチオン界面活性剤、ノニオン界面活性剤、アニオン界面活性剤、糖及びそれらの組合せからなる群から選択され、そして結晶の核形成又は結晶化が開始する前に、合成混合物の他の成分に添加される。2種以上のモルフォロジー変性剤Lの混合物も使用されてよく、そしてそのようなプロセスは本発明の範囲内である。
(R1)q(R2)4−qN+(Xn−)1/n (1)
(式中、それぞれのR1は、独立して、線形又は分岐鎖、飽和又は不飽和、好ましくは線形且つ飽和であり得るC1〜C6、任意選択的にC1〜C4ヒドロカルビル基であり、且つそれぞれのヒドロカルビルは、任意選択的に酸素、硫黄、窒素及びハロゲン化物から選択される1個又はそれ以上のヘテロ原子を含み得;R2は、分岐鎖又は線形、飽和又は不飽和、好ましくは線形且つ飽和であり得るC12〜C30、任意選択的にC14〜C30、任意選択的にC16〜C30、任意選択的にC18〜C30ヒドロカルビルであり、且つそれぞれのヒドロカルビルは、1個又はそれ以上の芳香族又は脂肪族環式基及び/又は任意選択的に酸素、硫黄、窒素及びハロゲン化物から選択される1個又はそれ以上のヘテロ原子を含み得;qは、1又は2、好ましくは1であり;Xn−は、nが好ましくは1である原子価nのアニオンであり、Xn−は、任意選択的にヒドロキシアニオン又はハロゲン化物アニオン、特にフッ化物、塩化物又は臭化物から選択されるハロゲン化物アニオンであり、R1は任意選択的にメチルである)を有するカチオン界面活性剤である。
(R3)3R4N+A− (2)
(式中、A−は、アニオン、好ましくは水酸化物又はハロゲン化物であり、且つ好ましくは、OH−、Cl−及びBr−から選択され、それぞれのR3は、独立して、水素及びC1〜C4アルキル、好ましくはメチルから選択され、且つR4は、分岐鎖又は線形、且つ飽和又は不飽和であり得、任意選択的に1個又はそれ以上の環式基を含有し、且つ好ましくは飽和且つ線形であるC12〜C30アルキル基、好ましくはC14〜C20アルキル基である)を有するカチオン界面活性剤である。
結晶化は、例えば、ポリプロピレンジャー又はTeflon(登録商標)ボトル、酸消化容器、Teflon(登録商標)加工又はステンレス鋼オートクレーブ、プラウ剪断混合機又は反応ケトルなどの適切な反応装置容器中で静的又は撹拌条件下で実行することができる。結晶化は、典型的に、約80℃〜約250℃、任意選択的に100℃〜約200℃、任意選択的に約150℃〜約170℃の温度で、使用された温度において結晶化が生じるために十分な時間、例えば、約1日〜約100日、特に1〜50日、例えば約2日〜約40日間、実行される。その後、合成された結晶は、濾過又は遠心分離などのいずれかの都合のよい方法によって母液から分離され、回収される。次いで、結晶を例えば大気条件下で乾燥させるか、アセトン、メタノール、エタノール又はプロパノールなどの低沸点溶媒で洗浄するか、マイクロ波条件を用いるか、或いは最高150℃までの温度でオーブン乾燥させる。
本プロセスは、任意選択的に、ステップc)において回収された結晶を焼成して、モレキュラーシーブの焼成された形態を得るステップを含む。焼成の条件は、典型的に「製造されたままの」形態でモレキュラーシーブの細孔中に捕捉される、残留モルフォロジー変性剤L及び/又は構造指向剤Q(存在する場合)などの、残留するいずれかの有機残渣を少なくとも部分的に除去するために選択されるであろう。
本発明のモレキュラーシーブは、いずれの種類のものであってもよい。モレキュラーシーブは、例えば、シリケート、アルミノシリケート、ボロシリケート、ガロシリケート、チタノシリケート、ゲルマノシリケート、ジンコシリケート、アルミノホスフェート(ALPO)、シリコアルミノホスフェート(SAPO)及び混合酸化物骨格(MOF)からなる群から;好ましくはシリケート、アルミノシリケート、アルミノホスフェート(ALPO)及びシリコアルミノホスフェート(SAPO)から;より好ましくはシリケート及びアルミノシリケートから選択され得る。
mSDA:(SixAlyPz)O2
(式中、mは、(SixAlyPz)O2の1モルあたりのSDAのモル数であり、且つmは、合成されたままの形態において、0.01〜0.5、好ましくは0.04〜0.35の値を有し;x、y及びzは、それぞれ、四面体酸化物としてのSi、Al及びPのモル分率を表し、×+y+z=1であり、且つy及びz0.25以上である)によって表され得る。好ましくは、シリコアルミノホスフェートモレキュラーシーブの場合、xは0より大きく、且つ任意選択的に、xは0〜約0.31の範囲にある。yの範囲は0.25〜0.5であり、且つzは0.25〜0.5の範囲であり、好ましくはy及びzは0.4〜0.5の範囲である。
追加的に、又は代わりに、本開示は、以下の実施形態の1つ又はそれ以上を含むことができる。
a.四価元素Xの供給源、モルフォロジー変性剤L、水、任意選択的に水酸化物イオンの供給源、任意選択的に構造指向剤Q、任意選択的に三価元素Yの供給源、任意選択的に五価元素Zの供給源、任意選択的にハロゲン化物イオンW−の供給源、任意選択的にアルカリ金属イオンM+及び/又はアルカリ土類金属カチオンM2+の供給源、並びに任意選択的に1種又はそれ以上の他の成分を組み合わせて、合成混合物を形成するステップと;
b.約1時間〜100日間の時間、結晶化条件下で、前記合成混合物を加熱し、モレキュラーシーブの結晶を形成するステップと;
c.合成混合物からモレキュラーシーブの前記結晶を回収するステップと
を含み、モルフォロジー変性剤Lは、少なくとも12個の炭素原子を有する少なくとも1個のヒドロカルビル基を含む単一第四級アンモニウム基を有するカチオン界面活性剤、ノニオン界面活性剤、アニオン界面活性剤、糖及びその組合せからなる群から選択され、且つ結晶の核形成又は結晶化が開始する前に合成混合物中に存在し;
モレキュラーシーブが構造指向剤Qを必要とするものである場合、モルフォロジー変性剤Lは構造指向剤Qとは異なり、且つ構造指向剤Qに加えて存在し;
合成混合物中のモル比L:Xは0.0001〜0.03の範囲であり;且つ
合成混合物は、液体又は固体及び液体の混合物であり、液体は実質的に単相である、調製プロセス。
(R1)q(R2)4−qN+(Xn−)1/n (1)
(式中、それぞれのR1は、独立して、線形又は分岐鎖、飽和又は不飽和、好ましくは線形且つ飽和であり得るC1〜C6、任意選択的にC1〜C4アルキル基であり;R2は、分岐鎖又は線形、飽和又は不飽和、好ましくは線形且つ飽和であり得るC12〜C30、任意選択的にC14〜C30、任意選択的にC16〜C30、任意選択的にC18〜C30アルキルであり;qは、1又は2、好ましくは1であり;X−は原子価nのアニオンであり、且つX−は、任意選択的にヒドロキシアニオン又はハロゲン化物アニオン、特にフッ化物、塩化物又は臭化物から選択されるハロゲン化物アニオンである)を有するカチオン界面活性剤である、上記実施形態のいずれか1つのプロセス。
14.8gの水中に1.26gの25%二塩化ヘキサメソニウム(HMDC)を希釈する。撹拌して、確実に溶液を均一にさせる。構造指向剤溶液に、0.62gのアルミン酸ナトリウム溶液(7.8%のNa2O、10.0%のAl2O3、82.2%の水)を添加する。撹拌して、溶液を均質化する。HMDC/アルミン酸塩溶液に、3.6gの10%NaOH溶液を添加する。撹拌して、混合物を均質化する。アルミン酸塩混合物に0.73gのコロイド状ベータ種(17.2重量%の種)を添加する。この混合物に、3.95gのUltrasil VN3 PM変性沈澱シリカ(92.4%のSiO2)を添加する。15分間混合物を撹拌し、均一なスラリーを調製する。混合物に関するおよそのモルゲル組成は、以下の通りである:
SiO2/Al2O3=100.0
OH−/SiO2=0.175
HMDC/SiO2=0.019
変性剤/SiO2=0.000
H2O/SiO2=18.7
約5100ppmの種
13.0gの水中に1.27gの25%二塩化ヘキサメソニウム(HMDC)を希釈する。撹拌して、確実に溶液を均一にさせる。構造指向剤溶液に、0.59gのアルミン酸ナトリウム溶液(7.5%のNa2O、10.2%のAl2O3、82.3%の水)を添加する。撹拌して、溶液を均質化する。HMDC/アルミン酸塩溶液に、3.6gの10%NaOH溶液を添加する。撹拌して、混合物を均質化する。アルミン酸塩混合物に0.75gのコロイド状ベータ種(16.7重量%の種)を添加する。1.96gのBrij L4(ノニオン界面活性剤モルフォロジー変性剤としてのポリエチレングリコールドデシルエーテル)の19.2重量%溶液を添加し、そして混合物を撹拌し、ゼオライト成長変性剤を溶解させる。この混合物に、3.89gのUltrasil VN3 PM変性沈澱シリカ(92.4%のSiO2)を添加する。15分間混合物を撹拌し、均一なスラリーを調製する。混合物に関するおよそのモルゲル組成は、以下の通りである:
SiO2/Al2O3=100.0
OH−/SiO2=0.175
HMDC/SiO2=0.019
変性剤/SiO2=0.018
H2O/SiO2=18.7
約5200ppmの種
12.9gの水中に1.27gの25%二塩化ヘキサメソニウム(HMDC)を希釈する。撹拌して、確実に溶液を均一にさせる。構造指向剤溶液に、0.59gのアルミン酸ナトリウム溶液(7.5%のNa2O、10.2%のAl2O3、82.3%の水)を添加する。撹拌して、溶液を均質化する。HMDC/アルミン酸塩溶液に、3.6gの10%NaOH溶液を添加する。撹拌して、混合物を均質化する。アルミン酸塩混合物に0.75gのコロイド状ベータ種(16.7重量%の種)を添加する。2.02gのBrij 93(ノニオン界面活性剤モルフォロジー変性剤としてのポリエチレングリコールロレイルエーテル)の18.5重量%溶液を添加し、そして混合物を撹拌し、ゼオライト成長変性剤を溶解させる。この混合物に、3.89gのUltrasil VN3 PM変性沈澱シリカ(92.4%のSiO2)を添加する。15分間混合物を撹拌し、均一なスラリーを調製する。混合物に関するおよそのモルゲル組成は、以下の通りである:
SiO2/Al2O3=100.0
OH−/SiO2=0.175
HMDC/SiO2=0.019
変性剤/SiO2=0.018
H2O/SiO2=18.7
約5200ppmの種
13.0gの水中に1.27gの25%二塩化ヘキサメソニウム(HMDC)を希釈する。撹拌して、確実に溶液を均一にさせる。構造指向剤溶液に、0.60gのアルミン酸ナトリウム溶液(7.5%のNa2O、10.2%のAl2O3、82.3%の水)を添加する。撹拌して、溶液を均質化する。HMDC/アルミン酸塩溶液に、3.6gの10%NaOH溶液を添加する。撹拌して、混合物を均質化する。アルミン酸塩混合物に0.75gのコロイド状ベータ種(16.7重量%の種)を添加する。1.86gのオクチル硫酸ナトリウムの20重量%溶液を添加し、そして混合物を撹拌し、ゼオライト成長変性剤を溶解させる。この混合物に、3.89gのUltrasil VN3 PM変性沈澱シリカ(92.4%のSiO2)を添加する。15分間混合物を撹拌し、均一なスラリーを調製する。混合物に関するおよそのモルゲル組成は、以下の通りである:
SiO2/Al2O3=100.0
OH−/SiO2=0.175
HMDC/SiO2=0.019
変性剤/SiO2=0.027
H2O/SiO2=18.7
約5200ppmの種
13.1gの水中に1.27gの25%二塩化ヘキサメソニウム(HMDC)を希釈する。撹拌して、確実に溶液を均一にさせる。構造指向剤溶液に、0.60gのアルミン酸ナトリウム溶液(7.5%のNa2O、10.2%のAl2O3、82.3%の水)を添加する。撹拌して、溶液を均質化する。HMDC/アルミン酸塩溶液に、3.6gの10%NaOH溶液を添加する。撹拌して、混合物を均質化する。アルミン酸塩混合物に0.75gのコロイド状ベータ種(16.7重量%の種)を添加する。1.86gの1,2−ヘキサンジオールの20.1重量%溶液を添加し、そして混合物を撹拌し、ゼオライト成長変性剤を溶解させる。この混合物に、3.89gのUltrasil VN3 PM変性沈澱シリカ(92.4%のSiO2)を添加する。15分間混合物を撹拌し、均一なスラリーを調製する。混合物に関するおよそのモルゲル組成は、以下の通りである:
SiO2/Al2O3=100.0
OH−/SiO2=0.175
HMDC/SiO2=0.019
変性剤/SiO2=0.053
H2O/SiO2=18.7
約5200ppmの種
12.5gの水中に1.26gの25%二塩化ヘキサメソニウム(HMDC)を希釈する。撹拌して、確実に溶液を均一にさせる。構造指向剤溶液に、0.61gのアルミン酸ナトリウム溶液(7.8%のNa2O、10.0%のAl2O3、82.2%の水)を添加する。撹拌して、溶液を均質化する。HMDC/アルミン酸塩溶液に、3.6gの10%NaOH溶液を添加する。撹拌して、混合物を均質化する。アルミン酸塩混合物に0.73gのコロイド状ベータ種(17.2重量%の種)を添加する。2.51gのトリメチルオクタデシルアンモニウムブロミド(カチオン界面活性剤モルフォロジー変性剤)の20重量%溶液を添加し、そして混合物を撹拌し、モルフォロジー変性剤を溶解させる。この混合物に、3.87gのUltrasil VN3 PM変性沈澱シリカ(92.4%のSiO2)を添加する。15分間混合物を撹拌し、均一なスラリーを調製する。混合物に関するおよそのモルゲル組成は、以下の通りである:
SiO2/Al2O3=100.0
OH−/SiO2=0.175
HMDC/SiO2=0.019
変性剤/SiO2=0.021
H2O/SiO2=18.7
約5100ppmの種
12.5gの水中に1.24gの25%二塩化ヘキサメソニウム(HMDC)を希釈する。撹拌して、確実に溶液を均一にさせる。構造指向剤溶液に、0.61gのアルミン酸ナトリウム溶液(7.8%のNa2O、10.0%のAl2O3、82.2%の水)を添加する。撹拌して、溶液を均質化する。HMDC/アルミン酸塩溶液に、3.6gの10%NaOH溶液を添加する。撹拌して、混合物を均質化する。アルミン酸塩混合物に0.73gのコロイド状ベータ種(17.2重量%の種)を添加する。2.5gのラウリル硫酸ナトリウム(アニオン界面活性剤モルフォロジー変性剤)の20重量%溶液を添加し、そして混合物を撹拌し、モルフォロジー変性剤を溶解させる。この混合物に、3.90gのUltrasil VN3 PM変性沈澱シリカ(92.4%のSiO2)を添加する。15分間混合物を撹拌し、均一なスラリーを調製する。混合物に関するおよそのモルゲル組成は、以下の通りである:
SiO2/Al2O3=100.2
OH−/SiO2=0.174
HMDC/SiO2=0.019
変性剤/SiO2=0.028
H2O/SiO2=18.6
約5100ppmの種
13.1gの水中に1.24gの25%二塩化ヘキサメソニウム(HMDC)を希釈する。撹拌して、確実に溶液を均一にさせる。構造指向剤溶液に、0.61gのアルミン酸ナトリウム溶液(7.8%のNa2O、10.0%のAl2O3、82.2%の水)を添加する。撹拌して、溶液を均質化する。HMDC/アルミン酸塩溶液に、3.6gの10%NaOH溶液を添加する。撹拌して、混合物を均質化する。アルミン酸塩混合物に0.73gのコロイド状ベータ種(17.2重量%の種)を添加する。1.88gのベンジルヘキサデシルジメチルアンモニウムクロリド(カチオン界面活性剤モルフォロジー変性剤)の20重量%溶液を添加し、そして混合物を撹拌し、モルフォロジー変性剤を溶解させる。この混合物に、3.89gのUltrasil VN3 PM変性沈澱シリカ(92.4%のSiO2)を添加する。15分間混合物を撹拌し、均一なスラリーを調製する。混合物に関するおよそのモルゲル組成は、以下の通りである:
SiO2/Al2O3=100.0
OH−/SiO2=0.175
HMDC/SiO2=0.019
変性剤/SiO2=0.016
H2O/SiO2=18.7
約5100ppmの種
13.1gの水中に1.24gの25%二塩化ヘキサメソニウム(HMDC)を希釈する。撹拌して、確実に溶液を均一にさせる。構造指向剤溶液に、0.61gのアルミン酸ナトリウム溶液(7.8%のNa2O、10.0%のAl2O3、82.2%の水)を添加する。撹拌して、溶液を均質化する。HMDC/アルミン酸塩溶液に、3.6gの10%NaOH溶液を添加する。撹拌して、混合物を均質化する。アルミン酸塩混合物に0.73gのコロイド状ベータ種(17.2重量%の種)を添加する。1.86gのジヘキサデシルジメチルアンモニウムブロミド(カチオン界面活性剤モルフォロジー変性剤)の20重量%溶液を添加し、そして混合物を撹拌し、モルフォロジー変性剤を溶解させる。この混合物に、3.89gのUltrasil VN3 PM変性沈澱シリカ(92.4%のSiO2)を添加する。15分間混合物を撹拌し、均一なスラリーを調製する。混合物に関するおよそのモルゲル組成は、以下の通りである:
SiO2/Al2O3=100.0
OH−/SiO2=0.175
HMDC/SiO2=0.019
変性剤/SiO2=0.012
H2O/SiO2=18.7
約5100ppmの種
13.1gの水中に1.24gの25%二塩化ヘキサメソニウム(HMDC)を希釈する。撹拌して、確実に溶液を均一にさせる。構造指向剤溶液に、0.61gのアルミン酸ナトリウム溶液(7.8%のNa2O、10.0%のAl2O3、82.2%の水)を添加する。撹拌して、溶液を均質化する。HMDC/アルミン酸塩溶液に、3.6gの10%NaOH溶液を添加する。撹拌して、混合物を均質化する。アルミン酸塩混合物に0.73gのコロイド状ベータ種(17.2重量%の種)を添加する。1.86gのドデシル硫酸リチウム(アニオン界面活性剤モルフォロジー変性剤)の20重量%溶液を添加し、そして混合物を撹拌し、モルフォロジー変性剤を溶解させる。この混合物に、3.89gのUltrasil VN3 PM変性沈澱シリカ(92.4%のSiO2)を添加する。15分間混合物を撹拌し、均一なスラリーを調製する。混合物に関するおよそのモルゲル組成は、以下の通りである:
SiO2/Al2O3=100.0
OH−/SiO2=0.175
HMDC/SiO2=0.019
変性剤/SiO2=0.023
H2O/SiO2=18.7
約5100ppmの種
13.7gの水中に1.25gの25%二塩化ヘキサメソニウム(HMDC)を希釈する。撹拌して、確実に溶液を均一にさせる。構造指向剤溶液に、0.61gのアルミン酸ナトリウム溶液(7.8%のNa2O、10.0%のAl2O3、82.2%の水)を添加する。撹拌して、溶液を均質化する。HMDC/アルミン酸塩溶液に、3.6gの10%NaOH溶液を添加する。撹拌して、混合物を均質化する。アルミン酸塩混合物に0.73gのコロイド状ベータ種(17.2重量%の種)を添加する。1.24gのPluronic EO−PO−EOトリブロックコポリマー(ノニオン界面活性剤モルフォロジー変性剤)の20重量%溶液を添加し、そして混合物を撹拌し、モルフォロジー変性剤を溶解させる。この混合物に、3.91gのUltrasil VN3 PM変性沈澱シリカ(92.4%のSiO2)を添加する。15分間混合物を撹拌し、均一なスラリーを調製する。混合物に関するおよそのモルゲル組成は、以下の通りである:
SiO2/Al2O3=100.0
OH−/SiO2=0.175
HMDC/SiO2=0.019
変性剤/SiO2=0.0007
H2O/SiO2=18.7
約5100ppmの種
12.0gの水中に3.54gの硫酸アルミニウム八水和物の40重量%溶液を希釈する。硫酸アルミニウム溶液に4.1gの20%NaOH溶液を添加する。撹拌して、混合物を均質化する。アルミン酸ナトリウム溶液に、3.46gのUltrasil VN3 PM変性沈澱シリカ(92.4%のSiO2)を添加する。スラリーが均一に見えるようになるまで、混合物を撹拌する。スラリーに1.86gのヘキサメチレンイミン(HMI)を添加する。混合物を10分間撹拌し、均一なスラリーを調製する。混合物に関するおよそのモルゲル組成は、以下の通りである:
SiO2/Al2O3=25.0
OH−/SiO2=0.390
HMI/SiO2=0.350
変性剤/SiO2=0.000
H2O/SiO2=18.5
10.9gの水中に3.51gの硫酸アルミニウム八水和物の40重量%溶液を希釈する。硫酸アルミニウム溶液に4.1gの20%NaOH溶液を添加する。撹拌して、混合物を均質化する。アルミン酸ナトリウム溶液に、3.42gのUltrasil VN3 PM変性沈澱シリカ(92.4%のSiO2)を添加する。スラリーが均一に見えるようになるまで、混合物を撹拌する。スラリーに1.85gのヘキサメチレンイミン(HMI)を添加する。スラリーに、1.26gのセチルトリメチルアンモニウムブロミド(カチオン界面活性剤モルフォロジー変性剤)の20重量%溶液を添加する。混合物を10分間撹拌し、均一なスラリーを調製する。混合物に関するおよそのモルゲル組成は、以下の通りである:
SiO2/Al2O3=25.0
OH−/SiO2=0.390
HMI/SiO2=0.350
変性剤/SiO2=0.013
H2O/SiO2=19.6
10.9gの水中に3.51gの硫酸アルミニウム八水和物の40重量%溶液を希釈する。硫酸アルミニウム溶液に4.1gの20%NaOH溶液を添加する。撹拌して、混合物を均質化する。アルミン酸ナトリウム溶液に、3.42gのUltrasil VN3 PM変性沈澱シリカ(92.4%のSiO2)を添加する。スラリーが均一に見えるようになるまで、混合物を撹拌する。スラリーに1.85gのヘキサメチレンイミン(HMI)を添加する。スラリーに、1.26gのラウリル硫酸ナトリウム(アニオン界面活性剤モルフォロジー変性剤)の20重量%溶液を添加する。混合物を10分間撹拌し、均一なスラリーを調製する。混合物に関するおよそのモルゲル組成は、以下の通りである:
SiO2/Al2O3=25.0
OH−/SiO2=0.390
HMI/SiO2=0.350
変性剤/SiO2=0.016
H2O/SiO2=19.6
14.4gの水中に1.39gの56%二塩化ヘキサメソニウム(HMDC)を希釈する。撹拌して、確実に溶液を均一にさせる。構造指向剤溶液に、1.42gのアルミン酸ナトリウム溶液(20%のNaOH、7.8%のAl(OH)3、72.2%の水)を添加する。撹拌して、溶液を均質化する。HMDC/アルミン酸塩溶液に、2.6gの10%NaOH溶液を添加する。撹拌して、混合物を均質化する。アルミン酸塩混合物に0.03gのZSM−48種を添加する。0.63gのフルクトースの39.7%溶液を添加し、そして撹拌して混合物を均質化する。この混合物に、4.62gのUltrasil VN3 PM変性沈澱シリカ(92.4%のSiO2)を添加する。15分間混合物を撹拌し、均一なスラリーを調製する。混合物に関するおよそのモルゲル組成は、以下の通りである:
SiO2/Al2O3=99.9
OH−/SiO2=0.190
HMDC/SiO2=0.040
変性剤/SiO2=0.020
H2O/SiO2=14.9
約1000ppmの種
上記実施例1〜15によって製造されたモレキュラーシーブの試料に以下の処理を行った。
Claims (18)
- モレキュラーシーブの結晶の調製方法であって、
a.少なくとも四価元素Xの供給源、モルフォロジー変性剤L及び水を組み合わせて、合成混合物を形成するステップと;
b.約1時間〜100日間の時間、結晶化条件下で、前記合成混合物を加熱し、前記モレキュラーシーブの前記結晶を形成するステップと;
c.前記合成混合物から前記モレキュラーシーブの前記結晶を回収するステップと
を含み、前記モルフォロジー変性剤Lは、少なくとも12個の炭素原子を有する少なくとも1個のヒドロカルビル基を含んで成る単一第四級アンモニウム基を有するカチオン界面活性剤、ノニオン界面活性剤、アニオン界面活性剤、糖及びその組合せからなる群から選択され、且つ前記結晶の核形成又は結晶化が開始する前に前記合成混合物中に存在し;
前記モレキュラーシーブが構造指向剤Qを必要とするものである場合、前記モルフォロジー変性剤Lは構造指向剤Qとは異なり、且つ構造指向剤Qに加えて存在し;
前記合成混合物中のモル比L:Xは0.0001〜0.03の範囲であり;且つ
前記合成混合物は、液体又は固体及び液体の混合物であり、前記液体は実質的に単相である、調製方法。 - ステップa)において、水酸化物イオンの供給源、構造指向剤Q、三価元素Yの供給源、五価元素Zの供給源、ハロゲン化物イオンW−の供給源、並びにアルカリ金属イオンM+及び/又はアルカリ土類金属カチオンM2+の供給源からなる群から選択される1つ又はそれ以上のさらなる成分も前記合成混合物中に組み合わせられる、請求項1に記載の方法。
- XがSi、Ge及びその混合物から選択され、且つ前記合成混合物が三価元素Yの供給源も含んで成り、YがAl、B、Ga、Zn及びその混合物から選択される、請求項1に記載の方法。
- X=Si及びY=Alである、請求項3に記載の方法。
- 前記モレキュラーシーブが、MRE、MWW、MTW、FAU、EMT、MFS、MEI、BEA並びにその多形体、TON及びMTTからなる群から選択される骨格構造を有する、請求項1に記載の方法。
- 前記合成混合物中のL:Xのモル比が0.001〜0.025の範囲である、請求項1に記載の方法。
- 前記モルフォロジー変性剤Lが、単一第四級アンモニウム基と、前記単一第四級アンモニウム基に結合した少なくとも1個のC12〜C30アルキル基を有するカチオン界面活性剤である、請求項1に記載の方法。
- 前記モルフォロジー変性剤Lが、式(1)
(R1)q(R2)4−qN+(Xn−)1/n (1)
(式中、それぞれのR1は、独立して、線形又は分岐鎖、飽和又は不飽和、好ましくは線形且つ飽和であり得るC1〜C6、任意選択的にC1〜C4アルキル基であり;R2は、分岐鎖又は線形、飽和又は不飽和、好ましくは線形且つ飽和であり得るC12〜C30、任意選択的にC14〜C30、任意選択的にC16〜C30、任意選択的にC18〜C30アルキル基であり;qは、1又は2、好ましくは1であり;X−は原子価nのアニオンであり;且つX−は、任意選択的にヒドロキシアニオン又はハロゲン化物アニオン、特にフッ化物、塩化物又は臭化物から選択されるハロゲン化物アニオンである)を有するカチオン界面活性剤である、請求項1に記載の方法。 - 前記モルフォロジー変性剤Lが単糖類である、請求項1に記載の方法。
- 前記モルフォロジー変性剤Lがアニオン界面活性剤である、請求項1に記載の方法。
- 前記モルフォロジー変性剤Lがノニオン界面活性剤である、請求項1に記載の方法。
- ステップc)において回収された前記結晶を焼成して、前記モレキュラーシーブの焼成された形態を得るステップを含む、請求項1に記載の方法。
- 請求項1に記載の方法によって調製された、製造されたままの形態の、又はその焼成された形態のモレキュラーシーブ。
- 合成混合物がいずれのモルフォロジー変性剤Lも含まないことを除き、同等の方法を使用して製造されたモレキュラーシーブの外部酸性度の少なくとも1.10倍の外部酸性度を有する、請求項13に記載のモレキュラーシーブ。
- 合成混合物がいずれのモルフォロジー変性剤Lも含まないことを除き、同等の方法を使用して製造されたモレキュラーシーブの外部表面積の少なくとも1.10倍の外部表面積を有する、請求項13に記載のモレキュラーシーブ。
- 請求項13に記載のモレキュラーシーブを含んで成り、且つ任意選択的にバインダーを含む、触媒。
- 炭化水素供給原料を、請求項16に記載の触媒と接触させるステップを含む、炭化水素変換方法。
- 脱蝋、オリゴマー化、アルキル化、異性化又は分解方法である、請求項17に記載の炭化水素変換方法。