JP2019157107A - 弾性複合材プロセス及びその製品 - Google Patents
弾性複合材プロセス及びその製品 Download PDFInfo
- Publication number
- JP2019157107A JP2019157107A JP2018176511A JP2018176511A JP2019157107A JP 2019157107 A JP2019157107 A JP 2019157107A JP 2018176511 A JP2018176511 A JP 2018176511A JP 2018176511 A JP2018176511 A JP 2018176511A JP 2019157107 A JP2019157107 A JP 2019157107A
- Authority
- JP
- Japan
- Prior art keywords
- mixture
- elastic composite
- phr
- composite material
- elastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
前記混合ステップは、更に滑剤とコア形成剤を、第1混合物、第2混合物、抗酸化黄変防止剤、耐加水分解剤、紫外線吸收剤とミキサで撹拌混合し、滑剤の加入重量は、0.5〜1PHR、コア形成剤の加入重量は、2〜5PHRであることを含む。
2 表皮層
3 内層
31 気泡孔
Claims (6)
- 第1混合物、第2混合物、抗酸化黄変防止剤、耐加水分解剤、紫外線吸収剤をミキサで撹拌混合し、第1混合物は、熱可塑性ポリアミド弾性体であり、その密度が1〜1.01g/cm3であり、ショア硬度がA80〜A95であり、加入重量は、40〜80PHR(組成物の100部あたりの総成分の対応する部数)であり、第2混合物は、熱可塑性ポリウレタン弾性体であり、その密度は1.1g/cm3〜1.2g/cm3であり、ショア硬度は、A80〜A95であり、加入重量は、20〜60PHRであり、抗酸化黄変防止剤の加入重量は、0.5〜1PHRであり、耐加水分解剤の加入重量は、0.5〜1.5PHRであり、紫外線吸収剤の加入重量は、0.5〜1PHRである混合ステップと、
第1混合物、第2混合物、抗酸化黄変防止剤、耐加水分解剤、紫外線吸收剤を均一に混合した後、混練機に入れ、複合粒子を得て、前記混練機の設定温度は、150℃〜170℃である混練ステップと、
前記複合粒子及び水分散液、エントレーナーを高圧釜に入れ、撹拌混合後、高圧流体を高圧釜に入れ、高圧釜を加熱し、複合粒子及び高圧流体に溶解平衡を達成させ、高圧釜の放圧及び水蒸気及び高圧空気の高圧釜への充填を経て、発泡の弾性複合材を得て、前記高圧流体は、CO2及びN2であり、且つCO2圧力は、8〜9MPaであり、N2圧力は、5〜7MPaであり、前記高圧釜を加熱する温度は、110℃〜150℃であり、且つ高圧釜を加熱する時間は、0.5時間〜2時間である発泡ステップと、を含む弾性複合材プロセス。 - 混合ステップは、更に滑剤とコア形成剤を、第1混合物、第2混合物、抗酸化黄変防止剤、耐加水分解剤、紫外線吸收剤とミキサで撹拌混合し、滑剤の加入重量は、0.5〜1PHR、コア形成剤の加入重量は、2〜5PHRであることを含む請求項1に記載の弾性複合材プロセス。
- 発砲ステップの水分散液は、水と界面活性剤を含み、エントレーナーがシクロペンタン、ブタン、エタノールまたはメタノールの何れか一者であり、且つ水と表面活性剤とエントレーナーの比が1?0.002?0.02〜1?0.01?0.05であり、発泡ステップの溶解平衡は、0.5〜2時間の浸漬を含む請求項2に記載の弾性複合材プロセス。
- 混練ステップの混練機は、ミキサまたは一軸スクリュー押出機または二軸スクリュー押出機であり、複合粒子の粒径は、1〜2mmであり、発泡の弾性複合材の粒径の大きさが3mm〜7mmである請求項3に記載の弾性複合材プロセス。
- 第1混合物及び第2混合物を割合に従って混練し、発泡成型を経た固形粒子であり、
該弾性複合材は、表皮層、及び該表皮層に完全に被覆された内層を含み、該内層が複数の気泡孔を有し、且つ該複数の気泡孔は、部分的に互いに連通し、部分的に互いに連通せず、該複数の気泡孔が部分的連通する割合は、5%以下であり、互いに連通しない割合は95%以上であり、
前記第1混合物は、熱可塑性ポリアミド弾性体であり、
前記第2混合物は、熱可塑性ポリウレタン弾性体であり、
弾性複合材が含む第1混合物の百分比は、それが含む第2混合物の百分比よりも大きい弾性複合材。 - 前記第1混合物は、40〜80PHR(組成物の100部あたりの総成分の対応する部数)であり、該第2混合物は、10〜40PHRであり、該弾性複合材の硬度は、92A〜94Aであり、該弾性複合材の密度は、1.01g/cm3から1.07g/cm3であり、該弾性複合材の抗拉強度は、183.5kg/cm2〜243.9kg/cm2であり、該弾性複合材の延伸率は、529.83%〜727.19%であり、該弾性複合材の引裂強度は、140kg/cm〜149kg/cmであり、該弾性複合材の反発力は、52%〜54%であり、該弾性複合材の粒径の寸法は、3mm〜7mmであり、該表皮層の厚さの寸法は、100μm〜200μmであり、且つ該表皮層の該表面は、滑らかである請求項5に記載の弾性複合材。