CN110217851A - A kind of ion pottery ball and preparation method thereof based on pelelith element - Google Patents
A kind of ion pottery ball and preparation method thereof based on pelelith element Download PDFInfo
- Publication number
- CN110217851A CN110217851A CN201910590001.9A CN201910590001A CN110217851A CN 110217851 A CN110217851 A CN 110217851A CN 201910590001 A CN201910590001 A CN 201910590001A CN 110217851 A CN110217851 A CN 110217851A
- Authority
- CN
- China
- Prior art keywords
- annulus
- sphere
- green body
- pelelith
- hemispherical
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Ion pottery ball that the invention discloses a kind of based on pelelith element and preparation method thereof, including sphere, the sphere is made of aperture volcano stone material, and the outside of the sphere is covered with hemispherical upper cover and hemispherical lower cover respectively, and the outer ring of the upper cover bottom end is fixed with the first annulus, the outer ring on the lower cover top is fixed with the second annulus, internal screw thread is offered on the inside of first annulus, the production method of ion pottery ball includes the following steps, step 1, sphere production;Step 2, ceramic material sintering;Step 3, ceramic material processing;Step 4 coats elastic cushion;Step 5, elastic cushion aperture;Step 6, overall package;The invention, sphere is directly made up of pelelith, need not move through ceramic post sintering recycling, it is time saving and energy saving, and pelelith itself have it is porous, the big feature of surface area, the heavy metal ion such as chromium, arsenic etc. that the harmful bacteria in water can be adsorbed and organism is had an impact, or even including remaining chlorine in some water.
Description
Technical field
The present invention relates to ion pottery ball technical field, specially a kind of ion pottery ball and its production based on pelelith element
Method.
Background technique
In recent years, due to environmental pollution, water resource wrecks seriously, and most of provinces and cities resident, which is forced to drink, passes through large size
The pure water that water purifier is processed into.Water quality expert thinks, same although pure water is filtered out exceeded harmful substance is polluted
When also being dispelled to microelement needed by human, beneficial, minerals.Long-term drinking be easy to cause a large amount of calcium deficiency of human body,
The mineral trace elements such as potassium, magnesium, sodium cause weakness of limbs, lassitude.
Water body is handled using ion pottery ball currently, also having, existing ion pottery ball has the disadvantage in that 1, is existing
Ion pottery ball generally pass through plurality of raw materials and be sintered, production process is complicated, time-consuming and laborious, and existing ion pottery ball does not have
Standby microelement, cannot directly have been drunk by the lake river water of sanitary wastewater, the contaminated wastewater of factory, it is necessary to carry out to organic matter
Biological treatment, chlorine sterilization processing, finally destroy Equilibrium of Trace Elements, so that drinking water is pale tasteless, and generate a large amount of halogen
Compound toxicity carcinogen;2, existing ion pottery ball is easy to happen friction or collision between each other in use, causes
Damage, influences water quality.
Summary of the invention
Ion pottery ball that the purpose of the present invention is to provide a kind of based on pelelith element and preparation method thereof, on solving
State the problem of proposing in background technique.
In order to solve the above technical problem, the present invention provides following technical solutions: a kind of ion based on pelelith element
It makes pottery ball, including sphere, the sphere be made of aperture volcano stone material, the outside of the sphere is covered with hemispherical upper respectively
Lid and hemispherical lower cover, the outer ring of the upper cover bottom end are fixed with the first annulus, and the outer ring fixation on the lower cover top is set
There is the second annulus, internal screw thread is offered on the inside of first annulus, is offered on the outside of second annulus and internal screw thread phase
Matched external screw thread, the outside screw that the inside of first annulus matches the second annulus by internal screw thread with external screw thread connect
It connects, first annulus and the second annulus are made of ceramic materials, the outer wall of first annulus and the inner wall of the second annulus
It is fixed with elastic cushion, the upper cover and lower cover are made of ceramic materials, and the tegmental wall of upper cover and the tegmental wall of lower cover are opened
Equipped with several apertures, upper and lower cover of the upper cover offers the different opening of several sizes, the outside of the upper cover
It is coated with elastic cushion with the outside of lower cover, the outside and inside of the elastic cushion are uniformly provided with several both ends with aperture
The limbers communicated.
A kind of production method of the ion pottery ball based on pelelith element, includes the following steps, step 1, sphere production;
Step 2, ceramic material sintering;Step 3, ceramic material processing;Step 4 coats elastic cushion;Step 5, elastic cushion aperture;Step
Six, overall package;
Wherein in the above step 1, sphere production the following steps are included:
1) choosing aperture pelelith is raw material, and raw material is cut into square;
2) it utilizes cutting machine to cut corner angle material block, nearly round shape green body is made;
3) fine polishing is carried out to it using sander, green body outer surface is made to tend to be smooth;
4) spherome surface is rinsed using giant, it is spare washes away particle dust;Wherein in above-mentioned steps two,
Ceramic material sintering the following steps are included:
1) ceramic batch is fabricated to hemispherical green body and annulus green body, and the section of annulus green body is rectangle;
2) the different opening of several sizes is produced into the outer surface of hemispherical green body, is in Openworks shape;
3) it stands 10-20min and stabs out several apertures on its surface when hemispherical green body and annulus green body form slightly;
4) hemispherical green body and annulus green body are put into sintering furnace and are sintered;
Wherein in above-mentioned steps three, internal screw thread or external screw thread, and interior spiral shell are processed on the inside or outside of annulus green body
Line and external screw thread are mutually matched;
Wherein in above-mentioned steps four, cladding elastic cushion the following steps are included:
1) in the outer wall for opening up the first annulus of internal thread and the inner wall for offering externally threaded second annulus using by force
Power glue coats one layer of elastic cushion;
2) one layer of elastic cushion is coated using seccotine in the outside of hemispherical green body;
Wherein in above-mentioned steps five, limbers is processed into elastic cushion position corresponding with aperture;
Wherein in above-mentioned steps six, two hemispherical green bodies are located on the outside of sphere, the first annulus is socketed in half
The junction of spherical green body, then the second annulus is fixedly connected using screw thread with the first annulus.
According to the above technical scheme, there are gaps between the inner wall of the inner wall and lower cover of the sphere and upper cover.
According to the above technical scheme, the step 1 1) in, expect that the minimum length of block is 1.2 times of sphere format diameter.
According to the above technical scheme, the step 1 2) in, the minimum length of green body is 1.1 times of sphere diameter at this time.
According to the above technical scheme, the step 2 1) in, the maximum inner diameter of hemispherical green body is the 1.1 of sphere diameter
Times, the internal diameter of annulus green body is equal to the maximum outside diameter of hemispherical green body.
According to the above technical scheme, the step 2 3) in, it is needed after the completion of puncture by the flash removal at verge of opening.
According to the above technical scheme, the step 2 4) in, sintering temperature is 900-1300 DEG C, and sintering process is divided into heating
Process-consolidation process-temperature-fall period, and be 15-20h the time required to temperature-rise period, it is 2- the time required to pyroprocess
4h is 10-15h the time required to cooling.
Compared with prior art, the beneficial effects obtained by the present invention are as follows being: should based on pelelith element ion make pottery ball and
Its production method, sphere are directly made up of pelelith, need not move through ceramic post sintering recycling, time saving and energy saving, and pelelith sheet
Body has porous, the big feature of surface area, the harmful bacteria in water can be adsorbed and heavy metal that organism is had an impact from
Sub such as chromium, arsenic, or even including remaining chlorine in some water, while the microelement of pelelith release can promote zooblast
Metabolism, and take intracorporal harmful halide out of, the dirt cleared up in cell guarantees human health;Pass through upper cover and lower cover
The purpose that protection pottery ball can be played prevents in use process phase mutual friction or collision between sphere to cause breakage, passes through elasticity
Pad can further protect upper cover and lower cover, play the role of buffering;Simultaneous processing assembling process is simple, popularization easy to produce.
Detailed description of the invention
Attached drawing is used to provide further understanding of the present invention, and constitutes part of specification, with reality of the invention
It applies example to be used to explain the present invention together, not be construed as limiting the invention.In the accompanying drawings:
Fig. 1 is positive structure schematic of the present invention;
Fig. 2 is upper cover partial profile structure of the invention;
Fig. 3 is lower cover structure schematic diagram of the invention;
Fig. 4 is that technique of the invention founds flow chart.
In figure: 1, sphere;2, upper cover;3, lower cover;4, the first annulus;5, the second annulus;6, it is open;7, elastic cushion;8, it opens
Hole.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Fig. 1-4 is please referred to, the present invention provides a kind of technical solution: a kind of ion pottery ball based on pelelith element, including
Sphere 1, sphere 1 are made of aperture volcano stone material, and the outside of sphere 1 is covered with hemispherical upper cover 2 and hemispherical respectively
Lower cover 3, there are gaps between the inner wall of the inner wall and lower cover 3 of sphere 1 and upper cover 2, avoid upper cover 2 and lower cover 3 and sphere 1
It being in close contact, the outer ring of 2 bottom end of upper cover is fixed with the first annulus 4, and the outer ring on 3 top of lower cover is fixed with the second annulus 5, the
The inside of one annulus 4 offers internal screw thread, and the outside of the second annulus 5 offers the external screw thread to match with internal screw thread, the first circle
The inside of ring 4 is connect by internal screw thread with the outside screw that external screw thread matches the second annulus 5, the first annulus 4 and the second annulus
5 are made of ceramic materials, and the inner wall of the outer wall of the first annulus 4 and the second annulus 5 is fixed with elastic cushion 7,2 He of upper cover
Lower cover 3 is made of ceramic materials, and the tegmental wall of the tegmental wall of upper cover 2 and lower cover 3 offers several apertures 8, in upper cover 2 and
The different opening 6 of several sizes is offered on lower cover 3, the outside of upper cover 2 and the outside of lower cover 3 are coated with elastic cushion
7, the outside and inside of elastic cushion 7 are uniformly provided with several limbers communicated with the both ends of aperture 8.
A kind of production method of the ion pottery ball based on pelelith element, includes the following steps, step 1, sphere production;
Step 2, ceramic material sintering;Step 3, ceramic material processing;Step 4 coats elastic cushion;Step 5, elastic cushion aperture;Step
Six, overall package;
Wherein in the above step 1, sphere production the following steps are included:
1) choosing aperture pelelith is raw material, and raw material is cut into square, expects that the minimum length of block is that 1 specification of sphere is straight
1.2 times of diameter avoid the diameter accuracy for influencing sphere 1;
2) it utilizes cutting machine to cut corner angle material block, nearly round shape green body is made, the minimum length of green body is that sphere 1 is straight at this time
1.1 times of diameter avoid the diameter accuracy for influencing sphere 1;
3) fine polishing is carried out to it using sander, green body outer surface is made to tend to be smooth;
4) 1 surface of sphere is rinsed using giant, it is spare washes away particle dust;
Wherein in above-mentioned steps two, ceramic material sintering the following steps are included:
1) ceramic batch is fabricated to hemispherical green body and annulus green body, and the section of annulus green body is rectangle, it is hemispherical
The maximum inner diameter of green body is 1.1 times of 1 diameter of sphere, and the internal diameter of annulus green body is equal to the maximum outside diameter of hemispherical green body, is guaranteed
The accuracy of installation;
2) the different opening 6 of several sizes is produced into the outer surface of hemispherical green body, is in Openworks shape;
3) it stands 10-20min and stabs out several apertures on its surface when hemispherical green body and annulus green body form slightly
8, puncture needs to remove the flash of 8 edge of aperture after the completion, avoids obstruction aperture 8;
4) hemispherical green body and annulus green body are put into sintering furnace and are sintered, sintering temperature is 900-1300 DEG C, is burnt
Knot process is divided into temperature-rise period-consolidation process-temperature-fall period, and is 15-20h, high temperature mistake the time required to temperature-rise period
It is 2-4h the time required to journey, is 10-15h the time required to cooling;
Wherein in above-mentioned steps three, internal screw thread or external screw thread, and interior spiral shell are processed on the inside or outside of annulus green body
Line and external screw thread are mutually matched;
Wherein in above-mentioned steps four, cladding elastic cushion the following steps are included:
1) it is utilized in the outer wall for opening up the first annulus of internal thread 4 and the inner wall for offering externally threaded second annulus 5
Seccotine coats one layer of elastic cushion 7;
2) one layer of elastic cushion 7 is coated using seccotine in the outside of hemispherical green body;
Wherein in above-mentioned steps five, limbers is processed into the position corresponding with aperture 8 of elastic cushion 7;
Wherein in above-mentioned steps six, two hemispherical green bodies are located at 1 outside of sphere, the first annulus 4 is socketed in
The junction of hemispherical green body, then the second annulus 5 is fixedly connected using screw thread with the first annulus 4.
Based on above-mentioned, the present invention first will be that raw material glomerate sphere 1 of polishing be placed on by pelelith in use
The inside of lower cover 3, sphere 1 are directly made up of pelelith, need not move through ceramic post sintering recycling, time saving and energy saving, then pass through
The internal screw thread of first annulus 4 matches the top that upper cover 2 is threadably mounted to lower cover 3 with the external screw thread of the second annulus 5, is then
Can will be in pottery ball investment water, when water body is contacted by opening 6 with sphere 1, for pelelith sphere 1 itself with porous, surface area is big
The characteristics of, the heavy metal ion such as chromium, arsenic etc. that the harmful bacteria in water can be adsorbed and organism is had an impact, or even including
Remaining chlorine in some water, while the microelement of pelelith release can promote the metabolism of zooblast, and take out of in vivo
Harmful halide, clear up cell in dirt guarantee human health, and due to pelelith contain sodium, magnesium, aluminium, silicon, calcium,
Tens kinds of minerals such as titanium, manganese, iron, nickel, cobalt and molybdenum and microelement, it is ensured that the minerals such as human calcium, potassium, magnesium, sodium are micro-
Secondary element prevents disease, when friction or collision occurring between sphere 1, can play protection sphere 1 by upper cover 2 and lower cover 3
Purpose, prevent in use process phase mutual friction or collision between sphere 1 to cause breakage, can further be protected by elastic cushion 7
Upper cover 2 and lower cover 3 are protected, buffering is played the role of, guarantees that upper cover 2 and lower cover 3 can recycle, the pelelith sphere after use
1 can will be used with saturated brine after pelelith impregnate 30 hours, then continued to use after sufficiently eluriating net impurity with clear water,
It is more environmentally-friendly.
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.
Finally, it should be noted that the foregoing is only a preferred embodiment of the present invention, it is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
To modify the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features.
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in of the invention
Within protection scope.
Claims (8)
- Ball, including sphere (1) 1. a kind of ion based on pelelith element is made pottery, it is characterised in that: the sphere (1) is by aperture fire Stone material is made, and the outside of the sphere (1) is covered with hemispherical upper cover (2) and hemispherical lower cover (3) respectively, described The outer ring of upper cover (2) bottom end is fixed with the first annulus (4), and the outer ring on lower cover (3) top is fixed with the second annulus (5), internal screw thread is offered on the inside of first annulus (4), is offered and internal screw thread phase on the outside of second annulus (5) The inside of the external screw thread matched, first annulus (4) matches the outside screw of the second annulus (5) by internal screw thread with external screw thread Connection, first annulus (4) and the second annulus (5) are made of ceramic materials, the outer wall and second of first annulus (4) The inner wall of annulus (5) is fixed with elastic cushion (7), and the upper cover (2) and lower cover (3) are made of ceramic materials, and upper cover (2) tegmental wall of tegmental wall and lower cover (3) offers several apertures (8), opens up on the upper and lower lid (3) of upper cover (2) The opening (6) for having several sizes different, the outside of the upper cover (2) and the outside of lower cover (3) are coated with elastic cushion (7), The outside and inside of the elastic cushion (7) are uniformly provided with several limbers communicated with the both ends of aperture (8).
- 2. a kind of production method of the ion pottery ball based on pelelith element, includes the following steps, step 1, sphere production;Step Rapid two, ceramic material sintering;Step 3, ceramic material processing;Step 4 coats elastic cushion;Step 5, elastic cushion aperture;Step 6, Overall package;It is characterized by:Wherein in the above step 1, sphere production the following steps are included:1) choosing aperture pelelith is raw material, and raw material is cut into square;2) it utilizes cutting machine to cut corner angle material block, nearly round shape green body is made;3) fine polishing is carried out to it using sander, green body outer surface is made to tend to be smooth;4) sphere (1) surface is rinsed using giant, it is spare washes away particle dust;Wherein in above-mentioned steps two, ceramic material sintering the following steps are included:1) ceramic batch is fabricated to hemispherical green body and annulus green body, and the section of annulus green body is rectangle;2) the different opening of several sizes (6) is produced into the outer surface of hemispherical green body, is in Openworks shape;3) it stands 10-20min and stabs out several apertures (8) on its surface when hemispherical green body and annulus green body form slightly;4) hemispherical green body and annulus green body are put into sintering furnace and are sintered;Wherein in above-mentioned steps three, process internal screw thread or external screw thread on the inside or outside of annulus green body, and internal screw thread and External screw thread is mutually matched;Wherein in above-mentioned steps four, cladding elastic cushion the following steps are included:1) it is utilized in the outer wall for opening up the first annulus of internal thread (4) and the inner wall for offering externally threaded second annulus (5) Seccotine coats one layer of elastic cushion (7);2) one layer of elastic cushion (7) is coated using seccotine in the outside of hemispherical green body;Wherein in above-mentioned steps five, limbers is processed into elastic cushion (7) position corresponding with aperture (8);Wherein in above-mentioned steps six, two hemispherical green bodies are located on the outside of sphere (1), the first annulus (4) is socketed in The junction of hemispherical green body, then the second annulus (5) are fixedly connected using screw thread with the first annulus (4).
- The ball 3. a kind of ion based on pelelith element according to claim 1 is made pottery, it is characterised in that: the sphere (1) There are gaps between the inner wall of upper cover (2) and the inner wall of lower cover (3).
- 4. a kind of production method of ion pottery ball based on pelelith element according to claim 2, it is characterised in that: institute State step 1 1) in, expect that the minimum length of block is 1.2 times of sphere (1) format diameter.
- 5. a kind of production method of ion pottery ball based on pelelith element according to claim 2, it is characterised in that: institute State step 1 2) in, the minimum length of green body is 1.1 times of sphere (1) diameter at this time.
- 6. a kind of production method of ion pottery ball based on pelelith element according to claim 2, it is characterised in that: institute State step 2 1) in, the maximum inner diameter of hemispherical green body is 1.1 times of sphere (1) diameter, and the internal diameter of annulus green body is equal to hemisphere The maximum outside diameter of shape green body.
- 7. a kind of production method of ion pottery ball based on pelelith element according to claim 2, it is characterised in that: institute State step 2 3) in, it needs to remove the flash of aperture (8) edge after the completion of puncture.
- 8. a kind of production method of ion pottery ball based on pelelith element according to claim 2, it is characterised in that: institute State step 2 4) in, sintering temperature is 900-1300 DEG C, and sintering process is divided into temperature-rise period-consolidation process-and cooled down Journey, and be 15-20h the time required to temperature-rise period, it is 2-4h the time required to pyroprocess, is 10-15h the time required to cooling.