CN107903727A - A kind of civil engineering water-repellent paint formula and processing technology - Google Patents
A kind of civil engineering water-repellent paint formula and processing technology Download PDFInfo
- Publication number
- CN107903727A CN107903727A CN201711211406.4A CN201711211406A CN107903727A CN 107903727 A CN107903727 A CN 107903727A CN 201711211406 A CN201711211406 A CN 201711211406A CN 107903727 A CN107903727 A CN 107903727A
- Authority
- CN
- China
- Prior art keywords
- liquid
- pulvis
- water
- civil engineering
- repellent paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of civil engineering water-repellent paint formula and processing technology, including pulvis and liquid, the pulvis includes calcium carbonate, portland cement, aluminium hydroxide, toluene, mica powder and aluminium powder;The liquid includes pitch, subgroup boron nitride high-temperature ointment, turpentine oil, styrene-acrylic emulsion, isobutyl ethyl triethoxy silicane, potassium hydroxide, water and sodium pyrosulfite.Compared with prior art, the present invention is fabricated separately using pulvis and liquid, is waited to reconcile in proportion when in use and be can be used, have the characteristics that hardening time is short, hardness is high, cracking resistance, prevent from aoxidizing, weatherability it is high, service life is grown, and is had the value of popularization and application.
Description
Technical field
The present invention relates to field of material technology, more particularly to a kind of civil engineering water-repellent paint formula and processing technology.
Background technology
Water-repellent paint it is cured after formed waterproofing membrane have certain extensibility, elastoplasticity, crack resistance, impermeability and
Weatherability, can play waterproof, prevent blending protective effect.But water-repellent paint of the prior art all has the characteristics that respective difference,
But applied in civil engineering, it is necessary to expose to the sun and rain, water-repellent paint will aging, oxidation etc., service life is not high, therefore, need
Want a kind of water-repellent paint for being exclusively used in civil engineering.
The content of the invention
The purpose of the present invention is that to solve the above-mentioned problems and provides a kind of civil engineering water-repellent paint formula and add
Work technique.
The present invention is achieved through the following technical solutions above-mentioned purpose:
A kind of civil engineering water-repellent paint formula of the present invention, including pulvis and liquid,
The pulvis includes calcium carbonate, portland cement, aluminium hydroxide, toluene, mica powder and aluminium powder;
The liquid include pitch, subgroup boron nitride high-temperature ointment, turpentine oil, styrene-acrylic emulsion, isobutyl ethyl triethoxy silicane,
Potassium hydroxide, water and sodium pyrosulfite.
Specifically, by weight, every part of pulvis is containing the calcium carbonate 5%, the portland cement 60%, the hydrogen
Aluminium oxide 5%, the toluene 5%, the mica powder 5%, the aluminium powder 20%;
Every part of liquid containing the pitch 20%, the subgroup boron nitride high-temperature ointment 10%, the turpentine oil 10%,
The styrene-acrylic emulsion 40%, the isobutyl ethyl triethoxy silicane 5%, the potassium hydroxide 5%, the water 5%, the burnt sulfurous
Sour sodium 5%.
A kind of civil engineering water-repellent paint processing technology of the present invention, comprises the following steps:
(1) pulvis is made:After calcium carbonate, portland cement, aluminium hydroxide, toluene, mica powder and 100 mesh of aluminium powder are sieved
It is uniformly mixed;
(2) liquid is made, pitch, subgroup boron nitride high-temperature ointment, turpentine oil, styrene-acrylic emulsion are added in mixer, turned
Fast 500r/min starts to stir, and rotating speed to 1000r/min, stirring is improved after being sufficiently mixed and is stopped after 30 minutes;
(3) add isobutyl ethyl triethoxy silicane and start 1000r/min stirrings 10 minutes;
(4) add potassium hydroxide and start 1000r/min stirrings 10 minutes;
(5) add water and sodium pyrosulfite starts 1000r/min stirrings and can obtain liquid end product in 10 minutes;
(6) in use, mixing and being used the pulvis of step (1) and the liquid of step (5) with 1 to 1 ratio.
The beneficial effects of the present invention are:
The present invention is a kind of civil engineering water-repellent paint formula and processing technology, and compared with prior art, the present invention uses
Pulvis and liquid are fabricated separately, wait when in use in proportion reconcile i.e. can be used, have hardening time is short, hardness is high, cracking resistance, prevent
The characteristics of block, high weatherability, service life length, has the value of popularization and application.
Embodiment
The invention will be further described below:
A kind of civil engineering water-repellent paint formula of the present invention, including pulvis and liquid,
The pulvis includes calcium carbonate, portland cement, aluminium hydroxide, toluene, mica powder and aluminium powder;
The liquid include pitch, subgroup boron nitride high-temperature ointment, turpentine oil, styrene-acrylic emulsion, isobutyl ethyl triethoxy silicane,
Potassium hydroxide, water and sodium pyrosulfite.
Specifically, by weight, every part of pulvis is containing the calcium carbonate 5%, the portland cement 60%, the hydrogen
Aluminium oxide 5%, the toluene 5%, the mica powder 5%, the aluminium powder 20%;
Every part of liquid containing the pitch 20%, the subgroup boron nitride high-temperature ointment 10%, the turpentine oil 10%,
The styrene-acrylic emulsion 40%, the isobutyl ethyl triethoxy silicane 5%, the potassium hydroxide 5%, the water 5%, the burnt sulfurous
Sour sodium 5%.
A kind of civil engineering water-repellent paint processing technology of the present invention, comprises the following steps:
(1) pulvis is made:After calcium carbonate, portland cement, aluminium hydroxide, toluene, mica powder and 100 mesh of aluminium powder are sieved
It is uniformly mixed;
(2) liquid is made, pitch, subgroup boron nitride high-temperature ointment, turpentine oil, styrene-acrylic emulsion are added in mixer, turned
Fast 500r/min starts to stir, and rotating speed to 1000r/min, stirring is improved after being sufficiently mixed and is stopped after 30 minutes;
(3) add isobutyl ethyl triethoxy silicane and start 1000r/min stirrings 10 minutes;
(4) add potassium hydroxide and start 1000r/min stirrings 10 minutes;
(5) add water and sodium pyrosulfite starts 1000r/min stirrings and can obtain liquid end product in 10 minutes;
(6) in use, mixing and being used the pulvis of step (1) and the liquid of step (5) with 1 to 1 ratio.
The basic principle and main feature and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (3)
- A kind of 1. civil engineering water-repellent paint formula, it is characterised in that:Including pulvis and liquid,The pulvis includes calcium carbonate, portland cement, aluminium hydroxide, toluene, mica powder and aluminium powder;The liquid includes pitch, subgroup boron nitride high-temperature ointment, turpentine oil, styrene-acrylic emulsion, isobutyl ethyl triethoxy silicane, hydrogen-oxygen Change potassium, water and sodium pyrosulfite.
- 2. civil engineering water-repellent paint formula according to claim 1, it is characterised in that:By weight, every part of powder Agent is containing the calcium carbonate 5%, the portland cement 60%, the aluminium hydroxide 5%, the toluene 5%, the mica powder 5%th, the aluminium powder 20%;Every part of liquid is containing the pitch 20%, the subgroup boron nitride high-temperature ointment 10%, the turpentine oil 10%, described Styrene-acrylic emulsion 40%, the isobutyl ethyl triethoxy silicane 5%, the potassium hydroxide 5%, the water 5%, the sodium pyrosulfite 5%.
- 3. a kind of civil engineering water-repellent paint processing technology, it is characterised in that comprise the following steps:(1) pulvis is made:Mixed after calcium carbonate, portland cement, aluminium hydroxide, toluene, mica powder and 100 mesh of aluminium powder are sieved Uniformly;(2) liquid is made, pitch, subgroup boron nitride high-temperature ointment, turpentine oil, styrene-acrylic emulsion are added in mixer, rotating speed 500r/min starts to stir, and rotating speed to 1000r/min, stirring is improved after being sufficiently mixed and is stopped after 30 minutes;(3) add isobutyl ethyl triethoxy silicane and start 1000r/min stirrings 10 minutes;(4) add potassium hydroxide and start 1000r/min stirrings 10 minutes;(5) add water and sodium pyrosulfite starts 1000r/min stirrings and can obtain liquid end product in 10 minutes;(6) in use, mixing and being used the pulvis of step (1) and the liquid of step (5) with 1 to 1 ratio.