CN112391184A - 用中等变质焦煤生产高反应性焦炭的配煤方法 - Google Patents
用中等变质焦煤生产高反应性焦炭的配煤方法 Download PDFInfo
- Publication number
- CN112391184A CN112391184A CN202011072686.7A CN202011072686A CN112391184A CN 112391184 A CN112391184 A CN 112391184A CN 202011072686 A CN202011072686 A CN 202011072686A CN 112391184 A CN112391184 A CN 112391184A
- Authority
- CN
- China
- Prior art keywords
- coal
- percent
- coking
- gas
- coking coal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用中等变质焦煤生产高反应性焦炭的配煤方法，（1）配合煤中各单种煤的质量百分配比：气煤比例5%；气肥煤比例28%；1/3焦煤10%；13#焦煤比例2%；1/2弱粘煤比例10%;主焦煤比例45%，其中中等变质焦煤比例占55%，焦煤比例45%；（2）配合煤的挥发分26‑27%，成焦率75‑77%；（3）配煤后的焦炭成分12.5%：热态强度CSR 35%‑40%，反应性CRI 55%‑65%，M40＞89%，M10＜6.5%；（4）所述的气煤粉碎细度≥80%、气肥煤粉碎细度80‑82%，1/3焦煤粉碎细度85%，1/2中粘煤粉碎细度82‑84%，主焦煤粉碎细度80‑84%。本发明方法利用气煤、气肥煤、焦煤、弱粘煤生产焦炭，降低生产成本，提高企业竞争力。
Description
技术领域
本发明涉及一种用中等变质焦煤生产高反应性焦炭的配煤方法。
背景技术
八钢公司作为新疆乃至西部最重要的钢铁企业，面对钢铁市场的低迷，价格持续走低，转变思想，突破技术禁锢，坚持“低成本、经济炼铁”的发展道路，进一步转变对自产艾矿煤煤质差、少量使用疆内焦煤的认识。扩大炼焦煤资源，大比例使用新疆煤，减少疆外主焦煤用量，解决疆内焦化企业面临的配煤难题，而这一难题的核心是确定疆外煤的质量标准，进而弥补疆内焦煤的不足特性。
目前国内外炼铁行业应用于高炉冶炼的焦炭质量，首选依据《高炉炼铁工艺设计规范》GB50427—2008，2000级以上的高炉CSR大于 60%，CRI小于25%。而按照此焦炭热态强度标准进行配煤生产，配煤结构中疆外煤最少77%，疆内煤为23%，这种配比的焦炭成本非常高，而铁水成本将事情核心竞争力，八钢将产生巨大的亏损。
检索文献（1）吴小兵、张建良、孔德文、高冰、左海滨，高反应性焦炭在日本的研究与进展 2012年全国炼铁生产技术会议暨炼铁学术年会，季羡林，新疆炼焦煤改质制备高强度冶金焦炭的研究，重庆大学2015可知，目前仍没有使用具有非同寻常的高反应性（CRI50％左右），热态强度低（CSR30%左右）这一特征的焦炭，仅能限于100～300m3的小型高炉使用，极难应用于1000m3以上的中大型高炉的生产实践，造成了新疆疆内焦煤资源成为闲置资源。检索文献，石国京，朱子宗，武强，新疆低质炼焦煤炼焦经济效益分析，2018年6月，内蒙古煤炭经济，了解到，新疆煤炭的分布特性是“北富南贫”，即北部地区较为丰富，南部地区相对较少。煤炭种类齐全，总体以低变质程度的低灰、低硫、低磷的长焰煤、不黏煤和弱黏煤为主，约占80%，灰分低于15%的煤约占预测资源总量的 47% ，硫分低于1%的约占80%。其中，中等变质程度的炼焦煤包括气煤、1 /3 焦煤、气肥煤、肥煤、1/2 中黏煤、焦煤、瘦煤和贫瘦煤资源相对较少，约占资源储量的19%，炼焦煤以气煤居多，约占全疆炼焦煤总量的50%以上。
发明内容
本发明的目的在于提供一种用中等变质焦煤生产高反应性焦炭的配煤方法，利用气煤、气肥煤、焦煤、弱粘煤生产焦炭，降低生产成本，提高企业竞争力。
实现上述目的的一种用中等变质焦煤生产高反应性焦炭的配煤方法，（1）配合煤中各单种煤的质量百分配比：气煤比例5%；气肥煤比例28%；1/3焦煤10%；13#焦煤比例2%；1/2弱粘煤比例10%;主焦煤比例45%，其中中等变质焦煤比例占55%，焦煤比例45%；
（2）配合煤的挥发分26-27%，成焦率75-77%；
（3）配煤后的焦炭成分12.5%：热态强度CSR 35%-40%，反应性CRI 55%-65% ，M40＞89%，M10＜6.5%；
（4）所述的气煤粉碎细度≥80%、气肥煤粉碎细度80-82%，1/3焦煤粉碎细度85%，1/2中粘煤粉碎细度82-84%，主焦煤粉碎细度80-84%。
气煤特性：具有高挥发分、低灰分、低硫、中等粘结、冷、热态强度差等 ；气肥煤特性：具有高挥发分、低灰分、低硫、高粘结、高胶质层厚度、冷态强度偏低等；1/3焦煤特性：具有中等挥发分、低灰分、低硫、一般粘结等 ；1/2弱粘煤特性：具有中等挥发分、低灰分、低硫、低粘结、较好的热态强度等；主焦煤与中等变质焦煤的价格对比。目前公司进厂的主焦煤价格约1400元/吨（不含税），中等变质焦煤的采购价值在约830元/吨(不含税)，两者间差距为570元/吨（不含税）。通过优化以疆内低成本炼焦煤为主的配煤结构炼焦生产实践表明，201*年疆内煤累计配比在46.4%，2015年疆内煤累计配比68.2%，较201*年提高了21.8%；201*年疆内煤累计配比82.8%，较201*年提高了14.57%，较2014年提高了36.41%；2014年疆内煤价格570元/吨，疆外煤价格1305元/吨；201*年疆内煤价格726元/吨，疆外煤价格1213元/吨；201*年疆内煤价格670元/吨，疆外煤价格1370元/吨；而配用疆内炼焦煤实际预示着八钢采用优化配煤技术后，实现了低热强度炼焦原料煤的高比例配用，至少比行业同等条件下使用优质炼焦煤减少20%以上。其技术成果推广将使行业产生巨大的经济和社会效益。
具体实施方式
一种用中等变质焦煤生产高反应性焦炭的配煤方法，（1）配合煤中各单种煤的质量百分配比：气煤比例5%；气肥煤比例28%；1/3焦煤10%；13#焦煤比例2%；1/2弱粘煤比例10%;主焦煤比例45%，其中中等变质焦煤比例占55%，焦煤比例45%；
（2）配合煤的挥发分26-27%，成焦率75-77%；
（3）配煤后的焦炭成分12.5%：热态强度CSR 35%-40%，反应性CRI 55%-65% ，M40＞89%，M10＜6.5%；
（4）所述的气煤粉碎细度≥80%、气肥煤粉碎细度80-82%，1/3焦煤粉碎细度85%，1/2中粘煤粉碎细度82-84%，主焦煤粉碎细度80-84%。
实例1：1/2弱粘煤+气煤+气肥煤+主焦
（1）各种单种煤质量
| 煤种 | 灰分/% | 挥发分/% | 硫分/% | 粘结G | 胶质层Y/mm |
| 气煤 | 7.5 | 41.2 | 0.4 | 80 | 11 |
| 气肥煤 | 7.09 | 39.21 | 0.41 | 103 | 37 |
| 1/2中粘煤 | 9.50 | 33.45 | 0.44 | 53 | 13 |
| 主焦煤 | 10.56 | 21.32 | 2.8 | 85 | 15 |
（2）配合煤成分
| 煤种 | 灰分/% | 挥发分/% | 硫分/% | 粘结G | 胶质层Y/mm |
| 配合煤 | 10.24 | 26.58 | 1.19 | 90 | 23 |
（3）焦炭质量、成本
| 品种 | 灰分/% | 挥发分/% | 硫分/% | M40/% | M10/% | CSR/% | CRI/% | MS/mm | 成本/元/吨 |
| 焦炭 | 12.82 | 1.06 | 1.17 | 89.43 | 6.16 | 41.85 | 52 | 53.67 | 1188 |
实例2：1/3焦煤+13#焦煤+气煤+气肥煤+主焦
（1）各种单种煤质量
| 煤种 | 灰分/% | 挥发分/% | 硫分/% | 粘结G | 胶质层Y/mm |
| 气煤 | 7.5 | 41.2 | 0.4 | 80 | 11 |
| 气肥煤 | 7.09 | 39.21 | 0.41 | 103 | 37 |
| 13#焦煤 | 10.77 | 16.86 | 0.43 | 43 | 10 |
| 1/3焦煤 | 3.7 | 32.4 | 0.54 | 80 | 16 |
| 主焦煤 | 10.56 | 21.32 | 2.8 | 85 | 15 |
（2）配合煤成分
| 煤种 | 灰分/% | 挥发分/% | 硫分/% | 粘结G | 胶质层Y/mm |
| 配合煤 | 9.74 | 26.99 | 0.99 | 91 | 24 |
（3）焦炭质量、成本
| 品种 | 灰分/% | 挥发分/% | 硫分/% | M40/% | M10/% | CSR/% | CRI/% | MS/mm | 成本/元/吨 |
| 焦炭 | 12.32 | 1.13 | 1.08 | 89.57 | 6.4 | 40.8 | 65.6 | 53.41 | 1177 |
实例3：1/3焦煤+气煤+气肥煤+主焦
（1）各种单种煤质量
| 煤种 | 灰分/% | 挥发分/% | 硫分/% | 粘结G | 胶质层Y/mm |
| 气煤 | 7.5 | 41.2 | 0.4 | 80 | 11 |
| 气肥煤 | 7.09 | 39.21 | 0.41 | 103 | 37 |
| 1/3焦煤 | 3.7 | 32.4 | 0.54 | 80 | 16 |
| 主焦煤 | 10.56 | 21.32 | 2.8 | 85 | 15 |
（2）配合煤成分
| 煤种 | 灰分/% | 挥发分/% | 硫分/% | 粘结G | 胶质层Y/mm |
| 配合煤 | 9.69 | 25.39 | 0.83 | 82 | 21 |
（3）焦炭质量、成本
| 品种 | 灰分/% | 挥发分/% | 硫分/% | M40/% | M10/% | CSR/% | CRI/% | MS/mm | 成本/元/吨 |
| 焦炭 | 12.33 | 1.11 | 0.82 | 89.33 | 6.4 | 35.9 | 40.1 | 53.33 | 1185 |
实例4：13#焦煤+气煤+气肥煤+主焦
（1）各种单种煤质量
| 煤种 | 灰分/% | 挥发分/% | 硫分/% | 粘结G | 胶质层Y/mm |
| 气煤 | 7.5 | 41.2 | 0.4 | 80 | 11 |
| 气肥煤 | 7.09 | 39.21 | 0.41 | 103 | 37 |
| 13#焦煤 | 10.77 | 16.86 | 0.43 | 43 | 10 |
| 主焦煤 | 10.56 | 21.32 | 2.8 | 85 | 15 |
（2）配合煤成分
| 煤种 | 灰分/% | 挥发分/% | 硫分/% | 粘结G | 胶质层Y/mm |
| 配合煤 | 9.56 | 25.32 | 0.90 | 86 | 22 |
（3）焦炭质量、成本
| 品种 | 灰分/% | 挥发分/% | 硫分/% | M40/% | M10/% | CSR/% | CRI/% | MS/mm | 成本/元/吨 |
| 焦炭 | 12.21 | 1.03 | 0.9 | 89.2 | 6.45 | 35.2 | 50.23 | 53.4 | 1215 |
Claims (1)
1.一种用中等变质焦煤生产高反应性焦炭的配煤方法，其特征在于：（1）配合煤中各单种煤的质量百分配比：气煤比例5%；气肥煤比例28%；1/3焦煤10%；13#焦煤比例2%；1/2弱粘煤比例10%;主焦煤比例45%，其中中等变质焦煤比例占55%，焦煤比例45%；
（2）配合煤的挥发分26-27%，成焦率75-77%；
（3）配煤后的焦炭成分12.5%：热态强度CSR 35%-40%，反应性CRI 55%-65% ，M40＞89%，M10＜6.5%；
（4）所述的气煤粉碎细度≥80%、气肥煤粉碎细度80-82%，1/3焦煤粉碎细度85%，1/2中粘煤粉碎细度82-84%，主焦煤粉碎细度80-84%。