CN106670738B - 锅炉管道用g115钢的焊接工艺 - Google Patents

锅炉管道用g115钢的焊接工艺 Download PDF

Info

Publication number
CN106670738B
CN106670738B CN201610998356.8A CN201610998356A CN106670738B CN 106670738 B CN106670738 B CN 106670738B CN 201610998356 A CN201610998356 A CN 201610998356A CN 106670738 B CN106670738 B CN 106670738B
Authority
CN
China
Prior art keywords
welding
steel
arc welding
manual
heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610998356.8A
Other languages
English (en)
Other versions
CN106670738A (zh
Inventor
陈亮
李刚
卢征然
陆文龙
王炯祥
傅育文
王哮江
田国平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Electric Power Co Ltd
Shanghai Boiler Works Co Ltd
Original Assignee
Jiangsu Electric Power Co Ltd
Shanghai Boiler Works Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Electric Power Co Ltd, Shanghai Boiler Works Co Ltd filed Critical Jiangsu Electric Power Co Ltd
Priority to CN201610998356.8A priority Critical patent/CN106670738B/zh
Publication of CN106670738A publication Critical patent/CN106670738A/zh
Application granted granted Critical
Publication of CN106670738B publication Critical patent/CN106670738B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种锅炉管道用G115钢的焊接工艺，其特征在于，包括以下步骤：采用正火态及回火态供货的G115新型马氏体耐热钢制备管道；在两根需焊接的管道上分别制备坡口，并对坡口及其内外壁两侧用打磨进行清理，随后将两根需焊接的管道进行对口装配；采用手工氩弧焊及手工电弧焊进行焊接；对接环缝焊后，在760～780℃下热处理保温时间超过7h以上。本发明解决了G115钢采用何种焊接材料进行焊接的问题及G115钢焊后如何热处理的问题，并完整地推出了G115新型马氏体耐热钢的焊接工艺，对解决同类马氏体耐热钢的焊接问题具有极大的参考和借鉴意义。

Description

锅炉管道用G115钢的焊接工艺
技术领域
本发明涉及一种机组参数为630℃及以上的超超临界锅炉管道用选新型马氏体G115钢现场组装的焊接工艺。
背景技术
G115是北京钢铁研究总院开发的9Cr-3W-3Co新型马氏体耐热钢，650℃下其持久强度约是P92钢的1.4倍，其抗高温蒸汽氧化性能与P92钢相当，其650℃持久强度优于日本住友开发的P93钢。G115材料可满足650℃下的服役要求，是很有潜力成为630℃至650℃温度段用锅炉管道用钢。
目前，国际上同类型日本住友开发的630℃超超临界锅炉用候选耐热钢SAVE12AD的焊接还存在一些尚未解决的问题，SAVE12AD材料的焊接国际上推荐采用Gr.92等级或镍基焊材焊接，焊接接头的高温持久强度低于相关标准对母材的使用要求。因此，使用与母材匹配的新焊材，开发锅炉管道用G115新型马氏体钢现场组装的全位置对接的焊接工艺对解决同类马氏体耐热钢的焊接问题具有极大的参考和借鉴意义。
发明内容
本发明旨在解决630℃及以上超超临界锅炉用候选新型马氏体钢G115的焊接难题，为630℃及以上超超临界锅炉用候选新型马氏体钢G115的焊接提供一种新的焊接工艺。
为了达到上述目的，本发明的技术方案是提供了一种锅炉管道用G115钢的焊接工艺，其特征在于，包括以下步骤：
步骤1、采用正火态及回火态供货的G115新型马氏体耐热钢制备管道；
步骤2、在两根需焊接的管道上分别制备坡口，并对坡口及其内外壁两侧用打磨进行清理，随后将两根需焊接的管道进行对口装配；
步骤3、采用手工氩弧焊及手工电弧焊进行焊接，选用直径3.2～4.0mm的9Cr-3W-3Co耐热钢焊条，且手工氩弧焊选用直径2.4mm的9Cr-3W-3Co耐热钢条状焊丝；
步骤4、对接环缝焊后，在760～780℃下热处理保温时间超过7h以上。
优选地，在进行所述手工氩弧焊及手工电弧焊时，管道外壁保护气体采用100％Ar进行保护，外壁保护气体流量为6～12L/min，管道内壁(背面)保护气体采用100％Ar进行背面保护，背面保护气体流量为5～8L/min，氩气纯度在99.95％以上。
优选地，手工电弧焊过程中，采用多层多道焊，每一道焊完后彻底清除焊渣方进行下一道焊接，施焊过程中控制层间温度不超过300℃，焊接摆动幅度不超过焊条焊芯直径的3倍。
优选地，手工电弧焊过程中，每一道焊完后用砂轮打磨。
本发明具有如下有益效果：
G115钢采用何种焊接材料进行焊接及完整的焊接工艺还没有，本发明解决了G115钢采用何种焊接材料进行焊接的问题及G115钢焊后如何热处理的问题，并完整地推出了G115新型马氏体耐热钢的焊接工艺，对解决同类马氏体耐热钢的焊接问题具有极大的参考和借鉴意义。
具体实施方式
为使本发明更明显易懂，兹以优选实施例作详细说明如下。
本发明提供了一种锅炉管道用G115钢的焊接工艺，包括以下步骤：
步骤1、采用正火+回火态供货的G115新型马氏体耐热钢制备管道。
步骤2、焊前准备：①制备坡口，并对坡口及其内外壁两侧用打磨进行清理；②将两根需焊接的管道进行对口装配。
步骤3、采用手工氩弧焊+手工电弧焊(GTAW+SMAW)进行焊接，选用Φ2.4mm的9Cr-3W-3Co耐热钢条状焊丝(GTAW)、Φ3.2～Φ4.0mm的9Cr-3W-3Co耐热钢焊条。手工氩弧焊+手工电弧焊(GTAW+SMAW)焊接工艺如下：
①管道外壁保护气体采用100％Ar进行保护，外壁保护气体流量为6～12L/min，管道内壁(背面)保护气体采用100％Ar进行背面保护，背面保护气体流量为5～8L/min，氩气纯度在99.95％以上；
②焊接时的焊接规范参数见表1
表1 G115钢的焊接工艺参数
焊接工艺 规格(mm) 电流(A) 电压(V) 预热温度(℃)
GTAW Φ2.4 100～120 12～15 ≥100
SMAW Φ3.2 90～120 22～26 ≥200
SMAW Φ4.0 160～170 22～27 ≥200
③采用SMAW焊接过程中，采用多层多道焊，每一道焊完后需彻底清除焊渣方可进行下一道焊接，必要时用砂轮打磨，施焊过程中控制层间温度不超过300℃；采用手工电弧焊时，焊接摆动幅度不超过焊条焊芯直径的3倍。
步骤4、对接环缝焊后采用760～780℃×7h的热处理规范。

Claims (1)

1.一种锅炉管道用G115钢的焊接工艺，其特征在于，包括以下步骤：
步骤1、采用正火加回火态供货的G115新型马氏体耐热钢制备管道；
步骤2、焊前准备，包括以下步骤：
步骤201、制备坡口，并对坡口及其内外壁两侧用打磨进行清理；
步骤202、将两根需焊接的管道进行对口装配；
步骤3、采用手工氩弧焊加手工电弧焊进行焊接，手工氩弧焊时选用直径为2.4mm的9Cr-3W-3Co耐热钢条状焊丝，手工电弧焊时选用直径为3.2mm的9Cr-3W-3Co耐热钢焊条或直径为4.0mm的9Cr-3W-3Co耐热钢焊条，手工氩弧焊加手工电弧焊焊接工艺如下：
步骤301、管道外壁保护气体采用100％Ar进行保护，外壁保护气体流量为6～12L/min，管道内壁保护气体采用100％Ar进行背面保护，背面保护气体流量为5～8L/min，氩气纯度在99.95％以上；
步骤302、焊接时的焊接规范参数为：
选用直径为2.4mm的9Cr-3W-3Co耐热钢条状焊丝进行手工氩弧焊时，电流设定为100～120A，电压设定为12～15V，预热温度≥100℃；选用直径为3.2mm的9Cr-3W-3Co耐热钢焊条进行手工电弧焊时，电流设定为90～120A，电压设定为22～26V，预热温度≥200℃；选用直径为4.0mm的9Cr-3W-3Co耐热钢焊条进行手工电弧焊时，电流设定为160～170A，电压设定为22～27V，预热温度≥200℃；
步骤303、采用手工电弧焊焊接过程中，采用多层多道焊，每一道焊完后彻底清除焊渣后进行下一道焊接，用砂轮打磨，施焊过程中控制层间温度不超过300℃；采用手工电弧焊时，焊接摆动幅度不超过焊条焊芯直径的3倍；
步骤4、对接环缝焊后采用760～780℃×7h的热处理规范。
CN201610998356.8A 2016-11-14 2016-11-14 锅炉管道用g115钢的焊接工艺 Active CN106670738B (zh)