CN114213933A - Water-based two-component epoxy coating applied to wet-on-wet process and preparation method thereof - Google Patents
Water-based two-component epoxy coating applied to wet-on-wet process and preparation method thereof Download PDFInfo
- Publication number
- CN114213933A CN114213933A CN202111488892.0A CN202111488892A CN114213933A CN 114213933 A CN114213933 A CN 114213933A CN 202111488892 A CN202111488892 A CN 202111488892A CN 114213933 A CN114213933 A CN 114213933A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- wet
- water
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-based two-component epoxy coating applied to a wet-on-wet process and a preparation method thereof, and relates to the water-based two-component epoxy coating applied to the wet-on-wet process, which comprises a component A and a component B, wherein the component A comprises the following components in parts by weight: 20-35 parts of aqueous epoxy emulsion, 3-5 parts of antirust pigment, 1-3 parts of coloring pigment, 10-20 parts of extender, 5-10 parts of elastic polyacrylic emulsion, 1-3 parts of solvent, 1-2 parts of dispersing agent, 0.3-1 part of defoaming agent, 0.3-1 part of wetting agent, 0.5-1 part of flash rust inhibitor, 0.5-2 parts of thickening agent and 10-20 parts of deionized water; the component B comprises the following components in parts by weight: 20-50 parts of water-based amine curing agent, 15-30 parts of cosolvent and 20-30 parts of deionized water; the paint prepared by the invention has the advantages of extremely low VOC emission, excellent environmental protection performance, good water resistance and humidity resistance, ensures that a paint film has good leveling property, is not easy to crack and has good mechanical performance when the engineering machinery works in a high-temperature low-humidity environment, and is particularly suitable for the construction of the engineering machinery.
Description
Technical Field
The invention belongs to the technical field of coatings, and particularly relates to a water-based two-component epoxy coating applied to a wet-on-wet process and a preparation method thereof.
Background
In recent years, the national form of environmental protection is severe, and the industrial coating industry has gradually developed from the traditional solvent-based coating to the green coating. The water-based paint has the advantages that the discharge of VOC (volatile organic compounds) of the water-based paint is greatly reduced compared with that of a solvent-based paint by comprehensively analyzing the aspects of safety, coating performance, energy consumption, construction difficulty, equipment universality degree, economy and the like, and meanwhile, the water-based paint has low smell and low harm to human bodies and is more suitable for sensitive people.
At present, a matched coating product commonly used for engineering machinery is a water-based epoxy coating. And because the parts of the engineering machinery are mostly made of large and thick steel, the heat capacity of the workpiece is very large, the workpiece heating efficiency is relatively low, the energy consumption is large, the coating efficiency is extremely low, and the primer of the current engineering machinery field process needs to be baked when not completely dried, so that the construction efficiency is greatly delayed.
In order to solve the above-mentioned technical problems, research has been conducted on a water-based epoxy coating that can be wet-on-wet without baking. For example, Chinese patent publication No. CN 112831248A discloses a wet-on-wet ultra-fast dry water-based epoxy primer and a preparation method thereof, the components of the primer comprise a component A and a component B, wherein the raw materials of the component A comprise, by weight, 25-50 parts of epoxy resin, 0.1-0.5 part of defoaming agent, 0.1-1 part of anti-settling agent, 2-10 parts of pigment, 20-50 parts of filler, 0-10 parts of anti-rust pigment and 0-20 parts of deionized water; the raw materials of the component B comprise a water-based curing agent, the finally prepared water-based epoxy primer capable of being wetted by wet and ultra-fast dried is prepared at intervals of 10min on the bottom surface, the finish paint has no defects of air bubble miliaria and the like, and the water-based epoxy primer has good glossiness, realizes real wet and wet, greatly improves the construction efficiency, and is particularly suitable for assembly line construction. Although the invention achieves the effects of quick drying, no need of baking, no bubble miliaria in a paint film and the like, the quick-drying waterborne epoxy coating easily causes the problems of quick drying, poor leveling property of the paint film, cracking of the paint film, poor mechanical property and the like in a high-temperature low-humidity environment.
Disclosure of Invention
The invention aims to overcome the defects of the prior art and provides a water-based two-component epoxy coating applied to a wet-on-wet process and a preparation method thereof.
In order to achieve the aim, the invention designs a water-based two-component epoxy coating applied to a wet-on-wet process, which comprises a component A and a component B, wherein the component A is a main component of the water-based two-component epoxy coating applied to the wet-on-wet process and comprises the following raw materials in parts by weight:
20-35 parts of water-based epoxy emulsion,
3-5 parts of an anti-rust pigment,
1-3 parts of a coloring pigment,
10-20 parts of an extender filler,
5-10 parts of elastic polyacrylic acid emulsion,
1-3 parts of a solvent, namely,
1-2 parts of a dispersing agent,
0.3 to 1 portion of defoaming agent,
0.3 to 1 portion of wetting agent,
0.5-1 part of flash rust inhibitor,
0.5 to 2 portions of thickening agent,
10-20 parts of deionized water;
the component B is a curing agent part of a water-based bi-component epoxy coating applied to a wet-on-wet process, and comprises the following raw materials in parts by weight:
20-50 parts of a water-based amine curing agent,
15-30 parts of a cosolvent,
20-30 parts of deionized water.
Preferably, the water-based two-component epoxy coating applied to the wet-on-wet process further comprises the step of using the water-based epoxy emulsion as a base resin, and carrying out special molecular weight design and functional group modification on the quick-drying water-based epoxy emulsion.
Preferably, the aqueous two-component epoxy coating applied to the wet-on-wet process further comprises zirconium beads which are required to be added in the preparation process of the component A.
The preparation method of the water-based double-component epoxy coating applied to the wet-on-wet process comprises the following specific steps:
preparation of a component A:
(1) sequentially adding deionized water, a dispersing agent and a defoaming agent into a stirring container, dispersing for 5-10 minutes under the stirring condition of 800 revolutions per minute in 500 plus materials, and then sequentially adding an antirust pigment, a coloring pigment and an extender filler, and dispersing for 15 minutes at a high speed under the stirring condition of 1500 revolutions per minute in 1000 plus materials;
(2) adding zirconium beads, dispersing at high speed under the condition of 2000-2500 rpm, filtering and pouring into a paint mixing cylinder when the fineness reaches below 30 micrometers;
(3) in a paint mixing cylinder, sequentially adding the water-based epoxy emulsion, the elastic polyacrylic acid emulsion, the solvent, the defoaming agent, the wetting agent, the flash rust inhibitor and the thickening agent into the paint mixing cylinder for dispersing for 10-15 minutes under the stirring condition of 500-800 r/min respectively to prepare a component A;
b, preparation of a component:
sequentially adding deionized water, cosolvent and amine curing agent into a clean paint mixing cylinder, controlling the feeding time within 30 minutes, and stirring for 15 minutes to prepare a component B;
a preparation method of a water-based two-component epoxy coating applied to a wet-on-wet process comprises the following steps:
and mixing the component A and the component B according to the mass ratio of 7:1, and then adding 10% of water according to the construction viscosity requirement for mixing to obtain the water-based two-component epoxy coating applied to the wet-on-wet process.
Compared with the prior art, the invention has the following advantages:
1. low VOC emission and excellent environmental protection performance;
2. the paint film has good leveling property, is not easy to crack and has good mechanical property when the engineering machinery operates in a high-temperature low-humidity environment.
Detailed Description
The present invention will be further described with reference to the following examples. The following examples will assist those skilled in the art in further understanding the invention, but are not intended to limit the invention in any way. It should be noted that, for a person skilled in the art, several variations and modifications can be made without departing from the inventive concept, which falls within the scope of the present invention.
The key to realizing the water-based wet-on-wet coating is to adjust the drying speed of the water-based epoxy primer and control the volatilization gradient between two coatings. When the formula of the waterborne two-component epoxy primer is designed, the proper epoxy emulsion, amine curing agent, solvent system, flexible resin, and matched auxiliary agent system and pigment and filler system are screened through experiments under the condition of meeting the performance. The aqueous two-component epoxy systems require a particularly optimized equivalence ratio and play a crucial role in the paint film properties. Meanwhile, when the pigment volume concentration of the formula is designed, optimization design is required according to the characteristics of different powder and resin, so that the influence on the coating performance and dryness is great, and the influence on the appearance effect of the water-based double-component polyurethane finish paint in the field of wet-on-wet application is great.
The concrete steps of the embodiment are as follows;
(1) preparation of a component A: sequentially adding deionized water, a dispersing agent and a defoaming agent into a stirring container, dispersing for 5-10 minutes under the stirring condition of 800 revolutions per minute in 500 plus materials, and then sequentially adding an antirust pigment, a coloring pigment and an extender filler, and dispersing for 15 minutes at a high speed under the stirring condition of 1500 revolutions per minute in 1000 plus materials; adding zirconium beads, dispersing at high speed under the condition of 2000-2500 rpm, filtering and pouring into a paint mixing cylinder when the fineness reaches below 30 micrometers; in a paint mixing cylinder, sequentially adding the water-based epoxy emulsion, the elastic polyacrylic acid emulsion, the solvent, the defoaming agent, the wetting agent, the flash rust inhibitor and the thickening agent into the paint mixing cylinder for dispersing for 10-15 minutes under the stirring condition of 500-800 r/min respectively to prepare a component A;
(2) b, preparation of a component: sequentially adding deionized water, cosolvent and amine curing agent into a clean paint mixing cylinder, controlling the feeding time within 30 minutes, and stirring for 15 minutes to prepare a component B;
(3) a preparation method of a water-based two-component epoxy coating applied to a wet-on-wet process comprises the following steps: and mixing the component A and the component B according to the mass ratio of 7:1, and then adding 10% of water according to the construction viscosity requirement for mixing to obtain the water-based two-component epoxy coating applied to the wet-on-wet process.
The following examples are compared to conventional waterborne and solvent borne coatings for performance and are shown in Table 1:
TABLE 1
As can be seen from Table 1, the physicochemical properties of the aqueous wet-on-wet coating of the embodiment have the advantages of minimum VOC content, excellent environmental protection performance, good water resistance, good humidity resistance and good drying performance, and ensures that the leveling property of the paint film is good, the paint film is not easy to crack and the mechanical performance is good when the engineering machinery operates in a high-temperature low-humidity environment.
The above description is only for the purpose of illustrating the preferred embodiments of the present invention and is not to be construed as limiting the invention, and any modifications, equivalents, improvements and the like that fall within the spirit and principle of the present invention are intended to be included therein.
Claims (4)
1. The aqueous two-component epoxy coating applied to the wet-on-wet process comprises a component A and a component B, wherein the component A is a main component of the aqueous two-component epoxy coating applied to the wet-on-wet process, and the main raw materials comprise the following components in parts by weight:
20-35 parts of water-based epoxy emulsion,
3-5 parts of an anti-rust pigment,
1-3 parts of a coloring pigment,
10-20 parts of an extender filler,
5-10 parts of elastic polyacrylic acid emulsion,
1-3 parts of a solvent, namely,
1-2 parts of a dispersing agent,
0.3 to 1 portion of defoaming agent,
0.3 to 1 portion of wetting agent,
0.5-1 part of flash rust inhibitor,
0.5 to 2 portions of thickening agent,
10-20 parts of deionized water;
the component B is a curing agent part of a water-based bi-component epoxy coating applied to a wet-on-wet process, and comprises the following raw materials in parts by weight:
20-50 parts of a water-based amine curing agent,
15-30 parts of a cosolvent,
20-30 parts of deionized water.
2. The waterborne two-component epoxy coating applied to the wet-on-wet process according to claim 1, wherein the waterborne epoxy emulsion is a fast-drying waterborne epoxy emulsion based on solid epoxy resin and modified by special molecular weight design and functional groups.
3. The two-component waterborne epoxy coating for use in a wet-on-wet process of claim 1, wherein the A component requires the addition of zirconium beads during the preparation process.
4. A method of preparing a two-component waterborne epoxy coating for use in a wet-on-wet process according to any of claims 1-3, wherein the step of preparing the a-component comprises:
(1) sequentially adding deionized water, a dispersing agent and a defoaming agent into a stirring container, dispersing for 5-10 minutes under the stirring condition of 800 revolutions per minute in 500 plus materials, and then sequentially adding an antirust pigment, a coloring pigment and an extender filler, and dispersing for 15 minutes at a high speed under the stirring condition of 1500 revolutions per minute in 1000 plus materials;
(2) adding zirconium beads, dispersing at high speed under the condition of 2000-2500 rpm, filtering and pouring into a paint mixing cylinder when the fineness reaches below 30 micrometers;
(3) in a paint mixing cylinder, sequentially adding the water-based epoxy emulsion, the elastic polyacrylic acid emulsion, the solvent, the defoaming agent, the wetting agent, the flash rust inhibitor and the thickening agent into the paint mixing cylinder for dispersing for 10-15 minutes under the stirring condition of 500-800 r/min respectively to prepare a component A;
the preparation method of the component B comprises the following steps: sequentially adding deionized water, cosolvent and amine curing agent into a clean paint mixing cylinder, controlling the feeding time within 30 minutes, and stirring for 15 minutes to prepare a component B;
the preparation method of the water-based two-component epoxy coating applied to the wet-on-wet process comprises the steps of mixing the component A and the component B according to the mass ratio of 7:1, and then adding 10% of water according to the construction viscosity requirement for mixing to obtain the water-based two-component epoxy coating applied to the wet-on-wet process.