DE2258571B2 - ROAD MARKER DIMENSIONS - Google Patents

ROAD MARKER DIMENSIONS

Info

Publication number
DE2258571B2
DE2258571B2 DE19722258571 DE2258571A DE2258571B2 DE 2258571 B2 DE2258571 B2 DE 2258571B2 DE 19722258571 DE19722258571 DE 19722258571 DE 2258571 A DE2258571 A DE 2258571A DE 2258571 B2 DE2258571 B2 DE 2258571B2
Authority
DE
Germany
Prior art keywords
fibers
road marking
road marker
order
mass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19722258571
Other languages
German (de)
Other versions
DE2258571A1 (en
DE2258571C3 (en
Inventor
Karlheinz 8912 Kaufering Schreiber
Original Assignee
Bituleit-Bayerische Bitumen-Chemie Ferdinand Heinrich, 8912 Kaufering
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bituleit-Bayerische Bitumen-Chemie Ferdinand Heinrich, 8912 Kaufering filed Critical Bituleit-Bayerische Bitumen-Chemie Ferdinand Heinrich, 8912 Kaufering
Priority to DE19722258571 priority Critical patent/DE2258571C3/en
Priority claimed from DE19722258571 external-priority patent/DE2258571C3/en
Priority to FR7337107A priority patent/FR2209011A1/en
Priority to CA184,854A priority patent/CA1023890A/en
Publication of DE2258571A1 publication Critical patent/DE2258571A1/en
Publication of DE2258571B2 publication Critical patent/DE2258571B2/en
Application granted granted Critical
Publication of DE2258571C3 publication Critical patent/DE2258571C3/en
Expired legal-status Critical Current

Description

Die Erfindung betrifft eine Straßenmarkierungsmasse mit einem Gehalt an thermoplastischen Harzen.The invention relates to a road marking compound containing thermoplastic resins.

Bei solchen bekannten Massen, die insbesondere in ausgefrästen Rinnen in Straßenbelägen verlegt werden, hat sich herausgestellt, daß durch sehr hohe oder sehr niedrige Temperaturen oder durch mechanische Einflüsse von der umgebenden Straßendecke Spannungen in der verlegten Masse auftreten, die zu Beschädigungen, insbesondere zum Abbröckeln am Rand der verlegten Masse führen können.With such known masses, which are laid in particular in milled channels in road surfaces, It has been found that by very high or very low temperatures or by mechanical influences from the surrounding road surface tensions occur in the laid mass, which lead to damage, in particular can lead to crumbling at the edge of the laid compound.

Es sind auch Straßenmarkierungsmassen mit einem Gehalt an thermoplastischen Harzen und Glasfasern bzw. Asbestfasern bekannt (DPS 12 91 434, US-Patentschrift 36 74 525, britische Patentschrift 10 38 649), wobei die Länge der Fasern in der Größenordnung von Millimetern liegt (britische Patentschrift 10 38 649). Die Fasermenge beträgt dabei 1% und mehr der Masse. Es hat sich herausgestellt, daß eine so große Faserzugabe die Verarbeitungsviskosität der fertigen Markierungsmasse verschlechtert. There are also road marking compounds with a content of thermoplastic resins and glass fibers or asbestos fibers known (DPS 12 91 434, US Patent 36 74 525, British Patent 10 38 649), the length of the fibers being on the order of millimeters (British Patent 10 38 649). the The amount of fiber is 1% and more of the mass. It has been found that such a large fiber addition the processing viscosity of the finished marking compound deteriorates.

Der Erfindung liegt die Aufgabe zugrunde, eine Straßenmarkierungsmasse mit einem Gehalt an thermoplastischen Harzen und Fasern aus anorganischem Material einer Länge in der Größenordnung von Millimetern und einer Stärke in der Größenordnung von hundertstel Millimetern zu schaffen, die eine ausreichende Elastizität (Griffigkeit) und Festigkeit aufweist, ohne daß die Verarbeitungsviskosität beeinträchtigt wird. Gelöst wird diese Aufgabe dadurch, daß die Masse die Fasern in Mengen von 0,1 bis 0,3% enthält.The invention is based on the object of a road marking compound with a content of thermoplastic Resins and fibers of inorganic material on the order of length Millimeters and a thickness on the order of hundredths of a millimeter to create the one has sufficient elasticity (grip) and strength without adversely affecting the processing viscosity will. This problem is solved by the fact that the mass contains the fibers in amounts of 0.1 to 0.3% contains.

Die Fasern bestehen aus anorganischem Material, weil die thermoplastische Masse bei ihrer Aufbereitung und Verlegung einer wesentlichen Erwärmung, z. B. zwischen 140 und 25O°C, ausgesetzt ist, welche Wärmebeanspruchung organische Materialien nicht aushalten, sondern z. B. schmelzen, also in der verlegten Masse nicht mehr als Fasern enthalten sein würden. Für die mit der Erfindung gewünschte Elastizität ist aber gerade die in der verlegten Masse noch vorhandene Faserstruktur wesentlich.The fibers consist of inorganic material, because the thermoplastic mass in their preparation and relocation of substantial heating, e.g. B. between 140 and 25O ° C, which Organic materials cannot withstand thermal stress; B. melt, so in the misplaced Mass no more than fibers would be included. However, for the elasticity desired with the invention the fiber structure still present in the laid mass is essential.

Die Länge der Fasern kann insbesondere bis 10 mm betragen und die Fasern können bis zu 50 μ und insbesondere 10 bis 13 μ stark sein. Es kann auch eine Mischung von Fasern verschiedener Längen und verschiedener Stärken zugesetzt werden.The length of the fibers can in particular be up to 10 mm and the fibers can be up to 50 μ and especially 10 to 13 μ thick. It can also be a mixture of fibers of various lengths and different strengths can be added.

Mit der erfindungsgemäßen Straßenmarkierungsmasse sind Versuche im Vergleich zu Straßenmarkierungsmassen ohne Ginsfaserzugabe und einer Glasfaserzugabe von 1,0%, wie sie dem Stand der Technik entsprechen, durchgeführt worden, deren Ergebnisse nachfolgend angeführt sind.With the road marking compound according to the invention, tests are made in comparison with road marking compounds without the addition of gins fibers and a glass fiber addition of 1.0%, as in the prior art have been carried out, the results of which are given below.

GlasfasermengeFiber amount 0,1%0.1% 0,2%0.2% 0,3%0.3% 1,0%1.0% 0%0% 1850C185 0 C 1950C195 0 C 2050C205 0 C oberhalb derabove the Verarbeilungs-Processing 1850C185 0 C kritischencritical temperaturtemperature ZersetzungsDecomposition temperaturtemperature gutWell etwas kurza bit short kurzshort steif, keinestiff, none Viskosität bei Ver-Viscosity at gutWell brauchbareuseful arbeitungstemp.working temp. FließfähigkeitFluidity (Fließfähigkeit)(Flowability) nach 24 hafter 24 h nach 24 hafter 24 h nach 24 hafter 24 h WärmestandHeat level nach 24 hafter 24 h gutWell gutWell gutWell festigkeit bei 700Cstrength at 70 0 C abgetropftdrained ca. 2,90 mapprox. 2.90 m ca. 3,30 mapprox. 3.30 m ca. 3,50 mapprox. 3.50 m KugelfallprobeBall drop test ca. 2,60 mapprox. 2.60 m

Hieraus ergibt sich, daß mit zunehmendem Glasfaser- Fasergehalt von 0,1 bis 0,3 Gewichtsprozent optimaleFrom this it follows that with increasing glass fiber fiber content of 0.1 to 0.3 percent by weight optimum

anteil die Verarbeitungstemperatur ansteigt und die Verarbeitsbedingungen der- Massen einstellen undproportion increases the processing temperature and adjust the processing conditions of the masses and

Verarbeitungsviskosität höher wird, wobei überra- 60 Markierungen mit guter Wärmestandfestigkeit undProcessing viscosity becomes higher, with over 60 marks with good heat resistance and

schenderweise festzustellen ist, daß sich bei einem Elastizität gewonnen werden.It is to be noted that elasticity can be gained in one.

Claims (2)

Patentansprüche:Patent claims: 1. Straßenmarkierungsmasse mit einem Gehalt an thermoplastischen Harzen und Fasern aus anorganischem Material einer Länge in der Größenordnung von Millimetern und einer Stärke in der Größenordnung von hundertstel Millimetern, dadurch die Fasern in1. Road marking compound containing thermoplastic resins and inorganic fibers Material on the order of millimeters in length and on the order of thickness of hundredths of a millimeter, thereby keeping the fibers in gekennzeichnet, daß sie
Mengen von 0,1 bis 0,3% enthält.marked that they
Contains amounts of 0.1 to 0.3%. 2. Straßenmarkierungsmasse nach Anspruch 1, dadurch gekennzeichnet, daß sie als Fasern Glasfasern enthält.2. Road marking compound according to claim 1, characterized in that it is glass fibers as fibers contains.
DE19722258571 1972-11-30 1972-11-30 Road marking compound Expired DE2258571C3 (en)