JP2020124568A - Toilet tissue paper and toilet roll - Google Patents
Toilet tissue paper and toilet roll Download PDFInfo
- Publication number
- JP2020124568A JP2020124568A JP2020079348A JP2020079348A JP2020124568A JP 2020124568 A JP2020124568 A JP 2020124568A JP 2020079348 A JP2020079348 A JP 2020079348A JP 2020079348 A JP2020079348 A JP 2020079348A JP 2020124568 A JP2020124568 A JP 2020124568A
- Authority
- JP
- Japan
- Prior art keywords
- roll
- toilet paper
- toilet
- less
- embossing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、トイレットペーパー及びトイレットロールに関する。 The present invention relates to a toilet paper and a toilet roll.
トイレットペーパー製品は、トイレットペーパーウェブを1枚又は2枚以上に重ねたトイレットペーパーを所定の大きさに切断して製造される。一般的には長尺のトイレットペーパーがロール状に巻回されてなるトイレットロール(ロール状トイレットペーパー)が多用されている。1枚のトイレットペーパーウェブからなるトイレットペーパーは1プライのトイレットペーパーと称され、2枚重ねのトイレットペーパーウェブからなるトイレットペーパーは2プライのトイレットペーパーと称されている。 The toilet paper product is produced by cutting one or two or more toilet paper webs into a predetermined size. Generally, a toilet roll (rolled toilet paper) formed by winding a long toilet paper in a roll shape is often used. Toilet paper consisting of one sheet of toilet paper web is referred to as 1-ply toilet paper, and toilet paper consisting of two-ply toilet paper web is referred to as 2-ply toilet paper.
トイレットペーパーは、直接肌に触れるものであるから、滑らかでふっくらとした風合いが要求される。また、トイレットペーパーはロール形態で流通し、店頭に並ぶため、トイレットロール自体の手触り感や柔らかな触感が要求される場合がある。すなわち、トイレットロールを掴んだ際に、柔らかでふんわりとした触感が感じられる方が、高級感や高品質であるとの評価が得られる傾向がある。このため、トイレットロールの巻き密度を調整するなどして、トイレットロールの手触り感や触感を高めることが検討されている(例えば、特許文献1及び2)。 Toilet paper, which comes into direct contact with the skin, is required to have a smooth and fluffy texture. Further, since the toilet paper is distributed in the form of a roll and is lined up in stores, it may be required that the toilet roll itself has a touch and a soft touch. That is, when a toilet roll is gripped, a person who feels a soft and fluffy feel tends to be evaluated as having a high-class feeling and high quality. Therefore, it has been considered to enhance the feel and feel of the toilet roll by adjusting the winding density of the toilet roll (for example, Patent Documents 1 and 2).
しかしながら、従来のトイレットロールにおいては、ロールから巻き解かれ使用されるトイレットペーパーが有する滑らかでふっくらとした風合いと、トイレットロール自体の手触り感や柔らかな触感が高いレベルで両立されておらず、さらなる改善が求められていた。 However, in the conventional toilet roll, the smooth and plump texture of the toilet paper used by being unwound from the roll is not compatible at a high level with the feel and soft feel of the toilet roll itself, and further Improvement was sought.
そこで本発明者らは、このような従来技術の課題を解決するために、良好な肌触り感を有するトイレットペーパーであって、ロール形態とした際に優れた手触り感を発揮し得るトイレットペーパーを提供することを目的として検討を進めた。 Therefore, in order to solve the problems of the conventional techniques, the present inventors provide a toilet paper having a good feeling of touch, which can exhibit an excellent feeling of touch when formed into a roll form. The study was advanced for the purpose of doing.
上記の課題を解決するために鋭意検討を行った結果、本発明者らは、巻外側トイレットペーパーと、巻内側トイレットペーパーにそれぞれ異なる高さのエンボスを形成し、エンボス高さの差を所定の範囲とすることにより、良好な肌触り感を有するトイレットペーパーであって、ロール形態とした際に優れた手触り感を発揮し得るトイレットペーパーが得られることを見出した。
具体的に、本発明は、以下の構成を有する。
As a result of earnest studies to solve the above problems, the present inventors have formed an embossing with different heights on the roll-out toilet paper and the roll-inside toilet paper, respectively, with a predetermined difference in embossing height. It has been found that when the content is within the range, it is possible to obtain a toilet paper having a good feeling of touch and capable of exhibiting an excellent feeling of touch when formed into a roll form.
Specifically, the present invention has the following configurations.
[1] 巻外側トイレットペーパーと巻内側トイレットペーパーと、を有する2プライ以上のトイレットペーパーであって、巻外側トイレットペーパーのエンボス高さは90μm以上210μm以下であり、巻内側トイレットペーパーのエンボス高さは70μm以上170μm以下であり、巻外側トイレットペーパーのエンボス高さと、巻内側トイレットペーパーのエンボス高さの差が10μm以上50μm以下である2プライ以上のトイレットペーパー。
[2] 巻外側トイレットペーパーの圧縮回復率(RC1)が33%以上53%以下であり、巻内側トイレットペーパーの圧縮回復率(RC2)が35%以上55%以下であり、(RC1−RC2)の値が−12%以上−1%以下である[1]に記載のトイレットペーパー。
[3] 巻外側トイレットペーパーのエンボスパターンと、巻内側トイレットペーパーのエンボスパターンは異なるものである[1]又は[2]に記載のトイレットペーパー。
[4] 巻外側トイレットペーパーのエンボス密度は10個/cm2以上30個/cm2以下であり、巻内側トイレットペーパーのエンボス密度は20個/cm2以上100個/cm2以下である[1]〜[3]のいずれかに記載のトイレットペーパー
[5] [1]〜[4]のいずれかに記載のトイレットペーパーをロール状にしたトイレットロールであって、トイレットロールの巻き長さは25m以上60m以下であり、トイレットロールの巻き密度は0.50m/cm2以上1.4m/cm2以下である2プライ以上のトイレットロール。
[6] 巻外側トイレットペーパーに、エンボス高さが90μm以上210μm以下のエンボス加工を施す(A)工程と、巻内側トイレットペーパーに、エンボス高さが70μm以上170μm以下のエンボス加工を施す(B)工程と、(A)工程で得られた巻外側トイレットペーパーと、(B)工程で得られた巻内側トイレットペーパーを積層する工程と、を含み、(A)工程で得られた巻外側トイレットペーパーのエンボス高さと、(B)工程で得られた巻内側トイレットペーパーのエンボス高さの差が10μm以上50μm以下である2プライ以上のトイレットペーパーの製造方法。
[1] A two-ply or more toilet paper having a roll outside toilet paper and a roll inside toilet paper, wherein the roll outside toilet paper has an embossing height of 90 μm or more and 210 μm or less, and the roll inside toilet paper has an embossing height. Is 70 μm or more and 170 μm or less, and the difference between the embossing height of the roll outer toilet paper and the roll embossing height of the roll inner toilet paper is 10 μm or more and 50 μm or less.
[2] The compression recovery rate (RC 1 ) of the outside wound toilet paper is 33% or more and 53% or less, and the compression recovery rate (RC 2 ) of the inside toilet paper is 35% or more and 55% or less, (RC 1 The toilet paper according to [1], which has a value of −RC 2 ) of −12% or more and −1% or less.
[3] The toilet paper according to [1] or [2], wherein the embossing pattern of the roll-out toilet paper and the embossing pattern of the roll-inside toilet paper are different.
[4] The embossing density of the wound outer toilet paper is 10 pieces/cm 2 or more and 30 pieces/cm 2 or less, and the embossing density of the winding inner toilet paper is 20 pieces/cm 2 or more and 100 pieces/cm 2 or less [1 ]-[3] Toilet paper according to any one of [5] [1] to [4] is a toilet roll in the form of a roll, the winding length of the toilet roll is 25 m A toilet roll of 2 plies or more having a winding density of 60 m or less and a winding density of 0.50 m/cm 2 or more and 1.4 m/cm 2 or less.
[6] Step (A) of applying embossing height of 90 μm or more and 210 μm or less to the roll outside toilet paper, and applying embossing of roll embossing height of 70 μm or more and 170 μm or less to the roll inside toilet paper (B) An outer-side toilet paper roll obtained in the step (A), which includes a step, and a step of laminating the inner-side toilet paper roll obtained in the step (A) and the inner-roll toilet paper piece obtained in the step (B). And the embossing height of the wound-side toilet paper obtained in the step (B) is 10 μm or more and 50 μm or less.
本発明によれば、良好な肌触り感を有するトイレットペーパーであって、ロール形態とした際にも優れた手触り感を発揮し得るトイレットペーパーを得ることができる。本発明のトイレットペーパーから構成されるトイレットロールは、その手触り感が柔らかく、高級感や高品質感といった好ましい印象を与えることができる。 Advantageous Effects of Invention According to the present invention, it is possible to obtain a toilet paper having a good feel to the touch and capable of exhibiting an excellent feel to the touch even in the roll form. The toilet roll composed of the toilet paper of the present invention has a soft feel to the touch, and can give a favorable impression such as a high-grade feeling and a high-quality feeling.
以下において、本発明について詳細に説明する。以下に記載する構成要件の説明は、代表的な実施形態や具体例に基づいてなされることがあるが、本発明はそのような実施形態に限定されるものではない。 Hereinafter, the present invention will be described in detail. The description of the constituents described below may be made based on typical embodiments or specific examples, but the present invention is not limited to such embodiments.
(トイレットペーパー)
本発明は、巻外側トイレットペーパーと巻内側トイレットペーパーと、を有する2プライ以上のトイレットペーパーに関する。ここで、巻外側トイレットペーパーのエンボス高さは90μm以上210μm以下である。巻内側トイレットペーパーのエンボス高さは70μm以上170μm以下である。また、巻外側トイレットペーパーのエンボス高さと、巻内側トイレットペーパーのエンボス高さの差は10μm以上50μm以下である。
(Toilet Paper)
TECHNICAL FIELD The present invention relates to a two-ply or more toilet paper including a roll-out toilet paper and a roll-inside toilet paper. Here, the emboss height of the roll-side toilet paper is 90 μm or more and 210 μm or less. The embossing height of the roll-inside toilet paper is 70 μm or more and 170 μm or less. The difference between the embossed height of the roll-out toilet paper and the embossed height of the roll-inside toilet paper is 10 μm or more and 50 μm or less.
本発明のトイレットペーパーは、上記構成を有するため、使用時の肌触り感に優れている。具体的には、本発明のトイレットペーパーは、滑らかでふっくらとした風合いを備えている。さらに、本発明のトイレットペーパーは、ロール形態とした際にも優れた手触り感を発揮し得る。すなわち、本発明のトイレットペーパーから構成されるトイレットロールはそのロール自体に柔らかさがあり、手触り感に優れている。 Since the toilet paper of the present invention has the above-mentioned constitution, it has an excellent feel when used. Specifically, the toilet paper of the present invention has a smooth and plump texture. Furthermore, the toilet paper of the present invention can exhibit an excellent feel even when it is in a roll form. That is, the toilet roll composed of the toilet paper of the present invention has softness in itself and is excellent in touch feeling.
本発明のトイレットペーパーは2プライ以上のトイレットペーパーである。トイレットペーパーのプライ数はトイレットペーパーウェブの重ね合わせ枚数を意味する。プライ数は、2以上であればよく、2以上4以下であることが好ましく、2もしくは3であることがより好ましく、2であることが特に好ましい。 The toilet paper of the present invention is a toilet paper having two or more plies. The number of plies of toilet paper means the number of overlapping sheets of toilet paper. The number of plies may be 2 or more, preferably 2 or more and 4 or less, more preferably 2 or 3, and particularly preferably 2.
本発明では、トイレットペーパーは、トイレットロールを構成するトイレットペーパーであることが好ましい。すなわち、本発明のトイレットペーパーは、巻外側トイレットペーパーと巻内側トイレットペーパーを有するものである。巻外側トイレットペーパーは、トイレットペーパーをロール状に巻き取った際にロールの外周面側に配されるトイレットペーパーである。また、巻内側トイレットペーパーは、トイレットペーパーをロール状に巻き取った際にロールの内周面側に配される面である。
図1は本発明のトイレットペーパーの構成を説明する図である。図1には、トイレットロールと、トイレットロールを構成するトイレットペーパーの点線円部の拡大図が示されている。図1に示されているように、トイレットペーパー1は、トイレットロール100の外周面側に、巻外側トイレットペーパー12を有し、トイレットロール100の内周面側に、巻内側トイレットペーパー14を有している。なお、トイレットペーパーが3プライ以上のトイレットペーパーである場合は、最も外周面側に配されるトイレットペーパーを巻外側トイレットペーパーといい、最も内周面側に配されるトイレットペーパーを巻内側トイレットペーパーという。
In the present invention, the toilet paper is preferably a toilet paper forming a toilet roll. That is, the toilet paper of the present invention has a roll outside toilet paper and a roll inside toilet paper. The roll-out toilet paper is a toilet paper that is arranged on the outer peripheral surface side of the roll when the toilet paper is wound into a roll. In addition, the wound-side toilet paper is a surface that is arranged on the inner peripheral surface side of the roll when the toilet paper is wound into a roll.
FIG. 1 is a diagram illustrating the configuration of the toilet paper of the present invention. FIG. 1 shows an enlarged view of a toilet roll and a dotted-line circle portion of toilet paper constituting the toilet roll. As shown in FIG. 1, the toilet paper 1 has a roll
巻外側トイレットペーパーのエンボス高さは90μm以上210μm以下である。巻外側トイレットペーパーのエンボス高さは100μm以上であることが好ましく、130μm以上であることがより好ましく、190μm以上であることがさらに好ましい。また、巻外側トイレットペーパーのエンボス高さは210μm以下であることが好ましく、200μm以下であることが好ましい。本発明では、巻外側トイレットペーパーのエンボス高さを上記範囲内とすることにより、使用時の肌触り感を高めることができる。 The embossing height of the roll-out toilet paper is 90 μm or more and 210 μm or less. The emboss height of the roll-out toilet paper is preferably 100 μm or more, more preferably 130 μm or more, and further preferably 190 μm or more. Further, the emboss height of the roll-out toilet paper is preferably 210 μm or less, and more preferably 200 μm or less. In the present invention, by setting the emboss height of the roll-out toilet paper within the above range, it is possible to enhance the feeling of touch during use.
巻内側トイレットペーパーのエンボス高さは70μm以上170μm以下である。巻内側トイレットペーパーのエンボス高さは75μm以上あることが好ましく、90μm以上であることがより好ましく、110μm以上であることがさらに好ましく、150μm以上であることが特に好ましい。また、巻内側トイレットペーパーのエンボス高さは170μm以下であることが好ましく、160μm以下であることがより好ましい。 The embossing height of the roll-inside toilet paper is 70 μm or more and 170 μm or less. The embossing height of the roll-inside toilet paper is preferably 75 μm or more, more preferably 90 μm or more, further preferably 110 μm or more, and particularly preferably 150 μm or more. In addition, the emboss height of the inside roll toilet paper is preferably 170 μm or less, and more preferably 160 μm or less.
巻外側トイレットペーパーのエンボス高さと、巻内側トイレットペーパーのエンボス高さの差は10μm以上50μm以下である。エンボス高さの差は、12μm以上であることが好ましく、19μm以上であることがより好ましく、20μm以上であることがさらに好ましく、30μm以上であることがよりさらに好ましく、42μm以上であることが特に好ましい。また、エンボス高さの差は、50μm以下であることが好ましい。
本発明は、巻外側トイレットペーパーのエンボス高さと、巻内側トイレットペーパーのエンボス高さを上記範囲内とし、さらに、巻外側トイレットペーパーのエンボス高さと、巻内側トイレットペーパーのエンボス高さの差を上記範囲内とすることにより、トイレットペーパーの滑らかでふっくらとした風合いと、トイレットロールの良好な手触り感を両立することに成功したものである。
このような効果は、各トイレットペーパーに高さが異なるエンボスを形成することにより、トイレットロールを構成した際に、適度な間隔でトイレットペーパー同士が積層されることで得られるものと考えられる。すなわち、積層されたトイレットペーパー同士の間に適度な隙間が生じるために、圧縮性に優れた柔らかなトイレットロールが得られるものと考えられる。
The difference between the embossed height of the roll outer toilet paper and the embossed height of the roll inner toilet paper is 10 μm or more and 50 μm or less. The difference in embossing height is preferably 12 μm or more, more preferably 19 μm or more, further preferably 20 μm or more, further preferably 30 μm or more, and particularly preferably 42 μm or more. preferable. Further, the difference in emboss height is preferably 50 μm or less.
The present invention sets the embossing height of the roll outer toilet paper and the emboss height of the roll inner toilet paper within the above range, and further, the difference between the emboss height of the roll outer toilet paper and the emboss height of the roll inner toilet paper is described above. By setting the content within the range, the smooth and fluffy texture of the toilet paper and the good feel of the toilet roll are both succeeded.
It is considered that such an effect can be obtained by forming embossings having different heights on the respective toilet papers so that the toilet papers are laminated at appropriate intervals when the toilet roll is constructed. That is, it is considered that since a suitable gap is formed between the laminated toilet papers, a soft toilet roll having excellent compressibility can be obtained.
各トイレットペーパーのエンボス高さを測定する際には、まず、高精度形状測定システムKS−1100(KEYENCE社製)を用いて、巻外側トイレットペーパーと巻内側トイレットペーパーの表面(内側面)の高さデータを取得する。取得範囲は1cm角とし、画像取得ピッチは10μmとする。次いで、取得した画像データを、画像解析ソフトIOMate2007(株式会社アイ・スペック社製)に読み込み、得られた高さデータを256階調に分級する。穴などの欠陥部のデータを除去した後、横軸に階調、縦軸にデータの個数をとったグラフを作成する。作成したグラフについて、前後2点の合計5点で移動平均を取りグラフを描きなおし、新たに描きなおされたグラフの各点におけるグラフの傾きを、求める点とその前の点との2点の値を用いて算出する。得られた傾きのデータについて、前後3点の計7点で移動平均を取り、横軸を階調、縦軸を移動平均取得後の傾きとして、さらに別のグラフを作成する。得られた傾きのグラフの最下点以降の部分で最初に迎える変曲点の位置を目視判断し、その位置の横軸の階調を閾値として定める。次いで、定めた閾値を下回る部分について高さデータの加重平均を行い、得られた平均値を「非エンボス部分の平均高さ」とする。また、定めた閾値以上の部分についても高さデータの加重平均を行い、得られた平均値を「エンボス部分の平均高さ」とする。「エンボス部分の平均高さ」−「非エンボス部分の平均高さ」によって求められる値をエンボス高さとして定め、それぞれのプライについて算出する。 When measuring the embossing height of each toilet paper, first, the high-precision shape measuring system KS-1100 (manufactured by KEYENCE) is used to measure the height of the surface (inner surface) of the outer roll paper and the inner roll paper. Get the data. The acquisition range is 1 cm square, and the image acquisition pitch is 10 μm. Next, the acquired image data is read into the image analysis software IOMate2007 (manufactured by Eye Spec Co., Ltd.), and the obtained height data is classified into 256 gradations. After removing the data of defective portions such as holes, a graph is created with the horizontal axis representing gradation and the vertical axis representing the number of data. For the created graph, take a moving average at a total of 5 points, 2 points before and after, and redraw the graph, and calculate the slope of the graph at each point of the newly drawn graph. Calculate using the value. With respect to the obtained inclination data, a moving average is taken at a total of 7 points, 3 points before and after, and another graph is created with the horizontal axis as the gradation and the vertical axis as the inclination after the moving average is obtained. The position of the first inflection point that reaches after the lowest point of the obtained slope graph is visually determined, and the gradation of the horizontal axis at that position is set as the threshold value. Next, the weighted average of the height data is performed on the portion below the set threshold value, and the obtained average value is defined as the “average height of the non-embossed portion”. Further, the weighted average of the height data is performed also on the portion that is equal to or more than the set threshold value, and the obtained average value is set as the “average height of the embossed portion”. The value obtained by "the average height of the embossed portion"-"the average height of the non-embossed portion" is defined as the embossed height and calculated for each ply.
トイレットペーパーの坪量は、10g/m2以上であることが好ましく、12g/m2以上であることがより好ましく、15g/m2以上であることがさらに好ましい。一般的にトイレットペーパーの坪量の上限値は、25g/m2程度である。なお、本願明細書におけるトイレットペーパーの坪量は、2プライのトイレットペーパーを構成する1枚当たりの坪量を表す。巻外側トイレットペーパー及び巻内側トイレットペーパーの両方が各々上記範囲内であることが好ましい。 The basis weight of the toilet paper is preferably 10 g/m 2 or more, more preferably 12 g/m 2 or more, even more preferably 15 g/m 2 or more. Generally, the upper limit of the basis weight of toilet paper is about 25 g/m 2 . In addition, the grammage of the toilet paper in this-application specification represents the grammage per sheet which comprises 2 ply toilet paper. It is preferable that both the roll-out toilet paper and the roll-inside toilet paper fall within the above ranges.
巻外側トイレットペーパー及び巻内側トイレットペーパー各々の厚みは、50μm以上であることが好ましく、60μm以上であることがより好ましく、70μm以上であることがさらに好ましい。また、各トイレットペーパーの厚みは、100μm以下であることが好ましい。巻外側トイレットペーパー及び巻内側トイレットペーパーの両方が各々上記範囲内であることが好ましい。
本発明においてはトイレットペーパーの坪量と厚みを上記範囲内とすることにより、実用的強度を保持しつつも、滑らかな風合いと、ふっくらとした触感を発揮することができる。
The thickness of each of the roll-out toilet paper and the roll-inside toilet paper is preferably 50 μm or more, more preferably 60 μm or more, and further preferably 70 μm or more. The thickness of each toilet paper is preferably 100 μm or less. It is preferable that both the roll-out toilet paper and the roll-inside toilet paper fall within the above ranges.
In the present invention, by setting the basis weight and the thickness of the toilet paper within the above ranges, it is possible to exhibit a smooth texture and a soft touch while maintaining practical strength.
巻外側トイレットペーパー及び巻内側トイレットペーパーのそれぞれに0.5gf/cm2の圧力をかけた際の厚みをT0とした場合、巻外側トイレットペーパーのT0は、0.20mm以上であることが好ましく、0.45mm以下であることが好ましい。
また、巻内側トイレットペーパーのT0は、0.10mm以上であることが好ましく、0.40mm以下であることが好ましい。
If the thickness at the time of applying a pressure of 0.5 gf / cm 2 in each of Makisotogawa toilet paper and the take-inner toilet paper was T 0, T 0 of Makisotogawa toilet paper, not less than 0.20mm It is preferably 0.45 mm or less.
Further, T 0 of the wound-side toilet paper is preferably 0.10 mm or more, and preferably 0.40 mm or less.
さらに、巻外側トイレットペーパーのT0と巻内側トイレットペーパーのT0の差は、0.01mmよりも大きいことが好ましく、0.02mm以上であることがより好ましく、0.03mm以上であることがさらに好ましく、0.04mm以上であることが特に好ましい。本発明のトイレットペーパーにおいては、巻外側トイレットペーパーのT0と巻内側トイレットペーパーのT0の差が大きい点にも特徴がある。このようなT0の差も、トイレットペーパーの滑らかでふっくらとした風合いと、トイレットロールの良好な手触り感の両立に寄与しているものと考えられる。 Furthermore, the difference between T 0 of the roll-out toilet paper and T 0 of the roll-inside toilet paper is preferably larger than 0.01 mm, more preferably 0.02 mm or more, and more preferably 0.03 mm or more. More preferably, 0.04 mm or more is particularly preferable. The toilet paper of the present invention is also characterized in that the difference between T 0 of the roll-side toilet paper and T 0 of the roll-side toilet paper is large. It is considered that such a difference in T 0 also contributes to both the smooth and plump texture of the toilet paper and the good feel of the toilet roll.
本発明のトイレットペーパーに50gf/cm2の圧力をかけた際の厚みをTmとした場合、巻外側トイレットペーパー及び巻内側トイレットペーパーのそれぞれのTmは、0.05mm以上であることが好ましく、0.10mm以上であることがより好ましい。また、巻外側トイレットペーパー及び巻内側トイレットペーパーのそれぞれのTmは、0.30mm以下であることが好ましい。 When the thickness when the pressure of 50 gf/cm 2 is applied to the toilet paper of the present invention is T m , the T m of each of the outer roll paper and the inner roll paper is preferably 0.05 mm or more. , 0.10 mm or more is more preferable. Further, the T m of each of the roll-out toilet paper and the roll-inside toilet paper is preferably 0.30 mm or less.
ここで、上述したT0及びTmの値はKES FB3−AUTO−A自動化圧縮試験機(カトーテック株式会社製)を用いて測定することができる。具体的には、KES FB3−AUTO−A自動化圧縮試験機の2cm2の加圧板と受圧板間に10cm×20cmの大きさにカットしたサンプルを設置し、50秒/mmの速さで加圧板を下降させ、その際に変化する圧力とその時のサンプルの厚みを測定する。T0は圧力が0.5gf/cm2におけるサンプルの厚み(mm)であり、Tmは圧力が50gf/cm2におけるサンプルの厚み(mm)である。T0及びTmの値はエンボスの凹面(エンボスロールを押し当てた面)を加圧板側として10回の測定を行い、得られた測定データからHampel identifierの方法で異常値を除外し、平均値として算出した値である。なお、上記サンプルの測定はISO187に準拠した環境(温度23±1℃、相対湿度50±2%)で行う。 Here, the values of T 0 and T m described above can be measured using a KES FB3-AUTO-A automated compression tester (manufactured by Kato Tech Co., Ltd.). Specifically, a sample cut into a size of 10 cm×20 cm is installed between the pressure plate of 2 cm 2 and the pressure plate of the KES FB3-AUTO-A automated compression tester, and the pressure plate is pressed at a speed of 50 seconds/mm. Is lowered, and the pressure that changes at that time and the thickness of the sample at that time are measured. T 0 is the thickness (mm) of the sample at a pressure of 0.5 gf/cm 2 , and T m is the thickness (mm) of the sample at a pressure of 50 gf/cm 2 . The values of T 0 and T m were measured 10 times with the embossed concave surface (the surface against which the embossing roll was pressed) as the pressure plate side, and the abnormal values were excluded from the obtained measurement data by the method of Hampel identifier, and the average value was obtained. It is the value calculated as the value. In addition, the measurement of the sample is performed in an environment compliant with ISO187 (temperature 23±1° C., relative humidity 50±2%).
また、KES FB3−AUTO−A自動化圧縮試験機(カトーテック株式会社製)を用いて、圧縮かたさ(LC)、圧縮エネルギー(WC)、圧縮回復率(RC)を算出することもできる。圧縮かたさ(LC)は、押し込み深さに対する反発力の直線比例性を表すものであり、その値が大きいほど圧縮が固く反発性があることを示す。圧縮エネルギー(WC)は、圧縮時に要したエネルギーを表し、その値が大きければ圧縮されやすいことを示す。また、圧縮回復率(RC)は圧縮された状態から元に戻る際の回復性を示しており、100%に近いほど回復性があることを示す。 Moreover, the compression hardness (LC), compression energy (WC), and compression recovery rate (RC) can also be calculated using a KES FB3-AUTO-A automated compression tester (manufactured by Kato Tech Co., Ltd.). The compression hardness (LC) represents the linear proportionality of the repulsive force with respect to the indentation depth, and the larger the value, the harder the compression is and the more the repulsive force is. The compression energy (WC) represents the energy required for compression, and the larger the value, the easier the compression. Further, the compression recovery rate (RC) shows the recoverability when returning from the compressed state to the original state, and the closer to 100%, the more recoverable.
巻外側トイレットペーパーの圧縮かたさ(LC)は0.40以上0.80以下であることが好ましい。巻内側トイレットペーパーの圧縮かたさ(LC)は0.30以上0.70以下であることが好ましい。巻外側トイレットペーパーの圧縮かたさ(LC)と、巻内側トイレットペーパーの圧縮かたさ(LC)の差は、0.02以上であることが好ましく、0.03以上であることがより好ましく、0.04以上であることがさらに好ましい。 The compression hardness (LC) of the roll-side toilet paper is preferably 0.40 or more and 0.80 or less. The compression hardness (LC) of the roll-inside toilet paper is preferably 0.30 or more and 0.70 or less. The difference between the compression hardness (LC) of the roll-side toilet paper and the compression hardness (LC) of the roll-side toilet paper is preferably 0.02 or more, more preferably 0.03 or more, and 0.04. It is more preferable that the above is satisfied.
巻外側トイレットペーパーの圧縮エネルギー(WC)は、0.10gf・cm/cm2以上0.50gf・cm/cm2以下であることが好ましい。巻内側トイレットペーパーの圧縮エネルギー(WC)は、0.10gf・cm/cm2以上0.40gf・cm/cm2以下であることが好ましい。巻外側トイレットペーパーの圧縮エネルギー(WC)と、巻内側トイレットペーパーの圧縮エネルギー(WC)の差は、0.02gf・cm/cm2以上であることが好ましく、0.03gf・cm/cm2以上であることがより好ましく、0.05gf・cm/cm2以上であることがさらに好ましい。 The compression energy (WC) of the roll-out toilet paper is preferably 0.10 gf·cm/cm 2 or more and 0.50 gf·cm/cm 2 or less. The compression energy (WC) of the wound-side toilet paper is preferably 0.10 gf·cm/cm 2 or more and 0.40 gf·cm/cm 2 or less. And Makisotogawa toilet paper compression energy (WC), the difference in compression energy (WC) of the winding inside toilet paper, is preferably 0.02gf · cm / cm 2 or more, 0.03gf · cm / cm 2 or more Is more preferable, and 0.05 gf·cm/cm 2 or more is further preferable.
巻外側トイレットペーパーの圧縮回復率(RC1)は、33%以上53%以下であることが好ましい。巻内側トイレットペーパーの圧縮回復率(RC2)は、35%以上55%以下であることが好ましい。巻外側トイレットペーパーの圧縮回復率(RC1)と、巻内側トイレットペーパーの圧縮回復率(RC2)の差(RC1−RC2)は、−12%以上−1%以下であることがより好ましい。 The compression recovery rate (RC 1 ) of the wound outer toilet paper is preferably 33% or more and 53% or less. The compression recovery rate (RC 2 ) of the wound-side toilet paper is preferably 35% or more and 55% or less. The difference (RC 1 −RC 2 ) between the compression recovery rate (RC 1 ) of the roll-side toilet paper and the compression recovery rate (RC 2 ) of the roll-side toilet paper is more preferably −12% or more and −1% or less. preferable.
本発明のトイレットペーパーの巻外側トイレットペーパーの露出側表面のハンドフィール値(HF値)と、巻内側トイレットペーパーの露出側表面のハンドフィール値の平均は75.0以上であることが好ましく、78.0以上であることがより好ましい。なお、HF値の上限は特に限定されるものではないが、一般的に95.0以下であることが好ましい。 The average of the handfeel value (HF value) on the exposed side surface of the roll-side toilet paper of the present invention and the handfeel value on the exposed side surface of the roll-side toilet paper is preferably 75.0 or more, and 78 It is more preferably at least 0.0. The upper limit of the HF value is not particularly limited, but is generally preferably 95.0 or less.
ここで、ハンドフィール値(HF値)は、ティシューソフトネスアナライザー(Emtec Electronic GmbH社製)を用いて、以下の測定方法によって測定することができる。
まず、ティシューソフトネスアナライザーのサンプル台に、直径112.8mmの円形にカットしたサンプルを設置する。このサンプルに対し、ブレード付きローターを100mNの押し込み圧力をかけて上方から押し込む。その後、ブレード付きローターを回転数が2.0回転/秒となるように回転させ、その時の振動周波数を測定する。
また、直径112.8mmの円形にカットした別のサンプルに対し、ブレード付きローターを100mNと、60mNの圧力で押し込んだ際の上下方向の変形変位量を算出する。HF値は、振動周波数と変形変位量から算出される値であり、計算のアルゴリズムはTP IIを用いることができる。
HF値を算出する際は、巻外側トイレットペーパーの露出側表面と巻内側トイレットペーパーの露出側表面について測定をそれぞれ10回ずつ行い、得られた測定データからHampel identifierの方法で異常値を除外する。そして、各表面のHF値の平均値から、トイレットペーパーのHF値の平均値を算出する。
なお、上記サンプルの測定はISO187に準拠した環境(温度23±1℃、相対湿度50±2%)で行う。また、測定の際には、付属の説明書に従い標準サンプル(emetec ref.2X(nn.n))で校正し、アルゴリズムをTP IIに設定する。計算ソフトウェアとしてはemetec measurement system ver.3.22を使用する。
Here, the hand feel value (HF value) can be measured by the following measuring method using a tissue softness analyzer (manufactured by Emtec Electronic GmbH).
First, a circularly cut sample having a diameter of 112.8 mm is set on the sample stand of the tissue softness analyzer. A rotor with a blade is pressed into the sample from above by applying a pressing pressure of 100 mN. Then, the rotor with blades is rotated so that the rotation speed is 2.0 rotations/second, and the vibration frequency at that time is measured.
Further, the amount of deformation displacement in the up-down direction when the rotor with blades is pushed in at a pressure of 100 mN and 60 mN for another sample cut into a circle having a diameter of 112.8 mm is calculated. The HF value is a value calculated from the vibration frequency and the deformation displacement amount, and the calculation algorithm can use TP II.
When calculating the HF value, the exposed side surface of the roll outside toilet paper and the exposed side surface of the roll inside toilet paper are measured 10 times each, and the abnormal value is excluded from the obtained measurement data by the method of the Hampel identifier. .. Then, the average HF value of the toilet paper is calculated from the average HF value of each surface.
In addition, the measurement of the sample is performed in an environment compliant with ISO187 (temperature 23±1° C., relative humidity 50±2%). In addition, at the time of measurement, the standard sample (emetec ref.2X (nn.n)) is calibrated according to the attached instruction, and the algorithm is set to TP II. The calculation software is emetec measurement system ver. Use 3.22.
巻外側トイレットペーパー及び巻内側トイレットペーパー各々の長さ方向の引張強度は、0.90N/15mm以上であることが好ましく、1.00N/15mm以上であることがより好ましい。また、各トイレットペーパーの長さ方向の引張強度は、1.60N/15mm以下であることが好ましく、1.55N/15mm以下であることがより好ましい。
各トイレットペーパーの幅方向の引張強度は0.20N/15mm以上であることが好ましく、0.30N/15mm以上であることがより好ましい。また、各トイレットペーパーの幅方向の引張強度は0.70N/15mm以下であることが好ましく、0.60N/15mm以下であることがより好ましく、0.50N/15mm以下であることがさらに好ましい。
なお、巻外側トイレットペーパー及び巻内側トイレットペーパーの両方が各々上記範囲内であることが好ましい。
The tensile strength in the longitudinal direction of each of the roll-out toilet paper and the roll-inside toilet paper is preferably 0.90 N/15 mm or more, more preferably 1.00 N/15 mm or more. Further, the tensile strength of each toilet paper in the length direction is preferably 1.60 N/15 mm or less, and more preferably 1.55 N/15 mm or less.
The tensile strength in the width direction of each toilet paper is preferably 0.20 N/15 mm or more, and more preferably 0.30 N/15 mm or more. The tensile strength in the width direction of each toilet paper is preferably 0.70 N/15 mm or less, more preferably 0.60 N/15 mm or less, and further preferably 0.50 N/15 mm or less.
In addition, it is preferable that both the roll outer toilet paper and the roll inner toilet paper are within the above ranges.
各トイレットペーパーの引張強度の測定は、横型引張試験機(熊谷理器社製)を用いて行うことができる。この場合、幅が15mmのサンプルを用い、引張速度50mm/分の条件で測定を行う。本願明細書における引張強度は1プライのトイレットペーパーの引張強度であり、6サンプルの平均値である。なお、引張強度の測定は、ISO187に準拠した環境(温度23±1℃、相対湿度50±2%)で行う。 The tensile strength of each toilet paper can be measured using a horizontal tensile tester (manufactured by Kumagai Riki Co., Ltd.). In this case, a sample with a width of 15 mm is used, and the measurement is performed under the condition of a tensile speed of 50 mm/min. The tensile strength in this specification is the tensile strength of 1-ply toilet paper, and is the average value of 6 samples. The tensile strength is measured in an environment compliant with ISO187 (temperature 23±1° C., relative humidity 50±2%).
本発明では、巻外側トイレットペーパーのエンボスパターンと、巻内側トイレットペーパーのエンボスパターンは異なるものであることが好ましい。
巻外側トイレットペーパーのエンボスパターンでは、1個のエンボス直径は0.5mm以上2mm以下が好ましく、0.7mm以上1.3mm以上がより好ましい。またエンボス密度は10個/cm2以上30個/cm2以下が好ましく、15個/cm2以上25個/cm2以下がより好ましい。
巻内側トイレットペーパーのエンボスパターンでは、1個のエンボス直径は0.2mm以上1.0mm以下が好ましく、0.3mm以上0.6mm以下がより好ましい。またエンボス密度は20個/cm2以上100個/cm2以下が好ましく、40個/cm2以上80個/cm2以下がより好ましい。
巻外側トイレットペーパーと巻内側トイレットペーパーにおけるエンボス直径の差は0.2mm以上が好ましく、0.4mm以上がより好ましい。
In the present invention, it is preferable that the embossing pattern of the roll outer toilet paper and the emboss pattern of the roll inner toilet paper are different.
In the embossing pattern of the roll-out toilet paper, one embossing diameter is preferably 0.5 mm or more and 2 mm or less, more preferably 0.7 mm or more and 1.3 mm or more. The embossing density is preferably 10 pieces/cm 2 or more and 30 pieces/cm 2 or less, and more preferably 15 pieces/cm 2 or more and 25 pieces/cm 2 or less.
In the embossed pattern of the roll-inside toilet paper, one embossed diameter is preferably 0.2 mm or more and 1.0 mm or less, more preferably 0.3 mm or more and 0.6 mm or less. The embossing density is preferably 20 pieces/cm 2 or more and 100 pieces/cm 2 or less, and more preferably 40 pieces/cm 2 or more and 80 pieces/cm 2 or less.
The difference in emboss diameter between the roll-out toilet paper and the roll-in toilet paper is preferably 0.2 mm or more, more preferably 0.4 mm or more.
巻外側トイレットペーパーのエンボスパターンの例としては、例えば図2に記載したようなエンボスパターンを挙げることができる。また、巻内側トイレットペーパーのエンボスパターンの例としては、例えば図3に記載したようなエンボスパターンを挙げることができる。 As an example of the embossing pattern of the roll-side toilet paper, the embossing pattern as shown in FIG. 2 can be cited. Moreover, as an example of the embossing pattern of the roll-inside toilet paper, for example, the embossing pattern as shown in FIG. 3 can be cited.
(繊維原料)
本発明のトイレットペーパーは、繊維原料を含むスラリーを抄紙することによって得られる。繊維原料としては、パルプを用いることが好ましい。パルプとしては、木材パルプ、非木材パルプ、脱墨パルプを挙げることができる。木材パルプとしては例えば、広葉樹パルプ(広葉樹クラフトパルプ(LKP))、針葉樹パルプ(針葉樹クラフトパルプ(NKP))、サルファイトパルプ(SP)、溶解パルプ(DP)、ソーダパルプ(AP)、未晒しクラフトパルプ(UKP)、酸素漂白クラフトパルプ(OKP)等の化学パルプ等が挙げられる。また、セミケミカルパルプ(SCP)、ケミグラウンドウッドパルプ(CGP)等の半化学パルプ、砕木パルプ(GP)、サーモメカニカルパルプ(TMP、BCTMP)等の機械パルプ等が挙げられるが、特に限定されない。非木材パルプとしてはコットンリンターやコットンリント等の綿系パルプ、麻、麦わら、バガス等の非木材系パルプ、ホヤや海草等から単離されるセルロース、キチン、キトサン等が挙げられるが、特に限定されない。脱墨パルプとしては古紙を原料とする脱墨パルプが挙げられるが、特に限定されない。パルプは上記の1種を単独で用いてもよいし、2種以上混合して用いてもよい。
(Fiber raw material)
The toilet paper of the present invention is obtained by making a slurry containing a fiber raw material. Pulp is preferably used as the fiber raw material. Examples of pulp include wood pulp, non-wood pulp, and deinked pulp. Examples of the wood pulp include hardwood pulp (hardwood kraft pulp (LKP)), softwood pulp (softwood kraft pulp (NKP)), sulfite pulp (SP), dissolving pulp (DP), soda pulp (AP), unbleached kraft. Examples thereof include chemical pulp such as pulp (UKP) and oxygen bleached kraft pulp (OKP). In addition, semi-chemical pulp (SCP), semi-chemical pulp such as chemiground wood pulp (CGP), mechanical pulp such as ground wood pulp (GP), thermomechanical pulp (TMP, BCTMP), and the like are mentioned, but not particularly limited. Examples of non-wood pulp include cotton-based pulp such as cotton linter and cotton lint, non-wood-based pulp such as hemp, straw and bagasse, cellulose isolated from ascidian and seaweed, chitin, chitosan and the like, but are not particularly limited. .. Examples of the deinked pulp include deinked pulp made from recycled paper, but are not particularly limited. As the pulp, one type of the above may be used alone, or two or more types may be mixed and used.
繊維原料としては、針葉樹パルプ及び広葉樹パルプから選択される少なくとも1種を用いることが好ましく、針葉樹パルプを用いることが好ましい。中でも、本発明においては、針葉樹パルプと広葉樹パルプを併用することが好ましく、針葉樹クラフトパルプ(NKP)と広葉樹クラフトパルプ(LKP)を併用することがより好ましい。 As the fiber raw material, it is preferable to use at least one selected from softwood pulp and hardwood pulp, and it is preferable to use softwood pulp. Among them, in the present invention, it is preferable to use the softwood pulp and the hardwood pulp together, and it is more preferable to use the softwood kraft pulp (NKP) and the hardwood kraft pulp (LKP) together.
繊維原料として針葉樹パルプが用いられる場合は、針葉樹パルプの含有量は、トイレットペーパーに含まれるパルプ成分の全質量に対して、20質量%以上であることが好ましく、30質量%以上であることがより好ましく、40質量%以上であることがさらに好ましい。また、針葉樹パルプの含有量は、トイレットペーパーに含まれるパルプ成分の全質量に対して、80質量%以下であることが好ましい。針葉樹パルプの含有量を上記範囲内とすることにより、トイレットペーパーのHF値や圧縮性等を所望の範囲内とすることが容易になる。 When softwood pulp is used as the fiber raw material, the content of softwood pulp is preferably 20% by mass or more, and more preferably 30% by mass or more, based on the total mass of pulp components contained in the toilet paper. More preferably, it is more preferably 40 mass% or more. The content of the softwood pulp is preferably 80% by mass or less based on the total mass of the pulp components contained in the toilet paper. By setting the content of the softwood pulp within the above range, it becomes easy to set the HF value, the compressibility and the like of the toilet paper within the desired range.
繊維原料としては、針葉樹パルプと広葉樹パルプを併用することが好ましい。すなわち、トイレットペーパーには、針葉樹パルプの他に広葉樹パルプがさらに含まれることが好ましい。広葉樹パルプの含有量は、トイレットペーパーに含まれるパルプ成分の全質量に対して、10質量%以上であることが好ましく、20質量%以上であることがより好ましく、30質量%以上であることがさらに好ましい。また、広葉樹パルプの含有量は、トイレットペーパーに含まれるパルプ成分の全質量に対して、70質量%以下であることが好ましい。広葉樹パルプの含有量を上記範囲内とすることにより、トイレットペーパーのHF値や圧縮性等を所望の範囲内とすることが容易になる。 As the fiber raw material, it is preferable to use softwood pulp and hardwood pulp in combination. That is, it is preferable that the toilet paper further contains hardwood pulp in addition to softwood pulp. The content of hardwood pulp is preferably 10% by mass or more, more preferably 20% by mass or more, and more preferably 30% by mass or more, based on the total mass of pulp components contained in the toilet paper. More preferable. Further, the content of the hardwood pulp is preferably 70% by mass or less based on the total mass of the pulp components contained in the toilet paper. By setting the content of the hardwood pulp within the above range, it becomes easy to set the HF value, the compressibility and the like of the toilet paper within the desired range.
繊維原料として用いる針葉樹パルプの長さ加重平均繊維長は1.6mm以上であることが好ましく、1.8mm以上であることがより好ましく、2.0mm以上であることがさらに好ましい。また、針葉樹パルプの長さ加重平均繊維長は2.5mm以下であることが好ましい。
繊維原料として用いる広葉樹パルプの長さ加重平均繊維長は0.5mm以上であることが好ましく、0.6mm以上であることがより好ましく、0.65mm以上であることがさらに好ましい。また、広葉樹パルプの長さ加重平均繊維長は1.0mm以下であることが好ましい。
繊維原料の長さ加重平均繊維長を上記範囲内とすることにより、トイレットペーパーのHF値や圧縮性等を所望の範囲内とすることが容易になる。なお、上記繊維原料の長さ加重平均繊維長は、原料としての繊維長であり、叩解処理等を施す前の繊維長である。
The length-weighted average fiber length of the softwood pulp used as the fiber raw material is preferably 1.6 mm or more, more preferably 1.8 mm or more, and further preferably 2.0 mm or more. The length-weighted average fiber length of the softwood pulp is preferably 2.5 mm or less.
The length-weighted average fiber length of the hardwood pulp used as the fiber raw material is preferably 0.5 mm or more, more preferably 0.6 mm or more, and further preferably 0.65 mm or more. The length-weighted average fiber length of the hardwood pulp is preferably 1.0 mm or less.
By setting the length-weighted average fiber length of the fiber raw material within the above range, it becomes easy to set the HF value and compressibility of the toilet paper within a desired range. The length-weighted average fiber length of the fiber raw material is the fiber length as a raw material, and is the fiber length before the beating treatment and the like.
トイレットペーパー中に含有される繊維成分(パルプ成分)のカナディアン・フリーネス・スタンダード(C.F.S)で表されるフリーネスは400ml以上であることが好ましく、450ml以上であることがより好ましく、500ml以上であることがさらに好ましい。また、フリーネスは700ml以下であることが好ましい。繊維成分のフリーネスを上記範囲内とすることにより、トイレットペーパーのHF値や圧縮性等を所望の範囲内とすることが容易になり、滑らかな風合いとふっくらとした触感が両立したトイレットペーパーが得られる。なお、繊維成分のフリーネスは後述するように、叩解条件を制御することにより調整することができる。 The freeness represented by Canadian Freeness Standard (CFS) of the fiber component (pulp component) contained in the toilet paper is preferably 400 ml or more, more preferably 450 ml or more, and 500 ml. It is more preferable that the above is satisfied. The freeness is preferably 700 ml or less. By setting the freeness of the fiber component within the above range, it becomes easy to set the HF value and compressibility of the toilet paper within the desired range, and a toilet paper having both a smooth texture and a soft touch is obtained. To be The freeness of the fiber component can be adjusted by controlling the beating conditions, as described later.
(任意成分)
本発明のトイレットペーパーには、繊維原料の他に任意成分が含まれていてもよい。任意成分としては、例えば、乾燥紙力剤、湿潤紙力剤、柔軟剤等を挙げることができる。乾燥紙力剤としては、例えば、カチオン化澱粉、ポリアクリルアミド(PAM)、カルボキシメチルセルロース(CMC)等を挙げることができる。湿潤紙力剤としては、ポリアミドエピクロロヒドリン、尿素、メラミン、熱架橋性ポリアクリルアミド等を挙げることができる。柔軟剤としては、例えば、アニオン系界面活性剤、ノニオン系界面活性剤、カチオン系界面活性剤等を挙げることができる。上記の任意成分は1種単独で用いてもよく、2種以上を併用してもよい。
(Arbitrary component)
The toilet paper of the present invention may contain optional components in addition to the fiber raw material. Examples of the optional component include a dry paper strength agent, a wet paper strength agent, and a softening agent. Examples of the dry paper strength agent include cationized starch, polyacrylamide (PAM), carboxymethyl cellulose (CMC) and the like. Examples of the wet paper strength agent include polyamide epichlorohydrin, urea, melamine, and heat-crosslinkable polyacrylamide. Examples of the softening agent include anionic surfactants, nonionic surfactants, cationic surfactants and the like. The above optional components may be used alone or in combination of two or more.
トイレットペーパーに乾燥紙力剤が含まれている場合は、乾燥紙力剤の含有量は、トイレットペーパーに含まれる繊維成分の100質量部に対して、0.01質量部以上0.50質量部以下であることが好ましい。
トイレットペーパーに湿潤紙力剤が含まれている場合は、湿潤紙力剤の含有量は、トイレットペーパーに含まれる繊維成分の100質量部に対して、0.001質量部以上0.10質量部以下であることが好ましい。
また、トイレットペーパーに柔軟剤が含まれている場合は、柔軟剤の含有量は、トイレットペーパーに含まれる繊維成分の100質量部に対して、0.01質量部以上0.50質量部以下であることが好ましい。
When the toilet paper contains a dry paper strength agent, the content of the dry paper strength agent is 0.01 parts by mass or more and 0.50 parts by mass with respect to 100 parts by mass of the fiber component contained in the toilet paper. The following is preferable.
When the toilet paper contains a wet strength agent, the content of the wet strength agent is 0.001 parts by mass or more and 0.10 parts by mass or more with respect to 100 parts by mass of the fiber component contained in the toilet paper. The following is preferable.
When the toilet paper contains a softening agent, the content of the softening agent is 0.01 parts by mass or more and 0.50 parts by mass or less with respect to 100 parts by mass of the fiber component contained in the toilet paper. Preferably.
(トイレットペーパーの製造方法)
本発明のトイレットペーパーの製造方法は、繊維原料を含むスラリーを抄紙し、1プライのトイレットペーパーウェブを得る工程と、1プライのトイレットペーパーウェブを積層する工程(以下、貼り合わせ工程ともいう)と、巻外側トイレットペーパーウェブと巻内側トイレットペーパーウェブにエンボス加工を施す工程と、巻外側トイレットペーパーと巻内側トイレットペーパーを再度積層する工程を含む。
(Method of manufacturing toilet paper)
The method for producing toilet paper of the present invention comprises a step of making a slurry containing a fiber raw material to obtain a 1-ply toilet paper web, and a step of laminating a 1-ply toilet paper web (hereinafter, also referred to as a bonding step). , A step of embossing the roll-outside toilet paper web and the roll-inside toilet paper web, and a step of re-laminating the roll-outside toilet paper and the roll-inside toilet paper.
1プライのトイレットペーパーウェブを得る工程の前には、繊維原料を漂白する工程を含んでもよい。漂白工程で使用する漂白剤としては、酸素系漂白剤や塩素系漂白剤等の公知の漂白剤を挙げることができる。 The step of bleaching the fiber raw material may be included before the step of obtaining the one-ply toilet paper web. Examples of the bleaching agent used in the bleaching step include known bleaching agents such as oxygen bleaching agents and chlorine bleaching agents.
1プライのトイレットペーパーウェブを得る工程は、繊維原料を含むスラリーを得る工程を含む。スラリーを得る工程においては、繊維原料を叩解する工程を含むことが好ましい。叩解工程においては、例えば、ダブルディスクリファイナー等を用いて叩解処理を施すことができる。この時、針葉樹パルプと広葉樹パルプをそれぞれ単独で叩解してもよいし、混合させた後に叩解してもよい。 The step of obtaining a one-ply toilet paper web includes the step of obtaining a slurry containing a fiber raw material. The step of obtaining the slurry preferably includes a step of beating the fiber raw material. In the beating step, for example, a beating process can be performed using a double disc refiner or the like. At this time, the softwood pulp and the hardwood pulp may be beaten individually, or may be beaten after being mixed.
1プライのトイレットペーパーウェブを得る工程は、繊維原料を含むスラリーを抄紙する工程を含む。抄紙する工程で用いられる抄紙機としては、例えば、サクションブレストフォーマー(円網タイプ、長網タイプ)、ツインワイヤーフォーマー、円網フォーマー(Cラップ、Sラップ)、クレセントフォーマー等の抄紙機を挙げることができる。 The step of obtaining a one-ply toilet paper web includes a step of papermaking a slurry containing a fiber raw material. As a paper machine used in the step of making paper, for example, a suction breast former (cylinder type, Fourdrinier type), twin wire former, cylinder former (C lap, S lap), crescent former, etc. Can be mentioned.
抄紙する工程では、網状のワイヤー上に繊維原料を含むスラリーが供給されてパルプの薄層が形成される。その後、プレスパートに向かって移送されながら、パルプの薄層の水分が網の下へ抜かれることでパルプの薄層は脱水される。このような工程を脱水工程と呼ぶこともある。一般に、ワイヤーは、金属またはプラスチック製の網を環にしたものである。 In the papermaking step, a slurry containing a fiber raw material is supplied onto a mesh wire to form a thin layer of pulp. After that, while being transferred to the press part, the moisture of the thin layer of pulp is drained to the bottom of the net to dehydrate the thin layer of pulp. Such a process may be called a dehydration process. In general, the wire is a ring made of metal or plastic mesh.
抄紙する工程では、例えば、針葉樹パルプと広葉樹パルプを混合したパルプスラリーを抄紙して均一な1つの層として湿紙を形成する方法、もしくは、針葉樹パルプ層と広葉樹パルプ層を抄き合わせて1枚の湿紙を形成する方法があるが、いずれの手法を採用してもよい。 In the step of papermaking, for example, a method of forming a wet paper as a uniform layer by making a pulp slurry in which softwood pulp and hardwood pulp are mixed, or a softwood pulp layer and a hardwood pulp layer are combined to form one sheet. There is a method for forming the wet paper web, but any method may be adopted.
脱水工程の後、湿紙はワイヤーからフェルトへと移動する。フェルトを介してプレスロールで圧力を加えることにより、湿紙はさらに機械的に搾水される。これを、プレス工程あるいは搾水工程と呼ぶこともある。 After the dewatering process, the wet paper web moves from the wire to the felt. The wet paper web is further mechanically squeezed by applying pressure with a press roll through the felt. This may be called a pressing process or a water squeezing process.
抄紙する工程は、搾水工程の後に、さらに乾燥工程を含むことが好ましい。乾燥工程は、例えば、湿紙に向かって熱風を吹き付ける工程、もしくは、ドライヤシリンダーを外周面に圧着させる工程であることが好ましい。 It is preferable that the paper making step further includes a drying step after the water squeezing step. The drying step is preferably, for example, a step of blowing hot air toward the wet paper, or a step of pressing the dryer cylinder onto the outer peripheral surface.
抄紙する工程では、乾燥工程の後にクレープを付与する工程が設けられることが好ましい。クレープはドクターブレードに原紙を衝突させ、紙の流れ方向に圧縮することで付与することができる。また、巻取リールとドライヤシリンダーとに速度差を設けることにより、所定のクレープ率とすることができる。 In the paper making step, it is preferable to provide a step of applying a crepe after the drying step. The crepe can be applied by colliding the base paper with a doctor blade and compressing it in the paper flow direction. Further, a predetermined crepe rate can be obtained by providing a speed difference between the take-up reel and the dryer cylinder.
クレープ付与工程の後には、原紙巻取り工程が設けられてもよい。原紙巻取り工程では、上記の工程を経て仕上げられたトイレットペーパーウェブ(薄葉紙)が巻取られることで、1プライの原紙巻取が得られる。この際、トイレットペーパーウェブ(薄葉紙)のドライヤシリンダーに圧着された面が原紙巻取の外周面となるように巻取ることが好ましい。 A raw paper winding step may be provided after the crepe applying step. In the base paper winding step, the toilet paper web (thin paper) finished through the above steps is wound to obtain a one-ply base paper winding. At this time, it is preferable to wind the toilet paper web (thin paper) so that the surface of the toilet paper web that is pressed against the dryer cylinder is the outer circumferential surface of the raw paper winding.
1プライのトイレットペーパーウェブを貼り合わせる工程は、原紙巻取2本をプライマシンにかけて巻き解き、2枚の原紙を積層する工程が含まれる。なお、貼り合せた後にカレンダー処理する工程が設けられてもよい。 The step of laminating the 1-ply toilet paper web includes a step of unwinding two rolls of base paper using a ply machine to unwind the two base papers. Note that a step of calendering after bonding may be provided.
エンボス加工を施す工程は、巻外側トイレットペーパーに、エンボス高さが90μm以上210μm以下のエンボス加工を施す(A)工程と、巻内側トイレットペーパーに、エンボス高さが90μm以上170μm以下のエンボス加工を施す(B)工程を含む。(A)工程で得られた巻外側トイレットペーパーのエンボス高さと、(B)工程で得られた巻内側トイレットペーパーのエンボス高さの差が10μm以上50μm以下となる。 The embossing process includes embossing the outer roll of toilet paper with an embossing height of 90 μm or more and 210 μm or less (A) and the embossing of the inner roll of toilet paper with an embossing height of 90 μm or more and 170 μm or less. The step (B) of applying is included. The difference between the embossed height of the roll-out toilet paper obtained in the step (A) and the emboss height of the roll-inside toilet paper obtained in the step (B) is 10 μm or more and 50 μm or less.
エンボス加工は、エンボスパターンを構成する凸構造が設置されたエンボスロールとラバーロールとの間にトイレットペーパーウェブを通し、エンボスパターンを型押しすることによって行われる。エンボスロールのエンボス高さや、押し込み量、押し込み圧を変更することによって、上記範囲のエンボス高さを有するエンボス形状を形成することができる。
ここで、巻外側トイレットペーパーのエンボス加工に用いるエンボスロールには凸構造高さ0.75mm以上0.85mm以下の凸構造が設置されていることが好ましい。また、巻外側トイレットペーパーのエンボス加工に用いるエンボスロールには、凸構造密度(エンボス密度)10個/cm2以上30個/cm2以下の凸構造が設置されていることが好ましい。そして、巻外側トイレットペーパーのエンボス加工では、上記のエンボスロールを8kgf/cm2以上20kgf/cm2以下の圧力で型押しすることが好ましい。
また、巻内側トイレットペーパーのエンボス加工に用いるエンボスロールには凸構造高さ0.70mm以上0.80mm以下の凸構造が設置されていることが好ましい。また、巻内側トイレットペーパーのエンボス加工に用いるエンボスロールには、凸構造密度(エンボス密度)50個/cm2以上70個/cm2以下の凸構造が設置されていることが好ましい。そして、巻内側トイレットペーパーのエンボス加工では、上記のエンボスロールを5gf/cm2以上15kgf/cm2以下の圧力で型押しすることが好ましい。
The embossing is performed by passing a toilet paper web between an embossing roll having a convex structure forming the embossing pattern and a rubber roll and embossing the embossing pattern. By changing the embossing height of the embossing roll, the pushing amount, and the pushing pressure, an embossed shape having an embossing height within the above range can be formed.
Here, it is preferable that a convex structure having a convex structure height of 0.75 mm or more and 0.85 mm or less is provided on the embossing roll used for embossing the outside roll toilet paper. Further, it is preferable that the embossing roll used for the embossing of the roll-out toilet paper has a convex structure having a convex structure density (emboss density) of 10 pieces/cm 2 or more and 30 pieces/cm 2 or less. In the embossing of the roll-out toilet paper, it is preferable that the embossing roll is embossed with a pressure of 8 kgf/cm 2 or more and 20 kgf/cm 2 or less.
In addition, it is preferable that the embossing roll used for embossing the wound-side toilet paper is provided with a convex structure having a convex structure height of 0.70 mm or more and 0.80 mm or less. Further, it is preferable that the embossing roll used for the embossing of the wound-side toilet paper has a convex structure having a convex structure density (emboss density) of 50/cm 2 or more and 70/cm 2 or less. Then, in the embossing of the roll-inside toilet paper, it is preferable that the embossing roll is embossed with a pressure of 5 gf/cm 2 or more and 15 kgf/cm 2 or less.
上記エンボス工程の後には、巻外側トイレットペーパーと、巻内側トイレットペーパーを再度積層する工程を含む。この場合、エンボスの凸面(エンボスロールを押し当てた面とは反対側の面)が内側で向かい合うようにして貼り合せを行うことが好ましい。 After the embossing step, a step of stacking the roll-out toilet paper and the roll-inside toilet paper again is included. In this case, it is preferable that the embossing convex surfaces (surfaces on the opposite side to the surface on which the embossing roll is pressed) face each other on the inner side to perform the bonding.
上記貼り合わせ工程では、1プライのトイレットペーパーウェブを2枚以上積層し、貼り合わせを行う。この工程では、例えば、原紙を重ねた後に製品の端部となる部分に幅狭のコンタクトエンボスを付与することによって貼り合わせることができる。その際、エンボスロールによって押し込まれた面を外側にして貼り合わせる方が、手触り感の観点から好ましい。 In the bonding step, two or more 1-ply toilet paper webs are laminated and bonded. In this step, for example, the base papers can be laminated and then laminated by applying a narrow contact emboss to the end portion of the product. At that time, it is preferable from the viewpoint of the feeling of touch that it is preferable that the surface pressed by the embossing roll is placed outside.
貼り合わせ工程の後には、さらに巻取り工程が設けられる。この巻取り工程においては、所定の製品長を満たすように、所定の長さ分の巻取りを行う。そして、得られた巻取ロールを所定の幅に断裁する。
巻き取り工程では、例えばマンドレルシャフトを有するワインダーを用いて、以下のように行うことができる。(1)まず巻芯となる紙管をマンドレルシャフトに挿入し、固定する。(2)前記紙管に接着剤を付着させ、紙管にトイレットペーパーの始端部を接着固定する。(3)マンドレルシャフトを回転させることにより、2プライのトイレットペーパーを製品長さ分だけ芯管に巻き取る。
A winding process is further provided after the laminating process. In this winding step, winding for a predetermined length is performed so as to satisfy a predetermined product length. Then, the obtained winding roll is cut into a predetermined width.
The winding step can be performed as follows using a winder having a mandrel shaft, for example. (1) First, insert the paper tube to be the core into the mandrel shaft and fix it. (2) An adhesive is attached to the paper tube, and the starting end portion of the toilet paper is adhesively fixed to the paper tube. (3) By rotating the mandrel shaft, the 2-ply toilet paper is wound around the core tube by the product length.
(トイレットロール)
本発明は、上述したトイレットペーパーをロール状にしたトイレットロールに関するものでもある。本発明のトイレットロールは、上述したトイレットペーパーから構成されるものであるため、手触り感に優れている。手触り感に優れていることは、トイレットロールを掴んだ際に柔らかく、圧縮性に優れていることを意味する。
(Toilet roll)
The present invention also relates to a toilet roll obtained by rolling the above-mentioned toilet paper. Since the toilet roll of the present invention is composed of the above-mentioned toilet paper, it has an excellent feel. The excellent feel means that the toilet roll is soft when it is gripped and has excellent compressibility.
本発明のトイレットロールの巻き長さは25m以上60m以下であることが好ましい。ここで、トイレットロールの巻き長さは、2プライのトイレットロールであれば、トイレットペーパーを2枚重ねた2枚単位の巻き長さである。 The winding length of the toilet roll of the present invention is preferably 25 m or more and 60 m or less. Here, the winding length of the toilet roll is a winding length of two sheets of two sheets of toilet paper in the case of a two-ply toilet roll.
本発明のトイレットロールの巻き径(外径)は、110mm以上120mm以下であることが好ましい。ここで、トイレットロールの巻き径(外径)は、図4においてRで表されている。 The toilet roll of the present invention preferably has a winding diameter (outer diameter) of 110 mm or more and 120 mm or less. Here, the winding diameter (outer diameter) of the toilet roll is represented by R in FIG.
また、本発明のトイレットロールは、紙管にトイレットペーパーを巻いてなるものである。紙管径は30mm以上40mm以下であることが好ましい。トイレットロールの紙管径は、図4においてSで表されている。 Further, the toilet roll of the present invention is obtained by winding a toilet paper on a paper tube. The paper tube diameter is preferably 30 mm or more and 40 mm or less. The paper tube diameter of the toilet roll is represented by S in FIG.
本発明のトイレットロールの巻き密度は、0.16m/cm2以上であることが好ましく、0.20m/cm2以上であることがより好ましく、0.30m/cm2以上であることがさらに好ましく0.60以上であることが特に好ましい。また、トイレットロールの巻き密度は、1.40m/cm2以下であることが好ましく、1.08m/cm2以下であることがより好ましく、0.99m/cm2以下であることがさらに好ましく、0.80m/cm2以下であることがよりさらに好ましい。
中でも、巻き長さ25mのトイレットロールにおいては、巻き密度が0.60m/cm2以上0.68m/cm2以下であることが好ましく、巻き長さ30mのトイレットロールにおいては、巻き密度が0.73m/cm2以上0.82m/cm2以下であることが好ましく、巻き長さ45mのトイレットロールにおいては、0.90m/cm2以上1.08m/cm2以下であることが好ましく、巻き長さ60mのトイレットロールにおいては、巻き密度が1.25g/m2以上1.45g/m2以下であることが好ましい。
Winding density of toilet rolls of the present invention is preferably 0.16 m / cm 2 or more, more preferably 0.20 m / cm 2 or more, still more preferably 0.30 m / cm 2 or more It is particularly preferably 0.60 or more. Also, toilet winding density of the trawl is preferably at 1.40 m / cm 2 or less, more preferably 1.08 m / cm 2 or less, further preferably 0.99 m / cm 2 or less, It is even more preferably 0.80 m/cm 2 or less.
Above all, in the toilet roll having a winding length of 25 m, the winding density is preferably 0.60 m/cm 2 or more and 0.68 m/cm 2 or less, and in the toilet roll having a winding length of 30 m, the winding density is 0. preferably 73m / cm 2 or more 0.82 / cm 2 or less, in the toilet rolls in winding length 45 m, is preferably 0.90 m / cm 2 or more 1.08 m / cm 2 or less, the winding length In a 60 m-long toilet roll, the winding density is preferably 1.25 g/m 2 or more and 1.45 g/m 2 or less.
トイレットロールの巻き密度は、2プライのトイレットロールの巻き長さの2倍の長さを紙管の断面積を除いたロールの断面積(図4におけるP(ドット状模様部分))で除すことにより算出した値である。すなわち、巻き密度は下記の式で算出することができる。
巻き密度(m/cm2)=巻き長さ×2/ロール断面積
The roll density of the toilet roll is obtained by dividing the double length of the roll length of the 2-ply toilet roll by the roll cross-sectional area (P (dot-shaped pattern portion) in FIG. 4) excluding the cross-sectional area of the paper tube. It is the value calculated by That is, the winding density can be calculated by the following formula.
Winding density (m/cm 2 )=winding length×2/roll cross-sectional area
以下に実施例と比較例を挙げて本発明の特徴をさらに具体的に説明する。以下の実施例に示す材料、使用量、割合、処理内容、処理手順等は、本発明の趣旨を逸脱しない限り適宜変更することができる。したがって、本発明の範囲は以下に示す具体例により限定的に解釈されるべきものではない。 The features of the present invention will be described more specifically below with reference to Examples and Comparative Examples. The materials, usage amounts, ratios, processing contents, processing procedures, and the like shown in the following examples can be appropriately changed without departing from the spirit of the present invention. Therefore, the scope of the present invention should not be limitedly interpreted by the following specific examples.
(実施例1)
パルプ成分(100質量%)のうち、広葉樹クラフトパルプ(以下「LBKP」)が70質量%、針葉樹クラフトパルプ(以下「NBKP」)が30質量%となるようにパルプスラリーを調製した。さらに、パルプスラリーには、柔軟剤(星光PMC株式会社製)を0.1質量%(対パルプ成分質量比)及びカチオン化デンプン(王子コンスターチ社製)を0.01質量%となるように添加した。このように調製したパルプスラリーを、ツインワイヤーヤンキーマシンを用いて抄造しトイレットペーパーウェブを得た。
(Example 1)
A pulp slurry was prepared so that 70% by mass of hardwood kraft pulp (hereinafter "LBKP") and 30% by mass of softwood kraft pulp (hereinafter "NBKP") were contained in the pulp component (100% by mass). Further, to the pulp slurry, 0.1% by mass of a softening agent (manufactured by SEIKO PMC Co., Ltd.) (mass ratio to pulp component) and 0.01% by mass of cationized starch (manufactured by Oji Konstarch Co., Ltd.) were added. did. The pulp slurry thus prepared was made into paper using a twin wire Yankee machine to obtain a toilet paper web.
得られた原紙巻取2本をプライマシンにかけ、巻き解きながら2プライへの貼り合せを行った。貼り合せ後、7kg/cm2の線圧でカレンダー処理して再度巻取り、2プライのトイレットペーパーウェブ巻取を得た。 The two rolls of base paper thus obtained were put on a ply machine, and while unwinding, the two plies were laminated. After the lamination, a calendar treatment was performed with a linear pressure of 7 kg/cm 2 and the roll was rewound to obtain a two-ply toilet paper web roll.
得られた2プライのトイレットペーパーウェブ巻取を加工機にかけ、巻き解きながらトイレットペーパーウェブ表面にエンボス加工を施した。エンボス加工工程では、エンボスパターンを構成する凸構造が設置されたスチール製のエンボスロールとラバーロールとの間にトイレットペーパーウェブを通し、エンボスパターンを型押しすることによってエンボスを形成した。
エンボス加工工程では、巻外側トイレットペーパーと巻内側トイレットペーパーでそれぞれ異なるエンボスパターンを形成した。巻外側トイレットペーパーには凸構造高さ0.80mm、凸構造密度(エンボス密度)21.2個/cm2のエンボスパターンAを有するエンボスロールを14kgf/cm2の圧力で型押してエンボスを形成した。また、巻内側トイレットペーパーには凸構造高さ0.75mm、凸構造密度(エンボス密度)60個/cm2のエンボスパターンBを有するエンボスロールを12kgf/cm2の圧力で型押してエンボスを形成した。
エンボス加工工程後は巻外側トイレットペーパーと巻内側トイレットペーパーのエンボスの凸面が内側で向かい合うようにして巻内側トイレットペーパーから巻外側トイレットペーパー側へ突出するようにコンタクトエンボスを形成し、2プライへの貼り合せを行った。その後、幅方向に横切る破断用ミシン目を長手方向に沿って一定間隔で形成し、表1に記載の巻き長さのロール状トイレットロールを得た。得られたトイレットロールの巻き径(図4におけるR)は表1の通りであった。得られたトイレットロールを所定の幅に断裁することで2プライのトイレットロール(トイレットロール製品)を得た。
The obtained 2-ply toilet paper web winding was applied to a processing machine, and the surface of the toilet paper web was embossed while being unwound. In the embossing step, a toilet paper web was passed between a rubber roll and a steel embossing roll having a convex structure forming the embossing pattern, and the embossing pattern was embossed to form the embossing pattern.
In the embossing process, different embossing patterns were formed on the roll outer toilet paper and the roll inner toilet paper, respectively. Makisotogawa toilet paper convex structure height 0.80 mm, to form embossed by pressing convex structure Density (embossed density) type an embossing roll having 21.2 cells / cm 2 of the embossing pattern A at a pressure of 14 kgf / cm 2 .. In addition, an embossing roll having an embossing pattern B having a convex structure height of 0.75 mm and a convex structure density (embossing density) of 60 pieces/cm 2 was embossed on the inner roll toilet paper by a pressure of 12 kgf/cm 2 . ..
After the embossing process, the contact embossing is formed so that the convex sides of the embossing on the inside roll and the inside roll are facing each other on the inside and the contact emboss is projected from the inside roll to the outside roll. Bonding was performed. After that, perforation lines for breaking that crossed in the width direction were formed at regular intervals along the longitudinal direction to obtain a roll-shaped toilet roll having a winding length shown in Table 1. The wound diameter (R in FIG. 4) of the obtained toilet roll was as shown in Table 1. The obtained toilet roll was cut into a predetermined width to obtain a 2-ply toilet roll (toilet roll product).
(実施例2)
エンボスパターンを型押しする圧力を巻外側トイレットペーパーは11kgf/cm2とし、巻内側トイレットペーパーは9kgf/cm2にし、坪量、巻き長さを表2に記載の通りに変更した以外は実施例1と同様にして2プライのトイレットロールを得た。
(Example 2)
The embossing pattern was embossed with a pressure of 11 kgf/cm 2 for the roll-side toilet paper and 9 kgf/cm 2 for the roll-side toilet paper, and the basis weight and roll length were changed as shown in Table 2. A two-ply toilet roll was obtained in the same manner as in 1.
(比較例1)
巻外側トイレットペーパーと巻内側トイレットペーパーの両方に、凸構造高さ0.8mm、凸構造密度(エンボス密度)21.2個/cm2のエンボスパターンAを14kgf/cm2の圧力で型押してエンボスを形成した以外は実施例1と同様にして2プライのトイレットロールを得た。
(Comparative Example 1)
An embossing pattern A having a convex structure height of 0.8 mm and a convex structure density (embossing density) of 21.2 pcs/cm 2 is embossed on both of the roll outside toilet paper and the roll inside toilet paper with a pressure of 14 kgf/cm 2. A two-ply toilet roll was obtained in the same manner as in Example 1 except for forming
(比較例2)
巻外側トイレットペーパーと巻内側トイレットペーパーの両方に、凸構造高さ0.75mm、凸構造密度(エンボス密度)60個/cm2のエンボスパターンBを9kgf/cm2の圧力で型押してエンボスを形成し、坪量を表1に記載の通りに変更した以外は、実施例1と同様にして2プライのトイレットロールを得た。
(Comparative example 2)
The embossed pattern B having a convex structure height of 0.75 mm and a convex structure density (embossing density) of 60 pieces/cm 2 is embossed by a pressure of 9 kgf/cm 2 on both of the roll outside toilet paper and the roll inside toilet paper. Then, a 2-ply toilet roll was obtained in the same manner as in Example 1 except that the basis weight was changed as shown in Table 1.
(比較例3)
巻外側トイレットペーパーと巻内側トイレットペーパーの両方に、凸構造高さ0.75mm、凸構造密度(エンボス密度)60個/cm2のエンボスパターンAを11kgf/cm2の圧力で型押してエンボスを形成し、坪量、巻き長さを表2に記載の通りに変更した以外は、実施例1と同様にして2プライのトイレットロールを得た。
(Comparative example 3)
The emboss pattern A having a convex structure height of 0.75 mm and a convex structure density (emboss density) of 60 pieces/cm 2 is embossed on both of the roll outside toilet paper and the roll inside toilet paper with a pressure of 11 kgf/cm 2 to form an emboss. Then, a 2-ply toilet roll was obtained in the same manner as in Example 1 except that the basis weight and the winding length were changed as shown in Table 2.
(評価)
(エンボス高さ)
まず、高精度形状測定システムKS−1100(KEYENCE社製)を用いて、巻外側トイレットペーパーと巻内側トイレットペーパーの表面(内側面)の高さデータを取得した。取得範囲は1cm角とし、画像取得ピッチは10μmとした。次いで、取得した画像データを、画像解析ソフトIOMate2007(株式会社アイ・スペック社製)に読み込み、得られた高さデータを256階調に分級した。穴などの欠陥部のデータを除去した後、横軸に階調、縦軸にデータの個数をとったグラフを作成した。作成したグラフについて、前後2点の合計5点で移動平均を取りグラフを描きなおし、新たに描きなおされたグラフの各点におけるグラフの傾きを、求める点とその前の点との2点の値を用いて算出した。得られた傾きのデータについて、前後3点の計7点で移動平均を取り、横軸を階調、縦軸を移動平均取得後の傾きとして、さらに別のグラフを作成した。得られた傾きのグラフの最下点以降の部分で最初に迎える変曲点の位置を目視判断し、その位置の横軸の階調を閾値として定めた。次いで、定めた閾値を下回る部分について高さデータの加重平均を行い、得られた平均値を「非エンボス部分の平均高さ」とした。また、定めた閾値以上の部分についても高さデータの加重平均を行い、得られた平均値を「エンボス部分の平均高さ」とする。「エンボス部分の平均高さ」−「非エンボス部分の平均高さ」によって求められる値をエンボス高さとして定め、それぞれのプライについて算出した。
(Evaluation)
(Emboss height)
First, the height data of the surface (inner surface) of the roll outside toilet paper and the roll inside toilet paper was acquired using the high precision shape measuring system KS-1100 (manufactured by KEYENCE). The acquisition range was 1 cm square, and the image acquisition pitch was 10 μm. Next, the acquired image data was read into the image analysis software IOMate2007 (manufactured by Eye Spec Co., Ltd.), and the obtained height data was classified into 256 gradations. After removing the data of defective portions such as holes, a graph was created with the horizontal axis representing gradation and the vertical axis representing the number of data. For the created graph, take a moving average at a total of 5 points, 2 points before and after, and redraw the graph, and calculate the slope of the graph at each point of the newly drawn graph. Calculated using the values. With respect to the obtained inclination data, a moving average was taken at a total of 7 points, 3 points before and after, and another graph was created with the horizontal axis as the gradation and the vertical axis as the gradient after the acquisition of the moving average. The position of the first inflection point reached after the lowest point of the obtained slope graph was visually determined, and the gradation on the horizontal axis at that position was set as the threshold value. Next, a weighted average of the height data is performed on the portion below the defined threshold, and the obtained average value is defined as the “average height of the non-embossed portion”. Further, the weighted average of the height data is performed also on the portion that is equal to or more than the set threshold value, and the obtained average value is set as the “average height of the embossed portion”. The value obtained by "the average height of the embossed portion"-"the average height of the non-embossed portion" was defined as the embossed height and calculated for each ply.
(坪量)
坪量の測定値は、1プライのトイレットペーパーの測定値を示している。坪量は、JIS P 8124の規定に従って測定した。
(Basis weight)
The measured value of the basis weight indicates the measured value of 1-ply toilet paper. The basis weight was measured according to JIS P 8124.
(紙厚)
厚さの測定値は、1プライのトイレットペーパーの測定値を示している。厚さは、ISO187に準拠した環境で、厚さ計(ハイブリッジ製作所製)を用いて、測定子を1秒間に1mm以下の速度で下ろした時の値を読み取った。なお、測定は1プライのトイレットペーパー10枚を1枚ずつ測定し、取得した10枚の厚さを平均したものを紙厚とした。
(Paper thickness)
The measurement value of the thickness indicates the measurement value of 1-ply toilet paper. Regarding the thickness, a value when the probe was lowered at a speed of 1 mm or less per second was read using a thickness meter (manufactured by Highbridge Seisakusho) in an environment conforming to ISO187. In the measurement, 10 sheets of 1-ply toilet paper were measured one by one, and the obtained thickness of 10 sheets was averaged to obtain the paper thickness.
(HF値)
トイレットペーパーのHF値は、ティシューソフトネスアナライザー(Emtec Electronic GmbH社製)を用いて測定した。サンプル台に、直径112.8mmの円形にカットしたサンプルを設置し、このサンプルに対し、ブレード付きローターを100mNの押し込み圧力をかけて上方から押し込んだ。その後、ブレード付きローターを回転数が2.0回転/秒となるように回転させ、その時の振動周波数を測定した。また、直径112.8mmの円形にカットした別のサンプルに対し、ブレード付きローターを100mNと、60mNの圧力で押し込んだ際の上下方向の変形変位量を算出した。HF値は、振動周波数と変形変位量から、算出される値であり、計算のアルゴリズムはTP IIを用いた。なお、上記の測定は、各サンプルの巻外側トイレットペーパーの露出側表面と巻内側トイレットペーパーの露出側表面についてそれぞれ10回ずつ行い、得られた測定データからHampel identifierの方法で異常値を除外し、各表面について各々平均値を算出した。さらにこのようにして算出した、各表面のHF値の平均値から、両面のHF値の平均値を算出し、それをHF値として評価に用いた。
なお、上記サンプルの測定はISO187に準拠した環境(温度23±1℃、相対湿度50±2%)で行った。また、測定の際には、付属の説明書に従い標準サンプル(emetec ref.2X(nn.n))で校正し、アルゴリズムをTP IIに設定した。計算ソフトウェアにはemtec measurement system Ver.3.22を使用した。
(HF value)
The HF value of the toilet paper was measured using a tissue softness analyzer (manufactured by Emtec Electronic GmbH). A circular sample having a diameter of 112.8 mm was set on the sample table, and a rotor with a blade was pressed into the sample from above by applying a pressing pressure of 100 mN. Then, the rotor with a blade was rotated so that the rotation speed was 2.0 rotations/second, and the vibration frequency at that time was measured. Further, the deformation displacement amount in the vertical direction when the rotor with a blade was pressed at a pressure of 100 mN and a pressure of 60 mN to another sample cut into a circle having a diameter of 112.8 mm was calculated. The HF value is a value calculated from the vibration frequency and the deformation displacement amount, and TP II was used as the calculation algorithm. In addition, the above-mentioned measurement was performed 10 times for each of the exposed side surface of the roll outside toilet paper and the exposed side surface of the roll inside toilet paper of each sample, and the abnormal value was excluded from the obtained measurement data by the method of Hampel identifier. An average value was calculated for each surface. Further, the average value of the HF values on both surfaces was calculated from the thus calculated average value of the HF values on each surface, and this was used as the HF value for evaluation.
The measurement of the above sample was performed in an environment (temperature 23±1° C., relative humidity 50±2%) in accordance with ISO187. In addition, at the time of measurement, a standard sample (emtec ref.2X (nn.n)) was calibrated according to the attached instruction, and the algorithm was set to TP II. The calculation software includes emtec measurement system Ver. 3.22 was used.
(圧縮性)
トイレットペーパーの圧縮性について、KES FB3−AUTO−A自動化圧縮試験機(カトーテック株式会社製)を用いて測定した。2cm2の加圧板と受圧板間に縦10cm×横20cm角に切り出したサンプルを設置し、50mm/秒の速さで加圧板を下降させ、その際に時々刻々と変化する圧力とその時のサンプルの厚みを測定することで、下記の項目を算出した。
T0:圧力0.5gf/cm2下におけるサンプルの厚み
Tm:圧力50gf/cm2下におけるサンプルの厚み
LC:圧縮直線性
WC:圧縮仕事量
RC:厚み回復性
上記の項目の値は、巻外側トイレットペーパーと巻内側トイレットペーパーについてそれぞれ測定し、エンボスの凹面(エンボスロールを押し当てた面)を加圧板側として10回の測定を行い、得られた測定データからHampel identifierの方法で異常値を除外し、平均値として算出した値である。なお、上記サンプルの測定はISO187に準拠した環境(温度23±1℃、相対湿度50±2%)で行った。
(Compressibility)
The compressibility of the toilet paper was measured using a KES FB3-AUTO-A automated compression tester (manufactured by Kato Tech Co., Ltd.). A sample cut into a length of 10 cm and a width of 20 cm is installed between a pressure plate of 2 cm 2 and a pressure plate, and the pressure plate is lowered at a speed of 50 mm/sec. The following items were calculated by measuring the thickness of the.
T 0 : thickness of sample under pressure of 0.5 gf/cm 2 T m : thickness of sample under pressure of 50 gf/cm 2 LC: linearity of compression WC: work of compression RC: thickness recovery Each of the outside roll paper and the inside roll paper was measured, and the concave surface of the emboss (the surface against which the emboss roll was pressed) was used as the pressure plate side for 10 times of measurement. From the obtained measurement data, it was abnormal by the method of the Hampel identifier. It is a value calculated as an average value excluding the value. The measurement of the above sample was performed in an environment (temperature 23±1° C., relative humidity 50±2%) in accordance with ISO187.
(引張強度)
引張強度の測定値は、1プライのトイレットペーパーの測定値であり、乾燥引張強度を示している。引張強度は、JIS P 8113に準拠して測定した。縦方向の引張強度と、横方向の引張強度を各6サンプルずつ測定し、その平均値を算出して引張強度とした。
(Tensile strength)
The measured tensile strength is the measured value of 1-ply toilet paper, and shows the dry tensile strength. The tensile strength was measured according to JIS P8113. Tensile strength in the longitudinal direction and tensile strength in the lateral direction were measured for each 6 samples, and the average value was calculated as the tensile strength.
(巻き密度)
2プライのトイレットロールの巻き密度を算出した。巻き密度は、2プライのトイレットロールの巻き長さの2倍の長さを紙管の断面積を除いたロールの断面積(図4におけるP(ドット状模様部分))で除すことにより算出した。すなわち、巻き密度は下記の式で算出することができる。
巻き密度(m/cm2)=巻き長さ×2/ロール断面積
(Winding density)
The winding density of a 2-ply toilet roll was calculated. The winding density is calculated by dividing twice the winding length of a 2-ply toilet roll by the roll cross-sectional area (P (dot-shaped pattern portion) in FIG. 4) excluding the paper tube cross-sectional area. did. That is, the winding density can be calculated by the following formula.
Winding density (m/cm 2 )=winding length×2/roll cross-sectional area
(官能評価)
肌触り感、ロールの柔らかさの評価は10人の評価者によって3段階評価で行った。肌触り感はロールから40cm程度巻き解いて切り離した状態のトイレットペーパーを肌に当てて、柔らかさを評価した。
ロールの柔らかさは、ロールを手で掴んだ時の柔らかさを評価した。なお、柔らかさは同じ巻き長さのトイレットロール同士で比較した。評価結果は巻き長さが25mの場合は○△×の3段階、巻き長さが45mの場合はABCの3段階で表記した。
<肌触り感>
○またはA:優れている
△またはB:やや劣る
×またはC:劣る
<ロールの柔らかさ>
○またはA:柔らかい
△またはB:やや固い
×またはC:固い
(sensory evaluation)
The touch feeling and the softness of the roll were evaluated by 10 evaluators in 3 grades. The softness was evaluated by applying to the skin a toilet paper that was unwound from the roll by about 40 cm and separated.
The softness of the roll was evaluated by the softness when the roll was gripped by hand. The softness was compared between toilet rolls having the same winding length. The evaluation results are shown in three grades of ◯Δ× when the winding length is 25 m, and in three grades of ABC when the winding length is 45 m.
<Feeling touch>
○ or A: excellent △ or B: slightly inferior × or C: inferior <softness of roll>
○ or A: soft △ or B: somewhat hard × or C: hard
実施例で得られたトイレットペーパーは優れた肌触り感を有しており、手触り感に優れたトイレットロールを形成している。 The toilet paper obtained in the examples has an excellent feel to the touch, and forms a toilet roll excellent in the feel.
1 トイレットペーパー
12 巻外側トイレットペーパー
14 巻内側トイレットペーパー
100 トイレットロール
P ロールの断面積
R ロールの巻き径
S 紙管径
1
Claims (6)
前記巻外側トイレットペーパーのエンボス高さは90μm以上210μm以下であり、前記巻内側トイレットペーパーのエンボス高さは70μm以上170μm以下であり、
前記巻外側トイレットペーパーのエンボス高さと、前記巻内側トイレットペーパーのエンボス高さの差が10μm以上50μm以下である2プライ以上のトイレットペーパー。 A two-ply or more toilet paper having a roll-out toilet paper and a roll-inside toilet paper,
The embossing height of the roll outer toilet paper is 90 μm or more and 210 μm or less, and the embossing height of the roll inner toilet paper is 70 μm or more and 170 μm or less,
A two-ply or more toilet paper in which the difference between the embossed height of the roll outer toilet paper and the embossed height of the roll inner toilet paper is 10 μm or more and 50 μm or less.
前記巻内側トイレットペーパーのエンボス密度は20個/cm2以上100個/cm2以下である請求項1〜3のいずれか1項に記載のトイレットペーパー。 The embossing density of the outside roll toilet paper is 10 pieces/cm 2 or more and 30 pieces/cm 2 or less,
The toilet paper according to any one of claims 1 to 3, wherein the embossing density of the roll-inside toilet paper is 20 pieces/cm 2 or more and 100 pieces/cm 2 or less.
前記トイレットロールの巻き長さは25m以上60m以下であり、
前記トイレットロールの巻き密度は0.50m/cm2以上1.4m/cm2以下である2プライ以上のトイレットロール。 A toilet roll obtained by rolling the toilet paper according to any one of claims 1 to 4,
The toilet roll has a winding length of 25 m or more and 60 m or less,
A two-ply or more toilet roll having a winding density of 0.50 m/cm 2 or more and 1.4 m/cm 2 or less.
前記(A)工程で得られた巻外側トイレットペーパーと、前記(B)工程で得られた巻内側トイレットペーパーを積層する工程と、を含み、
前記(A)工程で得られた巻外側トイレットペーパーのエンボス高さと、前記(B)工程で得られた巻内側トイレットペーパーのエンボス高さの差が10μm以上50μm以下である2プライ以上のトイレットペーパーの製造方法。 An embossing process for embossing height of 90 μm or more and 210 μm or less on the roll outer toilet paper (A), and a process (B) for embossing height of 70 μm or more and 170 μm or less on the roll inner toilet paper,
And a step of stacking the roll-out toilet paper obtained in the step (A) and the roll-inside toilet paper obtained in the step (B),
A two-ply or more toilet paper in which the difference between the emboss height of the outside roll toilet paper obtained in the step (A) and the emboss height of the inside toilet paper roll obtained in the step (B) is 10 μm or more and 50 μm or less. Manufacturing method.