CN106976300A - A kind of five layers of corrugated paper production technology - Google Patents
A kind of five layers of corrugated paper production technology Download PDFInfo
- Publication number
- CN106976300A CN106976300A CN201710103070.3A CN201710103070A CN106976300A CN 106976300 A CN106976300 A CN 106976300A CN 201710103070 A CN201710103070 A CN 201710103070A CN 106976300 A CN106976300 A CN 106976300A
- Authority
- CN
- China
- Prior art keywords
- parts
- layers
- added
- production technology
- gluing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of five layers of corrugated paper production technology, are related to field of packaging material, it is characterised in that:Comprise the following steps, 1) facial tissue, core paper are heat-treated respectively respectively, gluing processing is carried out to the surface of fluting medium;2) one layer of fluting medium by facial tissue, core paper respectively with coated glue is combined, and forms two single face corrugated boards;3) inner paper is added, inner paper is located between two single face corrugated boards, and carries out gluing by gluing machine, is then combined;4) cooling treatment after drying.The Recipe of the present invention is novel, five layers of corrugated paper, and intensity is high, it is not easy to ftracture, cost of material is low, the production time is short, binding agent quality.
Description
Technical field:
The present invention relates to field of packaging material, and in particular to a kind of five layers of corrugated paper production technology.
Background technology:
Packing board is the general name for the cardboard for Gong being packed for.Including white board, yellow plate paper, kraft liner, corrugated board etc..
It is general to require that there is tough folding strength and good bendability.It is raw material by timber, rice wheat straw etc., using distinct methods system
Slurry, manufactures paper with pulp on lap machine and forms.It is mainly used in packing carton processed, also serves as packaging material or printing material etc..Packing board
With lightweight, facilitate the characteristics of, but its low intensity, easily cracking, the poor-performing of waterproof.But what existing starch made
The method of board pasted additive is relatively simple, and the time needed for production is long, and process is unreasonable, causes the quality of starch adesive
It is poor, the corrugated board of layer 2-4 can only be produced, low intensity easily ftractures.
The content of the invention:
The technical problems to be solved by the invention are to provide a kind of intensity height, it is not easy to five layers of corrugated paper production of cracking
Process.
The technical problems to be solved by the invention are realized using following technical scheme:
A kind of five layers of corrugated paper production technology, it is characterised in that:Comprise the following steps,
1) facial tissue, core paper are heat-treated respectively respectively, gluing processing is carried out to the surface of fluting medium;
2) one layer of fluting medium by facial tissue, core paper respectively with coated glue is combined, and forms two single face corrugated boards;
3) inner paper is added, inner paper is located between two single face corrugated boards, and carries out gluing, Ran Houfu by gluing machine
Close;
4) cooling treatment after drying.
The binding agent of described gluing includes following components, starch by weight:200 parts, hard and infertile alkali:It is 22 parts, strong to urge
Agent:9 parts, borax:6 parts, defoamer:5 parts, 33 parts of sodium hypochlorite, water:1000 parts, industrial grade hydrogen peroxide:3 parts, permanganic acid
Potassium:2 parts.
Described binding agent preparation method is as follows,
1) water, is added in a kettle., 60-70 DEG C is heated to, then adds cornstarch to stir 3-5 minutes is pasted
Change;
2), sodium hypochlorite, hydrogen peroxide and potassium permanganate are dissolved by 5-10 times of water, adds in reactor and stirs 5-20
Minute;
3), hard and infertile alkali is added in reactor with 3-5 times of cold-water solution, stirred 20-40 minutes;
4), borax and defoamer are added in reactor with 6-10 times of dissolved in boiled water, stirs 3-5 minutes, then stands 2-4
Minute;
5), strong catalyst is added and stirred in reactor.
Described strong catalyst includes following components, 2.5 parts of benzoyl peroxide, 4 parts of Firebrake ZB, cyaniding by weight
15 parts of 1.5 parts of potassium and calcium stearate.
Described defoamer includes following components, 5-6 parts of tributyl phosphate, 2-4 parts of polyimides, diphenyl by weight
1-3 parts of 3-4 parts of silicon diol and petroleum sodium sulfonate.
The present invention is specially gelatinized to cornstarch, is conducive to improving the viscosity of binding agent, defoamer is together with borax
Mixing is added, and is conducive to shortening the time produced, the production efficiency of raising, is first to have carried out the reaction of froth breaking then in the present invention
Strong catalyst is being added, and is first adding strong catalyst froth breaking again in the prior art, the effect of froth breaking can be caused poor, therefore this
Invention can improve the effect of froth breaking, can also shorten the time of froth breaking.
The beneficial effects of the invention are as follows:The Recipe of the present invention is novel, five layers of corrugated paper, and intensity is high, it is not easy to ftracture,
Cost of material is low, and the production time is short, binding agent quality.
Embodiment:
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific example is closed, the present invention is expanded on further.
A kind of five layers of corrugated paper production technology, comprise the following steps,
1) facial tissue, core paper are heat-treated respectively respectively, gluing processing is carried out to the surface of fluting medium;
2) one layer of fluting medium by facial tissue, core paper respectively with coated glue is combined, and forms two single face corrugated boards;
3) inner paper is added, inner paper is located between two single face corrugated boards, and carries out gluing, Ran Houfu by gluing machine
Close;
4) cooling treatment after drying.
The binding agent of gluing includes following components, starch by weight:200 parts, hard and infertile alkali:22 parts, strong catalyst:9
Part, borax:6 parts, defoamer:5 parts, 33 parts of sodium hypochlorite, water:1000 parts, industrial grade hydrogen peroxide:3 parts, potassium permanganate:2 parts.
Binding agent preparation method is as follows,
1) water, is added in a kettle., 60-70 DEG C is heated to, then adds cornstarch to stir 3-5 minutes is pasted
Change;
2), sodium hypochlorite, hydrogen peroxide and potassium permanganate are dissolved by 5-10 times of water, adds in reactor and stirs 5-20
Minute;
3), hard and infertile alkali is added in reactor with 3-5 times of cold-water solution, stirred 20-40 minutes;
4), borax and defoamer are added in reactor with 6-10 times of dissolved in boiled water, stirs 3-5 minutes, then stands 2-4
Minute;
5), strong catalyst is added and stirred in reactor.
Strong catalyst includes following components, 2.5 parts of benzoyl peroxide, 4 parts of Firebrake ZB, potassium cyanide 1.5 by weight
15 parts of part and calcium stearate.
Defoamer includes following components, 5-6 parts of tributyl phosphate, 2-4 parts of polyimides, diphenyl silanediol by weight
3-4 parts and 1-3 parts of petroleum sodium sulfonate.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (5)
1. a kind of five layers of corrugated paper production technology, it is characterised in that:Comprise the following steps,
1) facial tissue, core paper are heat-treated respectively respectively, gluing processing is carried out to the surface of fluting medium;
2), one layer of fluting medium by facial tissue, core paper respectively with coated glue is combined, and forms two single face corrugated boards;
3) inner paper is added, inner paper is located between two single face corrugated boards, and carries out gluing by gluing machine, is then combined;
4) cooling treatment after drying.
2. a kind of five layers of corrugated paper production technology according to claim 1, it is characterised in that:The bonding of described gluing
Agent includes following components, starch by weight:200 parts, hard and infertile alkali:22 parts, strong catalyst:9 parts, borax:6 parts, defoamer:5
Part, 33 parts of sodium hypochlorite, water:1000 parts, industrial grade hydrogen peroxide:3 parts, potassium permanganate:2 parts.
3. a kind of five layers of corrugated paper production technology according to claim 2, it is characterised in that:Described binding agent making side
Method is as follows,
1) water, is added in a kettle., 60-70 DEG C is heated to, then adds cornstarch to stir 3-5 minutes is gelatinized;
2), sodium hypochlorite, hydrogen peroxide and potassium permanganate are dissolved by 5-10 times of water, 5-20 points of stirring in reactor are added
Clock;
3), hard and infertile alkali is added in reactor with 3-5 times of cold-water solution, stirred 20-40 minutes;
4), borax and defoamer are added in reactor with 6-10 times of dissolved in boiled water, stirs 3-5 minutes, then stands 2-4 points
Clock;
5), strong catalyst is added and stirred in reactor.
4. a kind of five layers of corrugated paper production technology according to claim 2, it is characterised in that:Described strong catalyst is pressed
Parts by weight include following components, 15 parts of 2.5 parts of benzoyl peroxide, 4 parts of Firebrake ZB, 1.5 parts of potassium cyanide and calcium stearate.
5. a kind of five layers of corrugated paper production technology according to claim 1, it is characterised in that:Described defoamer is by weight
Part includes following components, 5-6 parts of tributyl phosphate, 2-4 parts of polyimides, 3-4 parts of diphenyl silanediol and petroleum sodium sulfonate 1-3
Part.