CN106284919A - Plastic floor - Google Patents
Plastic floor Download PDFInfo
- Publication number
- CN106284919A CN106284919A CN201610726665.XA CN201610726665A CN106284919A CN 106284919 A CN106284919 A CN 106284919A CN 201610726665 A CN201610726665 A CN 201610726665A CN 106284919 A CN106284919 A CN 106284919A
- Authority
- CN
- China
- Prior art keywords
- opp film
- layer
- binder layer
- parts
- plastic floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of plastic floor, including the wearing layer set gradually from top to bottom, printing film, binder layer and OPP film layer, is coated with silicone oil between described binder layer and described OPP film layer.Plastic floor of the present invention, arranges OPP film layer in the side of binder layer, avoids it to sustain damage in transport and storing process with the protection group bed of material.Between binder layer and OPP film layer, it is coated with silicone oil so that the adhesive force on OPP film surface reduces, it is easier to peel off OPP film layer, reduces spoilage when OPP film is peeled off, thus improve the repeat usage of OPP film, and then reduce production cost.
Description
Technical field
The present invention relates to technical field of floor, particularly relate to a kind of plastic floor.
Background technology
Plastic floor i.e. PVC floor, it is mainly composed of pvc material.PVC floor is enriched due to its pattern,
Color is various and is widely used in each side of house and business.Plastic floor is that in the world today, popular one is novel
Light body floor decorative material, also referred to as " light body ground material ", be a kind of product very popular in American-European and Asia Japan and Korea S, fashionable
Abroad, initially entering Chinese market from the beginning of the eighties, big and medium-sized cities the most at home have obtained universal accreditation, use non-
Often extensively, the various fields such as such as indoor family, hospital, school, office building, factory, public place, supermarket, business, stadiums
Institute.
In existing plastic floor, in order to control expansion rate and the shrinkage factor of product, add substantial amounts of inorganic filler (carbonic acid
Calcium), but add substantial amounts of inorganic filler and can bring new problem: and along with the increase of inorganic flavoring agent, the density of product, hardness are also
Meeting is along with increase, and toughness can decline, then the edge of product easily becomes fragile, and easily causes damage during transport.To this end,
For the product that hardness is higher, outside the binder layer of plastic floor, one layer of OPP film of increase is as protective layer, to transport and to deposit
During storage, binder layer is played certain protective effect.During use, this OPP film layer needs to be stripped.But, existing product
In product, the cohesive between binder layer and OPP film layer is preferable, therefore, when peeling off OPP film, is not easily stripped, is easily damaged OPP
Film, the OPP film of damage can not reuse, and adds production cost.
Summary of the invention
The invention aims to solve the above-mentioned problems in the prior art, it is provided that a kind of plastic floor, make OPP
Film layer is easily peeled off, and improves the repeat usage of OPP film, and then reduces production cost.
In order to achieve the above object, the present invention provides a kind of plastic floor, including the wearing layer set gradually from top to bottom,
Printing film, binder layer and OPP film layer, be coated with silicone oil between described binder layer and described OPP film layer.At binder layer and OPP
Silicone oil it is coated with so that the adhesive force on OPP film surface reduces, it is easier to peel off OPP film layer between film layer.
In one embodiment of the invention, described binder layer is made up of the raw material of following weight portion: polrvinyl chloride 100-110
Part, DOTP 35-45 part, calcium-zinc composite stabilizing agent 1.5-2.5 part, white carbon black 0.2-0.5 part, calcium carbonate 450-
470 parts.Adjusting the component formula of binder layer so that contractibility declines, hardness improves, so that OPP film during hot pressing
Shrinkage factor reduces so that the OPP film after stripping is hardly damaged, and can be used repeatedly.
In one embodiment of the invention, described binder layer is made up of the raw material of following weight portion: polrvinyl chloride 100 parts, right
Dioctyl phthalate 35 parts, calcium-zinc composite stabilizing agent 1.5 parts, white carbon black 0.2 part, calcium carbonate 450 parts.
In one embodiment of the invention, described binder layer is made up of the raw material of following weight portion: polrvinyl chloride 105 parts, right
Dioctyl phthalate 40 parts, calcium-zinc composite stabilizing agent 2 parts, white carbon black 0.4 part, calcium carbonate 460 parts.
In one embodiment of the invention, described binder layer is made up of the raw material of following weight portion: polrvinyl chloride 110 parts, right
Dioctyl phthalate 45 parts, calcium-zinc composite stabilizing agent 2.5 parts, white carbon black 0.5 part, calcium carbonate 470 parts.
In one embodiment of the invention, the coating thickness of described silicone oil is 0.001-0.002mm.The silicone oil of this thickness makes
OPP film layer and cohesive between binder layer less, OPP film is more easily peelable.
In one embodiment of the invention, the density of described OPP film layer is 0.95-1.0g/cm3.The OPP film layer of existing product
Usually 1.4g/cm3Left and right, in the present invention, the density of OPP film layer reduces, so that its surface stickiness declines, thus more
Add and beneficially peel off.
Compared with prior art, the technical program provides the benefit that:
Plastic floor of the present invention, arranges OPP film layer in the side of binder layer, avoids it in transport and to deposit with the protection group bed of material
Sustain damage during storage.Silicone oil it is coated with so that the adhesive force on OPP film surface reduces, and more holds between binder layer and OPP film layer
It is easily peeled OPP film layer, reduces spoilage when OPP film is peeled off, thus improve the repeat usage of OPP film, and then reduce
Production cost.
Additionally, adjust the component formula of binder layer so that contractibility declines, hardness improves, so that during hot pressing
The shrinkage factor of OPP film reduces so that the OPP film after stripping is hardly damaged, and can be used repeatedly, and is beneficial to reduce production cost.
Accompanying drawing explanation
Fig. 1 is the structural representation of plastic floor of the present invention.
Detailed description of the invention
Below in conjunction with the accompanying drawings, by specific embodiment, technical scheme is carried out clear, complete description.
Embodiment 1
A kind of plastic floor, including the wearing layer 1 set gradually from top to bottom, printing film 2, binder layer 3 and OPP film layer
5, it is coated with silicone oil 4 between described binder layer 3 and described OPP film layer 5.Described binder layer 3 is made up of the raw material of following weight portion:
Polrvinyl chloride 100 parts, DOTP 35 parts, calcium-zinc composite stabilizing agent 1.5 parts, white carbon black 0.2 part, calcium carbonate 450 parts.
Binder layer 3 is prepared by the following method: material pvc, DOTP, calcium-zinc composite stabilizing agent and white carbon black
Mix according to aforementioned proportion, add calcium carbonate after mix homogeneously and continue mixing, add in internal rubber mixer after mix homogeneously, close
It is 180 DEG C that enclosed rubber mixing machine controls temperature, discharging after banburying 5 minutes, regulates thickness, control slice temperature in open mill
Degree is 40 DEG C, and rolling out film i.e. can get binder layer 3.
The coating thickness of described silicone oil 4 is 0.001mm.
The density of described OPP film layer 5 is 0.95g/cm3。
Plastic floor is prepared by the following method: prepare wearing layer 1, printing film 2, binder layer 3 and OPP film layer 5 respectively,
At the coated on one side silicone oil 4 of OPP film layer 5, the most successively wearing layer 1, printing film 2, binder layer 3 and OPP film layer 5 are folded
Putting, OPP film layer 5 is coated with the one of silicone oil 4 facing to described binder layer 3.Hot pressing afterwards gets final product forming plastic cement floor, hot pressing temperature
Degree is 120 DEG C, and hot pressing time is 60 minutes.
Embodiment 2
A kind of plastic floor, including the wearing layer 1 set gradually from top to bottom, printing film 2, binder layer 3 and OPP film layer
5, it is coated with silicone oil 4 between described binder layer 3 and described OPP film layer 5.Described binder layer 3 is made up of the raw material of following weight portion:
Polrvinyl chloride 102 parts, DOTP 38 parts, calcium-zinc composite stabilizing agent 1.8 parts, white carbon black 0.3 part, calcium carbonate 455 parts.
Binder layer 3 is prepared by the following method: material pvc, DOTP, calcium-zinc composite stabilizing agent and white carbon black
Mix according to aforementioned proportion, add calcium carbonate after mix homogeneously and continue mixing, add in internal rubber mixer after mix homogeneously, close
It is 180 DEG C that enclosed rubber mixing machine controls temperature, discharging after banburying 5 minutes, regulates thickness, control slice temperature in open mill
Degree is 40 DEG C, and rolling out film i.e. can get binder layer 3.
The coating thickness of described silicone oil 4 is 0.002mm.
The density of described OPP film layer 5 is 1.0g/cm3。
Plastic floor is prepared by the following method: prepare wearing layer 1, printing film 2, binder layer 3 and OPP film layer 5 respectively,
At the coated on one side silicone oil 4 of OPP film layer 5, the most successively wearing layer 1, printing film 2, binder layer 3 and OPP film layer 5 are folded
Putting, OPP film layer 5 is coated with the one of silicone oil 4 facing to described binder layer 3.Hot pressing afterwards gets final product forming plastic cement floor, hot pressing temperature
Degree is 120 DEG C, and hot pressing time is 60 minutes.
Embodiment 3
A kind of plastic floor, including the wearing layer 1 set gradually from top to bottom, printing film 2, binder layer 3 and OPP film layer
5, it is coated with silicone oil 4 between described binder layer 3 and described OPP film layer 5.Described binder layer 3 is made up of the raw material of following weight portion:
Polrvinyl chloride 105 parts, DOTP 40 parts, calcium-zinc composite stabilizing agent 2 parts, white carbon black 0.4 part, calcium carbonate 460 parts.Base
The bed of material 3 is prepared by the following method: material pvc, DOTP, calcium-zinc composite stabilizing agent and white carbon black are pressed
Mix according to aforementioned proportion, add calcium carbonate after mix homogeneously and continue mixing, add in internal rubber mixer after mix homogeneously, airtight
It is 180 DEG C that formula rubber mixing machine controls temperature, discharging after banburying 5 minutes, regulates thickness, control slice temperature in open mill
It is 40 DEG C, rolling out film, i.e. can get binder layer 3.
The coating thickness of described silicone oil 4 is 0.002mm.
The density of described OPP film layer 5 is 0.98g/cm3。
Plastic floor is prepared by the following method: prepare wearing layer 1, printing film 2, binder layer 3 and OPP film layer 5 respectively,
At the coated on one side silicone oil 4 of OPP film layer 5, the most successively wearing layer 1, printing film 2, binder layer 3 and OPP film layer 5 are folded
Putting, OPP film layer 5 is coated with the one of silicone oil 4 facing to described binder layer 3.Hot pressing afterwards gets final product forming plastic cement floor, hot pressing temperature
Degree is 120 DEG C, and hot pressing time is 60 minutes.
Embodiment 4
A kind of plastic floor, including the wearing layer 1 set gradually from top to bottom, printing film 2, binder layer 3 and OPP film layer
5, it is coated with silicone oil 4 between described binder layer 3 and described OPP film layer 5.Described binder layer 3 is made up of the raw material of following weight portion:
Polrvinyl chloride 108 parts, DOTP 42 parts, calcium-zinc composite stabilizing agent 2.2 parts, white carbon black 0.5 part, calcium carbonate 465 parts.
Binder layer 3 is prepared by the following method: material pvc, DOTP, calcium-zinc composite stabilizing agent and white carbon black
Mix according to aforementioned proportion, add calcium carbonate after mix homogeneously and continue mixing, add in internal rubber mixer after mix homogeneously, close
It is 180 DEG C that enclosed rubber mixing machine controls temperature, discharging after banburying 5 minutes, regulates thickness, control slice temperature in open mill
Degree is 40 DEG C, and rolling out film i.e. can get binder layer 3.
The coating thickness of described silicone oil 4 is 0.001mm.
The density of described OPP film layer 5 is 0.98g/cm3。
Plastic floor is prepared by the following method: prepare wearing layer 1, printing film 2, binder layer 3 and OPP film layer 5 respectively,
At the coated on one side silicone oil 4 of OPP film layer 5, the most successively wearing layer 1, printing film 2, binder layer 3 and OPP film layer 5 are folded
Putting, OPP film layer 5 is coated with the one of silicone oil 4 facing to described binder layer 3.Hot pressing afterwards gets final product forming plastic cement floor, hot pressing temperature
Degree is 120 DEG C, and hot pressing time is 60 minutes.
Embodiment 5
A kind of plastic floor, including the wearing layer 1 set gradually from top to bottom, printing film 2, binder layer 3 and OPP film layer
5, it is coated with silicone oil 4 between described binder layer 3 and described OPP film layer 5.Described binder layer 3 is made up of the raw material of following weight portion:
Polrvinyl chloride 110 parts, DOTP 45 parts, calcium-zinc composite stabilizing agent 2.5 parts, white carbon black 0.5 part, calcium carbonate 470 parts.
Binder layer 3 is prepared by the following method: material pvc, DOTP, calcium-zinc composite stabilizing agent and white carbon black
Mix according to aforementioned proportion, add calcium carbonate after mix homogeneously and continue mixing, add in internal rubber mixer after mix homogeneously, close
It is 180 DEG C that enclosed rubber mixing machine controls temperature, discharging after banburying 5 minutes, regulates thickness, control slice temperature in open mill
Degree is 40 DEG C, and rolling out film i.e. can get binder layer 3.
The coating thickness of described silicone oil 4 is 0.002mm.
The density of described OPP film layer 5 is 0.98g/cm3。
Plastic floor is prepared by the following method: prepare wearing layer 1, printing film 2, binder layer 3 and OPP film layer 5 respectively,
At the coated on one side silicone oil 4 of OPP film layer 5, the most successively wearing layer 1, printing film 2, binder layer 3 and OPP film layer 5 are folded
Putting, OPP film layer 5 is coated with the one of silicone oil 4 facing to described binder layer 3.Hot pressing afterwards gets final product forming plastic cement floor, hot pressing temperature
Degree is 120 DEG C, and hot pressing time is 60 minutes.
The detection shrinkage factor of plastic floor of embodiment 1-5, hardness and OPP film shrinkage factor, the peeling effect of OPP film layer 5.
The shrinkage factor of plastic floor: use precision high temperature roaster HQ-WG-550 to be measured.
The hardness of plastic floor: use Shore durometer SLX-D to be measured.
The shrinkage factor of OPP film: OPP film is carried out hot pressing 20 times, uses vulcanizing press (XLB-D) to measure the receipts of OPP film
Shrinkage.
The peeling effect of OPP film: manual removal OPP film, observes the damaged condition of OPP film.
Testing result is as shown in table 1.
Table 1
Plastic floor yield of the present invention is relatively low, and hardness is higher, has preferably serviceability.
The OPP film of existing product is not easily stripped, fragile, and OPP film is more serious through 20 hot pressing after-contraction, shrinkage factor
It is about 1.0%;The average service rate of OPP film is 14 times/.And the plastic floor of the present invention, OPP film is easily peeled, and is hardly damaged,
OPP film is less through 20 hot pressing after-contraction, and shrinkage factor is about 0.8%, and the average service rate of OPP film is 20 times/, relative to
The service life of existing product OPP film is greatly improved, such that it is able to effectively control material cost.
Although the present invention is open as above with preferred embodiment, but it is not for limiting the present invention, any this area
Technical staff without departing from the spirit and scope of the present invention, may be by the method for the disclosure above and technology contents to this
Bright technical scheme makes possible variation and amendment, therefore, every content without departing from technical solution of the present invention, according to the present invention
Technical spirit any simple modification, equivalent variations and modification that above example is made, belong to technical solution of the present invention
Protection domain.
Claims (7)
1. a plastic floor, it is characterised in that the wearing layer that includes setting gradually from top to bottom, printing film, binder layer and
OPP film layer, is coated with silicone oil between described binder layer and described OPP film layer.
Plastic floor the most according to claim 1, it is characterised in that described binder layer is by the raw material system of following weight portion
Become: polrvinyl chloride 100-110 part, DOTP 35-45 part, calcium-zinc composite stabilizing agent 1.5-2.5 part, white carbon black 0.2-
0.5 part, calcium carbonate 450-470 part.
Plastic floor the most according to claim 2, it is characterised in that described binder layer is by the raw material system of following weight portion
Become: polrvinyl chloride 100 parts, DOTP 35 parts, calcium-zinc composite stabilizing agent 1.5 parts, white carbon black 0.2 part, calcium carbonate 450
Part.
Plastic floor the most according to claim 2, it is characterised in that described binder layer is by the raw material system of following weight portion
Become: polrvinyl chloride 105 parts, DOTP 40 parts, calcium-zinc composite stabilizing agent 2 parts, white carbon black 0.4 part, calcium carbonate 460
Part.
Plastic floor the most according to claim 2, it is characterised in that described binder layer is by the raw material system of following weight portion
Become: polrvinyl chloride 110 parts, DOTP 45 parts, calcium-zinc composite stabilizing agent 2.5 parts, white carbon black 0.5 part, calcium carbonate 470
Part.
Plastic floor the most according to claim 1, it is characterised in that the coating thickness of described silicone oil is 0.001-
0.002mm。
Plastic floor the most according to claim 1, it is characterised in that the density of described OPP film layer is 0.95-1.0g/cm3。