CN109734445A - A kind of electric field-assisted flash sintering method of Ultra-fine Grained hafnium oxide ceramics - Google Patents

A kind of electric field-assisted flash sintering method of Ultra-fine Grained hafnium oxide ceramics Download PDF

Info

Publication number
CN109734445A
CN109734445A CN201910166428.6A CN201910166428A CN109734445A CN 109734445 A CN109734445 A CN 109734445A CN 201910166428 A CN201910166428 A CN 201910166428A CN 109734445 A CN109734445 A CN 109734445A
Authority
CN
China
Prior art keywords
electric field
hafnium oxide
assisted
sample
ultra
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910166428.6A
Other languages
Chinese (zh)
Inventor
张帆
周楚同
张金咏
王为民
傅正义
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan University of Technology WUT
Original Assignee
Wuhan University of Technology WUT
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan University of Technology WUT filed Critical Wuhan University of Technology WUT
Priority to CN201910166428.6A priority Critical patent/CN109734445A/en
Publication of CN109734445A publication Critical patent/CN109734445A/en
Pending legal-status Critical Current

Abstract

The present invention provides a kind of electric field-assisted flash sintering method of Ultra-fine Grained hafnium oxide ceramics, which comprises the steps of: 1) weighs HfO2Powder is pressed into green body;2) electric field-assisted sintering equipment is provided;3) sample is put between the top electrode of electric field-assisted agglomerating plant and lower electrode, after so that sample temperature is risen to 800-1300 DEG C using at least two radiant heating heaters, initially enters holding stage;4) voltage at sample both ends is increased several times while entering holding stage, is then shut off sample both end voltage and radiant heating apparatus, makes sample cooled to room temperature to get ceramic to the Ultra-fine Grained hafnium oxide.Present invention application DC electric field assisted sintering technology, quickly prepares hafnium oxide ceramics, and the hafnium oxide ceramic material of consistency height, homogeneous grain size is obtained by process conditions such as regulation threshold temperature, field strength, electric currents.

Description

A kind of electric field-assisted flash sintering method of Ultra-fine Grained hafnium oxide ceramics
Technical field
The present invention relates to a kind of electric field-assisted flash sintering methods of Ultra-fine Grained hafnium oxide ceramics.
Background technique
Hafnium oxide (HfO2) it is Group IVB oxide, fusing point is 2800 DEG C, and thermal capacitance is 271kcal/mol, can be used as high temperature Refractory material.Hafnium oxide (HfO2) as a kind of oxide ceramic material with broad-band gap and high dielectric constant, film Because having high rigidity, high chemical stability and excellent dielectric properties, especially HfO2Manufactured optical thin film has high rigidity, High refractive index, high-strength laser damage threshold and good through performance of the near ultraviolet to middle infrared band the features such as are high in preparation Important application is suffered from terms of performance device and superlaser.Under high pressure, HfO2Have higher elastomer modulus and Intensity is considered as the optional object of superhard material.HfO simultaneously2Also there is very big neutron cross-section face absorption coefficient (> 150cm2/ atom×1024), nuclear reaction can be efficiently controlled.In addition, when being used in mixed way with other oxides, it is also possible to make catalyst, protection Coating and artificial gem.
However, but few people are related to the research in terms of the preparation to hafnium oxide ceramics.Due to hafnium oxide fusing point Height if not only energy consumption is high, the time is long using traditional sintering method, but also is difficult to make its densification.And select the two of nano-scale Hafnium oxide powder is sintered, although its high specific surface area can reduce sintering temperature to a certain degree, exists simultaneously crystal grain The problem of excessively growing up.It solves the above problems so needing to explore a kind of suitable sintering processing.
Summary of the invention
The present invention provides a kind of electric field-assisted Fast Sintering of Ultra-fine Grained hafnium oxide ceramics to solve above-mentioned technical problem Method.This method can obtain the hafnium oxide ceramic material that consistency is high, crystallite dimension is small, and sintering process cleaning, section Energy.
To achieve the goals above, technical scheme is as follows:
A kind of electric field-assisted flash sintering method of Ultra-fine Grained hafnium oxide ceramics, includes the following steps:
1) HfO is weighed2Powder is pressed into green body at 100-200MPa;
2) electric field-assisted sintering equipment is provided, the electric field-assisted sintering equipment includes electric field-assisted agglomerating plant and radiation Heating equipment;The electric field-assisted agglomerating plant includes top electrode and lower electrode, and sample is set to the top electrode and lower electrode Between, the radiant heating apparatus includes at least two radiant heating heaters, and at least two radiant heatings heater is set The two sides of sample are placed in, electric current carries out electric current heating to sample by top electrode and lower electrode;
3) sample is put between the top electrode of electric field-assisted agglomerating plant and lower electrode, utilizes at least two radiant heatings After heater makes sample temperature rise to 800-1300 DEG C, holding stage is initially entered;
4) sample both end voltage is increased to 180-220V, heat-insulation pressure keeping 8-15min while entering holding stage, then will Voltage is increased to 230-270V, heat-insulation pressure keeping 8-15min, continues to bring the voltage up to 280-300V, heat-insulation pressure keeping 8-15min, Voltage is finally risen into 320V-360V, control cutoff current value is closed in 1-5A and after maintaining 60-180s after rising to 320V-360V Sample both end voltage and radiant heating apparatus are closed, sample cooled to room temperature is made to make pottery to get to the Ultra-fine Grained hafnium oxide Porcelain.
In above scheme, guarantee that maximum field strength is less than 800V/cm during voltage is raised in the step 4).
In above scheme, the top electrode and lower electrode are Si-Mo rod electrode.
In above scheme, each radiant heating fever volume morphing is cylinder-shaped or square tube shape.
In above scheme, at least two radiant heatings heater is dispersed in around sample.
In above scheme, the radiant heating heater is graphite using material.
In above scheme, HfO in step 1)2The purity of powder is greater than 99%.
In above scheme, HfO in step 1)2Powder is in monoclinic phase.
In above scheme, HfO in step 1)2The average particle diameter size 30-100nm of powder.
In above scheme, the diameter of phi 10-50mm of green body in step 1).
Compared with prior art, the present invention has the following advantages: solving hafnium oxide pottery using electric field-assisted sintering Porcelain is difficult to the problem of with conventional sintering mode densified sintering product.And the application of DC electric field improves powder electric conductivity, to form electricity The feedback loop of stream causes the melting of crystal boundary avalanche type, accelerates atom diffusion, completes densification process.It can not only make titanium dioxide Hafnium ceramic is fast densified, and can largely inhibit the growth of crystal grain, is conducive to the preparation of nano ceramics.And This method is efficient, cleans, energy conservation.Therefore, present invention application DC electric field assisted sintering technology carries out hafnium oxide ceramics fast Speed preparation, and high, homogeneous grain size the dioxy by the process conditions acquisition consistency such as regulation threshold temperature, field strength, electric current Change hafnium ceramic material.
Detailed description of the invention
Fig. 1 is to realize electric field-assisted sintering equipment of the invention.
Fig. 2 be embodiment 2 experiment condition under hafnium oxide ceramics obtained SEM figure.
In figure: 1- electrode;2- sample;3- radiant heating heater.
Specific embodiment
Embodiment 1
Weigh the HfO of 1.4g2Powder is pressed into the green body of Φ 10mm, thickness 4.5mm at 100MPa, sample is put into Between two Si-Mo rod electrodes, starts to heat to sample using the radiant heating heater of radiant heating apparatus, rise to 800 DEG C Afterwards, holding stage is initially entered, while the voltage at sample both ends is added into 200V (field strength is about 444.4V/cm), heat-insulation pressure keeping 10min, then voltage is added to 250V (field strength is about 555.6V/cm), after heat-insulation pressure keeping 10min, voltage rises to 300V, and (field strength is about For 666.7V/cm), after heat-insulation pressure keeping 10min, voltage is risen to 360V (field strength is about 800V/cm), and current value control is 5A, dimension Sample both end voltage and Muffle furnace power supply are closed after holding 60s, makes sample cooled to room temperature.Gained sample it is relatively compact Degree: 94.3% crystallite dimension: 0.32-1.19 μm.
Embodiment 2
Weigh the HfO of 30.5g2Powder is pressed into the green body of Φ 50mm, thickness 4.0mm at 200MPa, sample is put into Between two Si-Mo rod electrodes, starts to heat to sample using the radiant heating heater of radiant heating apparatus, rise to 1300 DEG C Afterwards, holding stage is initially entered, while the voltage at sample both ends is added into 200V (field strength is about 500.0V/cm), heat-insulation pressure keeping 10min, then voltage is added to 250V (field strength is about 625.0V/cm), after heat-insulation pressure keeping 10min, voltage rises to 300V, and (field strength is about For 750.0V/cm), after heat-insulation pressure keeping 10min, voltage is risen to 320V (field strength is about 800.0V/cm), and current value control is 1A, Sample both end voltage and Muffle furnace power supply are closed after maintaining 180s, makes sample cooled to room temperature.The opposite cause of gained sample Density: 95.9% crystallite dimension: 0.17-0.96 μm.
The above is only preferred embodiments of the invention, not does limitation in any form to the present invention, all According to the technical essence of the invention to any simple modification, equivalent change and modification made by above example, this hair is still fallen within In the range of bright technical solution.

Claims (10)

1. a kind of electric field-assisted flash sintering method of Ultra-fine Grained hafnium oxide ceramics, which comprises the steps of:
1) HfO is weighed2Powder is pressed into green body at 100-200MPa;
2) electric field-assisted sintering equipment is provided, the electric field-assisted sintering equipment includes electric field-assisted agglomerating plant and radiant heating Equipment;The electric field-assisted agglomerating plant includes top electrode and lower electrode, and sample is set between the top electrode and lower electrode, The radiant heating apparatus includes at least two radiant heating heaters, and at least two radiant heatings heater is set to sample The two sides of product, electric current carry out electric current heating to sample by top electrode and lower electrode;
3) sample is put between the top electrode of electric field-assisted agglomerating plant and lower electrode, is generated heat using at least two radiant heatings After body makes sample temperature rise to 800-1300 DEG C, holding stage is initially entered;
4) sample both end voltage is increased to 180-220V, heat-insulation pressure keeping 8-15min while entering holding stage, then by voltage It is increased to 230-270V, heat-insulation pressure keeping 8-15min, is continued to bring the voltage up to 280-300V, heat-insulation pressure keeping 8-15min, finally Voltage is risen into 320V-360V, control cutoff current value closes sample after 1-5A and maintenance 60-180s after rising to 320V-360V Product both end voltage and radiant heating apparatus make sample cooled to room temperature to get ceramic to the Ultra-fine Grained hafnium oxide.
2. the electric field-assisted flash sintering method of Ultra-fine Grained hafnium oxide ceramics as described in claim 1, which is characterized in that institute It states the raised maximum field strength of guarantee in the process of voltage in step 4) and is less than 800V/cm.
3. the electric field-assisted flash sintering method of Ultra-fine Grained hafnium oxide ceramics as described in claim 1, which is characterized in that institute It states top electrode and lower electrode is Si-Mo rod electrode.
4. the electric field-assisted flash sintering method of Ultra-fine Grained hafnium oxide ceramics as described in claim 1, which is characterized in that institute Stating each radiant heating fever volume morphing is cylinder-shaped or square tube shape.
5. the electric field-assisted flash sintering method of Ultra-fine Grained hafnium oxide ceramics as described in claim 1, which is characterized in that institute At least two radiant heating heaters are stated to be dispersed in around sample.
6. the electric field-assisted flash sintering method of Ultra-fine Grained hafnium oxide ceramics as described in claim 1, which is characterized in that institute It is graphite that radiant heating heater, which is stated, using material.
7. the electric field-assisted flash sintering method of Ultra-fine Grained hafnium oxide ceramics as described in claim 1, which is characterized in that step It is rapid 1) in HfO2The purity of powder is greater than 99%.
8. the electric field-assisted flash sintering method of Ultra-fine Grained hafnium oxide ceramics as described in claim 1, which is characterized in that step It is rapid 1) in HfO2Powder is in monoclinic phase.
9. the electric field-assisted flash sintering method of Ultra-fine Grained hafnium oxide ceramics as described in claim 1, which is characterized in that step It is rapid 1) in HfO2The average particle diameter size 30-100nm of powder.
10. the electric field-assisted flash sintering method of Ultra-fine Grained hafnium oxide ceramics as described in claim 1, which is characterized in that The diameter of phi 10-50mm of green body in step 1).
CN201910166428.6A 2019-03-06 2019-03-06 A kind of electric field-assisted flash sintering method of Ultra-fine Grained hafnium oxide ceramics Pending CN109734445A (en)