CN114671691A - 一种包衬可塑料 - Google Patents
一种包衬可塑料 Download PDFInfo
- Publication number
- CN114671691A CN114671691A CN202210215622.0A CN202210215622A CN114671691A CN 114671691 A CN114671691 A CN 114671691A CN 202210215622 A CN202210215622 A CN 202210215622A CN 114671691 A CN114671691 A CN 114671691A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic material
- clay
- borax
- graphite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种包衬可塑料,包括以下组分:石英砂、碳化硅、石墨、粘土、草酸、硼砂、硅酸钠,其由以下重量份组分组成:石英砂20‑70份、碳化硅0‑30份、硅微粉0‑30份、石墨0‑30份、粘土0‑30份、草酸0‑30份、硼砂0‑30份、硅酸钠0‑30份及微量进口化工,所述包衬可塑料可根据钢水包的形状进行塑造,且修补方便,无需使用胎具;所述包衬可塑料使用后,不会产生挂渣现象;所述包衬可塑料具有很强的耐侵蚀及抗冲刷性能;所述包衬可塑料使用后,一次烤干后可多次重复使用;所述包衬可塑料使用时会产生镜面化的烧结层,可提高钢水的质量,降低铸件的废品率。
Description
技术领域
本发明涉及耐火材料技术领域,具体是指一种包衬可塑料。
背景技术
钢水包也叫盛钢桶是冶金工业的重要容器件,起着储存、转运钢水的作用,同时还要进行炉外精炼的双重任务,随着炼钢技术的发展,我国的钢水包用耐火材料也得到了很好的发展,钢水包使用寿命的长短,不仅关系到耐火材料的消耗,而且直接影响炼钢的正常生产;
耐火可塑料是不定型耐火材料的一个重要品种,是由粒状和粉状物料与可塑黏土等结合剂和增塑剂配合后,再加入少量水分,经充分混炼所组成的一种呈硬泥膏状,并在较长时间内保持较高可塑性的不定型耐火材料,能够耐受较高的温度;
目前国内的钢水包炉衬主要是砖和不定形耐火材料并存并用的状态,近几年特别是随着转炉寿命的提高,连铸比的增加和炉外精炼技术的进步,钢水包处于容量大、钢种多、温度高、时间长等日益苛刻的使用条件,对钢水包用耐火材料的要求也不断提高。
发明内容
本发明要解决的技术问题是克服上述技术的缺陷,提供一种包衬可塑料。
为解决上述技术问题,本发明提供的技术方案为一种包衬可塑料,包括以下组分:石英砂、碳化硅、硅微粉、石墨、粘土、草酸、硼砂、硅酸钠及微量进口化工。
进一步地,由以下重量份组分组成:石英砂20-70份、碳化硅0-30份、硅微粉0-30份、石墨0-30份、粘土0-30份、草酸0-30份、硼砂0-30份、硅酸钠0-30份及微量进口化工。
进一步地,由以下重量份组分组成:石英砂20份、碳化硅1份、硅微粉1份、石墨1份、粘土1份、草酸1份、硼砂1份、硅酸钠1份及微量进口化工。
进一步地,由以下重量份组分组成:石英砂45份、碳化硅10份、硅微粉20份、石墨10份、粘土10份、草酸5份、硼砂10份、硅酸钠10份及微量进口化工。
进一步地,由以下重量份组分组成:石英砂70份、碳化硅5份、硅微粉10份、石墨5份、粘土5份、草酸5份、硼砂5份、硅酸钠5份及微量进口化工。
本发明与现有技术相比的优点在于:
1)所述包衬可塑料可根据钢水包的形状进行塑造,且修补方便,无需使用胎具;
2)所述包衬可塑料使用后,不会产生挂渣现象;
3)所述包衬可塑料具有很强的耐侵蚀及抗冲刷性能;
4)所述包衬可塑料使用后,一次烤干后可多次重复使用;
5)所述包衬可塑料使用时会产生镜面化的烧结层,可提高钢水的质量,降低铸件的废品率。
具体实施方式
下面结合实施例对本发明一种包衬可塑料做进一步的详细说明。
实施例1
一种包衬可塑料,由以下重量份组分组成:石英砂20份、碳化硅1份、硅微粉1份、石墨1份、粘土1份、草酸1份、硼砂1份、硅酸钠1份及微量进口化工。
实施例2
一种包衬可塑料,由以下重量份组分组成:石英砂45份、碳化硅10份、硅微粉20份、石墨10份、粘土10份、草酸5份、硼砂10份、硅酸钠10份及微量进口化工。
实施例3
一种包衬可塑料,由以下重量份组分组成:石英砂70份、碳化硅5份、硅微粉10份、石墨5份、粘土5份、草酸5份、硼砂5份、硅酸钠5份及微量进口化工。
实施例4
一种包衬可塑料,由以下重量份组分组成:石英砂70份、碳化硅15份、硅微粉0.5份、石墨5份、粘土15份、硼砂5份、硅酸钠5份及微量进口化工。
实施例5
一种包衬可塑料,由以下重量份组分组成:石英砂45份、碳化硅5份、硅微粉25份、石墨15份、粘土15份、草酸5份、硼砂10份、硅酸钠5份及微量进口化工。
实施例6
一种包衬可塑料,由以下重量份组分组成:石英砂40份、碳化硅5份、硅微粉30份、石墨10份、粘土10份、草酸15份、硼砂15份、硅酸钠5份及微量进口化工。
以上对本发明及其实施方式进行了描述,这种描述没有限制性。总而言之如果本领域的普通技术人员受其启示,在不脱离本发明创造宗旨的情况下,不经创造性的设计出与该技术方案相似的结构方式及实施例,均应属于本发明的保护范围。
Claims (5)
1.一种包衬可塑料,其特征在于,包括以下组分:石英砂、碳化硅、硅微粉、石墨、粘土、草酸、硼砂、硅酸钠及微量进口化工。
2.根据权利要求1所述的一种包衬可塑料,其特征在于,由以下重量份组分组成:石英砂20-70份、碳化硅0-30份、硅微粉0-30份、石墨0-30份、粘土0-30份、草酸0-30份、硼砂0-30份、硅酸钠0-30份。
3.根据权利要求1所述的一种包衬可塑料,其特征在于,由以下重量份组分组成:石英砂20份、碳化硅1份、硅微粉1份、石墨1份、粘土1份、草酸1份、硼砂1份、硅酸钠1份。
4.根据权利要求1所述的一种包衬可塑料,其特征在于,由以下重量份组分组成:石英砂45份、碳化硅10份、硅微粉20份、石墨10份、粘土10份、草酸5份、硼砂10份、硅酸钠10份。
5.根据权利要求1所述的一种包衬可塑料,其特征在于,由以下重量份组分组成:石英砂70份、碳化硅5份、硅微粉10份、石墨5份、粘土5份、草酸5份、硼砂5份、硅酸钠5份。