CN117050578A - 一种尼龙印刷耐高温蒸煮水性油墨及其制备方法和应用 - Google Patents
一种尼龙印刷耐高温蒸煮水性油墨及其制备方法和应用 Download PDFInfo
- Publication number
- CN117050578A CN117050578A CN202311239365.5A CN202311239365A CN117050578A CN 117050578 A CN117050578 A CN 117050578A CN 202311239365 A CN202311239365 A CN 202311239365A CN 117050578 A CN117050578 A CN 117050578A
- Authority
- CN
- China
- Prior art keywords
- water
- temperature
- based ink
- resistant
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种尼龙印刷耐高温蒸煮水性油墨及其制备方法和应用。本发明的尼龙印刷耐高温蒸煮水性油墨是由水性聚氨酯树脂、颜料、水性消泡剂、表面润湿剂、润湿分散剂、水性快干剂、水性pH值中和剂、固化剂和水组成。应用于尼龙薄膜上，具有很好的附着力和流平性，高温蒸煮121℃/30min和135℃/15min时，油墨无渗出、褪色、复合起泡等不良现象。
Description
本申请是申请日为2018年04月27日、申请号为CN201810392081.2、发明名称为《一种尼龙印刷耐高温蒸煮水性油墨及其制备方法》的分案申请。
技术领域
本发明涉及一种印刷用水性油墨，具体涉及一种尼龙印刷耐高温蒸煮水性油墨及其制备方法和应用。
背景技术
众所周知，传统的食品包装用油墨是苯酮溶型的，尽管对溶剂残留做了严格要求，但也存在对健康所产生的伤害和印刷后溶剂残留影响食品的气味和食品安全等问题。苯溶型复合油墨由于其以大量的芳香烃作为溶剂，已经逐渐不能适应我国日益发达的软包装行业的要求。出于对食品安全性的考虑和适应日益严格的安全法规，人们迫切需要环保型油墨，即希望不要在印刷油墨中以及油墨的使用过程中添加甲苯、二甲苯等芳香烃类溶剂。
因此，积极开发和应用符合环保要求的绿色凹印油墨及水性油墨将成为一个必然趋势，此时耐蒸煮水性油墨应运而生，其具有无毒、无刺激性气味、无腐蚀性、不燃不爆使用安全、可直接用水稀释等众多优点，对环境和人类都不存危害，属于典型的绿色环保产品。水性油墨作为溶剂油墨的替代体系已引起许多关注，但时至今日包装薄膜印刷中的水性化仍得不到广泛应用。市面上的水墨产品多数存在对颜料分散性差、光泽低、上版效果差和网版转移低等缺点，所以更不能用于蒸煮。
发明内容
本发明的主要目的，在于提供一种尼龙印刷耐高温蒸煮水性油墨及其制备方法和应用，以有效地克服上述的不足。
为了实现上述目的，本发明的尼龙印刷耐高温蒸煮水性油墨是由水性聚氨酯树脂、颜料、水性消泡剂、表面润湿剂、润湿分散剂、水性快干剂、水性pH值中和剂、固化剂和水组成。
本发明的尼龙印刷耐高温蒸煮水性油墨各组分的重量百分比为：
所述的水性聚氨酯分子量在20000～25000，固含量为30～35％，通过以下方法制成：所述的水性聚氨酯的原料组成按重量比由聚碳酸酯二元醇50～55份、异佛尔酮二异氰酸酯15～20份、二月桂酸二丁基锡10～15份和二羟甲基丙酸5～10份组成；称取聚碳酸酯二元醇和异佛尔酮二异氰酸酯加入到反应釜，加热并缓慢搅拌，保持温度在50～60℃高速搅拌20～40min，开始滴加剩余原料，最后加入水，并迅速将反应釜温度降至20～30℃，测试合成的水性聚氨酯的各项性能，各指标达到要求后，包装待用；
所述的水性消泡剂是含脂肪族矿物油的混合物；
所述的表面润湿剂是聚醚硅氧烷共聚物；
所述的水性pH值中和剂是荷兰艾德化学的活性含量90％的水溶性氨基醇混合物；
所述的润湿分散剂不含VOC和溶剂；
所述的水性快干剂是丙烯酸型氧化锌乳液，其制备方法为：先用154g水溶解112g碳酸铵3～5分钟，再添加75g氧化锌，2～3分钟后变成不透明液体，再加入159g的28％浓度的氨水，3～5分钟后得500g含量为15％的氧化锌溶液；取15份氧化锌溶液，往氧化锌溶液中顺序加入2份28％的氨水、15份去离子水和68份水性丙烯酸乳液(阿根廷diransa，型号SF)，得到所述的水性丙烯酸型快干剂；
所述的固化剂是上海尤恩化工型号178固化剂。
优选地，所述的颜料为耐200℃高温的有机颜料或无机颜料。
优选地，所述的有机颜料为经过颜料化处理的缩合偶氮类、苯并咪唑酮偶氮类、酞青蓝BGS和酞青绿G中的至少一种；所述的无机颜料为金红石型钛白粉或高色素炭黑。
优选地，所述的表面润湿剂是Tego Flow425聚醚硅氧烷共聚物，有效含量100％，黏度约100mPa·s。
优选地，所述的润湿分散剂是德国毕克化学润湿分散剂BYK-191。
优选地，所述的固化剂是上海尤恩化工型号178固化剂，具有流动性好，黏度低等特点，可以在本发明水墨里保存半年甚至更久。
本发明提供了上述技术方案所述尼龙印刷耐高温蒸煮水性油墨的制备方法，包括以下步骤：
1)按照尼龙印刷耐高温蒸煮水性油墨的原料组成称取各原料；
2)加入15～20％水性聚氨酯到反应釜中，再缓慢加入部分水性消泡剂和其他助剂，低速搅拌10～15分钟；
3)向反应釜中加入颜料，高速搅拌，研磨至物料细度达到要求为止；
4)加入剩余水性聚氨酯和水性消泡剂，高速搅拌20～40min，再加入水调整所需黏度，继续高速搅拌5～10分钟，过滤包装。
本发明还提供了上述技术方案所述尼龙印刷耐高温蒸煮水性油墨或上述技术方案所述制备方法制备的尼龙印刷耐高温蒸煮水性油墨在尼龙印刷中的应用。
本发明的有益效果在于采用了自制的水性聚氨酯树脂具有复溶性好、对颜料润湿分散好、耐高剪切力等优点，在尼龙上有很好的附着力和流平性。同时，加入的固化剂有别常规的固化剂，具有流动性好黏度低等优点，可以在本发明水性油墨里保存半年甚至更久，不会和树脂中的羧基交联，只有当印刷后水墨水分挥发后，固化剂才会产生交联。加入的水性快干剂，可使印刷速度达150～200m/min(烘箱温度60℃)，避免尼龙吸水导致薄膜变形。颜料可在200℃以上使用，耐高温抗迁移。
具体实施方式
下面通过实例对本发明做进一步的详细说明，这些实例仅用于帮助理解本发明的方法和核心思想，并不限制本发明的范围。应当指出，在不脱离本发明的前提下，本领域的技术人员仍可对本发明进行若干的改进和修饰，这些改进和修饰也落入本发明权利要求的保护范围内。
实施例1
本实施例的配方如下(按重量分数比)：
所述的水性聚氨酯分子量在22000左右，固含量为35％，通过以下方法制成：所述的水性聚氨酯的原料组成有聚碳酸酯二元醇50份、异佛尔酮二异氰酸酯20份、二月桂酸二丁基锡15份、二羟甲基丙酸10份；称取聚碳酸酯二元醇和异佛尔酮二异氰酸酯加入到反应釜，加热并缓慢搅拌，保持温度在55℃左右高速搅拌半小时，开始滴加剩余原料，最后加入适量水，并迅速将反应釜温度降至25℃左右，测试合成的水性聚氨酯的各项性能，各指标达到要求后，包装待用。
所述的水性快干剂是丙烯酸型氧化锌乳液，其制备方法为：先用154g水溶解112g碳酸铵5分钟，再添加75g氧化锌，2～3分钟后变成不透明液体，再加入159g的28％浓度的氨水，5分钟后即得500g含量为15％的氧化锌溶液；取15份氧化锌溶液，往氧化锌溶液中顺序加入2份28％的氨水、15份去离子水和68份水性丙烯酸乳液，即为水性丙烯酸型快干剂。
所述的颜料为耐200℃高温的有机颜料。
所述的水性消泡剂是Tego Foamex K8脂肪族矿物油的混合物。
所述的表面润湿剂是Tego Flow425聚醚硅氧烷共聚物，有效含量100％，黏度约100mPa·s。
所述的润湿分散剂是德国毕克化学润湿分散剂BYK-191。
所述的水性pH值中和剂是荷兰艾德化学的活性含量90％的水溶性氨基醇混合物。
所述的固化剂是上海尤恩化工型号178固化剂。
一种尼龙印刷耐高温蒸煮水性油墨的制备方法，包括以下步骤：
1)按照尼龙印刷耐高温蒸煮水性油墨的配比称取各原料；
2)加入20％水性聚氨酯到反应釜中，再缓慢加入部分消泡剂和其他助剂，低速搅拌10分钟；
3)向反应釜中加入颜料，高速搅拌，研磨至物料细度达到要求为止；
4)加入剩余水性聚氨酯和消泡剂，高速搅拌半小时左右，再加入水调整所需黏度，继续高速搅拌10分钟，过滤包装。
将本油墨应用于尼龙上印刷，印刷速度达150～200m/min(烘箱温度60℃)，其主要技术指标能达到国内外同类产品的质量要求：
1)颜料分散及稳定性：在50℃下静置30天，无颜料絮凝、沉淀和胶化等不良现象；
2)附着力：在尼龙膜上，用3M胶带粘于墨膜表面，用力揭去，95％不脱落；
3)耐蒸煮性：121℃/30min和135℃/15min，油墨无渗出、褪色、复合起泡等不良现象。
实施例2
本实施例的配方如下(按重量分数比)：
所述的水性聚氨酯分子量在22000左右，固含量为33％，可通过以下方法制成：所述的水性聚氨酯的原料组成有聚碳酸酯二元醇50份、异佛尔酮二异氰酸酯18份、二月桂酸二丁基锡10份、二羟甲基丙酸5份；称取聚碳酸酯二元醇和异佛尔酮二异氰酸酯加入到反应釜，加热并缓慢搅拌，保持温度在55℃左右高速搅拌半小时，开始滴加剩余原料，最后加入适量水，并迅速将反应釜温度降至25℃左右，测试合成的水性聚氨酯的各项性能，各指标达到要求后，包装待用。
所述的水性快干剂是丙烯酸型氧化锌乳液，其制备方法为：先用154g水溶解112g碳酸铵3分钟，再添加75g氧化锌，2～3分钟后变成不透明液体，再加入159g的28％浓度的氨水，3～5分钟后即得500g含量为15％的氧化锌溶液；取15份氧化锌溶液，往氧化锌溶液中顺序加入2份28％的氨水、15份去离子水和68份水性丙烯酸乳液，即为水性丙烯酸型快干剂。
所述的颜料为耐200℃高温的无机颜料。
所述的水性消泡剂是Tego Foamex K8脂肪族矿物油的混合物。
所述的表面润湿剂是Tego Flow425聚醚硅氧烷共聚物，有效含量100％，黏度约100mPa·s。
所述的润湿分散剂是德国毕克化学润湿分散剂BYK-191。
所述的水性pH值中和剂是荷兰艾德化学的活性含量90％的水溶性氨基醇混合物。
所述的固化剂是上海尤恩化工型号178固化剂。
一种尼龙印刷耐高温蒸煮水性油墨的制备方法，包括以下步骤：
1)按照尼龙印刷耐高温蒸煮水性油墨的配比称取各原料；
2)加入15％水性聚氨酯到反应釜中，再缓慢加入部分消泡剂和其他助剂，低速搅拌15分钟；
3)向反应釜中加入颜料，高速搅拌，研磨至物料细度达到要求为止；
4)加入剩余水性聚氨酯和消泡剂，高速搅拌半小时左右，再加入水调整所需黏度，继续高速搅拌10分钟，过滤包装。
将本油墨应用于尼龙上印刷，印刷速度达150～200m/min(烘箱温度60℃)，其主要技术指标能达到国内外同类产品的质量要求：
1)颜料分散及稳定性：在50℃下静置30天，无颜料絮凝、沉淀和胶化等不良现象；
2)附着力：在尼龙膜上，用3M胶带粘于墨膜表面，用力揭去，95％不脱落；
3)耐蒸煮性：121℃/30min和135℃/15min，油墨无渗出、褪色、复合起泡等不良现象。
实施例3
本实施例的配方如下(按重量分数比)：
所述的水性聚氨酯分子量在22000左右，固含量为30％，可通过以下方法制成：所述的水性聚氨酯的原料组成有聚碳酸酯二元醇53份、异佛尔酮二异氰酸酯15份、二月桂酸二丁基锡12份、二羟甲基丙酸8份；称取聚碳酸酯二元醇和异佛尔酮二异氰酸酯加入到反应釜，加热并缓慢搅拌，保持温度在55℃左右高速搅拌半小时，开始滴加剩余原料，最后加入适量水，并迅速将反应釜温度降至25℃左右，测试合成的水性聚氨酯的各项性能，各指标达到要求后，包装待用。
所述的水性快干剂是丙烯酸型氧化锌乳液，其制备方法为：先用154g水溶解112g碳酸铵5分钟，再添加75g氧化锌，2～3分钟后变成不透明液体，再加入159g的28％浓度的氨水，3～5分钟后即得500g含量为15％的氧化锌溶液；取15份氧化锌溶液，往氧化锌溶液中顺序加入2份28％的氨水、15份去离子水和68份水性丙烯酸乳液，即为水性丙烯酸型快干剂。
所述的颜料为耐200℃高温的有机颜料。
所述的水性消泡剂是Tego Foamex K8脂肪族矿物油的混合物。
所述的表面润湿剂是Tego Flow425聚醚硅氧烷共聚物，有效含量100％，黏度约100mPa·s。
所述的润湿分散剂是德国毕克化学润湿分散剂BYK-191。
所述的水性pH值中和剂是荷兰艾德化学的活性含量90％的水溶性氨基醇混合物。
所述的固化剂是上海尤恩化工型号178固化剂。
一种尼龙印刷耐高温蒸煮水性油墨的制备方法，包括以下步骤：
1)按照尼龙印刷耐高温蒸煮水性油墨的配比称取各原料；
2)加入20％水性聚氨酯到反应釜中，再缓慢加入部分消泡剂和其他助剂，低速搅拌15分钟；
3)向反应釜中加入颜料，高速搅拌，研磨至物料细度达到要求为止；
4)加入剩余水性聚氨酯和消泡剂，高速搅拌半小时左右，再加入水调整所需黏度，继续高速搅拌10分钟，过滤包装。
将本油墨应用于尼龙上印刷，印刷速度达150～200m/min(烘箱温度60℃)，其主要技术指标能达到国内外同类产品的质量要求：
1)颜料分散及稳定性：在50℃下静置30天，无颜料絮凝、沉淀和胶化等不良现象；
2)附着力：在尼龙膜上，用3M胶带粘于墨膜表面，用力揭去，95％不脱落；
3)耐蒸煮性：121℃/30min和135℃/15min，油墨无渗出、褪色、复合起泡等不良现象。
尽管上述实施例对本发明做出了详尽的描述，但它仅仅是本发明一部分实施例，而不是全部实施例，人们还可以根据本实施例在不经创造性前提下获得其他实施例，这些实施例都属于本发明保护范围。
Claims (8)
1.一种尼龙印刷耐高温蒸煮水性油墨，其特征在于，按重量比，原料为如下组分：
1)所述的水性聚氨酯分子量在20000～25000，固含量为30～35％，通过以下方法制成：所述的水性聚氨酯的原料组成按重量比由聚碳酸酯二元醇50～55份、异佛尔酮二异氰酸酯15～20份、二月桂酸二丁基锡10～15份和二羟甲基丙酸5～10份组成；称取聚碳酸酯二元醇和异佛尔酮二异氰酸酯加入到反应釜，加热并缓慢搅拌，保持温度在50～60℃高速搅拌20～40min，开始滴加剩余原料，最后加入水，并迅速将反应釜温度降至20～30℃，测试合成的水性聚氨酯的各项性能，各指标达到要求后，包装待用；
2)所述的水性消泡剂是含脂肪族矿物油的混合物；
3)所述的表面润湿剂是聚醚硅氧烷共聚物；
4)所述的水性pH值中和剂是荷兰艾德化学的活性含量90％的水溶性氨基醇混合物；
5)所述的润湿分散剂不含VOC和溶剂；
6)所述的水性快干剂是丙烯酸型氧化锌乳液，其制备方法为：先用154g水溶解112g碳酸铵3～5分钟，再添加75g氧化锌，2～3分钟后变成不透明液体，再加入159g的28％浓度的氨水，3～5分钟后得500g含量为15％的氧化锌溶液；取15份氧化锌溶液，往氧化锌溶液中顺序加入2份28％的氨水、15份去离子水和68份水性丙烯酸乳液，得到所述的水性丙烯酸型快干剂；
所述的固化剂是上海尤恩化工型号178固化剂。
2.根据权利要求1所述的尼龙印刷耐高温蒸煮水性油墨，其特征在于，所述的颜料为耐200℃高温的有机颜料或无机颜料。
3.根据权利要求2所述的尼龙印刷耐高温蒸煮水性油墨，其特征在于，所述的有机颜料为经过颜料化处理的缩合偶氮类、苯并咪唑酮偶氮类、酞青蓝BGS和酞青绿G中的至少一种；所述的无机颜料为金红石型钛白粉或高色素炭黑。
4.根据权利要求1所述的尼龙印刷耐高温蒸煮水性油墨，其特征在于，所述的水性消泡剂是Tego Foamex K8。
5.根据权利要求1所述的尼龙印刷耐高温蒸煮水性油墨，其特征在于，所述的表面润湿剂是Tego Flow425。
6.根据权利要求1所述的尼龙印刷耐高温蒸煮水性油墨，其特征在于，所述的润湿分散剂是德国毕克化学润湿分散剂BYK-191。
7.一种尼龙印刷耐高温蒸煮水性油墨的制备方法，包括以下步骤：
1)按照权利要求1所述的尼龙印刷耐高温蒸煮水性油墨的原料组成称取各原料；
2)加入15～20％水性聚氨酯到反应釜中，再缓慢加入部分水性消泡剂和其他助剂，低速搅拌10～15分钟；
3)向反应釜中加入颜料，高速搅拌，研磨至物料细度达到要求为止；
4)加入剩余水性聚氨酯和水性消泡剂，高速搅拌20～40min，再加入水调整所需黏度，继续高速搅拌5～10分钟，过滤包装。
8.权利要求1～6任一项所述尼龙印刷耐高温蒸煮水性油墨或权利要求7所述制备方法制备的尼龙印刷耐高温蒸煮水性油墨在尼龙印刷中的应用。