CN1250813A - 用转炉包渣作调渣剂改造低Si铁水或半钢炼钢渣系的方法 - Google Patents
用转炉包渣作调渣剂改造低Si铁水或半钢炼钢渣系的方法 Download PDFInfo
- Publication number
- CN1250813A CN1250813A CN98125194A CN98125194A CN1250813A CN 1250813 A CN1250813 A CN 1250813A CN 98125194 A CN98125194 A CN 98125194A CN 98125194 A CN98125194 A CN 98125194A CN 1250813 A CN1250813 A CN 1250813A
- Authority
- CN
- China
- Prior art keywords
- slag
- steel
- converter
- cinder inclusion
- molten iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
调渣剂 | 缺点 |
河砂 | 1、熔点高>1600℃,初渣形成慢达5~8min。2、炉口粘结严重,“海绵”状粘结物致使炉口处理困难。3、属生料,热损失大。 |
火砖块 | 1、熔点高>1600℃,初渣形成慢达5~8min。2、Al2O3含量较高,炉渣太稀,易发生金属喷溅。 |
辉绿岩、玄武岩 | 结晶水含量高,热损失严重。 |
污泥、白云石粉制球 | 用量大,占用场地多。 |
焙烧玄武岩 | 玄武岩开采困难 |
安山岩配锰矿助熔剂 | 成本高 |
石英砂 | 熔点高,初渣形成慢。 |
炉号 | 原料及装入量 | C% | S% | Si% |
2722155 | 半钢36t | 3.6 | 0.060 | 痕迹 |
2722200 | 半钢34t、废钢2.5t | 3.5 | 0.050 | 痕迹 |
2722201 | 半钢36t | 3.6 | 0.055 | 痕迹 |
炉号 | 白灰(kg) | 萤石(kg) | 包渣(kg) | 石墨(kg) |
2722155 | 700 | ------ | 400 | 470 |
2722200 | 750 | ------ | 450 | 450 |
2722201 | 800 | ------ | 500 | ------ |
炉号 | 使用氧压Mpa | 氧气耗量Nm3 | 供氧时间min | 化渣时间min |
2722155 | 0.7~1.0 | 1812 | 13.0 | 4.5 |
2722200 | 0.8~1.0 | 1792 | 12.9 | 3.3 |
2722201 | 0.75~1.1 | 1405 | 9.6 | 2.7 |
炉号 | 白灰(kg) | 萤石(kg) | 包渣(kg) | 化渣情况 |
2722155 | 1400 | 150 | 400 | 无“返干” |
2722200 | 1300 | 100 | 500 | 无“返干” |
2722201 | 1300 | ------ | 440 | 无“返干” |
炉号 | C% | P% | S% | 温度℃ | 终点C | 出钢量t |
2722155 | 0.72 | 0.012 | 0.025 | 1617 | 0.09 | 32.75 |
2722200 | 0.35 | 0.010 | 0.026 | 1648 | 0.06 | 32.73 |
2722201 | 0.30 | 0.015 | 0.026 | 1590 | 0.075 | 32.96 |
炉号 | 白灰(kg) | 萤石(kg) | 包渣(kg) | 石墨(kg) |
2722155 | 2100 | 150 | 800 | 470 |
2722200 | 2050 | 100 | 950 | 450 |
2722201 | 2100 | ------ | 940 | ------ |
Claims (2)