CN113782331A - 一种高性能双硬磁相纳米复合磁体的制备方法 - Google Patents
一种高性能双硬磁相纳米复合磁体的制备方法 Download PDFInfo
- Publication number
- CN113782331A CN113782331A CN202111096922.3A CN202111096922A CN113782331A CN 113782331 A CN113782331 A CN 113782331A CN 202111096922 A CN202111096922 A CN 202111096922A CN 113782331 A CN113782331 A CN 113782331A
- Authority
- CN
- China
- Prior art keywords
- magnetic
- powder
- mnbi
- magnetic powder
- equal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种高性能双硬磁相纳米复合磁体的制备方法,属于磁性材料技术领域。该制备方法包括:分别制备Ce基纳米晶磁粉和MnBi基纳米晶磁粉,然后将其按一定的质量比例混合均匀后进行高能球磨,通过氩气高速气流将软磁α‑Fe粉进行加速,并喷射到球磨罐体里的混合磁粉中,使α‑Fe粉能够充分包覆Ce基磁粉和MnBi基磁粉的表面,获得混合粉体;随后通过磁场取向低温辅助成型技术制备压坯,并采用磁场辅助激光快烧技术对压坯进行烧结处理,实现了双硬磁相和软磁相之间的有效复合,提升了耦合强度,制得高性能双硬磁相纳米复合磁体。有利于该磁体在更多器件中的应用,以满足市场需求。
Description
技术领域
本发明涉及磁性材料技术领域,尤其涉及一种高性能双硬磁相纳米复合磁体的制备方法。
背景技术
近年来,随着世界稀土资源的日益减少、价格快速增长,及时开发一类新型高磁性低稀土永磁体,是磁性产品发展的要求,更是我国稀土产业可持续发展的重大课题。MnBi永磁体具有价格低廉、不易腐蚀、力学性能好等优点,特别是它在一定温度范围内矫顽力呈正的温度系数,可以弥补稀土永磁体的不足之处。将(Ce,Nd)-Fe-B合金与MnBi合金在纳米尺度进行复合,通过纳米晶之间的两相交换耦合作用,该纳米复合磁体可以兼具MnBi合金的高磁晶各向异性和(Ce,Nd)-Fe-B永磁材料的高饱和磁化强度,同时可以弥补(Ce,Nd)永磁体温度稳定性差的不足之处,以期获得低矫顽力温度系数甚至正矫顽力温度系数的复合永磁体。
双相纳米晶结构永磁体中的硬磁相为合金提供高的矫顽力,软磁相为合金提供高的剩磁,两相之间的交换耦合作用直接体现在了合金的磁性能。目前,国内外研究较多的是NdFeB/α-Fe、SmCo/(α-Fe,Fe-Co)等复合磁体上。而在双硬磁相复合磁体中,对其研究的较少。因此,本专利创造性的采用Ce基纳米晶合金和MnBi基纳米晶合金作为双硬磁相,同时通过氩气高速气流将软磁α-Fe粉进行加速并喷射到球磨罐体里的混合磁粉中,使α-Fe粉能够充分包覆Ce基磁粉和MnBi基磁粉的表面,获得混合粉体;另外,本专利采用磁场辅助激光快烧技术,利用磁场提升了磁体晶粒取向的一致性,实现了双硬磁相和软磁相的有效复合和耦合增强,最终获得了高性能双硬磁相纳米复合磁体。
发明内容
针对现有技术中存在的问题,本发明目的在于提供一种高性能双硬磁相纳米复合磁体的制备方法。
本发明的高性能双硬磁相纳米复合磁体的制备方法,包括如下步骤:
(1)采用熔体快淬法制备Ce基合金薄带,铜辊转速为18~48 m/s;随后通过行星式球磨将合金薄带破碎至粒度为1~10 μm的磁粉,球磨时间为1~3 h;然后将磁粉在400~700℃下晶化时效热处理,热处理时间为5~30 min,制得Ce基纳米晶磁粉;
(2)采用真空感应熔炼制备MnBi基铸锭,随后将MnBi基铸锭在200~400 ℃下时效热处理,时效热处理时间为5~10 h;采用高能球磨工艺将MnBi基铸锭破碎至粒度为2~8μm的MnBi基纳米晶磁粉,高能球磨的时间为4~10 h;
(3)将步骤(1)获得的Ce基纳米晶磁粉和步骤(2)获得的MnBi基纳米晶磁粉按一定的质量比例混合均匀后进行高能球磨,球磨时间为10~40 min;整个球磨运行过程中,通过氩气高速气流将粒径为15~50 nm的软磁α-Fe粉加速到20~40 m/s后,喷射到球磨罐体里的混合磁粉中,使α-Fe粉能够充分包覆Ce基磁粉和MnBi基磁粉的表面,获得混合粉体;
(4)将步骤(3)获得的混合粉体进行磁场取向低温辅助成型技术制备压坯,磁场强度为1~3 T,温度为100~150 ℃,压力为50~150 MPa;
(5)采用磁场辅助激光快烧技术对压坯进行烧结处理,实现双硬磁相纳米复合磁体内部晶界润滑,磁场强度为4~8 T,激光功率为600~1200 W,光斑直接为3~5 mm,升温速率为40~80 ℃/s,烧结温度为400~800 ℃,保温时间为1~3 min。
进一步的,步骤(1)中所述的Ce基合金为按原子百分比的(CexNd1-x)aFe100-a-b- cRbBc,x,a,b和c满足以下关系:0.5≤x≤1,4≤a≤12,1≤b≤4,8≤c≤15,R为Co、Hf、Ti、Cr、Ni,Si、Ga、Mn、Al中的一种或几种。
进一步的,步骤(2)中所述的MnBi基合金为按原子百分比的MnaBibR100-a-b,a和b 满足以下关系:20≤a≤35,60≤b≤80,R为V、Mo、Si、Ga、Ni、Zr,Ti中的一种或几种。
进一步的,步骤(3)中所述的Ce基纳米晶磁粉和MnBi基纳米晶磁粉的质量比例为1~10:1。
与现有的技术相比,本发明具有如下优点和有益效果:本发明通过氩气高速气流将软磁α-Fe粉进行加速并喷射到球磨罐体里的混合磁粉中,使α-Fe粉能够充分包覆Ce基磁粉和MnBi基磁粉的表面;同时通过磁场辅助激光快烧技术有效抑制了Ce-Nd-Fe-B相和Mn-Bi相元素的互扩散、相分离;利用磁场提升了磁体晶粒取向的一致性,磁体中Ce-Nd-Fe-B相提供较高的矫顽力,MnBi相提供较高的正矫顽力温度系数,巧妙地利用了软磁α-Fe粉的包覆,实现了双硬磁相和软磁相的有效复合和耦合增强,最终获得了高性能双硬磁相纳米复合磁体。
具体实施方式
下面将结合实施例对本发明做进一步的详细说明,但本发明并不仅仅局限于以下实施例。
实施例1
(1)采用熔体快淬法制备(Ce0.9Nd0.1)4Fe81R1B14 (R=Co0.5Ti0.5)合金薄带,铜辊转速为18 m/s;随后通过行星式球磨将合金薄带破碎至粒度为10 μm的磁粉,球磨时间为1 h;然后将磁粉在480 ℃下晶化时效热处理,热处理时间为5 min,制得Ce基纳米晶磁粉;
(2)采用真空感应熔炼制备Mn20Bi75R5 (R=V0.5Zr0.5)铸锭,随后将铸锭在200 ℃下时效热处理,时效热处理时间为5 h;采用高能球磨工艺将铸锭破碎至粒度为2 μm的MnBi基纳米晶磁粉,高能球磨的时间为10 h;
(3)将步骤(1)获得的Ce基纳米晶磁粉和步骤(2)获得的MnBi基纳米晶磁粉按质量比例为1:1的比例混合均匀后进行高能球磨,球磨时间为10 min;整个球磨运行过程中,通过氩气高速气流将粒径为50 nm的软磁α-Fe粉加速到20 m/s后,喷射到球磨罐体里的混合磁粉中,使α-Fe粉能够充分包覆Ce基磁粉和MnBi基磁粉的表面,获得混合粉体;
(4)将步骤(3)获得的混合粉体进行磁场取向低温辅助成型技术制备压坯,磁场强度为1 T,温度为100 ℃,压力为60 MPa;
(5)采用磁场辅助激光快烧技术对压坯进行烧结处理,实现双硬磁相纳米复合磁体内部晶界润滑,磁场强度为4 T,激光功率为600 W,光斑直接为5 mm,升温速率为80 ℃/s,烧结温度为500 ℃,保温时间为3 min,获得具有高磁性能的双硬磁相纳米复合磁体。
采用本发明制备的高性能双硬磁相纳米复合磁体经磁性能测量,矫顽力为21.7kOe,磁能积为26.8 MGOe,密度为7.83 g/cm3。
实施例2
(1)采用熔体快淬法制备 (Ce0.7Nd0.3)8Fe79R2B11 (R=Ti0.7Ga0.3)合金薄带,铜辊转速为30 m/s;随后通过行星式球磨将合金薄带破碎至粒度为6 μm的磁粉,球磨时间为2 h;然后将磁粉在550 ℃下晶化时效热处理,热处理时间为15 min,制得Ce基纳米晶磁粉;
(2)采用真空感应熔炼制备Mn27Bi69R4 (R=Mo0.7Ti0.3)铸锭,随后将铸锭在300 ℃下时效热处理,时效热处理时间为8 h;采用高能球磨工艺将铸锭破碎至粒度为5 μm的MnBi基纳米晶磁粉,高能球磨的时间为8 h;
(3)将步骤(1)获得的Ce基纳米晶磁粉和步骤(2)获得的MnBi基纳米晶磁粉按质量比例为4:1的比例混合均匀后进行高能球磨,球磨时间为25 min;整个球磨运行过程中,通过氩气高速气流将粒径为40 nm的软磁α-Fe粉加速到30 m/s后,喷射到球磨罐体里的混合磁粉中,使α-Fe粉能够充分包覆Ce基磁粉和MnBi基磁粉的表面,获得混合粉体;
(4)将步骤(3)获得的混合粉体进行磁场取向低温辅助成型技术制备压坯,磁场强度为2 T,温度为125 ℃,压力为90 MPa;
(5)采用磁场辅助激光快烧技术对压坯进行烧结处理,实现双硬磁相纳米复合磁体内部晶界润滑,磁场强度为6 T,激光功率为900 W,光斑直接为4 mm,升温速率为60 ℃/s,烧结温度为650 ℃,保温时间为2 min,获得具有高磁性能的双硬磁相纳米复合磁体。
采用本发明制备的高性能双硬磁相纳米复合磁体经磁性能测量,矫顽力为23.5kOe,磁能积为27.9 MGOe,密度为7.87 g/cm3。
实施例3
(1)采用熔体快淬法制备 (Ce0.5Nd0.5)12Fe76R4B8 (R=Cr0.3Mn0.3Al0.3Ni0.1)合金薄带,铜辊转速为45 m/s;随后通过行星式球磨将合金薄带破碎至粒度为3 μm的磁粉,球磨时间为3 h;然后将磁粉在680 ℃下晶化时效热处理,热处理时间为25 min,制得Ce基纳米晶磁粉;
(2)采用真空感应熔炼制备Mn34Bi63R3 (R=Si0.4Ga0.4Zr0.2)铸锭,随后将铸锭在400℃下时效热处理,时效热处理时间为10 h;采用高能球磨工艺将铸锭破碎至粒度为8 μm的MnBi基纳米晶磁粉,高能球磨的时间为5 h;
(3)将步骤(1)获得的Ce基纳米晶磁粉和步骤(2)获得的MnBi基纳米晶磁粉按质量比例为8:1的比例混合均匀后进行高能球磨,球磨时间为40 min;整个球磨运行过程中,通过氩气高速气流将粒径为20 nm的软磁α-Fe粉加速到40 m/s后,喷射到球磨罐体里的混合磁粉中,使α-Fe粉能够充分包覆Ce基磁粉和MnBi基磁粉的表面,获得混合粉体;
(4)将步骤(3)获得的混合粉体进行磁场取向低温辅助成型技术制备压坯,磁场强度为3 T,温度为150 ℃,压力为135 MPa;
(5)采用磁场辅助激光快烧技术对压坯进行烧结处理,实现双硬磁相纳米复合磁体内部晶界润滑,磁场强度为8 T,激光功率为1200 W,光斑直接为3 mm,升温速率为40 ℃/s,烧结温度为800 ℃,保温时间为1 min,获得具有高磁性能的双硬磁相纳米复合磁体。
采用本发明制备的高性能双硬磁相纳米复合磁体经磁性能测量,矫顽力为24.9kOe,磁能积为28.3 MGOe,密度为7.89 g/cm3。
Claims (4)
1.一种高性能双硬磁相纳米复合磁体的制备方法,其特征在于包括如下步骤:
(1)采用熔体快淬法制备Ce基合金薄带,铜辊转速为18~48 m/s;随后通过行星式球磨将合金薄带破碎至粒度为1~10 μm的磁粉,球磨时间为1~3 h;然后将磁粉在400~700 ℃下晶化时效热处理,热处理时间为5~30 min,制得Ce基纳米晶磁粉;
(2)采用真空感应熔炼制备MnBi基铸锭,随后将MnBi基铸锭在200~400 ℃下时效热处理,时效热处理时间为5~10 h;采用高能球磨工艺将MnBi基铸锭破碎至粒度为2~8μm的MnBi基纳米晶磁粉,高能球磨的时间为4~10 h;
(3)将步骤(1)获得的Ce基纳米晶磁粉和步骤(2)获得的MnBi基纳米晶磁粉按一定的质量比例混合均匀后进行高能球磨,球磨时间为10~40 min;整个球磨运行过程中,通过氩气高速气流将粒径为15~50 nm的软磁α-Fe粉加速到20~40 m/s后,喷射到球磨罐体里的混合磁粉中,使α-Fe粉能够充分包覆Ce基磁粉和MnBi基磁粉的表面,获得混合粉体;
(4)将步骤(3)获得的混合粉体进行磁场取向低温辅助成型技术制备压坯,磁场强度为1~3 T,温度为100~150 ℃,压力为50~150 MPa;
(5)采用磁场辅助激光快烧技术对压坯进行烧结处理,实现双硬磁相纳米复合磁体内部晶界润滑,磁场强度为4~8 T,激光功率为600~1200 W,光斑直接为3~5 mm,升温速率为40~80 ℃/s,烧结温度为400~800 ℃,保温时间为1~3 min。
2.根据权利要求1 所述的一种高性能双硬磁相纳米复合磁体的制备方法,其特征在于:步骤(1)中所述的Ce基合金为按原子百分比的(CexNd1-x)aFe100-a-b-cRbBc,x,a,b和c满足以下关系:0.5≤x≤1,4≤a≤12,1≤b≤4,8≤c≤15,R为Co、Hf、Ti、Cr、Ni,Si、Ga、Mn、Al中的一种或几种。
3.根据权利要求1 所述的一种高性能双硬磁相纳米复合磁体的制备方法,其特征在于:步骤(2)中所述的MnBi基合金为按原子百分比的MnaBibR100-a-b,a和b 满足以下关系:20≤a≤35,60≤b≤80,R为V、Mo、Si、Ga、Ni、Zr,Ti中的一种或几种。
4.根据权利要求1 所述的一种高性能双硬磁相纳米复合磁体的制备方法,其特征在于:步骤(3)中所述的Ce基纳米晶磁粉和MnBi基纳米晶磁粉的质量比例为1~10:1。