CN110294986A - 一种高点蚀电位的松香基与丙烯酰胺热聚合防腐膜的制备方法 - Google Patents
一种高点蚀电位的松香基与丙烯酰胺热聚合防腐膜的制备方法 Download PDFInfo
- Publication number
- CN110294986A CN110294986A CN201910627322.1A CN201910627322A CN110294986A CN 110294986 A CN110294986 A CN 110294986A CN 201910627322 A CN201910627322 A CN 201910627322A CN 110294986 A CN110294986 A CN 110294986A
- Authority
- CN
- China
- Prior art keywords
- mol
- acrylamide
- thermal polymerization
- abietyl
- prevention film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种高点蚀电位的松香基与丙烯酰胺热聚合防腐膜的制备方法,以丙烯酰胺为单体、丙烯海松酸(乙二胺)酰胺为交联剂、偶氮二异丁腈为引发剂,通过热聚合方法制备了一种高点蚀电位的松香基与丙烯酰胺热聚合防腐膜,该膜层具有较高的点蚀电位,耐点腐蚀性能良好、简单实用,克服了以往防腐膜层腐蚀电位低的缺点。该膜层可应用于空调、电热水器、空调、冰箱等电气设备及拖拉机、起重机等机械设备的金属零部件的防腐工程。
Description
技术领域
本发明涉及防腐蚀涂膜领域,尤其是涉及一种高点蚀电位的松香基与丙烯酰胺热聚合防腐膜的制备方法。
背景技术
由于空调、电热水器、空调、冰箱等电气设备及拖拉机、起重机等机械设备的金属零部件,由于材料点蚀电位(Pitting corrosion potential)较低,极易受到周围环境的腐蚀,特别是金属零部件长期处于在潮湿、腐蚀介质的环境中极易引起点蚀、起粉、起泡等现象。目前处理的方法是在高分子涂层中添加大量的六价铬盐或四氧化三铅等重金属化合物,然而这类防腐涂层不断地有这些重金属铅等离子析出,严重污染海洋、河流及土壤环境,给全球生态环境及人体造成严重影响。但是由于目前没有适合的替代技术,因此,寻找适合的替代技术具有重要意义。
聚丙烯酰胺由于存在氨基、羰基,可以形成很多氢键, 所以聚丙烯酰胺涂层具有较好的耐腐蚀性、抗渗透性、耐磨性以及较好的附着力等特性, 广泛在用于空调、电热水器、空调、冰箱等电气设备及拖拉机、起重机等机械设备的金属零部件防腐,但聚丙烯酰胺涂层性能单一,这样制备的涂层点蚀电位较低,如果涂层长期处于潮湿、腐蚀介质中会引起点蚀、起泡、起粉等现象,防腐性能不佳,满足不了实际恶劣环境的需要。
发明内容
本发明要解决的技术问题是提供一种设备简单、制造容易、一种高点蚀电位的松香基与丙烯酰胺热聚合防腐膜的制备方法。
为解决上述技术问题,本发明采用如下技术方案:以丙烯酰胺为单体、偶氮二异丁腈为引发剂、丙烯海松酸(乙二胺)酰胺为交联剂制备。
上述一种高点蚀电位的松香基与丙烯酰胺热聚合防腐膜的制备方法,以丙烯酰胺为单体、偶氮二异丁腈为引发剂、丙烯海松酸(乙二胺)酰胺为交联剂,混匀后,将金属部件浸入其混合溶液中10分钟,再取出部件加热聚合即得。
一种高点蚀电位的松香基与丙烯酰胺热聚合防腐膜的制备方法,包括以下过程:
<1> 向1 L溶剂乙醇中,依次加入0.0 1 mol~0.50 mol的单体丙烯酰胺、0. 001 mol~0.01 mol的引发剂偶氮二异丁腈、0. 01mol ~0.50 mol的交联剂丙烯海松酸(乙二胺)酰胺,每加入一种化学试剂超声波溶解2分钟;
<2> 将干净光滑的金属部件浸入步骤<1>的混合物中10分钟,再取出部件置于80 ℃的真空干燥箱内热聚合 1.5小时即得。
实验发现,以丙烯酰胺为单体、偶氮二异丁腈为引发剂、丙烯海松酸(乙二胺)酰胺为交联剂,混匀后,将6063铝合金片浸入其中10分钟,再取出铝合金片加热聚合即得。采用电化学工作上测试,裸露面积为1 平方厘米,点蚀电位提高近 80 mV;另外,将浸有该热聚合膜的6063铝合金片,在3.5% 的氯化钠溶液中浸泡100小时时没点蚀,也不起泡、不起粉。因此,制备的松香基与丙烯酰胺热聚合防腐膜具有较高的抗点蚀性能,而且其它防腐性能也较优良,超过目前的丙烯酰胺热聚合防腐膜,并且设备简单、制作容易。
附图说明
图1是实施例1中高点蚀电位的含不含丙烯海松酸(乙二胺)酰胺的热聚合防腐膜的极化曲线图。
具体实施方式
实施例1
一、6063铝合金片的处理
将6063铝合金片在抛光布上依次用1.0 μm、0.3 μm的氧化铝粉抛光,然后放入5%的氢氧化钠溶液中超声5 min,再放入去离子水中超声清洗5 min,最后放入无水乙醇中超声6min后烘干备用。
二、丙烯酰胺热聚合防腐膜的制备
<1> 向1 L溶剂乙醇中,依次加入0.0 1 mol~0.50 mol的单体丙烯酰胺、0. 001 mol~0.01 mol的引发剂偶氮二异丁腈、0. 01mol ~0.50 mol的交联剂丙烯海松酸(乙二胺)酰胺,每加入一种化学试剂超声波溶解2分钟制备含松香的丙烯酰胺混合溶液;将干净光滑的6063铝合金片浸入的混合溶液中10分钟,再取出部件置于80 ℃的真空干燥箱内热聚合1.5小时即得松香基丙烯海松酸(乙二胺)酰胺与丙烯酰胺热聚合防腐膜;
<2> 不含松香基丙烯海松酸(乙二胺)酰胺的热聚合防腐膜制备过程除了不加丙烯海松酸(乙二胺)酰胺外,其它过程与步骤<1>完全相同,即得不含丙烯海松酸(乙二胺)酰胺的热聚合防腐膜。
三、丙烯酰胺热聚合防腐膜的防腐性能测试
<1> 将制备的两块涂有含与不含松香基丙烯海松酸(乙二胺)酰胺与丙烯酰胺热聚合防腐膜的6063铝合金片,使涂膜的裸露面积为1 平方厘米,然后在3.5% 的氯化钠溶液中进行电化学极化曲线测试,比较腐蚀电流及点蚀电位,发现加了丙烯海松酸(乙二胺)酰胺的防腐蚀涂膜,不但腐蚀电流降低了,点蚀电位提高近80 mV。
<2>将制备的两块涂有含与不含松香基丙烯海松酸(乙二胺)酰胺与丙烯酰胺热聚合防腐膜6063铝合金片浸泡于3.5% 的氯化钠溶液中,浸泡100小时,含松香基丙烯海松酸(乙二胺)酰胺与丙烯酰胺热聚合防腐膜的6063铝合金片无点蚀、无起泡、无开裂、无脱落现象; 不含丙烯海松酸(乙二胺)酰胺的防腐膜发生严重的点蚀、起泡、起粉现象。
因此,本发明制备的松香基与丙烯酰胺热聚合防腐膜具有较高的防点蚀性能及其它防腐蚀性能。
Claims (1)
1. 一种高点蚀电位的松香基与丙烯酰胺热聚合防腐膜的制备方法,其特征在于以0.01 mol/L~0.50 mol/L的丙烯酰胺为单体、0. 001 mol /L~0.01 mol/mL的偶氮二异丁腈为引发剂、0. 01mol /L~0.50 mol/L丙烯海松酸(乙二胺)酰胺为交联剂,混匀后,将金属部件浸入其混合溶液中10分钟,再取出部件加热聚合,即得;
具体按以下操作进行:
<1> 向1 L溶剂乙醇中,依次加入0.0 1 mol~0.50 mol的单体丙烯酰胺、0. 001 mol~0.01 mol的引发剂偶氮二异丁腈、0. 01mol ~0.50 mol的交联剂丙烯海松酸(乙二胺)酰胺,每加入一种化学试剂超声波溶解2分钟;
<2> 将干净光滑的金属部件浸入步骤<1>的混合物中10分钟,再取出部件置于80 ℃的真空干燥箱内热聚合 1.5小时即得。