CN108947428A - 一种煤矸石自燃的防治方法 - Google Patents
一种煤矸石自燃的防治方法 Download PDFInfo
- Publication number
- CN108947428A CN108947428A CN201810766684.4A CN201810766684A CN108947428A CN 108947428 A CN108947428 A CN 108947428A CN 201810766684 A CN201810766684 A CN 201810766684A CN 108947428 A CN108947428 A CN 108947428A
- Authority
- CN
- China
- Prior art keywords
- gangue
- layer
- spontaneous combustion
- flyash
- building
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种煤矸石自燃的防治方法，包括以下步骤：1.清除煤矸石内的可燃物；2.煤矸石+粉煤灰+电石渣+自主研发高效粉煤灰激发剂，按照比例进行混合；3.搅拌均匀进行放置，制作成煤矸石混凝土；4.进行模板的搭建，搭建完成后用煤矸石混凝土进行浇筑；5.根据需要进行分层浇筑，每层之间安插钢筋进行各层之间的固定；6.铺设土工布进行加固墙体；7.对搭建的建筑进行外形美化，如造型和绿化。本发明与现有技术相比的优点在于：强度高，防酸碱侵蚀，能有效隔绝空气，雨水等煤矸石自燃的必要条件，彻底解决煤矸石的自燃，扬尘等问题，真正做到以工业固废治理工业固废，对我国矿山环境治理有着重大意义。
Description
技术领域
本发明涉及煤矸石处理领域，具体是指一种煤矸石自燃的防治方法。
背景技术
煤矸石是煤炭开采及洗选加工过程中排出的固体废弃物，由于矸石中含有大量的黄铁矿及煤等促燃可燃物质，经长期堆积，在环境条件适宜的情况下往往会发生自燃，并产生大量的SO2、CO、H2S、CO2等有毒有害气体，严重影响矿区的环境和人民生命财产的安全。现有技术对煤矸石的处理一方面治理费用大，另一方面对环境产生二次污染，而且成功率低，另一方面不能有效解决表面强度和酸碱侵蚀问题，不能有效隔绝空气，雨水等煤矸石自燃的必要条件。
发明内容
本发明要解决的技术问题是，针对以上问题提供一种能够有效防止煤矸石自燃的方法。
为解决上述技术问题，本发明提供的技术方案为：一种煤矸石自燃的防治方法，包括以下步骤：
1.清除煤矸石内的可燃物；
2.煤矸石+粉煤灰+电石渣+自主研发高效粉煤灰激发剂，按照比例进行混合；
3.搅拌均匀进行放置，制作成煤矸石混凝土；
4.进行模板的搭建，搭建完成后用煤矸石混凝土进行浇筑；
5.根据需要进行分层浇筑，每层之间安插钢筋进行各层之间的固定；
6.铺设土工布进行加固墙体；
7.对搭建的建筑进行外形美化，如造型和绿化。
本发明与现有技术相比的优点在于：煤矸石+粉煤灰+电石渣+自主研发高效粉煤灰激发剂，合成新型环保无筋混凝土强度高，防酸碱侵蚀，能有效隔绝空气，雨水等煤矸石自燃的必要条件，利用煤矸石环保无筋混凝土对已有煤矸石渣堆进行围堰，覆盖，造型，绿化等，彻底解决煤矸石的自燃，扬尘等问题，同时科学的解决了粉煤灰，电石渣等工业固废的环保处置问题，真正做到以工业固废治理工业固废，对我国矿山环境治理有着重大意义。
作为改进，所述自主研发高效粉煤灰激发剂成分按质量如下：
电石渣7-11g、芒硝9-16g、脱硫石膏33-51g、消石灰15-22g、氢氧化钠6-13g、硫酸钠12-17g为主要成分合成高效粉煤灰激发剂各组分的配比比例。
作为改进，所述自助研发高效粉煤灰激发剂加入水后需要静置一段时间进行反应。
具体实施方式
本发明在具体实施时，一种煤矸石自燃的防治方法，包括以下步骤：
一种煤矸石自燃的防治方法，包括以下步骤：
1.清除煤矸石内的可燃物；
2.煤矸石+粉煤灰+电石渣+自主研发高效粉煤灰激发剂，按照比例进行混合；
3.搅拌均匀进行放置，制作成煤矸石混凝土；
4.进行模板的搭建，搭建完成后用煤矸石混凝土进行浇筑；
5.根据需要进行分层浇筑，每层之间安插钢筋进行各层之间的固定；
6.铺设土工布进行加固墙体；
7.对搭建的建筑进行外形美化，如造型和绿化。
能够有效的将矿业废渣进行再利用，节省了大量的材料资源和废料处理费，将工业废料转变成可利用资源后进行防护建筑的搭建工作，一举两得，节省了围堰等功能性工程建筑的浪费资源的问题。
所述自主研发高效粉煤灰激发剂成分按质量如下：
电石渣7-11g、脱硫石膏33-51g、消石灰15-22g、氢氧化钠6-13g、硫酸钠12-17g为主要成分合成高效粉煤灰激发剂各组分的配比比例。
所述自助研发高效粉煤灰激发剂加入水后需要静置一段时间进行反应。
以煤矸石为原料，就地取材，现场施工，现场治理煤矸石，改善矿山环境过程中，不产生二次污染，不消耗任何资源。煤矸石+粉煤灰+电石渣+自主研发高效粉煤灰激发剂，合成新型环保无筋混凝土强度高，防酸碱侵蚀，能有效隔绝空气，雨水等煤矸石自燃的必要条件，利用煤矸石环保无筋混凝土对已有煤矸石渣堆进行围堰，覆盖，造型，绿化等，彻底解决煤矸石的自燃，扬尘等问题，改善矿区生态环境。
电石废渣制水泥在国内已有众多成熟的企业，专有一条水泥生产线消化电石废渣。采用浓缩池将渣浆浓度由5％-8％浓缩到35％、砂泵送入料槽，在分去一部分上清液后和砂岩、粘土浆配制成水泥生料，再送回转窑煅烧制水泥。脱硫石膏粉与一般石膏粉的区分在于，脱硫石膏粉具有可再生，粒度小，成分稳定，有害杂质含量少，纯度高等特点，更加环保，还保证了石膏的凝胶作用，消石灰作为混凝土的主要材料，氢氧化钠加速化学反应时间，硫酸钠用于对混凝土凝固后进行加固，整个混凝土材料的选取更加环保，采用的都是采矿废料，进行混合后再生产，避免了废料处理所消耗的费用和劳动力，还减少了污染物的排放，能够起到环保的作用。
实施例：
实施例一：一种煤矸石自燃的防治方法，包括以下步骤：
1.清除煤矸石内的可燃物；
2.煤矸石+粉煤灰+电石渣+自主研发高效粉煤灰激发剂，按照比例进行混合；
3.搅拌均匀进行放置，制作成煤矸石混凝土；
4.进行模板的搭建，搭建完成后用煤矸石混凝土进行浇筑；
5.根据需要进行分层浇筑，每层之间安插钢筋进行各层之间的固定；
6.铺设土工布进行加固墙体；
7.对搭建的建筑进行外形美化，如造型和绿化，在土工布上进行植土，加水养护后在土层内种植绿化。
所述自主研发高效粉煤灰激发剂成分按质量如下：
电石渣7g、脱硫石膏33g、消石灰15g、氢氧化钠6g、硫酸钠12g为主要成分合成高效粉煤灰激发剂各组分的配比比例。
实施例二：一种煤矸石自燃的防治方法，包括以下步骤：
1.清除煤矸石内的可燃物；
2.煤矸石+粉煤灰+电石渣+自主研发高效粉煤灰激发剂，按照比例进行混合；
3.搅拌均匀进行放置，制作成煤矸石混凝土；
4.进行模板的搭建，搭建完成后用煤矸石混凝土进行浇筑；
5.根据需要进行分层浇筑，每层之间安插钢筋进行各层之间的固定；
6.铺设土工布进行加固墙体；
7.对搭建的建筑进行外形美化，如造型和绿化，使用人工草皮直接移植到土工布上，绿化成果显著。
所述自主研发高效粉煤灰激发剂成分按质量如下：
电石渣11g、脱硫石膏51g、消石灰22g、氢氧化钠13g、硫酸钠17g为主要成分合成高效粉煤灰激发剂各组分的配比比例。
实施例三：一种煤矸石自燃的防治方法，包括以下步骤：
1.清除煤矸石内的可燃物；
2.煤矸石+粉煤灰+电石渣+自主研发高效粉煤灰激发剂，按照比例进行混合；
3.搅拌均匀进行放置，制作成煤矸石混凝土；
4.进行模板的搭建，造型参考梯田，搭建完成后用煤矸石混凝土进行浇筑；
5.根据需要进行浇筑，浇筑完毕后进行拆模；
6.铺设土工布进行加固墙体；
7.对于煤矸石渣堆治理，采用分层退台的方式，每一层平台处为预留绿化带，在渣堆密封的同时，保证了最为稳定的堆放结构，同时，营造出类似梯田的景观造型，开辟了治理矿山环境和美化绿化同步进行的新途径。
所述自主研发高效粉煤灰激发剂成分按质量如下：
电石渣11g、脱硫石膏51g、消石灰22g、氢氧化钠13g、硫酸钠17g为主要成分合成高效粉煤灰激发剂各组分的配比比例。
以上对本发明及其实施方式进行了描述，这种描述没有限制性，以上所示的也只是本发明的实施方式之一，实际的结构并不局限于此。总而言之如果本领域的普通技术人员受其启示，在不脱离本发明创造宗旨的情况下，不经创造性的设计出与该技术方案相似的结构方式及实施例，均应属于本发明的保护范围。
Claims (3)
1.一种煤矸石自燃的防治方法，其特征在于：包括以下步骤：
1.清除煤矸石内的可燃物；
2.煤矸石+粉煤灰+电石渣+自主研发高效粉煤灰激发剂，按照比例进行混合；
3.搅拌均匀进行放置，制作成煤矸石混凝土；
4.进行模板的搭建，搭建完成后用煤矸石混凝土进行浇筑；
5.根据需要进行分层浇筑，每层之间安插钢筋进行各层之间的固定；
6.铺设土工布进行加固墙体；
7.对搭建的建筑进行外形美化，如造型和绿化。
2.根据权利要求1所述的一种煤矸石自燃的防治方法，其特征在于：所述自主研发高效粉煤灰激发剂成分按质量如下：
电石渣7-11g、脱硫石膏33-51g、消石灰15-22g、氢氧化钠6-13g、硫酸钠12-17g为主要成分合成高效粉煤灰激发剂各组分的配比比例。
3.根据权利要求1所述的一种煤矸石自燃的防治方法，其特征在于：所述自助研发高效粉煤灰激发剂加入水后需要静置一段时间进行反应。